IEC TR 63114:2018
(Main)Electrical steel - Reverse bend test method of electrical steel strip and sheet
Electrical steel - Reverse bend test method of electrical steel strip and sheet
IEC TR 63114:2018(E) describes the general principle and technical details of the reverse bend test method used for evaluating the ductility of electrical steel strip and sheet. This test method is applicable to Epstein test strip specimens obtained from non-oriented and grain-oriented electrical steel of any grade. The test specimens shall not be annealed.
General Information
Standards Content (Sample)
IEC TR 63114 ®
Edition 1.0 2018-04
TECHNICAL
REPORT
Electrical steel – Reverse bend test method for electrical steel strip and sheet
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form
or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from
either IEC or IEC's member National Committee in the country of the requester. If you have any questions about IEC
copyright or have an enquiry about obtaining additional rights to this publication, please contact the address below or
your local IEC member National Committee for further information.
IEC Central Office Tel.: +41 22 919 02 11
3, rue de Varembé info@iec.ch
CH-1211 Geneva 20 www.iec.ch
Switzerland
About the IEC
The International Electrotechnical Commission (IEC) is the leading global organization that prepares and publishes
International Standards for all electrical, electronic and related technologies.
About IEC publications
The technical content of IEC publications is kept under constant review by the IEC. Please make sure that you have the
latest edition, a corrigenda or an amendment might have been published.
IEC Catalogue - webstore.iec.ch/catalogue Electropedia - www.electropedia.org
The stand-alone application for consulting the entire The world's leading online dictionary of electronic and
bibliographical information on IEC International Standards, electrical terms containing 21 000 terms and definitions in
Technical Specifications, Technical Reports and other English and French, with equivalent terms in 16 additional
documents. Available for PC, Mac OS, Android Tablets and languages. Also known as the International Electrotechnical
iPad. Vocabulary (IEV) online.
IEC publications search - webstore.iec.ch/advsearchform IEC Glossary - std.iec.ch/glossary
The advanced search enables to find IEC publications by a 67 000 electrotechnical terminology entries in English and
variety of criteria (reference number, text, technical French extracted from the Terms and Definitions clause of
committee,…). It also gives information on projects, replaced IEC publications issued since 2002. Some entries have been
and withdrawn publications. collected from earlier publications of IEC TC 37, 77, 86 and
CISPR.
IEC Just Published - webstore.iec.ch/justpublished
Stay up to date on all new IEC publications. Just Published IEC Customer Service Centre - webstore.iec.ch/csc
details all new publications released. Available online and If you wish to give us your feedback on this publication or
also once a month by email. need further assistance, please contact the Customer Service
Centre: sales@iec.ch.
IEC TR 63114 ®
Edition 1.0 2018-04
TECHNICAL
REPORT
Electrical steel – Reverse bend test method for electrical steel strip and sheet
INTERNATIONAL
ELECTROTECHNICAL
COMMISSION
ICS 29.030 ISBN 978-2-8322-5616-9
– 2 – IEC TR 63114:2018 © IEC 2018
CONTENTS
FOREWORD . 3
INTRODUCTION . 5
1 Scope . 6
2 Normative references . 6
3 Terms and definitions . 6
4 Symbols and designations . 7
5 Principles . 7
6 Apparatus . 7
7 Test specimen . 8
8 Procedure . 8
9 Expression of results . 10
Annex A (informative) An example of the apparatus used for the reverse bend test . 11
Annex B (informative) Dependence of the number of bends on tensile force applied to
the test specimen. 13
B.1 General . 13
B.2 Test results . 13
B.3 Deformation situation of the specimen after failure . 14
B.4 Conclusions . 15
Bibliography . 16
Figure 1 – Apparatus for the reverse bend test of Mode A and Mode B . 7
Figure 2 – Schematic view of the mandrels for Mode A and Mode B . 8
Figure 3 – Method of counting reverse bends. 9
Figure A.1 – Schematic view of a specially designed apparatus for the reverse bend test . 11
Figure B.1 – Number of bends for different tensile forces with Mode A . 13
Figure B.2 – Number of bends for different tensile forces with Mode B . 14
Figure B.3 – Side views of the specimens after failure with Mode A and Mode B for
different tensile forces . 14
INTERNATIONAL ELECTROTECHNICAL COMMISSION
____________
ELECTRICAL STEEL –
REVERSE BEND TEST METHOD FOR
ELECTRICAL STEEL STRIP AND SHEET
FOREWORD
1) The International Electrotechnical Commission (IEC) is a worldwide organization for standardization comprising
all national electrotechnical committees (IEC National Committees). The object of IEC is to promote
international co-operation on all questions concerning standardization in the electrical and electronic fields. To
this end and in addition to other activities, IEC publishes International Standards, Technical Specifications,
Technical Reports, Publicly Available Specifications (PAS) and Guides (hereafter referred to as “IEC
Publication(s)”). Their preparation is entrusted to technical committees; any IEC National Committee interested
in the subject dealt with may participate in this preparatory work. International, governmental and non-
governmental organizations liaising with the IEC also participate in this preparation. IEC collaborates closely
with the International Organization for Standardization (ISO) in accordance with conditions determined by
agreement between the two organizations.
2) The formal decisions or agreements of IEC on technical matters express, as nearly as possible, an international
consensus of opinion on the relevant subjects since each technical committee has representation from all
interested IEC National Committees.
3) IEC Publications have the form of recommendations for international use and are accepted by IEC National
Committees in that sense. While all reasonable efforts are made to ensure that the technical content of IEC
Publications is accurate, IEC cannot be held responsible for the way in which they are used or for any
misinterpretation by any end user.
4) In order to promote international uniformity, IEC National Committees undertake to apply IEC Publications
transparently to the maximum extent possible in their national and regional publications. Any divergence
between any IEC Publication and the corresponding national or regional publication shall be clearly indicated in
the latter.
5) IEC itself does not provide any attestation of conformity. Independent certification bodies provide conformity
assessment services and, in some areas, access to IEC marks of conformity. IEC is not responsible for any
services carried out by independent certification bodies.
6) All users should ensure that they have the latest edition of this publication.
7) No liability shall attach to IEC or its directors, employees, servants or agents including individual experts and
members of its technical committees and IEC National Committees for any personal injury, property damage or
other damage of any nature whatsoever, whether direct or indirect, or for costs (including legal fees) and
expenses arising out of the publication, use of, or reliance upon, this IEC Publication or any other IEC
Publications.
8) Attention is drawn to the Normative references cited in this publication. Use of the referenced publications is
indispensable for the correct application of this publication.
9) Attention is drawn to the possibility that some of the elements of this IEC Publication may be the subject of
patent rights. IEC shall not be held responsible for identifying any or all such patent rights.
The main task of IEC technical committees is to prepare International Standards. However, a
technical committee may propose the publication of a technical report when it has collected
data of a different kind from that which is normally published as an International Standard, for
example "state of the art".
IEC TR 63114, which is a technical report, has been prepared by IEC Technical Committee 68:
Magnetic alloys and steels.
The text of this technical report is based on the following documents:
Enquiry draft Report on voting
68/565/DTR 68/579A/RVDTR
Full information on the voting for the approval of this technical report can be found in the
report on voting indicated in the above table.
– 4 – IEC TR 63114:2018 © IEC 2018
This document has been drafted in accordance with the ISO/IEC Directives, Part 2.
The committee has decided that the contents of this document will remain unchanged until the
stability date indicated on the IEC website under "http://webstore.iec.ch" in the data related to
the specific document. At this date, the document will be
• reconfirmed,
• withdrawn,
• replaced by a revised edition, or
• amended.
A bilingual version of this publication may be issued at a later date.
INTRODUCTION
Before the preparation of this document, the working group discussed the actual situation of
industry concerning the application of reverse bend tests for the evaluation of the ductility of
electrical steel strip and sheet, including non-oriented and grain-oriented materials. The
following points were noted:
– The reverse bend test is widely used in industry for the evaluation of ductility of electrical
steel, and is referenced by the products standards;
– In actual industry practice, the reverse bend test mainly uses as test specimens Epstein
strips of 30 mm in width;
– The product standards of IEC 60404-8-4 [1] , IEC 60404-8-7 [2] and IEC 60404-8-8 [3]
refer to ISO 7799 for the reverse bend test. However, ISO 7799 specified the width of test
specimen to be less than the width of the Epstein strip (30 mm). Therefore, the Epstein
strip does not meet with the requirement of ISO 7799;
– There are two modes for the reverse bend test, Europe generally adopts the method of
reverse bend test according to ISO 7799 (defined as Mode A), alternatively America and
Asia generally adopt that according to ASTM A720 [4] (for non-oriented materials) and
JIS C2550 [5] (defined as Mode B), see also the references [6-7];
NOTE ASTM A721 [8] defined a bend method, which is different from the reverse bend test, to determine the
ductility of grain-oriented materials.
– The apparatus and the requirements for the reverse bend test are slightly different
between Mode A and Mode B, especially on the gap between the specimen and the round
edges of the clamp and the requirement that a tensile force is applied to the test specimen;
This may cause different deformation mechanisms during bending;
– A comparison test between the two modes has been carried out. It was revealed that
number of bends obtained with Mode A and Mode B are different.
The above points indicate the need for a standardization of the reverse bend test method
particular to electrical steel to explain how to use the two modes in industry.
This document describes the general principle and technical details of the reverse bend test
especially for the evaluation of the ductility of electrical steel with respect to the two modes,
Mode A according to ISO 7799 and Mode B according to ASTM A720 and JIS C2550.
Annex A provides information on a specially designed apparatus for the reverse bend test,
which can be used for both modes.
Annex B gives test results on the dependence of the number of bends on the tensile force
applied to the specimen. The results were obtained using the apparatus described in Annex A
in different conditions for Mode A and for Mode B.
___________
Numbers in square brackets refer to the Bibliography.
– 6 – IEC TR 63114:2018 © IEC 2018
ELECTRICAL STEEL –
REVERSE BEND TEST METHOD FOR
ELECTRICAL STEEL STRIP AND SHEET
1 Scope
This Technical Report describes the general principle and technical details of the reverse
bend test method used for evaluating the ductility of electrical steel strip and sheet.
This test method is applicable to Epstein test strip specimens obtained from non-oriented and
grain-oriente
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.