ISO 306:1987

Plastics — Thermoplastic materials — Determination of Vicat softening temperature

Plastiques — Matières thermoplastiques — Détermination de la température de ramollissement Vicat

General Information

• Status: Withdrawn
• Publication Date: 16-Dec-1987
• Withdrawal Date: 16-Dec-1987
• ICS: 83.080.20 - Thermoplastic materials
• Technical Committee: ISO/TC 61/SC 2 - Mechanical behavior
• Drafting Committee: ISO/TC 61/SC 2 - Mechanical behavior
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 31-Jul-1994

Relations

• Revised: ISO 306:1994 - Plastics — Thermoplastic materials — Determination of Vicat softening temperature (VST)
• Effective Date: 15-Apr-2008
• Revised: SIST ISO 306:1996 - Plastics -- Thermoplastic materials -- Determination of Vicat softening temperature (VST)
• Effective Date: 12-May-2008
• Revises: ISO 306:1974 - Plastics — Determination of the Vicat softening temperature of thermoplastics
• Effective Date: 15-Apr-2008

Standards Content (Sample)

:so
306
INTERNATIONAL STANDARD
econd edition
987-12-15
~~
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
MEXAYHAPOAHAR OPTAHM3AuMR il0 CTAHAAPTM3AuMM
~ .
Plastics - Thermoplastic materials - Determination
of Vicat softening temperature
Plastiques - Matières thermoplastiques - Détermination de la température de
ramollissement Vicat
Reference number
IS0 306 : 1987 (E)

---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 306 was prepared by Technical Committee ISO/TC 61,
Plastics.
This second edition cancels and replaces the first edition (IS0 306 : 1974). of which it
constitutes a technical revision.
Users should note that all International Standards undergo revision from time to time
and that any reference made herein to any other International Standard implies its
latest edition, unless otherwise stated.
O International Organization for Standardization, 1987 0
Printed in Switzerland

---------------------- Page: 2 ----------------------
IS0 306 : 1987 (E)
INTERNATIONAL STANDARD
Plastics - Thermoplastic materials - Determination
of Vicat softening temperature
4 Apparatus
1 Scope and field of application
The apparatus consists essentially of:
1 .I This International Standard specifies two methods for
the determination of the Vicat softening temperature of ther-
4.1 Rod, provided with a load-carrying plate (4.4), held in a
moplastic materials :
rigid metal frame so that it can move freely in the vertical
-
Method A using a load of 10 N
direction, the base of the frame serving to support the test
'4
specimen under the indenting tip at the end of the rod (see the
-
Method 6 using a load of 50 N
figure).
Unless the rod and frame members have the same linear expan-
1.2 The methods specified are applicable only to thermo-
sion coefficient, the differential change in the length of these
plastics, for which they give a measure of the temperature at
parts introduces an error in the readings of the apparent defor-
which the thermoplastics start to soften rapidly.
mation of the test specimen. A blank test shall be made on each
apparatus using a test specimen made of rigid material having a
low coefficient of expansion.1) The temperature ranges to be
used shall be covered and a correction term determined for
2 References
each temperature. If the correction term is 0,02 mm or greater,
its algebraic sign shall be noted and the term applied to each
IS0 291, Plastics - Standard atmospheres for conditioning
test by adding it algebraically to the reading of apparent
and testing.
penetration. It is recommended that the apparatus be con-
structed of low thermal expansion alloy.
IS0 293, Plastics - Recommended practice for compression
moulding test specimens of thermoplastic materials.
4.2 indenting tip, preferably of hardened steel, 3 mm long,
IS0 294, Plastics - Injection moulding test specimens of ther-
of circular cross-section, and area 1 ,O00 k 0,015 mm2, fixed at
moplastic materials.
the bottom of the rod (4.1). The lower surface of the indenting
tip shall be plane and perpendicular to the axis of the rod and
IS0 2818, Plastics - Preparation of test specimens by
free from burrs.
*C machining.
IS0 3167, Plastics - Preparation and use of multi-purpose test
4.3 Calibrated micrometer dial gauge (or other suitable
specimens.
measuring instrument), to measure to 11 0,Ol mm the penetra-
tion of the indenting tip into the test specimen. The thrust of
the dial gauge, which contributes to the thrust on the, test
specimen, must be known (see 4.4).
3 Principle
NOTES
Determination of the temperature at which a standard indenter
1 In certain forms of execution of the apparatus, the force of the dial
penetrates 1 mm into the surface of a plastic test specimen
gauge spring is directed upward and is subtracted from the load; in
under one of the loads given in 1.1 when the temperature is
other forms, this force acts downward and is added to the load.
raised at a uniform rate.
2 Since the force exerted by the spring in certain dial gauges varies
The temperature at 1 mm penetration is quoted as the Vicat considerably over the stroke, this force is measured in that part of the
stroke which is to be used.
softening temperature (VST) in degrees Celsius.
lnvar and borosilicate glas have been found suitable for this purpose.
1)
1

---------------------- Page: 3 ----------------------
IS0 306 : 1987 (El
4.4 Load-carrying plate, fitted to the rod (4.1), and one surface (see IS0 2818), the other surface being left
centrally so that the total thrust intact; the test surface shall be the intact one:
suitable weights added
applied to the test specimen can be made up to 10 i 0,2 N
for method A and 50 +_ 1 N for method B. The combined b) if the thickness of the sheet is less than 3 mm, not more
downward thrust due to the rod, indenting tip, load-carrying than three pieces shall be stacked together in good contact
plate and the force of the dial gauge spring shall not ex- to give a total thickness between 3 and 6,5 mm and the
thickness of the upper (measured) piece shall be at least
ceed 1 N.
1,5 mm. Stacking of pieces of lesser thickness does not
always result in the same value of the measured quantity.
4.5 Heating bath, containing a suitable liquid in which the
apparatus is placed so that the specimen is at least 35 mm
below the surface of the liquid. An efficient stirrer shall be pro-
vided. The heating bath shall be equip
...

IS0
NORME INTERNATIONALE
306
Deuxième édition
1987-12-1 5
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION
ORGANISATION INTERNATIONALE DE NORMALISATION
MEXAYHAPOAHAR OPrAHM3AuMFi no CTAHjJAPTM3AuMM
Plastiques - Matières thermoplastiques -
Détermination de la température de
ram ol I issement Vicat
Plastics - Thermoplastic materials - Determination of Vicat softening temperature
Numéro de référence
IS0 306 : 1987 (F)

---------------------- Page: 1 ----------------------
Avant-propos
L‘ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est normalement confiée aux comités techniques de I’ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec I’ISO participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I‘ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I‘ISO qui requièrent l‘approbation de 75 % au moins des
comités membres votants.
La Norme internationale IS0 306 a été élaborée par le comité technique ISO/TC 61,
Plastiques.
Cette deuxième édition annule et remplace la première édition (IS0 306 : 19741, dont
elle constitue une révision technique.
L‘attention des utilisateurs est attirée sur le fait que toutes les Normes internationales
sont de temps en temps soumises à révision et que toute référence faite à une autre
Norme internationale dans le présent document implique qu’il s’agit, sauf indication
contraire, de la dernière édition.
O Organisation internationale de normalisation, 1987 O
Imprimé en Suisse

---------------------- Page: 2 ----------------------
~~
NORME INTERNATIONALE IS0 306 : 1987 (FI
Plastiques - Matières thermoplastiques -
Détermination de la température de
ra mol I issement Vicat
1 Objet et domaine d’application 4 Appareillage
L‘appareillage comprend essentiellement les éléments suivants:
1 .I La présente Norme internationale spécifie deux méthodes
de détermination de la température de ramollissement Vicat des
4.1 Tige, équipée d’un plateau porte-poids (4.4), montée
‘L thermoplastiques:
dans un équipage rigide en métal de facon qu’elle puisse se
-
déplacer librement dans une direction verticale, la base du mon-
Méthode A utilisant une charge de 10 N
tage servant de support à l’éprouvette sous la pointe du péné-
-
Méthode B utilisant une charge de 50 N
trateur située à l’extrémité de la tige (voir la figure).
Lorsque la tige et les éléments du montage n’ont pas le même
1.2 Les méthodes spécifiées sont seulement applicables aux
coefficient de dilatation linéique, leur variation différentielle de
thermoplastiques pour lesquels elles permettent de mesurer la
longueur entraîne une erreur dans les lectures de la déformation
température à laquelle leur ramollissement devient rapide.
apparente de l’éprouvette. Un essai à blanc doit être effectué
avec chaque appareil en utilisant une éprouvette en matière
rigide ayant un faible coefficient de dilatation.1) Cet essai doit
couvrir tout le domaine de température utilisable et un terme
2 Références
correctif doit être déterminé à chaque température. Si le terme
correctif est supérieur ou égal à 0,02 mm, son signe algébrique
IS0 291, Plastiques - Atmosphères normales de conditionne-
doit être noté et la correction doit être appliquée à chaque essai
ment et d‘essai.
en l’ajoutant algébriquement à la valeur lue de la pénétration
apparente. II est recommandé de construire l’appareillage avec
IS0 293, Plastiques - Moulage par compression des éprou-
un alliage de faible coefficient de dilatation.
vettes en matières thermoplastiques.
IS0 294, Plastiques - Moulage par injection des éprouvettes
4.2 Pointe de pénétrateur, en acier trempé de préférence, de
en matières thermoplastiques.
longueur 3 mm et de section circulaire, d’aire 1,ooO f 0,015 mm*,
L
fixée à l‘extrémité de la tige (4.1). La partie inférieure du pénétra-
IS0 2818, Plastiques - Préparation des éprouvettes par à l‘axe de la tige, et exempte
teur doit être plane et perpendiculaire
usinage. de bavures.
I SO 3167, Plastiques - Préparation et utilisation d‘éprouvettes
4.3 Micromètre à cadran étalonné (ou tout autre instru-
à usages multiples.
ment de mesure adapté), pour mesurer à 0,Ol mm près la péné-
tration de la pointe du pénétrateur dans l’éprouvette. La
poussée du micromètre, qui contribue à celle appliquée sur
l’éprouvette, doit être connue (voir 4.4).
3 Principe
NOTES
Détermination de la température à laquelle un pénétrateur nor-
malisé, soumis à l‘une des charges indiquées en 1 .l, s’enfonce 1 Dans certains modes de réalisation de l‘appareillage, la force du res-
de 1 mm dans la surface de l’éprouvette de plastique, quand la sort du micromètre à cadran est dirigée vers le haut et est retranchée de
la charge; dans d‘autres réalisations, cette force agit vers le bas et est
température est élevée à une vitesse constante.
ajoutée à la charge.
La température à laquelle la pénétration est de 1 mm est
2 Étant donné que, dans certains micromètres à cadran, la force
appelée température de ramollissement Vicat (VST) en degrés
excercée par le ressort varie considérablement dans l‘étendue de la
Celsius. course, celle-ci est mesurée dans le domaine utile de la course.
L’lnvar et le verre borosilicaté conviennent pour cet usage.
1)
1

---------------------- Page: 3 ----------------------
IS0 306 : 1987 (FI
4.4 Plateau porte-poids, fixé à la tige (4.1) et des poids 5.3 Pour les matières en plaques, l‘épaisseur des éprouvettes
doit être égale à l’épaisseur de la plaque, sinon comme suit:
appropriés déposés au centre, tels que la poussée totale appli-
quée à l’éprouvette puisse être ajustée à 10 f 0,2 N pour la
a) si l’épaisseur dépasse 6,5 mm, l’éprouvette doit être
méthode A et 50 k 1 N pour la méthode B. La poussée vers le
ramenée à une épaisseur de 3 à 6,5 mm par usinage d’une
bas due à l‘ensemble tige, pénétratreur, plateau porte-poids et
seule face (voir IS0 2818), l’autre étant laissée intacte;
la force du ressort du micromètre ne doit pas dépasser 1 N.
b) si l’épaisseur de la plaque est inférieure à 3 mm, trois
éléments, au plus, doivent être empilés en bon contact pour
4.5 Bain chauffant, contenant un liquide approprié dans
obtenir une épaisseur totale comprise entre 3 et 6,5 mm; la
lequel l‘appareillage est placé de facon que l’éprouvette soit au
face soumise à l’essai doit être la face non usinée et I’épais-
moins à 35 mm en dessous de la surface du liquide. Un agita-
seur de l’élé
...