Testing of welded joints of thermoplastics semi-finished products - Part 1: Bend test

Testing of welded joints of thermoplastics semi-finished products - Part 1: Bend test

This standard specifies the dimensions and the method for sampling and preparing test specimens, together with the conditions for carrying out the bend test. The result of the test is also influenced by the deformation behaviour of the tested material, the kind of welding process and the geometry of the sample. The test is applicable to plate and tube butt jointed assemblies made from thermoplastic materials filled or unfilled, but not reinforced, irrespective of the welding process used. It is not applicable to assemblies with a wall thickness < 3 mm.

Prüfen von Schweißverbindungen aus thermoplastischen Kunststoffen - Teil 1: Biegeversuch

Die vorliegende Norm legt die Maße, das Verfahren für die Probenahme und die Herstellung von Proben sowie die Bedingungen für die Durchführung des Biegeversuchs fest. Das Prüfergebnis wird unter anderem durch das Verformungsverhalten des geprüften Werkstoffs, die Art des Schweißverfahrens und die Probengeometrie beeinflußt. Die Prüfung ist unabhängig vom angewendeten Schweißverfahren auf stumpfgeschweißte Platten- oder Rohrverbindungen aus thermoplastischen Kunststoffen mit oder ohne Füllstoff anwendbar, die jedoch nicht verstärkt sein dürfen.

Essai des assemblages soudés sur produits semi-finis thermoplastiques - Partie 1: Essais de pliage

La présente norme européenne définit les dimensions et les méthodes pour le prélèvement et la préparation des éprouvettes, ainsi que les conditions de l'essai de pliage. Le résultat de l'essai est également influencé par le comportement à la déformation du matériau soumis à l'essai, par le procédé de soudage utilisé et par la géométrie de l'échantillon. Cet essai est applicable aux assemblages en matières thermoplastiques chargées ou non chargées, mais non renforcées, sous forme de plaque ou de tube, soudés bout à bout, quel que soit le procédé de soudage utilisé.

Preskus zvarjenih spojev plastomernih polizdelkov - 1. del: Preskus upogibnosti

General Information

Status
Published
Publication Date
16-Nov-1999
Withdrawal Date
30-May-2000
ICS
25.160.40 - Welded joints and welds
Technical Committee
CEN/TC 249 - Plastics
Drafting Committee
CEN/TC 249/SC 5/WG 2 - Testing of welded joints
Current Stage
Ref Project
SIST EN 12814-1:2001 - Testing of welded joints of thermoplastics semi-finished products - Part 1: Bend test

Relations

Corrected By
EN 12814-1:1999/AC:2003 - Testing of welded joints of thermoplastics semi-finished products - Part 1: Bend test
Effective Date
22-Dec-2008
Revised
prEN 12814-1 - Testing of welded joints of thermoplastics semi-finished products - Part 1: Bend test
Effective Date
31-Jan-2024
Child
EN 12814-2:2000 - Testing of welded joints of thermoplastics semi-finished products - Part 2: Tensile test
Effective Date
22-Dec-2008
Child
EN 12814-8:2001 - Testing of welded joints of thermoplastics semi-finished products - Part 8: Requirements
Effective Date
22-Dec-2008
Child
EN 12814-6:2000 - Testing of welded joints of thermoplastics semi-finished products - Part 6: Low temperature tensile test
Effective Date
22-Dec-2008
Child
EN 12814-4:2001 - Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test
Effective Date
22-Dec-2008
Child
EN 12814-7:2002 - Testing of welded joints of thermoplastics semi-finished products - Part 7: Tensile test with waisted test specimens
Effective Date
22-Dec-2008
Child
EN 12814-3:2000 - Testing of welded joints of thermoplastics semi-finished products - Part 3: Tensile creep test
Effective Date
22-Dec-2008
Child
EN 12814-5:2000 - Testing of welded joints of thermoplastics semi-finished products - Part 5: Macroscopic examination
Effective Date
22-Dec-2008

Buy Standard

EN 12814-1:2001EN 12814-1:2001
PreviousNext
Standard
EN 12814-1:2001
English language
15 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)


2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Preskus zvarjenih spojev plastomernih polizdelkov - 1. del: Preskus upogibnostiPrüfen von Schweißverbindungen aus thermoplastischen Kunststoffen - Teil 1: BiegeversuchEssai des assemblages soudés sur produits semi-finis thermoplastiques - Partie 1: Essais de pliageTesting of welded joints of thermoplastics semi-finished products - Part 1: Bend test25.160.40Varjeni spoji in variWelded jointsICS:Ta
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

CEN
EN 12814-7:2024(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 7: Tensile test with waisted test specimens
SIST EN 12814-7:2024

This document specifies the dimensions, the method of sampling, the preparation of the test specimens and the conditions for performing the tensile test with waisted test specimens in order to determine the tensile energy welding factor.
A tensile test with waisted specimens can be used in conjunction with other tests (e.g. bend, tensile, tensile creep, macro, etc.) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to co-axial or co-planar heated tool butt welded assemblies made from thermoplastics materials filled or unfilled, but not reinforced. It is not applicable to tubular assemblies with a nominal outside diameter less than 90 mm.

  • Standard
    10 pages
    English language
    sale 10% off
    e-Library read for
    1 day
  • Standard
    10 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 16296:2021(Main)
Imperfections in thermoplastics welded joints - Quality levels
SIST EN 16296:2021

This document specifies quality levels for imperfections in thermoplastics welded joints that have cooled to ambient temperature and is applicable to material thickness above 2,0 mm.
Three quality levels are specified in order to permit application for a wide range of welded fabrication. They are designated by symbols B, C and D, where B is the most stringent. The quality levels refer to production quality and not to the fitness-for-purpose (see 3.2) of the manufactured product.
The quality level necessary are expected to be defined by the application standard or by the fabricator in conjunction with the user and/or other parties concerned. The level is expected to be prescribed before the start of production, preferably at the enquiry or order stage.
This document applies to the following thermoplastic materials in Table 1:
and to the following welding processes:
-   heated tool welding;
-   electrofusion socket welding;
-   hot gas welding using filler rod only;
-   extrusion welding;
-   solvent welding of pipes.

  • Standard
    22 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-2:2021(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 2: Tensile test
SIST EN 12814-2:2021

This document specifies the dimensions, the method of sampling, the preparation of the test specimens and the conditions for performing the tensile test in order to determine the short-term tensile welding factor.
A tensile test can be used in conjunction with other tests (e.g. bend, tensile creep, macro) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to welded semi-finished products made from thermoplastics materials filled or unfilled, but not reinforced, irrespective of the welding process used.

  • Standard
    14 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-8:2021(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 8: Requirements
SIST EN 12814-8:2021

This document provides the requirements for the tests made on welded thermoplastics semi-finished products.
The selection of the appropriate test method(s) is made in accordance with the particular type and application of welded product.
The test results depend on the conditions of manufacture for the test specimen and on the test conditions. They can therefore only be related to the behaviour of the product or can only be used for designing a structure, if the test conditions can be related to the service conditions.

  • Standard
    17 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 13100-2:2019(Main)
Non-destructive testing of welded joints in thermoplastics semi- finished products - Part 2: X-ray radiographic testing
SIST EN 13100-2:2019

This document specifies fundamental radiographic techniques with film, which enable repeatable results to be obtained economically.
This document applies to the X-ray radiographic examination of heated tool, electrofusion, extrusion and hot gas joints in plastics materials.
It applies to joints in solid wall pipes and plates with a range of thicknesses from 5 mm to 100 mm. It only applies to pipes containing air or other gases at the time of X-ray testing.
This document does not specify acceptance levels of the indications.

  • Standard
    20 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 14728:2019(Main)
Imperfections in thermoplastic welds - Classification
SIST EN 14728:2019

This document specifies a system for classifying imperfections that may be encountered in thermoplastic welded joints during manufacture and provides examples of imperfections for the following welding processes:
-   heated tool butt welding;
-   heated tool socket welding;
-   electrofusion socket welding;
-   hot gas welding;
-   extrusion welding;
-   solvent socket welding.
This document does not describe imperfections that may be generated during service or imperfections present before welding, which are due to poor preparation or assembly of components (e.g. fit up). The correct preparation and assembly of components (e.g. fit up) are described in the relevant welding procedure specification (WPS).
This document is also not concerned with the search for the possible influence of these imperfections on the behaviour of joints in relation to the different types of stress to which the latter may be subjected or on methods for preventing such imperfections.
This document can be used in conjunction with EN 16296 [1] to determine the acceptance of welds.
Only imperfections giving rise to discontinuities of materials or changes in shape are taken into consideration in this document, specifying their type, their shape and their positions. This classification can be used to determine the possible origin or causes of the imperfections.

  • Standard
    33 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-4:2018/AC:2018(Corrigendum)
Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test
SIST EN 12814-4:2018/AC:2018

This document specifies the dimensions, the method of sampling and the preparation of the test specimens, and also the conditions for performing the peel test perpendicular to the weld in order to determine the peel resistance and the failure behaviour.
A peel test can be used in conjunction with other tests (e.g. tensile creep, macroscopic examination...) to assess the performance of welded assemblies, made from thermoplastics materials.
Peel tests are applicable to overlap welded assemblies made from thermoplastics materials.
The T-peel test as defined in Clause 5 will be used only for assessing welded sheet assemblies. This test is not applicable to welded test pieces containing sheets of different nominal thickness.
The decohesion test as defined in Clause 6 will be used only for assessing electrofusion joints with nominal thickness of pipe/fitting greater than 10 mm.
For socket fusion and for electrofusion socket joints with nominal outside diameter less than or equal to 90 mm, a crush test will be used, as defined in Clause 7.
The crush test can also be used for electrofusion joints with outside diameters greater than 90 mm.
The crush test for electrofusion saddle joints will be performed in accordance with ISO 13955 [1].
NOTE   A decohesion test is also defined in ISO 13954 [2].
The tests defined in this standard are not intended to be used for assessment and/or qualification of thermoplastic fittings that already have their own requirements, e.g. polyethylene fittings according to EN 1555-3 [3] and EN 12201-3 [4].

  • Corrigendum
    2 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-4:2018(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test
SIST EN 12814-4:2018

This document specifies the dimensions, the method of sampling and the preparation of the test specimens, and also the conditions for performing the peel test perpendicular to the weld in order to determine the peel resistance and the failure behaviour.
A peel test can be used in conjunction with other tests (e.g. tensile creep, macroscopic examination...) to assess the performance of welded assemblies, made from thermoplastics materials.
Peel tests are applicable to overlap welded assemblies made from thermoplastics materials.
The T-peel test as defined in Clause 5 will be used only for assessing welded sheet assemblies. This test is not applicable to welded test pieces containing sheets of different nominal thickness.
The decohesion test as defined in Clause 6 will be used only for assessing electrofusion joints with nominal thickness of pipe/fitting greater than 10 mm.
For socket fusion and for electrofusion socket joints with nominal outside diameter less than or equal to 90 mm, a crush test will be used, as defined in Clause 7.
The crush test can also be used for electrofusion joints with outside diameters greater than 90 mm.
The crush test for electrofusion saddle joints will be performed in accordance with ISO 13955 [1].
NOTE   A decohesion test is also defined in ISO 13954 [2].
The tests defined in this standard are not intended to be used for assessment and/or qualification of thermoplastic fittings that already have their own requirements, e.g. polyethylene fittings according to EN 1555-3 [3] and EN 12201-3 [4].

  • Standard
    16 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 13100-1:2017(Main)
Non destructive testing of welded joints of thermoplastics semi-finished products - Part 1: Visual examination
SIST EN 13100-1:2017

This European standard covers the visual examination of welds in thermoplastic materials. It may also be applied to visual testing of the joint prior to and during the welding.

  • Standard
    7 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-3:2014(Main)
Testing of welded joints in thermoplastics semi-finished products - Part 3: Tensile creep test
SIST EN 12814-3:2014

This European Standard specifies the dimensions, the method of sampling and the preparation of the test specimens, and the conditions for performing the tensile creep test perpendicular to the weld in order to determine the long-term tensile welding factor.
A tensile creep test may be used in conjunction with other tests (e.g. bend test, tensile test, macrographic examination,...) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to welded assemblies made from thermoplastics materials filled or unfilled such as tubes and fittings, sheets, plates and profiles, but not reinforced, irrespective of the welding process used.

  • Standard
    25 pages
    English language
    sale 10% off
    e-Library read for
    1 day