ISO 18921:2002

Imaging materials — Compact discs (CD-ROM) — Method for estimating the life expectancy based on the effects of temperature and relative humidity

Matériaux pour l'image — Disques compacts (CD-ROM) — Méthode d'estimation de l'espérance de vie basée sur les effets de la température et de l'humidité relative

General Information

• Status: Withdrawn
• Publication Date: 15-May-2002
• Withdrawal Date: 15-May-2002
• ICS: 35.220.30 - Optical storage devices
• ICS: 37.040.99 - Other standards related to photography
• Technical Committee: ISO/TC 42 - Photography
• Drafting Committee: ISO/TC 42/WG 5 - Physical properties and image permanence of photographic materials
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 06-Oct-2008

Relations

• Revised: ISO 18921:2008 - Imaging materials — Compact discs (CD-ROM) — Method for estimating the life expectancy based on the effects of temperature and relative humidity
• Effective Date: 15-Apr-2008
• Consolidated By: ISO 18113-5:2009 - In vitro diagnostic medical devices — Information supplied by the manufacturer (labelling) — Part 5: In vitro diagnostic instruments for self-testing
• Effective Date: 06-Jun-2022

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 18921
First edition
2002-04-15
Imaging materials — Compact discs
(CD-ROM) — Method for estimating the life
expectancy based on the effects of
temperature and relative humidity
Matériaux pour l'image — Disques compacts (CD-ROM) — Méthode
d'estimation de l'espérance de vie basée sur les effets de la température et
de l'humidité relative

Reference number
ISO 18921:2002(E)
©
ISO 2002

---------------------- Page: 1 ----------------------
ISO 18921:2002(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not be
edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file,
parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.
© ISO 2002
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's
member body in the country of the requester.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Printed in Switzerland
©
ii ISO 2002 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 18921:2002(E)
Contents Page
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Purpose and assumptions . 3
5 Measurements . 3
6 Accelerated stress test plan . 4
7 Data evaluation . 8
8 Disclaimer . 10
Annexes
A Numbering system for related International Standards. 11
B Step analysis outline. 13
C Example of a test plan and data analysis . 14
Bibliography. 21
©
ISO 2002 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 18921:2002(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this International Standard may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
International Standard ISO 18921 was prepared by Technical Committee ISO/TC 42, Photography.
This International Standard is one of a series of standards dealing with the physical properties and stability of
imaging materials. To facilitate identification of these International Standards, they are assigned a number within the
block from 18900 – 18999 (see annex A).
Annexes A, B and C of this International Standard are for information only.
©
iv ISO 2002 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 18921:2002(E)
Imaging materials — Compact discs (CD-ROM) — Method for
estimating the life expectancy based on the effects of temperature
and relative humidity
1 Scope
This International Standard specifies a test method for estimating the life expectancy (LE) of information stored on
compact disc (CD-ROM) media, including CD audio, but excluding recordable media. Only the effects of temperature
and relative humidity on the media are considered.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this International Standard. For dated references, subsequent amendments to, or revisions of, any of these
publications do not apply. However, parties to agreements based on this International Standard are encouraged to
investigate the possibility of applying the most recent editions of the normative documents indicated below. For
undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC
maintain registers of currently valid International Standards.
ISO/IEC 10149:1995, Information technology — Data interchange on read-only 120mm optical data disks
(CD-ROM)
IEC 60908:1999, Audio recording — Compact disc digital audio system
3 Terms and definitions
For the purposes of this International Standard, the following terms and definitions apply.
3.1
F (t)
probability that a random unit drawn from the population fails by time t, or the fraction of all units in the population
which fails by time t
3.2
R(t)
probability that a unit drawn from the population will survive at least time t, or the fraction of units in the population
that will survive at least time t
NOTE R(t)= 1−F (t).
3.3
baseline
condition representing the disc at time of manufacture
NOTE This is customarily the initial parameter measurement taken prior to any application of stress. The designation is usually
t = 0 for a stress time equal to zero hours.
©
ISO 2002 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO 18921:2002(E)
3.4
block error rate
BLER
ratio of erroneous blocks to total blocks measured at the input of the first (C1) decoder (before any error correction is
applied)
NOTE The more commonly reported value for BLER is the number of erroneous blocks per second measured at the input of the
C1-decoder during playback at the standard (1×) data rate.
[IEC 60908:1999]
3.5
CD-ROM
compact disc-read only medium
3.6
end-of-life
occurrence of any loss of information
3.7
information
signal or image recorded using the system
3.8
life expectancy
LE
length of time that information is predicted to be retrievable in a system under extended-term storage conditions
3.8.1
standardized life expectancy
SLE
95 % 95 %
minimum life span, predicted with confidence, of of the product stored at a temperature not exceeding
◦
25C5 and a relative humidity (RH) not exceeding 0% RH
3.9
retrievability
ability to access information as recorded
3.10
stress
experimental variable to which the specimen is exposed for the duration of the test interval
NOTE In this International Standard, the stress variables are confined to temperature and relative humidity.
3.11
system
combination of recording medium, hardware, software and documentation necessary to retrieve information
3.12
test cell
device that controls the stress to which the specimen is exposed
3.13
test pattern
distribution of the characters l and 0 within a block and the block-to-block variation
©
2 ISO 2002 – All rights reserved

---------------------- Page: 6 ----------------------
ISO 18921:2002(E)
4 Purpose and assumptions
4.1 Purpose
The purpose of this International Standard is to establish a methodology for estimating the life expectancy of
information stored on CD-ROMs. This methodology provides a technically and statistically sound procedure for
obtaining and evaluating accelerated test data.
4.2 Assumptions
The validity of the procedure defined by this International Standard relies on three assumptions:
— the dominant failure mechanism acting at the usage condition is the same as at the accelerated conditions;
— the dominant failure mechanism is appropriately modelled by an Eyring acceleration model;
— life expectancy is appropriately modelled by the two parameter Weibull distribution (see [1] in the Bibliography).
The shape parameter of the Weibull distribution is assumed to be independent of the stress level.
5 Measurements
5.1 Block error rate (BLER)
The objective of measuring the block error rate (BLER) is to establish a practical estimation of the system's ability to
read the pre-recorded bits using a standard drive. This International Standard considers BLER to be a high level
estimate of the performance of the system. A change in BLER in response to the time at an elevated temperature
and humidity is the principal quality parameter.
The true end-of-life is loss of information. Ideally, each specimen is tested until actual time of failure occurs.
Realistically, this is impractical. For the purposes of this International Standard, the maximum ten-second average of
the BLER, as specified in ISO/IEC 10149, shall be 220. This is very dependent on the system and its use here is an
arbitrary level chosen as a conservative prediction of the onset of unacceptable errors and thereby the end of disc
life.
5.2 Test equipment
5.2.1 Compact disc test system
Any compact disc test system (tester) that is in accordance with ISO/IEC 10149 may be used. The make, model and
version of the test equipment (including software) shall be reported with the test results.
5.2.2 Calibration and repeatability
Calibration according to the tester manufacturer's procedure shall be performed prior to any measurement data
being collected. A calibration disc shall be available from the tester manufacturer.
In addition to the calibration disc, one control disc shall be maintained at ambient conditions and its maximum BLER
measured before and after each data collection interval. A control chart shall be maintained for this control disc with
± 3σ action limits. The mean and standard deviation of the control disc shall be established by collecting at least five
measurements. Should any individual maximum BLER reading exceed the action limit, the problem shall be
corrected and all data collected since the last valid control point shall be remeasured.
If it becomes necessary to replace the tester, a method shall be followed for correlating tester outputs (see [2] in the
Bibliography).
©
ISO 2002 – All rights reserved 3

---------------------- Page: 7 ----------------------
ISO 18921:2002(E)
5.3 Test specimen
A test specimen is any disc that meets ISO/IEC 10149 specifications and contains representative data extending to
within 2mm of the maximum recording diameter.
6 Accelerated stress test plan
6.1 General
A CD-ROM of good manufacture should last several years or even decades. Consequently, it is necessary to conduct
accelerated ageing studies in order to develop a life expectancy estimate. The key is conducting and evaluating a test
plan that will provide the information necessary to satisfactorily evaluate the particular product.
Many accelerated life test plans follow a rather traditional approach in sampling, experimentation and data
evaluation. These “traditional plans” share the following characteristics:
— the total number of specimens is evenly divided amongst all the accelerated stresses;
— each stress is evaluated at the same time increments;
— the Arrhenius relationship is used as the acceleration model;
— the Least Squares method is used for all regressions;
— the calculated life expectancy is for the mean or median life rather than for the first few failure percentiles.
On the other hand, “optimum test plans” have been proposed which differ in significant aspects from traditional plans.
These plans have the following characteristics:
— two and only two acceleration levels for each stress;
— a large number of specimens distributed mostly in the lowest stress levels;
— the need to know the failure distribution, a priori, in order to develop the plan.
The maximum effectiveness of a plan can either be estimated before the test starts or determined after the results
have been obtained. As each CD-ROM system has different characteristics, a specific, detailed optimum plan is
impossible to forecast.
This test plan borrows from the optimum plan, the traditional plan, previous experience with the systems, test
equipment and accelerated test stresses to put together a “compromise test plan”. Modifications of this plan will be
required to design the best plan for other applications. The methodology shall be applicable to all CD-ROM media
assessments.
6.2 Stress conditions
6.2.1 Levels
As mentioned in 6.1, an optimum test plan utilizes only two stress levels for each parameter evaluated, since in an
ideal case the relationship between changes in the parameter investigated and changes in stress is known. The
compromise test plan documented in this International Standard does not make such an assumption; therefore, three
different stress levels per parameter shall be used so that the linearity of the parameter function versus the stress
level may be demonstrated.
The test plan shall have the majority of test specimens placed at the lowest stress condition. This minimizes the
estimation error at this condition and results in the best estimate of the degradation rate at a level close to the usage
condition. The greater number of specimens at the lower stress also tends to equalize the number of failures
observed by test completion.
©
4 ISO 2002 – All rights reserved

---------------------- Page: 8 ----------------------
ISO 18921:2002(E)
6.2.2 Conditions
For implementing the test plan documented in this International Standard, five stress conditions shall be used. The
minimum distribution of specimens among the stress points that shall be used is shown in Table 1. For improved
precision, additional specimens and conditions may be used if desired.
Table 1 — Summary of stress conditions
Minimum
Test cell Number of Incubation Minimum total Intermediate
Test stress equilibrium
number specimens duration time RH
duration
hh RH h
T /RH
int
inc inc
◦
80 C/85 % 31 %
1 RH 10 500 2 000 6
◦
80 C/70 % 31 %
2 RH 10 500 2 000 8
◦
80 C/55 % 31 %
3 RH 15 500 2 000 4
◦
70 C/85 % 33 %
4 RH 15 750 3 000 8
◦
60 C/85 % 36 %
5 RH 30 1 000 4 000 11
6.2.3 Temperature (T)
The temperature levels chosen for this test plan are based on the following:
— there shall be no change of phase within the test system over the test temperature range. This restricts the
◦ ◦
0 C 100 C
temperature to greater than and less than ;
— the temperature level shall not be so high that plastic deformation occurs.
◦
The typical substrate material for CD-ROMs is polycarbonate (glass transition temperature ∼ 150 C). The glass
transition temperature of other layers may be lower. Experience with high temperature testing of CD-ROMs indicates
◦
that an upper limit of 80 C is practical for most applications.
6.2.4 Relative humidity (RH)
Practical experience shows that 85 % RH is the upper limit within most accelerated test cells. This is due to the
tendency for condensation to occur on cool sections of the chamber, e.g., observation windows, cable ports, wiper
handles, etc. Droplets may become dislodged and entrained in the circulating air within the chamber. If these droplets
fall on the test specimen, false error signals could be produced.
6.2.5 Rate of stress change
The process described in this International Standard requires that discs be ramped from the test conditions to stress
conditions and back again a number of times during the course of testing. The ramp duration and conditions shall be
chosen to allow sufficient equilibration of absorbed substrate moisture.
Large departures from equilibrium conditions may result in the formation of liquid water droplets inside the substrate
or at its interface with the reflecting layer. Gradients in the water concentration through the thickness of the substrate
shall also be limited. These gradients drive expansion gradients which can cause significant disc deflection.
In order to minimize moisture concentration gradients, the ramp profile specified in Table 2 shall be used. The objects
of the profile are:
— to avoid any situation that may cause moisture condensation within the substrate;
— to minimize the time during which substantial moisture gradients exist in the substrate;
— to produce, at the end of the specified profile, a disc that is sufficiently equilibrated to proceed directly to testing
without delay.
©
ISO 2002 – All rights reserved 5

---------------------- Page: 9 ----------------------
ISO 18921:2002(E)
The profile accomplishes this by varying the moisture content of the disc only at the stress incubation temperature,
and allowing sufficient time for equilibration during ramp-down based on the diffusion coefficient of water in
polycarbonate.
Table 2 — Temperature and relative humidity transition (ramp) profile
Temperature Relative humidity Duration
Process step
◦
C% RH h
Start at T at RH —
amb
amb
T, RH ramp to T to RH 1,5± 0,5
inc int
RH ramp at T to RH 1,5± 0,5
inc inc
Incubation at T at RH See Table 1
inc inc
RH ramp at T to RH 1,5± 0,5
inc int
Equilibration at T at RH See Table 1
inc int
T, RH ramp to T to RH 1,5± 0,5
amb amb
End at T at RH
amb amb
NOTE 1 T and RH are room ambient temperature and relative humidity; T and RH are the stress incubation
amb amb inc inc
temperature and relative humidity; and RH is the intermediate relative humidity that at T supports the same equilibrium
int inc
moisture absorption in polycarbonate as that supported at T and RH (see Table 1).
amb amb
◦
NOTE 2 Transitions should not deviate from a linear change over the chosen duration by more than ± 2 C and ±3% RH.
Ramp transitions may be controlled automatically or manually.
Figure 1 graphically portrays the temperature and relative humidity changes that would occur during one cycle of
◦
incubation at 80C8 and 5% RH, as per Tables 1 and 2.
Key
____ Temperature (T)
........ Relative humidity (RH)
1 T, RH ramp
2 RH ramp
3 Incubation
4 RH ramp
5 Equilibration
6 T, RH ramp
◦
Figure 1 — Graph of nominal 80 C/85 % RH transition (ramp) profile
©
6 ISO 2002 – All rights reserved

---------------------- Page: 10 ----------------------
ISO 18921:2002(E)
6.2.6 Independent verification of chamber conditions
A system independent of the chamber control system shall be used to monitor temperature and humidity conditions
in the test chamber during the stress test.
6.2.7 Specimen placement
Disc specimens shall be placed uncovered, either vertically or horizontally, within the test chamber. Discs shall be
aligned so that their surface is parallel to the chamber airflow, and a space of at least 2mm shall be maintained
between them.
6.2.8 Other influences
During the course of the test, the discs shall be shielded from excessive illumination and potentially corrosive fumes,
gases and liquids.
6.3 Accelerated test cell specimen population
In order to estimate the shape and scale parameters of a Weibull distribution, at least ten failures shall be observed.
◦
Observing at least ten failures is generally not a problem for a realistic test time at 80 C/85 % RH, but becomes
more difficult at milder stress temperature and relative humidity combinations. Assigning a larger percentage of the
specimens at the lower stresses increases the chance of observing the necessary number of failures within a
practical time interval.
Specimens that have not failed at the end of the test duration shall be time censored. This is also known as Type I
censoring (see [3] in the Bibliography).
To compute the estimated failure time for each disc, it is necessary to first determine a transformation of the
maximum BLER, such as log (max. BLER), that results in a linear time dependence. Standard li
...