ASTM D2835-89(2007)
(Specification)Standard Specification for Lubricant for Installation of Preformed Compression Seals in Concrete Pavements
Standard Specification for Lubricant for Installation of Preformed Compression Seals in Concrete Pavements
ABSTRACT
This specification covers a lubricant suitable for facilitating the insertion and positioning of preformed elastomeric compression seals in prepared voids (usually contraction joints) in concrete pavements. The lubricant shall be based on polychloroprene, containing only soluble phenolic resins blended together with antioxidants and acid acceptors in a suitable mixture of organic solvents. The requirements of the lubricant are based on the performance of the lubricant as measured by its solids content, homogeneity, consistency and drying rate.
SCOPE
1.1 This specification covers a lubricant suitable for facilitating the insertion and positioning of preformed elastomeric compression seals in prepared voids (usually contraction joints) in concrete pavement.
1.2 The requirements of the lubricant are based on the performance of the lubricant as measured by its solids content, homogeneity, consistency and drying rate.
1.3 The values stated in inch-pound units are to be regarded as the standard. The metric equivalents of U.S. customary units may be approximate.
1.4 The following precautionary caveat pertains only to the test method portion, Section 7 of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D2835 −89(Reapproved2007)
StandardSpecification for
Lubricant for Installation of Preformed Compression Seals
in Concrete Pavements
This standard is issued under the fixed designation D2835; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope* 4. Requirements
4.1 Homogeneity—The lubricant shall be uniform and con-
1.1 This specification covers a lubricant suitable for facili-
tating the insertion and positioning of preformed elastomeric tain no lumps or agglomerates.
compression seals in prepared voids (usually contraction
4.2 SolidsContent—Thenonvolatilecontentofthelubricant
joints) in concrete pavement.
shall be no less than 24.0 weight %.
1.2 The requirements of the lubricant are based on the
4.3 Consistency—The lubricant shall exhibit a viscosity in
performance of the lubricant as measured by its solids content,
one of the following ranges:
homogeneity, consistency and drying rate.
4.3.1 TypeI—forhandormachineapplication,3000to8000
1.3 The values stated in inch-pound units are to be regarded cP.
asthestandard.ThemetricequivalentsofU.S.customaryunits 4.3.2 Type II—for machine application, 8000 to 15 000 cP.
may be approximate.
4.4 Drying Rate—A bond between lubricant-coated papers
1.4 The following precautionary caveat pertains only to the
prepared after 8-min drying time shall separate completely in
test method portion, Section 7 of this specification. This
less than 10 s when a 50-g load is applied in shear. A similar
standarddoesnotpurporttoaddressallofthesafetyconcerns,
bond prepared after 20-min drying time shall remain un-
ifany,associatedwithitsuse.Itistheresponsibilityoftheuser
separated for a minimum of 10 s when a 50-g load is applied
of this standard to establish appropriate safety and health
in shear.
practices and determine the applicability of regulatory limita-
tions prior to use.
5. Basis of Purchase
5.1 Each lot of lubricant shall be accompanied by the
2. Referenced Documents
manufacturer’s certified test results attesting compliance with
2.1 ASTM Standards: this specification, unless an alternative agreement is concluded
D1084 Test Methods for Viscosity of Adhesives
by the manufacturer and the purchaser.
D1644 Test Methods for Nonvolatile Content of Varnishes
6. Sampling
3. Classification
6.1 The lubricant samples shall be a 1-quart (1-litre) aliquot
3.1 The lubricant shall be based on polychloroprene, con- consisting of a composite taken when possible from three or
taining only soluble phenolic resins blended together with more separate containers chosen at random. Samples also shall
antioxidants and acid acceptors in a suitable mixture of organic be taken from containers which appear to be nonrepresentative
solvents.
and shall be tested separately. Before a sample is withdrawn,
the contents in the container shall be mixed to uniform
consistency. The sample shall be placed immediately in an
airtight-glass jar or metal can until tested.
This specification is under the jurisdiction of ASTM Committee D04 on Road
and Paving Materials and is the direct responsibility of Subcommittee D04.34 on
Preformed Joint Fillers, Sealers and Sealing Systems.
7. Test Methods
Current edition approved Dec. 1, 2007. Published January 2008. Originally
7.1 Homogeneity—Stir the test sample by hand for 2 min
approved in 1969. Last previous edition approved in 2003 as D2835 – 89 (2003).
DOI: 10.1520/D2835-89R07.
with a spatula.Withdraw the spatula and examine the lubricant
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
as it flows from the spatula for lumps or agglomerates.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Particles smaller in diameter than 0.015 in. (0.38 mm) shall not
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. be considered cause for rejection.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
D2835−89(Reapproved2007)
NOTE 1—At the consumer’s request, compliance with the 0.015-in.
drying 8 min overlap the cut edges of the first pair 1 in. and
(0.38-mm) requirement shall be determined by a sample diluted 1+4 with
place face-to-face to form a 1 by 2-in. area lap shear bond.
Xylene through a 40-mesh sieve.
Take care to align the two films so that a force applied along
7.2 Solids Content—Determine in accordance with Method
their center lines will impose a direct shear force without a
A of Test Methods D1644.
twisting movement. Form the bond by placing the overlapped
papers on a horizontal smooth surface, placing a ⁄8-in. thick, 1
7.3 Consistency—Determine in accordance with Method B
by 2-in. aluminum plate over the bond area, and placing a 500
ofTest Methods D1084. Use a No. 4 spindle at 20 rpm at a test
g laboratory weight on this plate for 10 s. Hang the bonded
temperature of 77 6 0.9°F (25 6 0.5°C).
pieces immediately in a vertical position and attach a 50-g
7.4 Drying Rate:
weight with a small loop of wire, weighing less than 1 g, to the
7.4.1 Apparatus:
lower piece of paperboard forming the bond.Align the point of
7.4.1.1 Film Applicator, 2-in. (50-mm) wide, 5 to 25-mils
supportandthepoi
...