ASTM C518-02

(Test Method)

Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter Apparatus

Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter Apparatus

SCOPE
1.1 This test method covers the measurement of steady state thermal transmission through flat slab specimens using a heat flow meter apparatus.
1.2 The heat flow meter apparatus is used widely because it is relatively simple in concept, rapid, and applicable to a wide range of test specimens. The precision and bias of the heat flow meter apparatus can be excellent provided calibration is carried out within the range of heat flows expected. This means calibration shall be carried out with similar types of materials, of similar thermal conductances, at similar thicknesses, mean temperatures, and temperature gradients, as expected for the test specimens.
1.3 This a comparative, or secondary, method of measurement since specimens of known thermal transmission properties shall be used to calibrate the apparatus. Properties of the calibration specimens must be traceable to an absolute measurement method. The calibration specimens should be obtained from a recognized national standards laboratory.
1.4 The heat flow meter apparatus establishes steady state one-dimensional heat flux through a test specimen between two parallel plates at constant but different temperatures. By appropriate calibration of the heat flux transducer(s) with calibration standards and by measurement of the plate temperatures and plate separation. Fourier's law of heat conduction is used to calculate thermal conductivity, and thermal resistivity or thermal resistance and thermal conductance.
1.5 This test method shall be used in conjunction with Practice C 1045. Many advances have been made in thermal technology, both in measurement techniques and in improved understanding of the principles of heat flow through materials. These advances have prompted revisions in the conceptual approaches to the measurement of the thermal transmission properties (1-4). All users of this test method should be aware of these concepts.
1.6 This test method is applicable to the measurement of thermal transmission through a wide range of specimen properties and environmental conditions. The method has been used at ambient conditions of 10 to 40°C with thicknesses up to approximately 250 mm, and with plate temperatures from- 195°C to 540°C at 25-mm thickness (5, 6).
1.7 This test method may be used to characterize material properties, which may or may not be representative of actual conditions of use. Other test methods, such as Test Methods C 236 or C 976 should be used if needed.
1.8 To meet the requirements of this test method the thermal resistance of the test specimen shall be greater than 0.10 m 2K/W in the direction of the heat flow and edge heat losses shall be controlled, using edge insulation, or a guard heater, or both.
1.9 It is not practical in a test method of this type to try to establish details of construction and procedures to cover all contingencies that might offer difficulties to a person without pertinent technical knowledge. Thus users of this test method shall have sufficient knowledge to satisfactorily fulfill their needs. For example, knowledge of heat transfer principles, low level electrical measurements, and general test procedures is required.
1.10 Standardization of this test method is not intended to restrict in any way the future development of improved or new methods or procedures by research workers.
1.11 Since the design of a heat flow meter apparatus is not a simple matter, a procedure for proving the performance of an apparatus is given in Appendix X3.
1.12 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to consult and establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Sep-2002
ICS
91.120.10 - Thermal insulation of buildings
Technical Committee
C16 - Thermal Insulation
Drafting Committee
C16.30 - Thermal Measurement
Current Stage
Ref Project

Relations

Replaced By
ASTM C518-02e1 - Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter Apparatus
Effective Date
10-Sep-2002

Buy Standard

ASTM C518-02 - Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter ApparatusASTM C518-02 - Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter Apparatus
PreviousNext
Standard
ASTM C518-02 - Standard Test Method for Steady-State Thermal Transmission Properties by Means of the Heat Flow Meter Apparatus
English language
14 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

Designation: C 518 – 02
Standard Test Method for
Steady-State Thermal Transmission Properties by Means of
1
the Heat Flow Meter Apparatus
This standard is issued under the fixed designation C 518; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope thermal transmission through a wide range of specimen prop-
erties and environmental conditions. The method has been used
1.1 This test method covers the measurement of steady state
at ambient conditions of 10 to 40°C with thicknesses up to
thermal transmission through flat slab specimens using a heat
approximately 250 mm, and with plate temperatures from–
flow meter apparatus.
195°C to 540°C at 25-mm thickness (5, 6).
1.2 The heat flow meter apparatus is used widely because it
1.7 This test method may be used to characterize material
is relatively simple in concept, rapid, and applicable to a wide
properties, which may or may not be representative of actual
range of test specimens. The precision and bias of the heat flow
conditions of use. Other test methods, such as Test Methods
meter apparatus can be excellent provided calibration is carried
C 236 or C 976 should be used if needed.
out within the range of heat flows expected. This means
1.8 To meet the requirements of this test method the thermal
calibration shall be carried out with similar types of materials,
resistance of the test specimen shall be greater than 0.10
of similar thermal conductances, at similar thicknesses, mean
2
m ·K/W in the direction of the heat flow and edge heat losses
temperatures, and temperature gradients, as expected for the
shall be controlled, using edge insulation, or a guard heater, or
test specimens.
both.
1.3 This a comparative, or secondary, method of measure-
1.9 It is not practical in a test method of this type to try to
ment since specimens of known thermal transmission proper-
establish details of construction and procedures to cover all
ties shall be used to calibrate the apparatus. Properties of the
contingencies that might offer difficulties to a person without
calibration specimens must be traceable to an absolute mea-
pertinent technical knowledge. Thus users of this test method
surement method. The calibration specimens should be ob-
shall have sufficient knowledge to satisfactorily fulfill their
tained from a recognized national standards laboratory.
needs. For example, knowledge of heat transfer principles, low
1.4 The heat flow meter apparatus establishes steady state
level electrical measurements, and general test procedures is
one-dimensional heat flux through a test specimen between two
required.
parallel plates at constant but different temperatures. By
1.10 Standardization of this test method is not intended to
appropriate calibration of the heat flux transducer(s) with
restrict in any way the future development of improved or new
calibration standards and by measurement of the plate tempera-
methods or procedures by research workers.
tures and plate separation. Fourier’s law of heat conduction is
1.11 Since the design of a heat flow meter apparatus is not
used to calculate thermal conductivity, and thermal resistivity
a simple matter, a procedure for proving the performance of an
or thermal resistance and thermal conductance.
apparatus is given in Appendix X3.
1.5 This test method shall be used in conjunction with
1.12 This standard does not purport to address all of the
Practice C 1045. Many advances have been made in thermal
safety concerns, if any, associated with its use. It is the
technology, both in measurement techniques and in improved
responsibility of the user of this standard to consult and
understanding of the principles of heat flow through materials.
establish appropriate safety and health practices and deter-
These advances have prompted revisions in the conceptual
mine the applicability of regulatory limitations prior to use.
approaches to the measurement of the thermal transmission
2
properties (1-4). All users of this test method should be aware
2. Referenced Documents
of these concepts.
2.1 ASTM Standards:
1.6 This test method is applicable to the measurement of
C 167 Test Methods for Thickness and Density of Blanket
3
or Batt Thermal Insulations
3
1
This test method is under the jurisdiction of ASTM Committee C16 on Thermal C 168 Terminology Relating to Thermal Insulation
Insulation and is the direct responsibility of Subcommittee C 16.30 on Thermal
C 177 Test Method for Steady-State Heat Flux Measure-
Measurement.
ments and Thermal Transmission Properties by Means of
Current edition approved Sept. 10, 2002. Published October 2002. Originally
published as C 518 – 63T. Last previous edition C 518 – 98.
2
The boldface numbers in parentheses refer to the list of references at the end of
3
this tes
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1373/C1373M-23(Practice)
Standard Practice for Determination of Thermal Resistance of Attic Insulation Systems Under Simulated Winter Conditions

SIGNIFICANCE AND USE
4.1 The thermal resistance of a ceiling system is used to characterize its steady-state thermal performance.  
4.2 The thermal resistance of insulation is related to the density and thickness of the insulation. Test data on thermal resistance are obtained at a thickness and density representative of the end use applications. In addition, the thermal resistance of the insulation system will be different from that of the thermal insulation alone because of the system construction and materials.  
4.3 This practice is needed because the in-service thermal resistance of some permeable attic insulations under winter conditions is different, lower or higher R, than that measured at or close to simulated room temperature conditions utilizing small-scale tests in which the insulation is sandwiched between two isothermal impermeable plates that have a temperature difference (ΔT) of 20 to 30°C [36 to 54°F]. When such insulation is installed in an attic, on top of a ceiling composed of normal building materials such as gypsum board or plywood, with an open top surface exposed to the attic air space, the thermal resistance under winter conditions with heat flow up and large temperature differences is significantly less because of additional heat transfer by natural convection. Fig. 1 illustrates the difference between results from small scale tests and tests under the conditions of this practice. See Ref (1-12) for discussions of this phenomenon.3
FIG. 1 Schematic of Thermal Resistance for a Permeable Attic Insulation Under Simulated Winter Conditions (Heat Flow Up)
Note 1: A constant hot-side temperature (T, hot) is used for both tests and the temperature difference increases as the cold side temperature (T, cold) is decreased. See 5.1.6 for requirements on size of air space.  
4.4 In normal use, the thickness of insulation products ranges from 75 mm [3 in.] to 500 mm [20 in.]. Installed densities will depend upon the product type, the installed thickness, the installa...
SCOPE
1.1 This practice presents a laboratory procedure to determine the thermal resistance of attic insulation systems under simulated steady-state winter conditions. The practice applies only to attic insulation systems that face an open attic air space.  
1.2 The thermal resistance of the insulation is inferred from calculations based on measurements on a ceiling system consisting of components consistent with the system being studied. For example, such a system might consist of a gypsum board or plywood ceiling, wood ceiling joists, and attic insulation with its top exposed to an open air space. The temperature applied to the gypsum board or plywood shall be in the range of 18 to 24°C [64 to 75°F]. The air temperature above the insulation shall correspond to winter conditions and ranges from –46°C to 10°C [–51 to 50°F]. The gypsum board or plywood ceiling shall be sealed to prevent direct airflow between the warm and cold sides of the system.  
1.3 This practice applies to a wide variety of loose-fill or blanket thermal insulation products including fibrous glass, rock/slag wool, or cellulosic fiber materials; granular types including vermiculite and perlite; pelletized products; and any other insulation material that is installed pneumatically or poured in place. The practice considers the effects on heat transfer of structures, specifically the ceiling joists, substrate, for example, gypsum board, air films, and possible facings, films, or other materials that are used in conjunction with the insulation.  
1.4 This practice measures the thermal resistance of the attic/ceiling system in which the insulation material has been preconditioned according to the material Specifications C549, C665, C739, and C764.  
1.5 The specimen preparation techniques outlined in this standard do not cover the characterization of loose-fill materials intended for enclosed applications.  
1.6 This practice is be used to characterize mate...

  • Standard
    8 pages
    English language
    sale 15% off
  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM C1859-23(Practice)
Standard Practice for Determination of Thermal Resistance of Pneumatically Installed Loose-Fill Building Insulation (Behind Netting) for Enclosed Applications of the Building Thermal Envelope

SIGNIFICANCE AND USE
4.1 The thermal resistance, R, of an insulation is used to describe its thermal performance.  
4.2 The thermal resistance of an insulation is related to the density and thickness of the insulation. It is desirable to obtain test data on thermal resistances at thicknesses and densities related to the end uses of the product.  
4.3 In normal use, the thickness of these products range from less than 100 mm (4 in.) to greater than 150 mm (6 in.). Installed densities depend upon the product type, the installed thickness, the installation equipment used, the installation techniques, and the geometry of the insulated space.  
4.4 Loose-fill insulations provide coverage information using densities selected by manufacturers to represent the product installed densities. Generally, it is necessary to know the product thermal performance at a representative density.  
4.5 When applicable specifications or codes do not specify the nominal thermal resistance level to be used for comparison purposes, a recommended practice is to use the Rsi (metric) = 2.65 m F/Btu]) label density and thickness for that measurement.  
4.6 If the density for test purposes is not available from the coverage chart, a test density shall be established by use of applicable specifications and codes or, if none apply, agreement between the requesting body and the testing organization.  
4.7 Generally, thin sections of these materials are not uniform. Thus, the test thickness must be greater than or equal to the product’s representative thickness if the results are to be consistent and typical of use.
Note 1: The representative thickness is specific for each product and is determined by running a series of tests in which the density is held constant but the thickness is increased. The representative thickness is defined here as that thickness above which there is no more than a 2 % change in the resistivity of the product. The representative thickness is a function of product blown density. In gene...
SCOPE
1.1 This practice presents a laboratory guide to determine the thermal resistance of pneumatically installed loose-fill building insulations for enclosed applications of the building thermal envelope behind netting at mean temperatures between –10 and 35°C (14 to 95°F).  
1.2 This practice applies to a wide variety of loose-fill thermal insulation products including but not limited to fibrous glass, rock/slag wool, or cellulosic fiber materials and any other insulation material that can be installed pneumatically. It does not apply to products that change their character after installation either by chemical reaction or the application of binders, adhesives or other materials that are not used in the sample preparation described in this practice, nor does it consider the effects of structures, containments, facings, or air films.  
1.3 Since this practice is designed for reproducible product comparison, it measures the thermal resistance of an insulation material which has been preconditioned to a relatively dry state. Consideration of changes of thermal performance of a hygroscopic insulation by sorption of water is beyond the scope of this practice.  
1.4 The sample preparation techniques outlined in this practice do not cover the characterization of loose-fill materials intended for open applications and not intended for spray-applied applications.  
1.5 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in t...

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM C1374-18(2023)(Test Method)
Standard Test Method for Determination of Installed Thickness of Pneumatically Applied Loose-Fill Building Insulation

SIGNIFICANCE AND USE
5.1 This test method was designed to give the manufacturer of loose-fill insulation products a way of determining what the initial installed thickness should be in a horizontal open attic for pneumatic applications.  
5.2 The installed thickness value developed by this test method is intended to provide guidance to the installer in order to achieve a minimum mass/unit area for a given R-value.  
5.3 For the purpose of product design, testing should be done at a variety of R-values. At least three R-values should be used: the lowest R-value on the product label, the highest R-value on the product label, and an R-value near the midpoint of the R-value range.
Note 1: For quality control purposes, testing may be done at one R-value of R-19 (h×ft 2×°F/Btu) or higher.  
5.4 Specimens are blown in a manner consistent with the intended installation procedure. Blowing machine settings should be representative of those typically used for field application with that machine.  
5.5 The material blown for a given R-value as part of the installed thickness test equals the installed mass/unit area times the test chamber area. This mass can be calculated from information provided on the package label at the R-value prescribed.
SCOPE
1.1 This test method covers determination of the installed thickness of pneumatically applied loose-fill building insulations prior to settling by simulating an open attic with horizontal blown applications.  
1.2 This test method is a laboratory procedure for use by manufacturers of loose-fill insulation for product design, label development, and quality control testing. The apparatus used produces installed thickness results at a given mass/unit area.  
1.3 This test method is not the same as the design density procedures described in Test Methods C520 or Specifications C739 or C764.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C1149-23(Specification)
Standard Specification for Self-Supported Spray Applied Cellulosic Thermal Insulation

ABSTRACT
This specification covers self-supported spray applied cellulosic thermal insulation for use as thermal insulation or acoustical absorbent material, or both. The chemically-treated cellulosic materials that are also covered in this specification are used for pneumatic applications operating within a specific temperature range. The materials are classified into two types based on the type of adhesive used and exposure of the application. Specimens for testing should be prepared and tested using the prescribed methods and should conform to the specified values of density, thermal resistance, surface bonding characteristics, adhesive strength, cohesive strength, smoldering combustion, fungi resistance, corrosion, moisture vapor absorption, odor, flame resistance permanency, substrate deflection, and air erosion.
SCOPE
1.1 The specification covers the physical properties of self-supported spray applied cellulosic fibers intended for use as thermal insulation or an acoustical absorbent material, or both.  
1.2 This specification covers chemically treated cellulosic materials intended for pneumatic applications where temperatures do not exceed 82.2°C and where temperatures will routinely remain below 65.6°C.  
1.2.1 Type I—Material applied with liquid adhesive and suitable for either exposed or enclosed applications.  
1.2.2 Type II—Materials containing a dry adhesive that is activated by water during installation and intended only for enclosed or covered applications.  
1.3 This is a material specification only and is not intended to deal with methods of application that are supplied by the manufacturer.  
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM C1594-23(Specification)
Standard Specification for Polyimide Rigid Cellular Thermal Insulation

ABSTRACT
This specification establishes the composition and physical properties of rigid polyimide cellular foams intended for use as thermal and sound-isolating insulation in commercial and industrial environments. The polyimide insulations covered are classified into three types (Types I, II, and III) according to closed cell content, and into four grades (Grades 1, 2, 3, and 4) according to density. Type II insulation is further divided into two classes (Classes 1 and 2) according to upper temperature limits. Materials shall be manufactured from the appropriate monomers and necessary ingredients. Specimens shall be sampled, tested, and conform accordingly to the following physical property requirements: apparent thermal conductivity; water and gas permeability; density; percent closed cell; upper temperature limit; high temperature stability; compressive strength; compressive force deflection; water vapor transmission; steam aging characteristics (tensile strength, dimensional and weight changes), corrosiveness; chemical resistance; vertical burn characteristics (flame application and time, burn length, and dripping); specific optical smoke density for both flaming and non-flaming exposures; toxic smoke generation; surface burning characteristics (flame spread and smoke developed indices); combustion by-products (carbon monoxide, hydrogen fluoride, hydrogen chloride, nitrogen oxides, sulfur dioxide, and hydrogen cyanide); oxygen index, and 14 scale room burn.
SCOPE
1.1 This specification covers the composition and physical properties of polyimide foam insulation with nominal densities from 1.0 lb/ft3 to 8.0 lb/ft3 (16 kg/m3 to 128 kg/m3) and intended for use as thermal and sound-isolating insulation for temperatures from −423°F to +600°F (−253°C to +316°C) in commercial and industrial environments.  
1.1.1 The annex shall apply to this specification for marine applications.  
1.1.2 This standard is designed as a material specification and not a design document.  
1.1.3 The values stated in Table 1 and Table 2 are not to be used as design values. It is the buyer’s responsibility to specify design requirements and obtain supporting documentation from the material supplier.  
* = Not available consult manufacturer for additional information.
NA = Not Applicable
NB = A manufacturer can only claim conformance to this standard to the values reported in this table. The * notes are confidential data to the manufacturers and as such are not considered part of any qualifying requirements for the standard and only tell the user to inquire about that data.  
* = Not available consult manufacturer for additional information.
NA = Not Applicable
NB = A manufacturer can only claim conformance to this standard to the values reported in this table. The * notes are confidential data to the manufacturers and as such are not considered part of any qualifying requirements for the standard and only tell the user to inquire about that data.
Note 1: The subject matter of this material specification is not covered by any other ASTM specification. There is no known ISO standard covering the subject of this standard.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical B...

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM C1058/C1058M-10(2023)(Practice)
Standard Practice for Selecting Temperatures for Evaluating and Reporting Thermal Properties of Thermal Insulation

SIGNIFICANCE AND USE
4.1 The various methods for measuring and calculating thermal properties provide data and information for manufacturer's published information, for comparison of related products, and for designers and users to evaluate insulation products for particular applications. For these purposes it is advisable to provide basic data and information produced under standard temperature conditions.  
4.2 It is possible that thermal properties of a specimen will change with mean temperature, with temperature difference across the specimens, and with high temperature exposure. Data and information at standard temperatures are necessary for valid comparison of thermal properties.  
4.3 The mean test temperatures to measure thermal properties shall be selected from those listed in Table 1. It is recommended that thermal properties of insulation materials be evaluated over a mean temperature range that represents the intended end use. For this situation, the lowest and greatest mean temperatures need to be within 10°C of the maximum and minimum mean temperature of interest. The temperature differences for any chosen mean temperature will depend upon both the thermal insulation application (see appropriate materials specification), the method of evaluation, and the limitations of the apparatus. Temperature differences or relevant temperature conditions required by ASTM material specifications shall take precedence over those recommended in this practice. (A) The values in degrees Fahrenheit given in this table are not intended to be exact conversions of those values in degrees Celsius.  
4.3.1 Standard conditions are presented where both surfaces are exposed to fixed ambient temperatures that are typical for testing building constructions, both insulated and uninsulated (Table 2). (A) Thermal transmission properties of panels of various building constructions are thermal transmittance (U), and thermal conductance (C).(B) Celsius temperatures are standard. The values in degrees Fa...
SCOPE
1.1 This practice covers standard mean temperatures for reporting thermal properties of thermal insulations, products, and materials, and of related systems and components, both insulated and uninsulated.  
1.2 Thermal properties shall be determined as a function of temperature by standard test methods. (Test Methods C177, C201, C335/C335M, C518, C745, C1114, C1363, Guide C653, and Practice C687, all in combination with Practice C1045.)  
Note 1: Standard referenced materials are needed to span the temperature range of the tests.  
1.3 This practice recommends standard conditions for use in testing and evaluating thermal properties as a function of temperature by standard test methods.  
1.4 General applications of thermal insulations include:  
1.4.1 Building envelopes,  
1.4.2 Mechanical systems or processes, and  
1.4.3 Building and industrial insulations.  
1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1919-22(Practice)
Standard Practice for Measurement of the Steady-State Thermal Transmission Properties of Small Specimens Using the Heat Flow Meter Apparatus

SIGNIFICANCE AND USE
5.1 Thermal conductivity measurements on small insulation specimens are important during new product development processes or when larger specimens cannot be collected during forensic investigation (that is, failure analysis) (1, 2).  
5.2 Numerous research projects have recently been initiated to develop insulation materials that have very high thermal resistivities (greater than 83 (m K)/W). Projects ranging from coatings to improve the thermal performance of single pane/layer glazing systems to the development of novel insulation products for building envelopes are being undertaken (1-4). All these projects have struggled in the development of new material technologies due to the difficulty associated with the measurement of thermal conductivity of small sections (approximately 0.025 m by 0.025 m) of high thermal resistance materials. As new materials are being developed, the size of each test specimen impacts the cost of development. Most of the existing test equipment and the methods do not align with the researcher’s need; the equipment requires a large specimen size is time consuming, and expensive to produce.  
5.3 This practice provides a standardized procedure to enable the thermal characterization of small specimens of insulation materials. Accurate, and reliable thermal metrology to assess thermal properties of new insulation materials, such as novel very low thermal conductivity (  
5.4 The ratio of the area of the specimen and the heat flux transducer has a significant impact on the uncertainty of the results obtained from this practice. As the specimen area decreases this ratio decreases, a smaller percentage of the total heat flow is associated with the unknown specimen. Information from the literature (4) shows that some heat-flow-meter apparatus, generally not available commercially and used by the research laboratories only, can be modified to change out the heat flux transducer so that transducers of varying sizes can be deployed. The observat...
SCOPE
1.1 This practice covers the measurement of steady state thermal transmission properties of the small flat slab thermal insulation specimen using a heat-flow-meter apparatus.  
1.2 This practice provides a supplemental procedure for use in conjunction with Test Method C518 for testing a small specimen. This practice is limited to only small specimens and, in all other particulars, the requirements of Test Method C518 apply.  
1.3 This practice characterizes small specimens having lateral dimensions less than the lateral dimensions of the heat flux transducer used to measure the heat flow. The procedure in Test Method C518 shall be used for specimens having lateral dimensions equal to or larger than the lateral dimensions of the heat flux transducer.
Note 1: The lower limit for specimen size is typically determined by the user for their particular material. As an example, Ref. (1)2 established a lower limit for specimen dimensions of 0.1 m by 0.1 m for several different thermal insulation materials for a 0.3 m by 0.3 m heat-flow-meter apparatus having a heat flux transducer 0.15 m by 0.15 m.  
1.4 This practice is intended only for research purposes, in particular, when larger specimens are unavailable. This practice shall not be used in conjunction with Test Method C518 for certification testing of products; compliance with ASTM Specifications; or compliance with regulatory or building code requirements.  
1.5 The values stated in SI units are to be regarded as the standard. No other units of measurement are included in this practice.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationall...

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM C1199-22(Test Method)
Standard Test Method for Measuring the Steady-State Thermal Transmittance of Fenestration Systems Using Hot Box Methods

SIGNIFICANCE AND USE
4.1 This test method details the calibration and testing procedures and necessary additional temperature instrumentation required in applying Test Method C1363 to measure the thermal transmittance of fenestration systems mounted vertically in the thermal chamber.  
4.2 The thermal transmittance of a test specimen is affected by its size and three-dimensional geometry. Care must be exercised when extrapolating to product sizes smaller or larger than the test specimen. Therefore, it is recommended that fenestration systems be tested at the recommended sizes specified in Practice E1423 or NFRC 100.  
4.3 Since both temperature and surface heat transfer coefficient conditions affect results, use of recommended conditions will assist in reducing confusion caused by comparing results of tests performed under dissimilar conditions. Standardized test conditions for determining the thermal transmittance of fenestration systems are specified in Practice E1423 and Section 6.2. The performance of a test specimen measured at standardized test conditions is potentially different than the performance of the same fenestration product when installed in the wall of a building located outdoors. Standardized test conditions often represent extreme summer or winter design conditions, which are potentially different than the average conditions typically experienced by a fenestration product installed in an exterior wall. For the purpose of comparison, it is essential to calibrate with surface heat transfer coefficients on the Calibration Transfer Standard (CTS) which are as close as possible to the conventionally accepted values for building design; however, this procedure can be used at other conditions for research purposes or product development.  
4.4 Similarly, it would be desirable to have a surround panel that closely duplicates the actual wall where the fenestration system would be installed. Since there are such a wide variety of fenestration system openings in North American...
SCOPE
1.1 This test method covers requirements and guidelines and specifies calibration procedures required for the measurement of the steady-state thermal transmittance of fenestration systems installed vertically in the test chamber. This test method specifies the necessary measurements to be made using measurement systems conforming to Test Method C1363 for determination of fenestration system thermal transmittance.  
Note 1: This test method allows the testing of projecting fenestration products (that is, garden windows, skylights, and roof windows) installed vertically in a surround panel. Current research on skylights, roof windows, and projecting products hopefully will provide additional information that can be added to the next version of this test method so that skylight and roof windows can be tested horizontally or at some angle typical of a sloping roof.  
1.2 This test method refers to the thermal transmittance, U of a fenestration system installed vertically in the absence of solar radiation and air leakage effects.
Note 2: The methods described in this document may also be adapted for use in determining the thermal transmittance of sections of building wall, and roof and floor assemblies containing thermal anomalies, which are smaller than the hot box metering area.  
1.3 This test method describes how to determine the thermal transmittance, US of a fenestration product (also called test specimen) at well-defined environmental conditions. The thermal transmittance is also a reported test result from Test Method C1363. If only the thermal transmittance is reported using this test method, the test report must also include a detailed description of the environmental conditions in the thermal chamber during the test as outlined in 10.1.14.  
1.4 For rating purposes, this test method also describes how to calculate a standardized thermal transmittance,  UST, which can be used to compare test results from labor...

  • Standard
    23 pages
    English language
    sale 15% off
  • Standard
    23 pages
    English language
    sale 15% off
ASTM
ASTM C1155-95(2021)(Practice)
Standard Practice for Determining Thermal Resistance of Building Envelope Components from the In-Situ Data

SIGNIFICANCE AND USE
5.1 Significance of Thermal Resistance Measurements—Knowledge of the thermal resistance of new buildings is important to determine whether the quality of construction satisfies criteria set by the designer, by the owner, or by a regulatory agency. Differences in quality of materials or workmanship may cause building components not to achieve design performance.  
5.1.1 For Existing Buildings—Knowledge of thermal resistance is important to the owners of older buildings to determine whether the buildings should receive insulation or other energy-conserving improvements. Inadequate knowledge of the thermal properties of materials or heat flow paths within the construction or degradation of materials may cause inaccurate assumptions in calculations that use published data.  
5.2 Advantage of In-Situ Data—This practice provides information about thermal performance that is based on measured data. This may determine the quality of new construction for acceptance by the owner or occupant or it may provide justification for an energy conservation investment that could not be made based on calculations using published design data.  
5.3 Heat Flow Paths—This practice assumes that net heat flow is perpendicular to the surface of the building envelope component within a given subsection. Knowledge of surface temperature in the area subject to measurement is required for placing sensors appropriately. Appropriate use of infrared thermography is often used to obtain such information. Thermography reveals nonuniform surface temperatures caused by structural members, convection currents, air leakage, and moisture in insulation. Practices C1060 and C1153 detail the appropriate use of infrared thermography. Note that thermography as a basis for extrapolating the results obtained at a measurement site to other similar parts of the same building is beyond the scope of this practice.  
5.4 User Knowledge Required—This practice requires that the user have knowledge that the data empl...
SCOPE
1.1 This practice covers how to obtain and use data from in-situ measurement of temperatures and heat fluxes on building envelopes to compute thermal resistance. Thermal resistance is defined in Terminology C168 in terms of steady-state conditions only. This practice provides an estimate of that value for the range of temperatures encountered during the measurement of temperatures and heat flux.  
1.2 This practice presents two specific techniques, the summation technique and the sum of least squares technique, and permits the use of other techniques that have been properly validated. This practice provides a means for estimating the mean temperature of the building component for estimating the dependence of measured R-value on temperature for the summation technique. The sum of least squares technique produces a calculation of thermal resistance which is a function of mean temperature.  
1.3 Each thermal resistance calculation applies to a subsection of the building envelope component that was instrumented. Each calculation applies to temperature conditions similar to those of the measurement. The calculation of thermal resistance from in-situ data represents in-service conditions. However, field measurements of temperature and heat flux may not achieve the accuracy obtainable in laboratory apparatuses.  
1.4 This practice permits calculation of thermal resistance on portions of a building envelope that have been properly instrumented with temperature and heat flux sensing instruments. The size of sensors and construction of the building component determine how many sensors shall be used and where they should be placed. Because of the variety of possible construction types, sensor placement and subsequent data analysis require the demonstrated good judgement of the user.  
1.5 Each calculation pertains only to a defined subsection of the building envelope. Combining results from different subsections to characterize...

  • Standard
    8 pages
    English language
    sale 15% off
ASTM
ASTM C1340/C1340M-10(2021)(Practice)
Standard Practice for Estimation of Heat Gain or Loss Through Ceilings Under Attics Containing Radiant Barriers by Use of a Computer Program

SIGNIFICANCE AND USE
5.1 Manufacturers of radiant barriers express the performance of their products in terms of the total hemispherical emittance. The purpose of a radiant barrier is to decrease the radiation heat transfer across the attic air space, and hence, to decrease the heat loss or gain through the ceiling below the attic. The amount of decrease in heat flow will depend upon a number of factors, such as weather conditions, amount of mass or reflective insulation in the attic, solar absorptance of the roof, geometry of the attic and roof, and amount and type of attic ventilation. Because of the infinite combinations of these factors, it is not practical to publish data for each possible case.  
5.2 The calculation of heat loss or gain of a system containing radiant barriers is mathematically complex, and because of the iterative nature of the method, it is best handled by computers.  
5.3 Computers are now widely available to most producers and consumers of radiant barriers to permit the use of this practice.  
5.4 The user of this practice may wish to modify the data input to represent accurately the structure. The computer program also may be modified to meet individual needs. Also, additional calculations may be desired, for example, to sum the hourly heat flows in some fashion to obtain estimates of seasonal or annual energy usages. This might be done using the hourly data as inputs to a whole-house model, and by choosing house balance points to use as cutoff points in the summations.
SCOPE
1.1 This practice covers the estimation of heat gain or loss through ceilings under attics containing radiant barriers by use of a computer program. The computer program included as an adjunct to this practice provides a calculational procedure for estimating the heat loss or gain through the ceiling under an attic containing a truss or rafter mounted radiant barrier. The program also is applicable to the estimation of heat loss or gain through ceilings under an attic without a radiant barrier. This procedure utilizes hour-by-hour weather data to estimate the hour-by-hour ceiling heat flows. The interior of the house below the ceiling is assumed to be maintained at a constant temperature. At present, the procedure is applicable to sloped-roof attics with rectangular floor plans having an unshaded gabled roof and a horizontal ceiling. It is not applicable to structures with flat roofs, vaulted ceilings, or cathedral ceilings. The calculational accuracy also is limited by the quality of physical property data for the construction materials, principally the insulation and the radiant barrier, and by the quality of the weather data.  
1.2 Under some circumstances, interactions between radiant barriers and HVAC ducts in attics can have a significant effect on the thermal performance of a building. Ducts are included in an extension of the computer model given in the appendix.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.