Standard Specification for Polyethylene Film and Sheeting

Standard Specification for Polyethylene Film and Sheeting

ABSTRACT
This specification covers the classification of polyethylene film and sheeting. Recycled polyethylene film or resin may be used as feedstock, and the film or sheeting may contain additives for surface property improvement, pigments, or stabilizers, or a combination of these, but they must conform to the requirements specified. Material covered in this specification shall be designated by a five-digit type number, with each numeral (from 0 to 5) indicating the cell limit within which the values of the density, impact strength, kinetic coefficient of friction, haze, and nominal thickness of the material falls under. The sheet or film shall be manufactured free, as commercially possible, of gels, streaks, pinholes, particles of foreign matter, and undispersed raw material, and without any other visible defects such as holes, tears, or blisters. The edges of the sheet or film shall be free of nicks and cuts. The surface of the sheet or film may also be treated by flame, corona discharge, or other means to improve the surface properties. Tests to determine the density, impact strength, kinetic coefficient of friction, haze, and nominal thickness of the material shall be performed and shall conform to the requirements specified.
SCOPE
1.1 This specification covers the classification of polyethylene film and sheeting up to 0.3 mm [0.012 in.] in thickness, inclusive. The film or sheeting may contain additives for the improvement of the surface properties, pigments, or stabilizers, or combinations thereof.
1.2 The values stated in SI units are to be regarded as standard. The values given in brackets are for information only.
1.3 The following precautionary caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
1.4 This specification allows for the use of recycled polyethylene film or resin as feedstock, in whole or in part, as long as all the requirements as governed by the producer and end user are also met (see Note 1).
Note 1—Guide D 5033 describes terminology and definitions related to recycled plastics.
Note 2—There is no known ISO equivalent to this specification.

General Information

Status
Historical
Publication Date
30-Nov-2005
ICS
83.140.10 - Films and sheets
Technical Committee
D20 - Plastics
Drafting Committee
D20.19 - Film, Sheeting, and Molded Products
Current Stage
Ref Project

Relations

Replaces
ASTM D2103-03 - Standard Specification for Polyethylene Film and Sheeting
Effective Date
01-Dec-2005
Replaced By
ASTM D2103-08 - Standard Specification for Polyethylene Film and Sheeting
Effective Date
01-Nov-2008
Referred By
ASTM D4649-20 - Standard Guide for Use of Stretch Films and Wrapping Application
Effective Date
01-Dec-2005
Referred By
ASTM D5748-95(2019) - Standard Test Method for Protrusion Puncture Resistance of Stretch Wrap Film
Effective Date
01-Dec-2005
Referred By
ASTM D4397-16 - Standard Specification for Polyethylene Sheeting for Construction, Industrial, and Agricultural Applications
Effective Date
01-Dec-2005
Referred By
ASTM D5459-95(2020) - Standard Test Method for Machine Direction Elastic Recovery and Permanent Deformation and Stress Retention of Stretch Wrap Film
Effective Date
01-Dec-2005
Referred By
ASTM D4801-08(2016) - Standard Specification for Polyethylene Sheeting in Thickness of 0.25 mm (0.010 in.) and Greater
Effective Date
01-Dec-2005
Referred By
ASTM D3981-09a(2016) - Standard Specification for Polyethylene Films Made from Medium-Density Polyethylene for General Use and Packaging Applications
Effective Date
01-Dec-2005
Referred By
ASTM D4635-16 - Standard Specification for Plastic Films Made from Low-Density Polyethylene and Linear Low-Density Polyethylene for General Use and Packaging Applications
Effective Date
01-Dec-2005

Buy Standard

ASTM D2103-05 - Standard Specification for Polyethylene Film and SheetingASTM D2103-05 - Standard Specification for Polyethylene Film and Sheeting
PreviousNext
Technical specification
ASTM D2103-05 - Standard Specification for Polyethylene Film and Sheeting
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D 2103 – 05
Standard Specification for
1
Polyethylene Film and Sheeting
This standard is issued under the fixed designation D 2103; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* of Transparent Plastics
D 1434 Test Method for Determining Gas Permeability
1.1 This specification covers the classification of polyethyl-
Characteristics of Plastic Film and Sheeting
ene film and sheeting up to 0.3 mm [0.012 in.] in thickness,
D 1505 Test Method for Density of Plastics by the Density-
inclusive. The film or sheeting may contain additives for the
Gradient Technique
improvementofthesurfaceproperties,pigments,orstabilizers,
D 1709 Test Methods for Impact Resistance of Plastic Film
or combinations thereof.
by the Free-Falling Dart Method
1.2 The values stated in SI units are to be regarded as
D 1746 Test Method for Transparency of Plastic Sheeting
standard.Thevaluesgiveninbracketsareforinformationonly.
3
D 1893 Test Method for Blocking of Plastic Film
1.3 The following precautionary caveat pertains only to the
D 1894 Test Method for Static and Kinetic Coefficients of
test method portion, Section 8, of this specification: This
Friction of Plastic Film and Sheeting
standard does not purport to address all of the safety concerns,
D 1922 Test Method for Propagation Tear Resistance of
if any, associated with its use. It is the responsibility of the user
Plastic Film and Thin Sheeting by Pendulum Method
of this standard to establish appropriate safety and health
D 1938 Test Method for Tear-Propagation Resistance
practices and determine the applicability of regulatory limita-
(Trouser Tear) of Plastic Film and Thin Sheeting by a
tions prior to use.
Single-Tear Method
1.4 This specification allows for the use of recycled poly-
D 2457 TestMethodforSpecularGlossofPlasticFilmsand
ethylene film or resin as feedstock, in whole or in part, as long
Solid Plastics
as all the requirements as governed by the producer and end
D 2578 Test Method for Wetting Tension of Polyethylene
user are also met (see Note 1).
and Polypropylene Films
NOTE 1—Guide D 5033 describes terminology and definitions related
D 2839 Practice for Use of a Melt Index Strand for Deter-
to recycled plastics.
mining Density of Polyethylene
NOTE 2—There is no known ISO equivalent to this specification.
D 3892 Practice for Packaging/Packing of Plastics
D 4321 Test Method for Package Yield of Plastic Film
2. Referenced Documents
D 4703 Practice for Compression Molding Thermoplastic
2
2.1 ASTM Standards:
Materials into Test Specimens, Plaques, or Sheets
D 374 Test Methods for Thickness of Solid Electrical Insu-
D 4976 SpecificationforPolyethylenePlasticsMoldingand
lation
Extrusion Materials
D 618 Practice for Conditioning Plastics for Testing
D 5033 Guide for Development of ASTM Standards Relat-
D 792 TestMethodsforDensityandSpecificGravity(Rela-
ing to Recycling and Use of Recycled Plastics
tive Density) of Plastics by Displacement
E 96/E 96M Test Methods for Water Vapor Transmission of
D 882 Test Method for Tensile Properties of Thin Plastic
Materials
Sheeting
F 1249 Test Method for Water Vapor Transmission Rate
D 883 Terminology Relating to Plastics
Through Plastic Film and Sheeting Using a Modulated
D 1003 Test Method for Haze and Luminous Transmittance
Infrared Sensor
3. Terminology
1
This specification is under the jurisdiction of ASTM Committee D20 on
3.1 Definitions:
Plastics and is the direct responsibility of Subcommittee D20.19 on Film and
Sheeting.
3.1.1 Unless otherwise specified, the definitions of plastics
Current edition approved Dec. 1, 2005. Published January 2006. Originally
used in this specification are in accordance with Terminology
approved in 1962. Last previous edition approved in 2003 as D 2103 – 03.
2 D 883.
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
3
the ASTM website. Withdrawn.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
D2103–05
3.2 Definitions of Terms Specific to This Standard: 5. General Requirements
3.2.1 treated—surface characteristics of the sheet or film
5.1 Appearance—The material shall have appearance quali-
have been modified by flame, corona discharge, or other me
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D4204-16(2023)(Practice)
Standard Practice for Preparing Plastic Film Specimens for a Round-Robin Study

SIGNIFICANCE AND USE
4.1 This practice is intended to assist task groups participating in a round-robin study with the preparation of test sets of film specimens from film samples in the form of rolls on a core.  
4.2 This practice assumes that the essential features of the round-robin protocol have already been established by following the guidance of Practice E691. In particular, it is assumed that the following are known: (1) the number of film samples to be used, (2) the number of participating laboratories, (3) the number of replicate test results to be generated by each laboratory for each sample, and (4) the number of test specimens required to yield one test result for each sample.  
4.3 In accordance with this practice, samples are partitioned into test sets so that real within-sample variability will not unduly distort the conclusions drawn from statistical analyses of the data generated in the round-robin study.
SCOPE
1.1 This practice covers the preparation of test sets of plastic film specimens for subsequent use in an interlaboratory round-robin study to evaluate the precision of a test method.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D5047-17(2023)(Specification)
Standard Specification for Polyethylene Terephthalate Film and Sheeting

ABSTRACT
This specification establishes the dimensional (length and width, thickness, and weight) requirements for biaxially oriented polyethylene terephthalate film and sheeting, both virgin and recycled. For this specification, polyethylene terephthalate film and sheeting shall be defined as the material derived from terephthalic acid and ethylene glycol and shall consist of at least 90 % polyethylene terephthalate homopolymer. The film or sheeting shall be furnished flat or in rolls in the dimensions specified. This specification does not apply to coated, coextruded, tinted, pigmented, or metallized film or sheeting.
SCOPE
1.1 This specification covers requirements for biaxially oriented polyethylene terephthalate film and sheeting in thicknesses from 1.5 μm (0.06 mil) to 355 μm (14.0 mil). For this specification, polyethylene terephthalate film and sheeting shall be defined as the material derived from terephthalic acid and ethylene glycol and shall consist of at least 90 % polyethylene terephthalate homopolymer. This specification does not apply to coated, coextruded, tinted, pigmented, or metallized film or sheeting.  
1.2 Polyethylene terephthalate materials, being thermoplastic, are reprocessable and recyclable.2 This specification allows for the use of those polyethylene terephthalate plastic materials, provided that any specific requirements as governed by the producer and end user are met.  
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.
Note 1: There is no known ISO equivalent to this specification.
Note 2: Film is defined as sheeting having a thickness of ≤250 microns (0.010 in.).  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4397-16(2023)(Specification)
Standard Specification for Polyethylene Sheeting for Construction, Industrial, and Agricultural Applications

ABSTRACT
This specification covers polyethylene sheeting with a determined thickness intended for construction, industrial and agricultural applications. The sheeting shall be made from polyethylene or modified polyethylene, such as an ethylene copolymer consisting of a major portion of ethylene in combination with a minor portion of some other monomer, or a mixture of polyethylene with a lesser amount of other polymers. General requirements for the material are also observed according to their appearance, dimensions in size and tolerance and minimum net weight. The sheeting may be natural, color-tinted, translucent or opaque. The tests given are intended primarily for use as production tests in conjunction with manufacturing processes and inspection methods to insure conformity of sheeting with the requirements of this specification. These tests shall be done in order to determine the following properties: thickness, length and width, weight, impact resistance, tensile properties, reflectance, luminous transmittance, water vapor transmission, and heat sealability.
SCOPE
1.1 This specification covers polyethylene sheeting, 250 μm (0.010 in. or 10 mils) or less in thickness, intended for construction, industrial, and agricultural applications.  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 The following precautionary statement pertains only to the test methods portion, Section 8 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
Note 1: There is no known ISO equivalent to this standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM D4272/D4272M-23(Test Method)
Standard Test Method for Total Energy Impact of Plastic Films by Dart Drop

SIGNIFICANCE AND USE
5.1 Evaluation of the impact toughness of film is important in predicting the performance of a material in applications such as packaging, construction, and other uses. The test simulates the action encountered in applications where moderate-velocity blunt impacts occur in relatively small areas of film.  
5.2 The values obtained by this test method are highly dependent on the method and conditions of film fabrication as well as the type and grade of resin.  
5.3 Test methods employing different missile velocities, impinging surface diameters, or effective specimen diameters will most likely produce different results. Data obtained by this test method cannot necessarily be compared directly with those obtained by other test methods.  
5.4 The impact resistance of a film, while partly dependent on thickness, does not have a simple correlation with sample thickness. Hence, impact values expressed in joules [ft·lbf] normalized over a range of thickness will not necessarily be linear with thickness. Data from this test method are comparable only for specimens that vary by no more than ±15 % from the nominal or average thickness of the specimens tested.  
5.5 The test results obtained by this test method are greatly influenced by the quality of film under test. The influence of variability of data obtained by this procedure will, therefore, depend strongly on the sample quality, uniformity of film thickness, the presence of die marks, contaminants, etc.  
5.6 Several impact test methods are used for film. It is sometimes desirable to know the relationships among test results derived by different test methods. A study was conducted in which four films made from two resins (polypropylene and linear low-density polyethylene), with two film thicknesses for each resin, were impacted using Test Methods D1709 (Test Method A), Test Method D3420 (Procedures A and B), and Test Method D4272. The test results are shown in Appendix X2. Differences in results between Test Methods...
SCOPE
1.1 This test method describes the determination of the total energy impact of plastic films by measuring the kinetic energy lost by a free-falling dart that passes through the film.  
1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Film has been arbitrarily defined as sheeting having nominal thickness not greater than 0.25 mm [0.010 in.].
Note 2: This test method and ISO 7765–2 address the same subject matter, but differ in technical content (and results cannot be directly compared between the two test methods). The ISO test method calls for a direct readout of energy by using a load cell as part of the impactor head, while Test Method D4272 calls for a constant weight impactor, then measuring the time of travel through a given distance to get energy values.
FIG. 1 Elements of an Instrumented Dart Drop System
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D1746-23(Test Method)
Standard Test Method for Transparency of Plastic Sheeting

SIGNIFICANCE AND USE
4.1 The attribute of clarity of a sheet, measured by its ability to transmit image-forming light, correlates with its regular transmittance. Sensitivity to differences improves with decreasing incident beam- and receptor-angle. If the angular width of the incident beam and of the receptor aperture (as seen from the specimen position) are of the order of 0.1° or less, sheeting of commercial interest have a range of transparency of about 10 to 90 % as measured by this test. Results obtained by the use of this test method are greatly influenced by the design parameters of the instruments; for example, the resolution is largely determined by the angular width of the receptor aperture. Caution should therefore be exercised in comparing results obtained from different instruments, especially for samples with low regular transmittance.  
4.2 Regular transmittance data in accordance with this test method correlate with the property commonly known as “see-through,” which is rated subjectively by the effect of a hand-held specimen on an observer's ability to distinguish clearly a relatively distant target. This correlation is poor for highly diffusing materials because of interference of scattered light in the visual test.
SCOPE
1.1 This test method covers the measurement of the transparency of plastic sheeting in terms of regular transmittance (Tr). Although generally applicable to any translucent or transparent material, it is principally intended for use with nominally clear and colorless thin sheeting.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.
Note 2: For additional information, see Terminology E284 and Practice E1164.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1922-23(Test Method)
Standard Test Method for Propagation Tear Resistance of Plastic Film and Thin Sheeting by Pendulum Method

SIGNIFICANCE AND USE
4.1 This test method is of value in ranking relative tearing resistance of various plastic films and thin sheeting of comparable thickness. Experience has shown the test to have its best reliability on relatively less extensible films and sheeting. Variable elongation and oblique tearing effects on the more extensible films preclude its use as a precise production-control tool for these types of plastics. This test method should be used for specification acceptance testing only after it has been demonstrated that the data for the particular material are acceptably reproducible. This test method should be used for service evaluation only after its usefulness for the particular application has been demonstrated with a number of different films.  
4.2 This test method has been widely used as one index of the tearing resistance of plastic film and thin sheeting used in packaging applications. While it is not always be possible to correlate film tearing data with its other mechanical or toughness properties, the apparatus of this test method provides a controlled means for tearing specimens at straining rates approximating some of those found in actual packaging service.  
4.3 Due to orientation during their manufacture, plastic films and sheeting frequently show marked anisotropy in their resistance to tearing. This is further complicated by the fact that some films elongate greatly during tearing, even at the relatively rapid rates of loading encountered in this test method. The degree of this elongation is dependent in turn on film orientation and the inherent mechanical properties of the polymer from which it is made. These factors make tear resistance of some films reproducible between sets of specimens to ±5 % of the mean value, while others potentially show no better reproducibility than ±50 %.  
4.4 Data obtained by this test method may supplement that from Test Method D1004, wherein the specimen is strained at a rate of 50 mm (2 in.) per minute. However, spec...
SCOPE
1.1 This test method2 covers the determination of the average force to propagate tearing through a specified length of plastic film or nonrigid sheeting after the tear has been started, using an Elmendorf-type tearing tester. Two specimens are cited, a rectangular type, and one with a constant radius testing length. The latter shall be the preferred or referee specimen.  
1.2 Because of (1) difficulties in selecting uniformly identical specimens, (2) the varying degree of orientation in some plastic films, and (3) the difficulty found in testing highly extensible or highly oriented materials, or both, the reproducibility of the test results may be variable and, in some cases, not good or misleading. Provisions are made in the test method to address oblique directional tearing which may be found with some materials.  
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in 13.1.
Note 1: Film has been arbitrarily defined as sheeting having nominal thickness not greater than 0.25 mm (0.010 in.).
Note 2: This standard is equivalent to ISO 6383-2.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D2578-23(Test Method)
Standard Test Method for Wetting Tension of Polyethylene and Polypropylene Films

SIGNIFICANCE AND USE
5.1 When a drop of liquid rests on the surface of a solid, and a gas is in contact with both, the forces acting at the interfaces must balance. These forces can be represented by surface energies acting in the direction of the surfaces and it follows that:
   where:
  θ  =  angle of contact of the edge of the drop with the solid surface,   γGL  =  surface energy of the gas - liquid interface,   γGS  =  surface energy of the gas - solid interface, and   γSL  =  surface energy of the solid - liquid interface.    
5.1.1 The right side of the above equation (the difference between the surface energies of the gas - solid and solid - liquid interfaces) is defined as the wetting tension of the solid surface. It is not a fundamental property of the surface but depends on interaction between the solid and a particular environment.  
5.1.2 When the gas is air saturated with vapors of the liquid, γGL will be the surface tension of the liquid. If the angle of contact is 0° the liquid is said to just wet the surface of the solid, and in this particular case (since cos θ = 1) the wetting tension of the solid will be equal to the surface tension of the liquid.  
5.2 The ability of polyethylene and polypropylene films to retain inks, coatings, adhesives, etc., is primarily dependent upon the character of their surfaces, and can be improved by one of several surface-treating techniques. These same treating techniques have been found to increase the wetting tension of a polyethylene or a polypropylene film surface in contact with mixtures of formamide and ethyl Cellosolve in the presence of air. It is therefore possible to relate the wetting tension of a polyethylene or a polypropylene film surface to its ability to accept and retain inks, coatings, adhesives, etc. The measured wetting tension of a specific film surface can only be related to acceptable ink, coating, or adhesive retention through experience. Wetting tension in itself is not a completely acceptable measur...
SCOPE
1.1 This test method covers the measurement of the wetting tension of a polyethylene or polypropylene film surface in contact with drops of specific test solutions in the presence of air.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard.
Note 1: This test method and the specified reagents were specifically developed for polyethylene and polypropylene films. It is possible to utilize this test method and the specified reagents for films composed of other polymers, but this can affect the surface energies of the gas-liquid and solid-liquid interfaces, which will affect the contact angle and wetting tension. The applicability and significance for use of non-polyolefin materials must be established by the user.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific hazards statements are given in Section 9.
Note 2: This test method is equivalent to ISO 8296.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D2291/D2291M-22(Practice)
Standard Practice for Fabrication of Ring Test Specimens for Glass-Resin Composites

SIGNIFICANCE AND USE
4.1 This practice provides a uniform procedure for fabricating glass fiber/thermoset resin ring samples for use as test specimens. Specimens so prepared can be used in Test Methods D2290 and D2344/D2344M.
SCOPE
1.1 This practice is intended for use in the fabrication of ring-type test specimens to be used in the evaluation of the mechanical properties of reinforcement and resins in a composite structure. The practice outlines the steps in the preparation of the test specimens, including the final specimen machining where applicable. Three final ring configurations are included.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this practice.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1494-22(Test Method)
Standard Test Method for Diffuse Light Transmission Factor of Reinforced Plastics Panels

SIGNIFICANCE AND USE
4.1 The purpose of this test method is to obtain the diffuse light transmittance factor of both flat and corrugated translucent building panels by the use of simple apparatus and by employing as a light source a combination of fluorescent tubes whose energy distribution closely approximates CIE Source C.
SCOPE
1.1 This test method covers the determination of the diffuse light transmission factor of translucent reinforced plastics building panels.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in the parentheses are for information only.  
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in Tables and Figures) shall not be considered as requirements of this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1593-22(Specification)
Standard Specification for Nonrigid Vinyl Chloride Plastic Film and Sheeting

ABSTRACT
This specification covers nonrigid, unsupported vinyl chloride plastic film and sheeting in which the resin portion of the composition contains at least 90 % vinyl chloride. The remaining 10 % may include one or more monomers copolymerized with vinyl chloride, or consist of other resins mechanically blended together with poly(vinyl chloride) or copolymers thereof. The film and sheeting covered herein shall be 0.075 to 0.25 mm (3 to 10 mils) in thickness for film and greater than 0.25 mm in thickness for sheet, and shall include the stabilizers and plasticizers necessary to meet the requirements of this specification. The material may be transparent, translucent, or opaque, and may be plain, printed, embossed, or otherwise surface treated. This specification designates three general-purpose types of vinyl chloride film and sheeting - calendered, extruded, and cast. The materials shall be tested for its tensile strength and elongation at rapture, tear resistance, volatile loss, water extraction, low temperature impact, burning rate, shrinkage, and color fastness to rubbing.
SCOPE
1.1 This specification covers nonrigid, unsupported vinyl chloride plastic film and sheeting in which the resin portion of the composition contains at least 90 % vinyl chloride. The remaining 10 % can include one or more monomers copolymerized with vinyl chloride, or consist of other resins mechanically blended together with poly(vinyl chloride) or copolymers thereof.  
1.2 The vinyl chloride plastic film and sheeting covered herein shall be 0.075 to 0.25 mm (3 to 10 mils) in thickness for film and greater than 0.25 mm in thickness for sheeting. The film and sheeting shall include the stabilizers and plasticizers necessary to meet the requirements of this specification. This specification covers transparent, translucent, or opaque film and sheeting that is plain, printed, embossed, or otherwise surface treated.  
1.3 The values stated in SI units are to be regarded as the standard.  
1.4 The following safety hazards caveat pertains only to the test methods portion, Section 10, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language