ISO 2285:2007

Rubber, vulcanized or thermoplastic - Determination of tension set under constant elongation, and of tension set, elongation and creep under constant tensile load

ISO 2285:2007 specifies a number of methods of determining the dimensional changes in test pieces of vulcanized or thermoplastic rubber during and after tensile loading for relatively short periods under constant elongation or constant loading. The constant-elongation test is intended to measure the ability of rubbers to retain their elastic properties after extension, at a standard laboratory temperature, to a specified strain which is maintained for a specified time at the same or at a specified higher temperature and then released at the test temperature or at the standard laboratory temperature. The constant-load test specifies a method for the determination of elongation, creep and tension set of rubbers subjected to a constant load at standard laboratory temperature. The test methods are intended to measure the elastic properties of rubber in the hardness range 20 IRHD to 94 IRHD. The creep measurement is not recommended for product design or the evaluation of low-creep materials. For these, reference should be made to ISO 8013. NOTE The constant-load test is primarily intended for the measurement of state of cure and the quality control of thin-walled products. An increase in the state of cure or degree of crosslinking is usually reflected in a decrease in set, creep or crosslinking.

Caoutchouc vulcanisé ou thermoplastique — Détermination de la déformation rémanente sous allongement constant et de la déformation rémanente, de l'allongement et du fluage sous charge constante de traction

L'ISO 2285:2007 spécifie un certain nombre de méthodes pour déterminer les variations dimensionnelles que subissent des éprouvettes de caoutchouc vulcanisé ou thermoplastique pendant et après l'application d'un chargement en traction, durant des périodes relativement courtes, sous allongement constant ou charge constante. L'essai réalisé sous allongement constant sert à mesurer l'aptitude des caoutchoucs à conserver leurs propriétés élastiques après avoir été soumis à un allongement à une température normale de laboratoire jusqu'à une déformation spécifiée, cette sollicitation étant maintenue pendant une durée définie à la même température ou à une température spécifiée plus élevée, puis supprimée à la température d'essai ou à la température normale de laboratoire. L'essai réalisé sous charge constante spécifie une méthode permettant de déterminer l'allongement, le fluage et la déformation rémanente des caoutchoucs soumis à une charge constante à température normale de laboratoire. Les méthodes d'essai sont destinées à mesurer les propriétés élastiques du caoutchouc dans l'échelle de dureté de 20 DIDC à 94 DIDC. Le mesurage du fluage n'est pas recommandé pour la conception de produits ou l'évaluation de matériaux à faible degré de fluage. Pour ces derniers, il convient de se référer à l'ISO 8013. NOTE L'essai sous charge constante est principalement destiné à mesurer le degré de vulcanisation et à apprécier la maîtrise de la qualité des produits à parois minces. Une augmentation du degré de vulcanisation ou de réticulation se traduit généralement par une diminution de la rémanence, du fluage ou de la réticulation.

General Information

• Status: Withdrawn
• Publication Date: 09-Jul-2007
• Withdrawal Date: 09-Jul-2007
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 2 - Visco-elastic properties
• Current Stage: 9599 - Withdrawal of International Standard
• Start Date: 03-Jan-2013
• Completion Date: 13-Dec-2025

Relations

• Revised: ISO 2285:2013 - Rubber, vulcanized or thermoplastic - Determination of tension set under constant elongation, and of tension set, elongation and creep under constant tensile load
• Effective Date: 13-Nov-2010
• Revises: ISO 2285:2001 - Rubber, vulcanized or thermoplastic - Determination of tension set under constant elongation, and of tension set, elongation and creep under constant tensile load
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 2285
Sixth edition
2007-07-15
Rubber, vulcanized or thermoplastic —
Determination of tension set under
constant elongation, and of tension set,
elongation and creep under constant
tensile load
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
déformation rémanente sous allongement constant et de la déformation
rémanente, de l'allongement et du fluage sous charge constante de
traction
Reference number
©
ISO 2007
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.

©  ISO 2007
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland
ii © ISO 2007 – All rights reserved

Contents Page
Foreword. iv
1 Scope. 1
2 Normative references. 1
3 Terms and definitions. 2
4 Apparatus. 2
5 Test pieces. 4
6 Procedure. 6
7 Expression of results. 8
8 Test report. 9

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 2285 was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This sixth edition cancels and replaces the fifth edition (ISO 2285:2001), which has been revised principally to
update the normative references (ISO 471, ISO 4648 and ISO 4661-1 have been replaced by ISO 23529). In
addition, the text has been clarified in places.

iv © ISO 2007 – All rights reserved

INTERNATIONAL STANDARD ISO 2285:2007(E)

Rubber, vulcanized or thermoplastic — Determination of
tension set under constant elongation, and of tension set,
elongation and creep under constant tensile load
WARNING — Persons using this International Standard should be familiar with normal laboratory
practice. This standard does not purport to address all of the safety problems, if any, associated with
its use. It is the responsibility of the user to establish appropriate safety and health practices and to
ensure compliance with any national regulatory conditions.
CAUTION — Certain procedures specified in this International Standard may involve the use or
generation of substances, or the generation of waste, that could constitute a local environmental
hazard. Reference should be made to appropriate documentation on safe handling and disposal after
use.
1 Scope
This International Standard specifies a number of methods of determining the dimensional changes in test
pieces of vulcanized or thermoplastic rubber during and after tensile loading for relatively short periods under
constant elongation or constant loading.
The constant-elongation test is intended to measure the ability of rubbers to retain their elastic properties after
extension, at a standard laboratory temperature, to a specified strain which is maintained for a specified time
at the same or at a specified higher temperature and then released at the test temperature or at the standard
laboratory temperature.
The constant-load test specifies a method for the determination of elongation, creep and tension set of
rubbers subjected to a constant load at standard laboratory temperature.
The test methods are intended to measure the elastic properties of rubber in the hardness range 20 IRHD to
94 IRHD.
The creep measurement is not recommended for product design or the evaluation of low-creep materials. For
these, reference should be made to ISO 8013. No agreement between the results of this test or those of
ISO 8013 should be inferred.
NOTE The constant-load test is primarily intended for the measurement of state of cure and the quality control of
thin-walled products. An increase in the state of cure or degree of crosslinking is usually reflected in a decrease in set,
creep or elongation.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 188, Rubber, vulcanized or thermoplastic — Accelerated ageing and heat resistance tests
ISO 8013, Rubber, vulcanized — Determination of creep in compression or shear
ISO 23529:2004, Rubber — General procedures for preparing and conditioning test pieces for physical test
methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply (see also the definitions of creep
functions given in ISO 8013).
3.1
tension set at constant load
elongation remaining in a test piece in the unloaded condition after it has been subjected to a constant load
during a specified time, expressed as a percentage of the original length in the unloaded condition
3.2
tension set at constant elongation
elongation remaining in a test piece in the relaxed condition after it has been subjected to a constant
elongation during a specified time, expressed as a percentage of the elongation
3.3
creep
increase in elongation of a test piece at constant load during a specified time, expressed as a percentage of
the elongation at the beginning of that time
4 Apparatus
4.1 Constant-elongation measurements
4.1.1 Straining device, consisting of a metal rod or other suitable guide fitted with pairs of holders, one
fixed and one moveable, for the ends of the test piece. The holders shall be in the form of self-tightening
clamps for strip test pieces, in the form of jaws to hold tab (enlarged) ends, and in the form of flat pulleys of
about 5 mm width and 10 mm diameter for ring test pieces.
If so desired, a means of operating the moving holder other than by hand can be provided, for example a
threaded rod, provided that the tolerances on extension speed are met (see 6.1.2). Suitable stops or
graduations can also be provided to avoid over-extension in the initial straining of the test piece.
The straining device shall be so designed that, when used at high temperatures in an oven, it can be placed
with the reference length of the test piece perpendicular to the direction of the air flow. It shall also be of
minimum mass in order to avoid excessive lag in the attainment of temperature equilibrium after its
introduction into the oven.
A multiple-unit straining device can be used, provided that the foregoing requirements are met.
4.1.2 Oven, conforming to the requirements of ISO 188 (if the test is to be carried at a temperature above
the standard laboratory temperature). For short heating times, controlled air flow is not necessary.
4.1.3 Length-measuring device, capable of measuring the reference length of the test piece to the nearest
0,1 mm in accordance with ISO 23529:2004, method B.
For strip test pieces, a bench marker shall be provided to mark the length used as the reference length.
For ring test pieces, the reference length can be the inner diameter of the ring, in which case a graduated
cone allowing measurements to be made to the nearest 0,1 mm shall be used. Alternatively, if measurements
are to be made on a straight reference length, a rigid channel, 3,5 mm deep and 20 mm wide for large ring
test pieces and 1,75 mm deep and 10 mm wide for small ring test pieces, shall be provided for straightening
portions of such test pieces during marking and measuring of the reference length.
2 © ISO 2007 – All rights reserved

4.2 Constant-load measurements
4.2.1 Straining device, comprising clamps and weights, or equivalent, for loading the test pieces (see
Figure 1).
Key
1 fixed clamp
2 test piece
3 clamp for holding weight
4 weight
Figure 1 — Straining device
4.2.2 Thickness- and width-measuring device, comprising a gauge for measuring the thickness and,
where appropriate, the width of the test piece in accordance with ISO 23529:2004, method A.
The width of die-cut test pieces shall be taken as the distance between the cutting edges of the die in the
narrow part, in which case a device capable of measuring the width to the nearest 0,05 mm in accordance
with ISO 23529 shall be provided.
4.2.3 Length-measuri
...

NORME ISO
INTERNATIONALE 2285
Sixième édition
2007-07-15
Caoutchouc vulcanisé ou
thermoplastique — Détermination de la
déformation rémanente sous allongement
constant et de la déformation rémanente,
de l'allongement et du fluage sous charge
constante de traction
Rubber, vulcanized or thermoplastic — Determination of tension set
under constant elongation, and of tension set, elongation and creep
under constant tensile load
Numéro de référence
©
ISO 2007
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.

DOCUMENT PROTÉGÉ PAR COPYRIGHT

©  ISO 2007
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse
ii © ISO 2007 – Tous droits réservés

Sommaire Page
Avant-propos. iv
1 Domaine d'application.1
2 Références normatives .1
3 Termes et définitions.2
4 Appareillage .2
5 Éprouvettes .4
6 Mode opératoire.6
7 Expression des résultats .9
8 Rapport d'essai .10

Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 2285 a été élaborée par le comité technique ISO/TC 45, Élastomères et produits à base d'élastomères,
sous-comité SC 2, Essais et analyses.
Cette sixième édition annule et remplace la cinquième édition (ISO 2285:2001) qui a été révisée pour mettre à
jour les références normatives (l'ISO 471, l'ISO 4648 et l'ISO 4661-1 ont été remplacées par l'ISO 23529). Le
texte a également été clarifié par endroits.

iv © ISO 2007 – Tous droits réservés

NORME INTERNATIONALE ISO 2285:2007(F)

Caoutchouc vulcanisé ou thermoplastique — Détermination
de la déformation rémanente sous allongement constant et de
la déformation rémanente, de l'allongement et du fluage sous
charge constante de traction
AVERTISSEMENT — Il convient que l'utilisateur de la présente Norme internationale connaisse bien
les pratiques courantes de laboratoire. La présente Norme Internationale n'a pas pour but de traiter
tous les problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur
de la présente Norme internationale d'établir des pratiques appropriées en matière d'hygiène et de
sécurité, et de s'assurer de la conformité à la réglementation nationale en vigueur.
ATTENTION — Certains modes opératoires spécifiés dans la présente Norme internationale peuvent
impliquer l'utilisation ou l'élaboration de substances ou bien la production de déchets pouvant
constituer un risque pour l'environnement local. Il convient de faire référence à une documentation
appropriée relative à la manipulation en toute sécurité et à la mise au rebut après l'emploi.
1 Domaine d'application
La présente Norme internationale spécifie un certain nombre de méthodes pour déterminer les variations
dimensionnelles que subissent des éprouvettes de caoutchouc vulcanisé ou thermoplastique pendant et
après l'application d'un chargement en traction, durant des périodes relativement courtes, sous allongement
constant ou charge constante.
L'essai réalisé sous allongement constant sert à mesurer l'aptitude des caoutchoucs à conserver leurs
propriétés élastiques après avoir été soumis à un allongement à une température normale de laboratoire
jusqu'à une déformation spécifiée, cette sollicitation étant maintenue pendant une durée définie à la même
température ou à une température spécifiée plus élevée, puis supprimée à la température d'essai ou à la
température normale de laboratoire.
L'essai réalisé sous charge constante spécifie une méthode permettant de déterminer l'allongement, le fluage
et la déformation rémanente des caoutchoucs soumis à une charge constante à température normale de
laboratoire.
Les méthodes d'essai sont destinées à mesurer les propriétés élastiques du caoutchouc dans l'échelle de
dureté de 20 DIDC à 94 DIDC.
Le mesurage du fluage n'est pas recommandé pour la conception de produits ou l'évaluation de matériaux à
faible degré de fluage. Pour ces derniers, il convient de se référer à l'ISO 8013. Aucune concordance entre
les résultats du présent essai et ceux de l'ISO 8013 ne peut être déduite.
NOTE L'essai sous charge constante est principalement destiné à mesurer le degré de vulcanisation et à apprécier
la maîtrise de la qualité des produits à parois minces. Une augmentation du degré de vulcanisation ou de réticulation se
traduit généralement par une diminution de la rémanence, du fluage ou de l'élongation.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 188, Caoutchouc vulcanisé ou thermoplastique — Essais de résistance au vieillissement accéléré et à la
chaleur
ISO 8013, Caoutchouc vulcanisé — Détermination du fluage en compression ou en cisaillement
ISO 23529:2004, Caoutchouc — Procédures générales pour la préparation et le conditionnement des
éprouvettes pour les méthodes d'essais physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s'appliquent. Voir également les
définitions des fonctions de fluage indiquées dans l'ISO 8013.
3.1
déformation rémanente sous charge constante
allongement résiduel d'une éprouvette hors charge, ayant été soumise à une charge constante pendant une
durée déterminée, exprimé en pourcentage de la longueur initiale hors charge
3.2
déformation rémanente sous allongement constant
allongement résiduel d'une éprouvette en état de relaxation, ayant été soumise à un allongement constant
pendant un temps déterminé, exprimé en pourcentage de l'allongement
3.3
fluage
augmentation de l'allongement d'une éprouvette à charge constante pendant un temps déterminé, exprimée
en pourcentage de l'allongement au début de ladite période de temps
4 Appareillage
4.1 Mesurages de l'allongement constant
4.1.1 Dispositif d'allongement, constitué d'une tige métallique ou de tout autre élément de guidage
approprié, équipé de deux fixations pour les extrémités de l'éprouvette, l'une étant fixe et l'autre mobile. Les
fixations doivent se présenter sous forme d'étriers autoserrants pour les éprouvettes en forme de bande, sous
forme de mâchoires pour le maintien des extrémités larges et planes, et sous forme de poulies plates
d'environ 5 mm de largeur et de 10 mm de diamètre, pour les éprouvettes annulaires.
Si on le souhaite, le déplacement de la fixation mobile peut être assuré par un moyen autre que manuel, par
exemple à l'aide d'une tige filetée, à condition de respecter les tolérances sur la vitesse d'allongement (voir
6.1.2). Il est également possible de prévoir des butées ou des graduations appropriées en vue d'éviter un
allongement excessif de l'éprouvette lors de l'allongement initial.
Le dispositif d'allongement doit être conçu de façon à pouvoir être placé de manière à orienter la longueur de
référence de l'éprouvette perpendiculairement au flux d'air, en cas d'utilisation à haute température dans une
étuve. Il doit également avoir une masse minimale pour éviter un temps de réponse excessif pour l'obtention
de l'équilibre thermique après sa mise en place dans l'étuve.
Il est possible d'utiliser un dispositif d'allongement multiposte sous réserve de satisfaire aux exigences
susmentionnées.
4.1.2 Étuve, conforme aux exigences de l'ISO 188 (lorsque l'essai doit être réalisé à une température
supérieure à la température normale de laboratoire). Pour les courtes durées de chauffage, la circulation d'air
forcée n'est pas nécessaire.
2 © ISO 2007 – Tous droits réservés

4.1.3 Dispositif de mesurage de longueur, capable de mesurer la longueur de référence de l'éprouvette à
0,1 mm près, conformément à l'ISO 23529:2004, méthode B.
Pour les éprouvettes en forme de bande, un marqueur doit être prévu pour marquer la longueur utilisée
comme longueur de référence.
Pour les éprouvettes annulaires, la longueur de référence peut correspondre au diamètre intérieur de
l'anneau, auquel cas un cône gradué permettant d'effectuer des mesurages à 0,1 mm près doit être utilisé. En
option, si l'on doit réaliser des mesurages sur une section droite de référence, un profilé rigide en U, de
3,5 mm de profondeur et de 20 mm de largeur pour les éprouvettes annulaires de grande taille, et de 1,75 mm
de profondeur et de 10 mm de largeur pour les éprouvettes annulaires de petite taille, doit être fourni pour
maintenir droites les parties de ces éprouvettes pendant le marquage et le mesurage de la longueur de
référence.
4.2 Mesurages à charge constante
4.2.1 Dispositif d'allongement, constitué de fixations et de masses, ou l'équivalent, pour soumettre les
éprouvettes à une charge (voir Figure 1).

Légende
1 fixation non mobile
2 éprouvette
3 fixation pour maintenir la masse
4 masse
Figure 1 — Dispositif d'allongement
4.2.2 Dispositif de mesurage d'épaisseur et de largeur, comportant une jauge de mesurage de
l'épaisseur et, le cas échéant, de la largeur de l'éprouvette conformément à l'ISO 23529:2004, méthode A.
La largeur des éprouvettes découpées à l'emporte-pièce doit être considérée comme la distance entre les
bords tranchants de l'emporte-pièce dans la partie étroite, ce qui nécessite alors de prévoir un dispositif
permettant de mesurer la largeur à 0,05 mm près, conformément à l'ISO 23529.
4.2.3 Dispositif de
...