ASTM C685/C685M-00a

Standard Specification for Concrete Made By Volumetric Batching and Continuous Mixing

SCOPE
1.1 This specification covers concrete made from materials continuously batched by volume, mixed in a continuous mixer, and delivered to the purchaser in a freshly mixed and unhardened state. Tests and criteria for batching accuracy and mixing efficiency are specified herein.
1.2 The values stated in either SI units, shown in brackets, or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.
1.3 This specification references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this specification.

General Information

• Status: Historical
• Publication Date: 09-Aug-2001
• ICS: 91.100.30 - Concrete and concrete products
• Technical Committee: C09 - Concrete and Concrete Aggregates
• Drafting Committee: C09.40 - Ready-Mixed Concrete

Relations

• Replaced By: ASTM C685/C685M-01 - Standard Specification for Concrete Made By Volumetric Batching and Continuous Mixing
• Effective Date: 10-Aug-2001
• Referred By: ASTM C1227-23 - Standard Specification for Precast Concrete Septic Tanks
• Effective Date: 10-Aug-2001
• Referred By: ASTM C1116/C1116M-23 - Standard Specification for Fiber-Reinforced Concrete
• Effective Date: 10-Aug-2001
• Referred By: ASTM C94/C94M-23 - Standard Specification for Ready-Mixed Concrete
• Effective Date: 10-Aug-2001
• Referred By: ASTM C1613-22 - Standard Specification for Precast Concrete Gravity Grease Interceptor Tanks
• Effective Date: 10-Aug-2001
• Referred By: ASTM F1090-15 - Standard Classification for Bank and Mercantile Vault Construction
• Effective Date: 10-Aug-2001
• Referred By: ASTM C172/C172M-17 - Standard Practice for Sampling Freshly Mixed Concrete
• Effective Date: 10-Aug-2001
• Referred By: ASTM C913-21 - Standard Specification for Precast Concrete Water and Wastewater Structures
• Effective Date: 10-Aug-2001

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: C 685/C 685M – 00a
Standard Specification for
Concrete Made by Volumetric Batching and Continuous
Mixing
This standard is issued under the fixed designation C 685/C 685M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope C 231 Test Method for Air Content of Freshly Mixed
Concrete by the Pressure Method
1.1 This specification covers concrete made from materials
C 260 Specification for Air-Entraining Admixtures for Con-
continuously batched by volume, mixed in a continuous mixer,
crete
and delivered to the purchaser in a freshly mixed and unhard-
C 330 Specification for Lightweight Aggregates for Struc-
ened state. Tests and criteria for batching accuracy and mixing
tural Concrete
efficiency are specified herein.
C 494 Specification for Chemical Admixtures for Concrete
1.2 The values stated in either SI units, shown in brackets,
C 567 Test Method for Unit Weight of Structural Light-
or inch-pound units are to be regarded separately as standard.
weight Concrete
The values stated in each system may not be exact equivalents;
C 595 Specifications for Blended Hydraulic Cements
therefore, each system shall be used independently of the other.
C 618 Specification for Coal Fly Ash and Raw or Calcined
Combining values from the two systems may result in noncon-
Natural Pozzolan for Use as a Mineral Admixture in
formance with the standard.
Portland Cement Concrete
1.3 This specification references notes and footnotes which
C 989 Specification for Ground Granulated Blast-Furnace
provide explanatory material. These notes and footnotes (ex-
Slag for Use in Concrete and Mortars
cluding those in tables and figures) shall not be considered as
C 1017/C 1017M Specification for Chemical Admixtures
requirements of this specification.
for Use in Producing Flowing Concrete
2. Referenced Documents C 1064 Test Method for Temperature of Freshly Mixed
Portland Cement Concrete
2.1 ASTM Standards:
C 1077 Practice for Laboratories Testing Concrete and Con-
C 31/C 31M Practice for Making and Curing Concrete Test
crete Aggregates for Use in Construction and Criteria for
Specimens in the Field
Laboratory Evaluation
C 33 Specification for Concrete Aggregates
C 1157 Performance Specification for Blended Hydraulic
C 39 Test Method for Compressive Strength of Cylindrical
Cement
Concrete Specimens
D 512 Test Methods for Chloride Ion in Water
C 109/C 109M Test Method for Compressive Strength of
D 516 Test Method for Sulfate Ion in Water
Hydraulic Cement Mortars (Using 2-in. or 50-mm Cube
2.2 ACI Documents:
Specimens)
CP-1 Technician Workbook for ACI Certification of Con-
C 138 Test Method for Unit Weight, Yield, and Air Content
crete Field Testing Technician-Grade I
(Gravimetric) of Concrete
211.1 Standard Practice for Selecting Proportions for Nor-
C 143/C 143M Test Method for Slump of Hydraulic Ce-
mal, Heavyweight, and Mass Concrete
ment Concrete
211.2 Standard Practice for Selecting Proportions for Struc-
C 150 Specification for Portland Cement
tural Lightweight Concrete
C 173 Test Method for Air Content of Freshly Mixed
214 Recommended Practice for Evaluation of Strength Test
Concrete by the Volumetric Method
Results of Concrete
C 191 Test Method for Time of Setting of Hydraulic Ce-
301 Standard Specifications for Structural Concrete
ment by Vicat Needle
305R Hot Weather Concreting
306R Cold Weather Concreting
This specification is under the jurisdiction of ASTM Committee C09 on
Concrete and Concrete Aggregates and is the direct responsibility of Subcommittee
C09.40 on Ready-Mixed Concrete.
Current edition approved Sept. 10, 2000. Published December 2000. Originally
published as C 685 – 71 T. Last previous edition C 685 – 00. Annual Book of ASTM Standards, Vol 11.01.
2 5
Annual Book of ASTM Standards, Vol 04.02. Available from the American Concrete Institute, 38800 Country Club Drive,
Annual Book of ASTM Standards, Vol 04.01. Farmington Hills, MI 48331.
Copyright © ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.
C 685/C 685M
318 Building Code Requirements for Structural Concrete 5.1.3 Water:
and Commentary 5.1.3.1 The mixing water shall be clear and apparently
2.3 Other Documents: clean. If it contains quantities of substances that discolor it or
Bureau of Reclamation Concrete Manual make it smell or taste unusual or objectionable, or cause
AASHTO T 26 Method of Test for Quality of Water to be suspicion, it shall not be used unless service records of
Used in Concrete concrete made with it (or other information) indicate that it is
not injurious to the quality of the concrete. Water of question-
3. Terminology
able quality shall be subject to the acceptance criteria of Table
1.
3.1 Definitions of Terms Specific to This Standard:
3.1.1 manufacturer, n—the contractor, subcontractor, sup- 5.1.3.2 Test results of wash water from mixer washout
operations to be used for mixing concrete shall comply with the
plier, or producer who furnishes the ready-mixed concrete.
3.1.2 purchaser, n—the owner, or representative thereof, physical test limits of Table 1. Wash water shall be tested at a
weekly interval for approximately 4 weeks, and thereafter at a
who buys the ready-mixed concrete.
monthly interval provided no single test exceeds the applicable
4. Basis of Purchase
limit (Note 3). Optional chemical limits in Table 2 shall be
specified by the purchaser when appropriate for the construc-
4.1 The basis of purchase shall be the cubic yard or cubic
tion. The testing frequency for chemical limits shall be as given
metre of plastic and unhardened concrete as it is continuously
above or as specified by the purchaser.
discharged from the batching and mixing apparatus.
NOTE 3—When recycled wash water is used, attention should be given
NOTE 1—It should be understood that the volume of hardened concrete
to effects on the dosage rate and batching sequence of air entraining and
may be, or may appear to be, less than expected due to waste and spillage,
other chemical admixtures and a uniform amount should be used in
over-excavation, spreading forms, some loss of entrained air, or settlement
consecutive batches.
of wet mixtures, none of which are the responsibility of the manufacturer.
5.1.4 Mineral Admixtures—Fly ash and raw or calcined
4.2 The volume of plastic and unhardened concrete shall be
3 3
natural pozzolan shall conform to Specification C 618 as
checked daily on projects requiring more than 50 yd [40 m ]
applicable.
of concrete per day (see 7.4). The amount of various ingredi-
5.1.5 Ground Granulated Blast-Furnace Slag—Ground
ents (cement, fine and coarse aggregate, admixtures, and water)
granulated blast furnace slag shall conform to Specification
shall be checked as required in 7.5.
C 989.
4.3 The manufacturer of the concrete shall conduct calibra-
5.1.6 Air-Entraining Admixtures—Air-entraining admix-
tion and mixer efficiency tests at intervals not exceeding 6
tures shall conform to Specification C 260. (Note 4)
months. Data on such tests using materials proposed for use in
5.1.7 Chemical Admixtures—Chemical admixtures shall
the project shall be furnished the purchaser upon request.
conform to either Specification C 494 or C 1017/C 1017M, as
5. Materials
applicable (Note 4).
5.1 In the absence of designated applicable specifications
NOTE 4—In any given instance, the required dosage of air-entraining,
covering requirements for quality of materials, the following
accelerating, and retarding admixtures may vary. Therefore, a range of
specifications shall govern: dosages should be allowed which will permit obtaining the desired effect.
5.1.1 Cement—Cement shall conform to Specification
6. Ordering Information
C 150, Specification C 595, or Specification C 1157 (Note 2).
6.1 In the absence of designated applicable general specifi-
The purchaser shall specify the type or types required, but if no
type is specified, the requirements of Type I as prescribed in cations, the purchaser shall specify the following:
6.1.1 Designated size or sizes of coarse aggregate,
Specification C 150 shall apply.
6.1.2 Slump or slumps desired at the point of delivery (see
NOTE 2—These different cements will produce concretes of different
10.3),
properties and should not be used interchangeably.
6.1.3 When air-entrained concrete is specified, the air con-
5.1.2 Aggregates—Aggregates shall conform to Specifica-
tent of samples taken at the point of discharge from the
tion C 33 or Specification C 330 if lightweight concrete is
transportation unit (see 10.4 and Table 3 for the total air content
specified by the purchaser.
and tolerances) (Note 5),
6.1.4 When structural lightweight concrete is specified, the
density as fresh density, equilibrium density, or oven-dry
Available from Superintendent of Documents, U.S. Government Printing
density (Note 6), and
Office, Washington, DC 20402.
6.1.5 Which of Options A, B, or C shall be used as a basis
Available from the American Association of State Highway and Transportation
for determining the proportions of the concrete to produce the
Officials, 444 N. Capitol St., NW, Suite 225, Washington, DC 20001.
TABLE 1 Acceptance Criteria for Questionable Water Supplies
Limits Test Method
A
Compressive strength, min, % control at 7 days 90 C 109/C 109M
A
Time of set, deviation from control from 1:00 earlier to 1:30 later C 191
A
Comparisons shall be based on fixed proportions and the same volume of test water compared to control mix using city water or distilled water.
C 685/C 685M
TABLE 2 Optional Chemical Limits for Wash Water
A
Limits Test Method
Chemical requirements, maximum concentration in mixing water,
B
ppm
Chloride as C1, ppm: D 512
C
Prestressed concrete or in bridge decks 500
C
Other reinforced concrete in moist environments or containing 1000
aluminum embedments or dissimilar metals or with stay-in-place
galvanized metal forms
Sulfate as SO , ppm 3000 D 516
Alkalies as (Na O + 0.658 K O), ppm 600
2 2
Total solids, ppm 50 000 AASHTO T26
A
Other test methods that have been demonstrated to yield comparable results are permitted to be used.
B
Wash water reused as mixing water in concrete is allowed to exceed the listed concentrations if it can be shown that the concentration calculated in the total mixing
water, including mixing water on the aggregates and other sources does not exceed the stated limits.
C
For conditions allowing use of CaCl accelerator as an admixture, the chloride limitation is permitted to be waived by the purchaser.
A
TABLE 3 Recommended Total Air Content for Air-Entrained Concrete
Total Air Content, %
B,C
Exposure Condition Nominal Max Sizes of Aggregate, in. [mm]
3 1 3 1
⁄8 [9.5] ⁄2 [12.5] ⁄4 [19.0] 1 [25.0] 1 ⁄2 [37.5] 2 [50.0] 3 [75.0]
Mild 4.5 4.0 3.5 3.0 2.5 2.0 1.5
Moderate 6.0 5.5 5.0 4.5 4.5 4.0 3.5
Severe 7.5 7.0 6.0 6.0 5.5 5.0 4.5
A
For air-entrained concrete, when specified.
B
For description of exposure conditions, refer to ACI Standard Practice 211.1, Section 6.3.3 with attention to accompanying footnotes.
C
Unless exposure conditions dictate otherwise, it is permissable to reduce air contents recommended above by up to 1 % for concretes with specified compressive
strength, f 8 , of 5000 psi [35 MPa] or above.
c
required quality (see 6.2, 6.3, or 6.4). purchaser that the materials to be used and proportions selected
will produce concrete of the quality specified.
NOTE 5—In selecting the specified air content, the purchaser should
6.3 Option B:
consider the exposure conditions to which the concrete will be subjected.
6.3.1 When the purchaser assumes responsibility for the
Air contents less than shown in Table 3 may not give the required
proportioning of the concrete mixture, the purchaser shall also
resistance to freezing and thawing, which is the primary purpose of
air-entrained concrete. Air contents higher than the levels shown may
specify the following in addition to the requirements of 6.1.1
reduce strength without contributing any further improvement of durabil-
through 6.1.5:
ity.
6.3.1.1 Cement content in bags or pounds per cubic yard or
NOTE 6—The density of fresh concrete, which is the only density
kilograms per cubic metre of concrete, or equivalent units,
determinable at the time of delivery, is always higher than the equilibrium
6.3.1.2 Maximum allowable water content in gallons per
density, or oven-dry density. Definitions of, and methods for determining
cubic yard or litres or kilograms per cubic metre of concrete or
or calculating equilibrium density and oven-dry density, are covered in
equivalent units, including surface moisture on the aggregates,
Test Method C 567.
but excluding water of absorption (Note 7), and
6.2 Option A:
6.3.1.3 If admixtures are required, the type, name, and
6.2.1 When the purchaser requires the manufacturer to
dosage range to be used. Those employed for air-entrainment
assume full responsibility for the selection of the proportions
or for control of set (acceleration, retardation) shall have
for the concrete mixture, the purchaser shall also specify the
maximum limitations set as to dosage. Admixtures shall not be
following in addition to the requirements of 6.1.1 through
used as a substitute for a portion of specified amounts of
6.1.5:
cement without the written approval of the purchaser.
6.2.1.1 Requirements for compressive strength as deter-
mined on samples taken from the mixer at the point of NOTE 7—The purchaser, in selecting requirements for which he as-
sumes responsibility should give consideration to requirements for work-
discharge and evaluated in accordance with Section 11. The
ability, placeability, durability, surface texture, and density, in addition to
purchaser shall specify the requirements in terms of the
those for structural design. The purchaser is referred to ACI Standard
compressive strength of standard specimens cured under stan-
Practice 211.1 for normal weight concrete, and ACI Standard Practice
dard curing conditions for moist curing. Unless otherwise
211.2 for lightweight concrete, for the selection of proportions that will
specified, the age at test shall be 28 days, and
result in concrete suitable for various types of structures and conditions of
6.2.2 At the request of the purchaser, the manufacturer shall,
exposure. The water-cement ratio of most structural lightweight concretes
prior to the actual delivery of the concrete, furnish a statement cannot be deter
...