Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement

Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement

SCOPE
1.1 This practice covers the technical training and experience of laboratory testing personnel and identifies the minimum technical requirements for laboratory equipment used in testing of hydraulic cement as prescribed by ASTM.
1.2 This practice provides minimum criteria for evaluating the capability of a laboratory to perform chemical or physical tests listed in the various specifications on hydraulic cement (see Note 1).
Note 1— Relevant hydraulic cement specifications are Specifications C 91, C 150, C 595, C 845, and Performance Specification C 1157.
1.3 The SI units are to be regarded as the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Jun-2005
ICS
71.040.10 - Chemical laboratories. Laboratory equipment
91.100.10 - Cement. Gypsum. Lime. Mortar
Technical Committee
C01 - Cement
Drafting Committee
C01.95 - Coordination of Standards
Current Stage
Ref Project

Relations

Replaces
ASTM C1222-03 - Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement
Effective Date
01-Jul-2005
Replaced By
ASTM C1222-05a - Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement
Effective Date
01-Nov-2005

Buy Standard

ASTM C1222-05 - Standard Practice for Evaluation of Laboratories Testing Hydraulic CementASTM C1222-05 - Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement
PreviousNext
Standard
ASTM C1222-05 - Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:C1222–05
Standard Practice for
1
Evaluation of Laboratories Testing Hydraulic Cement
This standard is issued under the fixed designation C 1222; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope C 185 Test Method for Air Content of Hydraulic Cement
Mortar
1.1 This practice covers the technical training and experi-
C 187 Test Method for Normal Consistency of Hydraulic
ence of laboratory testing personnel and identifies the mini-
Cement
mum technical requirements for laboratory equipment used in
C 191 Test Method for Time of Setting of Hydraulic Ce-
testing of hydraulic cement as prescribed by ASTM.
ment by Vicat Needle
1.2 This practice provides minimum criteria for evaluating
C 204 Test Method for Fineness of Hydraulic Cement by
the capability of a laboratory to perform chemical or physical
Air Permeability Apparatus
tests listed in the various specifications on hydraulic cement
C 219 Terminology Relating to Hydraulic Cement
(see Note 1).
C 230 Specification for Flow Table for Use in Tests of
NOTE 1—Relevant hydraulic cement specifications are Specifications
Hydraulic Cement
C91, C 150, C 595, C 845, and Performance Specification C 1157.
C 266 Test Method for Time of Setting of Hydraulic-
1.3 The SI units are to be regarded as the standard.
Cement Paste by Gillmore Needles
1.4 This standard does not purport to address all of the
C 305 PracticeforMechanicalMixingofHydraulicCement
safety concerns, if any, associated with its use. It is the
Pastes and Mortars of Plastic Consistency
responsibility of the user of this standard to establish appro-
C 451 Test Method for Early Stiffening of Portland Cement
priate safety and health practices and determine the applica-
(Paste Method)
bility of regulatory limitations prior to use.
C 595 Specification for Blended Hydraulic Cements
C 778 Specification for Standard Sand
2. Referenced Documents
C 845 Specification for Expansive Hydraulic Cement
2
2.1 ASTM Standards:
C 1157 Performance Specification for Blended Hydraulic
C91 Specification for Masonry Cement
Cement
C 109/C 109M Test Method for Compressive Strength of
E4 Practices for Force Verification of Testing Machines
Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube
2.2 Other Documents:
3
Specimens)
ACI 116R Cement and Concrete Terminology
C114 Test Methods for Chemical Analysis of Hydraulic
3. Terminology
Cement
C115 Test Method for Fineness of Portland Cement by the
3.1 Definitions:
Turbidimeter
3.1.1 inspection, n—a process of measuring, examining,
C 125 Terminology Relating to Concrete and Concrete
testing, gaging, or using other procedures to ascertain the
Aggregates
quality or state, detect errors or defects, or otherwise appraise
C 150 Specification for Portland Cement
materials, products, services, systems, or environments when
C 151 Test Method for Autoclave Expansion of Portland
compared to preestablished criteria.
Cement
3.1.2 Additional definitions may be found in Terminologies
C 125 and C 219, PracticesE4, and ACI 116R.
1 3.2 Definitions of Terms Specific to This Standard:
This practice is under the jurisdiction ofASTM Committee C01 on Cement and
is the direct responsibility of Subcommittee C01.95 on Coordination of Standards. 3.2.1 evaluation authority, n—an independent entity, apart
Current edition approved July 1, 2005. Published July 2005. Originally approved
from the organization being evaluated, that can provide an
in 1991. Last previous edition approved in 2003 as C 1222 – 03.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
3
Standards volume information, refer to the standard’s Document Summary page on Available fromAmerican Concrete Institute (ACI), P.O. Box 9094, Farmington
the ASTM website. Hills, MI 48333.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
C1222–05
unbiased evaluation of the organization and shall have the 6. Human Resources
capability to assess the technical activities of testing laborato-
6.1 The manager of the laboratory shall be a chemist,
ries (see Discussion).
materials analyst, or an engineer and a full-time employee of
3.2.1.1 Discussion—One such evaluation authority is the
the organization having at least three years supervisory expe-
4
Cement and Concrete Reference Laboratory (CCRL). Labo-
rience in the testing of hydraulic cement; however, a person
ratory inspection is broadened into accreditation programs by
with equivalent scie
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1222-23(Practice)
Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 The testing of hydraulic cement is an important element in obtaining quality construction. A testing laboratory must be selected with care.  
4.2 A testing laboratory shall be deemed qualified to perform and report the results of its tests if the laboratory meets the requirements of this practice.  
4.3 This practice provides guidance for evaluating the organization, personnel, facilities, and quality systems of the laboratory. This practice may be supplemented by criteria and requirements for particular projects.
SCOPE
1.1 This practice covers the technical training and experience of laboratory testing personnel and identifies the minimum technical requirements for laboratory equipment used in testing of hydraulic cement as prescribed by ASTM.  
1.2 This practice provides minimum criteria for evaluating the capability of a laboratory to perform chemical or physical tests listed in the various specifications on hydraulic cement (see Note 1).  
Note 1: Relevant hydraulic cement specifications are Specifications C91/C91M, C150/C150M, C595/C595M, C845/C845M, and C1157/C1157M.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C1222-23(Practice)
Standard Practice for Evaluation of Laboratories Testing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 The testing of hydraulic cement is an important element in obtaining quality construction. A testing laboratory must be selected with care.  
4.2 A testing laboratory shall be deemed qualified to perform and report the results of its tests if the laboratory meets the requirements of this practice.  
4.3 This practice provides guidance for evaluating the organization, personnel, facilities, and quality systems of the laboratory. This practice may be supplemented by criteria and requirements for particular projects.
SCOPE
1.1 This practice covers the technical training and experience of laboratory testing personnel and identifies the minimum technical requirements for laboratory equipment used in testing of hydraulic cement as prescribed by ASTM.  
1.2 This practice provides minimum criteria for evaluating the capability of a laboratory to perform chemical or physical tests listed in the various specifications on hydraulic cement (see Note 1).  
Note 1: Relevant hydraulic cement specifications are Specifications C91/C91M, C150/C150M, C595/C595M, C845/C845M, and C1157/C1157M.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM F1210-23(Guide)
Standard Guide for Ecological Considerations for the Use of Oil Spill Dispersants in Freshwater and Other Inland Environments, Lakes and Large Water Bodies

SIGNIFICANCE AND USE
3.1 This guide is meant to aid response teams who may use it during spill response planning and spill events.  
3.2 This guide should be adapted to site specific circumstance.
SCOPE
1.1 This guide covers the use of oil spill dispersants to assist in the control of oil spills. The guide is written with the goal of minimizing the environmental impacts of oil spills; this goal is the basis on which the recommendations are made. Aesthetic and socioeconomic factors are not considered, although these and other factors are often important in spill response.  
1.2 Spill responders have available several means to control or clean up spilled oil. Chemical dispersants should be given equal consideration with other spill countermeasures.  
1.3 This is a general guide only. Oil, as used in this guide, includes crude oils and refined petroleum products. Differences between individual dispersants or between different oil products are not considered. The dispersibility of the oil with the chosen dispersant should be evaluated.  
1.4 The guide is organized by habitat type, for example, small ponds and lakes, rivers and streams, and land. It considers the use of dispersants primarily to protect habitats from impact (or to minimize impacts).  
1.5 This guide applies only to freshwater and other inland environments. It does not consider the direct application of dispersants to subsurface waters.  
1.6 In making dispersant use decisions, appropriate government authorities should be consulted as required by law.  
1.7 This guide does not address getting regulatory approval.  
1.8 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM C596-23(Test Method)
Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement

SIGNIFICANCE AND USE
4.1 This test method establishes a selected set of conditions of temperature, relative humidity and rate of evaporation of the environment to which a mortar specimen of stated composition shall be subjected for a specified period of time during which its change in length is determined and designated “drying shrinkage.”  
4.2 The drying shrinkage of mortar as determined by this test method has a linear relation to the drying shrinkage of concrete made with the same cement and exposed to the same drying conditions.4 Hence this test method may be used when it is desired to develop data on the effect of a hydraulic cement on the drying shrinkage of concrete made with that cement.
SCOPE
1.1 This test method determines the change in length on drying of mortar bars containing hydraulic cement and graded standard sand.  
1.2 The values stated in SI units are to be regarded as standard. When combined standards are referenced, the selection of measurement system is at the user’s discretion subject to the requirements of the referenced standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Warning—Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure).2  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1751-23(Specification)
Standard Specification for Preformed Expansion Joint Filler for Concrete Paving and Structural Construction (Nonextruding and Resilient Asphalt Types)

SCOPE
1.1 This specification covers preformed expansion joint filler having relatively little extrusion and substantial recovery after release from compression.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
Note 1: Attention is called to Specifications D1752 and D994/D994M.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM D8139-23(Specification)
Standard Specification for Semi-Rigid, Closed-Cell Polypropylene Foam, Preformed Expansion Joint Fillers for Concrete Paving and Structural Construction

SCOPE
1.1 This specification covers preformed expansion joint fillers made from closed-cell polypropylene foam materials having suitable compressibility, recovery from compression, nonextruding, and weather-resistant characteristics.  
1.1.1 Type I, closed-cell polypropylene foam.  
1.2 These joint fillers are intended for use in concrete pavements in full-depth joints. There are several variations in size with typical thicknesses of 1/2 in. (12.7 mm), 3/4 in. (19.05 mm), and 1 in. (25.4 mm); typical widths of 31/2 in. (88.9 mm), 4 in. (101.6 mm), 5 in. (127 mm), 6 in. (152.5 mm), 7 in. (177.8 mm), 8 in. (203.2 mm), or 48 in. (1.2 m) sheet; and typical lengths of 5 ft (1.52 m) and 10 ft (3.05 m).  
1.3 The values stated in inch-pound units are to be regarded as the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM F3337-23(Guide)
Standard Guide for Taking Property and Behavior Measurements on Weathered Fractions of Oil

SIGNIFICANCE AND USE
5.1 A standard procedure is necessary to establish property changes for spilled oils or petroleum products at different oil weathering stages.  
5.2 This procedure employs standardized equipment, and test procedures.  
5.3 This procedure should be performed at the stages of weathering corresponding to the spill conditions of interest.
SCOPE
1.1 This guide summarizes methods to fractionate oil by evaporative weathering and then measure the properties and behavior of the weathered oil. The results of this guide can provide oil behavior data for input into oil spill models and response method selection.  
1.2 This guide covers general procedures for oil weathering and behavior and does not cover all possible procedures which may be applicable to this topic.  
1.3 The results obtained using this guide are intended to provide baseline data for the behavior of oil and petroleum products when spilled and input to oil spill models.  
1.4 The results obtained using this guide can be used directly to predict certain facets of oil spill behavior or as input to oil spill models.  
1.5 The accuracy of the guide depends very much on the representative nature of the oil sample used. Certain oils can have different properties depending on their chemical contents at the moment a sample is taken.  
1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    4 pages
    English language
    sale 15% off
  • Guide
    4 pages
    English language
    sale 15% off
ASTM
ASTM D6390-23(Test Method)
Standard Test Method for Determination of Draindown Characteristics in Uncompacted Asphalt Mixtures

SIGNIFICANCE AND USE
5.1 This test method can be used to determine whether the amount of draindown measured for a given asphalt mixture is within specified acceptable levels. The test provides an evaluation of the draindown potential of an asphalt mixture during mixture design and/or during field production. This test is primarily used for mixtures with high coarse aggregate content such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the amount of draindown in an uncompacted asphalt mixture sample when the sample is held at elevated temperatures comparable to those encountered during the production, storage, transport, and placement of the mixture. The test is particularly applicable to mixtures such as porous asphalt (open-graded friction course) and stone matrix asphalt (SMA).  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM B472-23(Specification)
Standard Specification for Nickel Alloy Billets and Bars for Reforging

ABSTRACT
This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, and UNS R30556 nickel alloy billets and bars for reforging. The products shall be hot worked from ingots by rolling, forging, extruding, hammering, or pressing. The material shall conform to the chemical composition requirements prescribed by the reference material. The chemical composition of the material shall be determined by chemical analysis in accordance with test method E1473.
SCOPE
1.1 This specification covers UNS N06002, UNS N06030, UNS N06035, UNS N06022, UNS N06200, UNS N10362, UNS N06230, UNS N06600, UNS N06617, UNS N06625, UNS N08020, UNS N08026, UNS N08024, UNS N08120, UNS N08926, UNS N08367, UNS N10242, UNS N10276, UNS N10665, UNS N10675, UNS N12160, UNS R20033, UNS N06059, UNS N06686, UNS N10629, UNS N08031, UNS N06045, UNS N06025, UNS N06699, and UNS R305562 billets and bars for reforging.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off