DRAFT INTERNATIONAL STANDARD
ISO/DIS 15177
ISO/TC 17/SC 12 Secretariat: ANSI
Voting begins on: Voting terminates on:
2019-12-24 2020-03-17
Steel sheet, hot-rolled twin-roll cast, of commercial quality
ICS: 77.140.50
THIS DOCUMENT IS A DRAFT CIRCULATED
FOR COMMENT AND APPROVAL. IT IS
THEREFORE SUBJECT TO CHANGE AND MAY
NOT BE REFERRED TO AS AN INTERNATIONAL
STANDARD UNTIL PUBLISHED AS SUCH.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL,
This document is circulated as received from the committee secretariat.
TECHNOLOGICAL, COMMERCIAL AND
USER PURPOSES, DRAFT INTERNATIONAL
STANDARDS MAY ON OCCASION HAVE TO
BE CONSIDERED IN THE LIGHT OF THEIR
POTENTIAL TO BECOME STANDARDS TO
WHICH REFERENCE MAY BE MADE IN
Reference number
NATIONAL REGULATIONS.
ISO/DIS 15177:2019(E)
RECIPIENTS OF THIS DRAFT ARE INVITED
TO SUBMIT, WITH THEIR COMMENTS,
NOTIFICATION OF ANY RELEVANT PATENT
RIGHTS OF WHICH THEY ARE AWARE AND TO
PROVIDE SUPPORTING DOCUMENTATION. ISO 2019
---------------------- Page: 1 ----------------------
ISO/DIS 15177:2019(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Fax: +41 22 749 09 47
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/DIS 15177:2019(E)
Contents Page
Foreword ........................................................................................................................................................................................................................................iv
1 Scope ................................................................................................................................................................................................................................. 1
2 Normative references ...................................................................................................................................................................................... 1
3 Terms and definitions ..................................................................................................................................................................................... 1
4 Dimensions ................................................................................................................................................................................................................. 2
5 Conditions of manufacture ........................................................................................................................................................................ 2
5.1 Steelmaking ............................................................................................................................................................................................... 2
5.2 Chemical composition ...................................................................................................................................................................... 2
5.3 Chemical analysis .................................................................................................................................................................................. 2
5.3.1 Heat analysis ...................................................................... .................................................................................................. 2
5.3.2 Product analysis ............................................................................................................................................................... 3
5.4 Mechanical properties ...................................................................................................................................................................... 3
5.5 Application ................................................................................................................................................................................................. 4
5.6 Weldability .................................................................................................................................................................................................. 4
5.7 Surface condition .................................................................................................................................................................................. 4
5.8 Oiling ................................................................................................................................................................................................................ 4
5.9 Skin passing ............................................................................................................................................................................................... 4
6 Dimensional and shape tolerances ................................................................................................................................................... 4
7 Tensile test sampling ....................................................................................................................................................................................... 4
8 Tensile test .................................................................................................................................................................................................................. 5
9 Retests ............................................................................................................................................................................................................................. 5
9.1 Machining and flaws........................................................................................................................................................................... 5
9.2 Elongation ................................................................................................................................................................................................... 5
9.3 Additional tests ....................................................................................................................................................................................... 5
10 Resubmission ........................................................................................................................................................................................................... 5
11 Workmanship .......................................................................................................................................................................................................... 5
12 Inspection and acceptance ......................................................................................................................................................................... 5
13 Coil size ........................................................................................................................................................................................................................... 6
14 Marking .......................................................................................................................................................................................................................... 6
15 Information to be supplied by the purchaser......................................................................................................................... 6
Bibliography ................................................................................................................................................................................................................................ 8
© ISO 2019 – All rights reserved iii---------------------- Page: 3 ----------------------
ISO/DIS 15177:2019(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International
Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies
casting a vote.Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 15177 was prepared by Technical Committee ISO/TC 17, Steel, Subcommittee SC 12, Continuous mill
flat rolled products.iv © ISO 2019 – All rights reserved
---------------------- Page: 4 ----------------------
DRAFT INTERNATIONAL STANDARD ISO/DIS 15177:2019(E)
Steel sheet, hot-rolled twin-roll cast, of commercial quality
1 Scope
This document specifies the requirements for hot-rolled twin-roll cast steel sheet of commercial quality.
The product is intended for many applications where the presence of oxide or scale or normal surface
imperfections disclosed after removal of oxide or scale, are not objectionable. It is not suitable for
applications where the surface is of prime importance.NOTE This document does not cover steel sheet that is to be subjected to subsequent rolling.
2 Normative referencesThe following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 6892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
ISO 16160, Hot-rolled steel sheet products — Dimensional and shape tolerances3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— IEC Electropedia: available at https:// www .electropedia .org/— ISO Online browsing platform: available at https:// www .iso .org/ obp
3.1
hot-rolled twin-roll cast steel sheet
product resulting from the twin-roll process to obtain the required sheet thickness and tolerances
3.2hot-rolled descaled steel sheet
hot-rolled steel sheet from which oxide or scale has been removed, commonly by pickling in an acid
solutionNote 1 to entry: Descaling may also be performed by mechanical methods such as grit blasting. Some change in
properties can result from descaling.3.3
skin pass
light cold rolling of hot-rolled steel sheet or hot-rolled descaled steel sheet.
Note 1 to entry: The purpose of the skin pass is to produce a higher degree of surface smoothness and thereby
improve the surface appearance. The shin pass also temporarily minimizes the occurrence of a surface condition
known as stretcher strain (Lüder’s Lines) or fluting during the fabrication of finished parts. The skin pass also
controls and improves flatness. Some increase in hardness and loss of ductility will result from skin passing.
© ISO 2019 – All...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.