ISO 12947-4:1998

Textiles - Determination of the abrasion resistance of fabrics by the Martindale method - Part 4: Assessment of appearance change

This part of ISO 12947 is applicable to the assessment of the appearance change of specimens covering all textile fabrics including nonwovens and fabrics where the specifier indicates the end performance as having a low abrasion wear life. This method differs appreciably from those in ISO 12947-2 and 12947-3. NOTE Further introductory comments are given in ISO 12947-1.

Textiles — Détermination de la résistance à l'abrasion des étoffes par la méthode Martindale — Partie 4: Évaluation du changement d'aspect

La présente partie de l'ISO 12947 s'applique pour l'évaluation du changement d'aspect des éprouvettes, de tous les types de textiles, y compris les nontissés mais pas d'étoffes pour lesquelles il est indiqué une faible résistance à l'abrasion dans la spécification de performance finale. La méthode décrite diffère sensiblement de celles figurant dans l'ISO 12947-2 et l'ISO 12947-3. NOTE D'autres observations d'introduction sont indiquées dans l'ISO 12947-1.

General Information

• Status: Published
• Publication Date: 19-Dec-1998
• ICS: 59.080.30 - Textile fabrics
• Technical Committee: ISO/TC 38/SC 24 - Conditioning atmospheres and physical tests for textile fabrics
• Drafting Committee: ISO/TC 38/SC 24/WG 2 - Fabrics - Physical Tests
• Current Stage: 9093 - International Standard confirmed
• Start Date: 17-Mar-2023
• Completion Date: 13-Dec-2025

Relations

• Consolidates: ISO 5659-2:1994 - Plastics - Smoke generation - Part 2: Determination of optical density by a single-chamber test
• Effective Date: 06-Jun-2022

Overview

ISO 12947-4:1998 specifies a standardized procedure for assessing appearance change of textile fabrics using the Martindale method. Part 4 covers all textile fabrics - including nonwovens, stretch fabrics and fabrics with low expected abrasion life - and defines how to evaluate surface change caused by abrasion rather than breakdown or mass loss. The method uses the Martindale abrasion testing apparatus (see ISO 12947-1) and differs appreciably from ISO 12947-2 and ISO 12947-3 which focus on specimen breakdown and mass loss respectively.

Key topics and technical requirements

• Test principle: circular specimens are rubbed against a standard abrasive medium (abradant) following a Lissajous translational movement while the abradant holder may freely rotate; evaluation is by visual assessment of appearance change.
• Apparatus & materials: use the Martindale apparatus as defined in ISO 12947-1; replace abradant and foam backing for every test; inspect felt substrate after each test.
• Conditioning: standard atmosphere per ISO 139 - 20 ± 2 °C and 65 ± 5% RH.
• Specimen dimensions: test specimens at least 140 mm diameter (or length/width); abradant diameter 38 mm; felt substrate 140 mm diameter; foam backing 38 mm diameter.
• Loading and mounting: typical spindle/specimen holder mass of 198 ± 2 g; pressing weight for mounting felt/specimen 2.5 ± 0.5 kg (diameter 120 ± 10 mm).
• Test procedure: two assessment options - (a) test to an agreed number of rubs and assess whether appearance change has occurred, or (b) test until an agreed appearance change is reached and record the interval in which it occurred.
• Test intervals: recommended rub-intervals depend on expected wear (table guidance in the standard; e.g., short tests start at 16 rubs then every 8).
• Special preparatory methods: Annex A covers specimen preparation for elastane (stretch) fabrics and cord/pile fabrics (including preparatory rubs for backing-free pile fabrics).
• Reporting: include reference to ISO 12947-4, specimen details, test series used, basis of assessment, individual results and mean (with confidence limits), shade-change assessment (ISO 105‑A02) and any departures from standard procedure.

Applications and users

• Quality control and acceptance testing for apparel, upholstery and technical textiles
• Textile laboratories performing abrasion resistance and appearance durability testing
• Product developers, specifiers and procurement teams assessing fabric suitability for end‑use where surface appearance is critical
• Manufacturers documenting compliance and comparative performance using the Martindale method

Related standards

• ISO 12947-1 (Martindale apparatus)
• ISO 12947-2 (breakdown)
• ISO 12947-3 (mass loss)
• ISO 139 (conditioning atmosphere)
• ISO 105‑A02 (grey scale for colour change)
• ISO 2859-1 (sampling) and ISO 5725 (precision/statistics)

Keywords: ISO 12947-4:1998, Martindale method, abrasion resistance, appearance change, textile testing, nonwovens, specimen preparation, abrasion test.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 12947-4
First edition
1998-12-15
Textiles — Determination of the abrasion
resistance of fabrics by the Martindale
method —
Part 4:
Assessment of appearance change
Textiles — Détermination de la résistance à l’abrasion des étoffes par la
méthode Martindale —
Partie 4: Évaluation du changement d’aspect
A
Reference number
Contents Page
1 Scope .1
2 Normative references .1
3 Definitions .1
4 Principle.1
5 Apparatus and materials.2
6 Conditioning and testing atmosphere.2
7 Sampling and preparation of test specimens.2
8 Abrasion test procedure .4
9 Results.4
10 Test report .4
Annex A (normative) Specimen preparation for specific fabrics .6
Bibliography.8
©  ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [e-mail]
Printed in Switzerland
ii
© ISO
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
International Standard ISO 12947-4 was prepared by Technical Committee ISO/TC 38, Textiles.
ISO 12947 consists of the following parts under the general title Textiles — Determination of the abrasion resistance
of fabrics by the Martindale method:
 Part 1: Martindale abrasion testing apparatus
 Part 2: Determination of specimen breakdown

Part 3: Determination of mass loss
 Part 4: Assessment of appearance change
Annex A forms an integral part of this part of ISO 12947.
iii
INTERNATIONAL STANDARD  © ISO ISO 12947-4:1998(E)
Textiles — Determination of the abrasion resistance of fabrics by
the Martindale method —
Part 4:
Assessment of appearance change
1 Scope
This part of ISO 12947 is applicable to the assessment of the appearance change of specimens covering all textile
fabrics including nonwovens and fabrics where the specifier indicates the end performance as having a low
abrasion wear life. This method differs appreciably from those in ISO 12947-2 and 12947-3.
NOTE Further introductory comments are given in ISO 12947-1.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this part of ISO 12947. For dated references, subsequent amendments to, or revisions of, any of these publications
do not apply. However, parties to agreements based on this part of ISO 12947 are encouraged to investigate the
possibility of applying the most recent editions of the normative documents indicated below. For undated
references, the latest edition of the normative document referred to applies. Members of ISO and IEC maintain
registers of currently valid International Standards.
ISO 105-A02:1993, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour.
ISO 139:1973, Textiles — Standard atmospheres for conditioning and testing.
1)
ISO 2859-1:— , Sampling procedures for inspection by attributes — Part 1: Sampling plans indexed by acceptable
quality level (AQL) for lot-by-lot inspection.
ISO 12947-1:1998, Textiles — Determination of the abrasion resistance of fabrics by the Martindale method —
Part 1: Martindale abrasion testing apparatus.
3 Definitions
For the purposes of this part of ISO 12947 the definitions given in ISO 12947-1 apply.
4 Principle
A circular specimen is subjected to a defined load and rubbed against an abrasive medium (standard fabric) in a
translational movement tracing a Lissajous figure. The specimen holder containing the abrasive medium is
additionally freely rotatable around its own axis perpendicular to the plane of the specimen. The evaluation of the
abrasion resistance of the textile fabric is determined from assessment of the appearance change.

1) To be published. (Revision of ISO 2859:1989)
© ISO
Tests are performed using the mass of the specimen holder and spindle alone at (198 2) g.
–
The surface change of the test specimen is assessed and compared with an untested specimen of the same fabric,
with the option of using two methods:
a) abrasion testing to an agreed number of rubs and assessing whether a surface change has occurred;
b) abrasion testing to an agreed surface change and determination of the test interval in which the surface change
has been produced.
5 Apparatus and materials
The test apparatus and auxiliary materials are specified in ISO 12947-1.
6 Conditioning and testing atmosphere
The standard temperate atmosphere for conditioning and testing textiles as defined in ISO 139 shall be used, i.e a
temperature of (20 – 2) °C and a relative humidity of (65 – 5) %.
7 Sampling and preparation of test specimens
7.1 General
Perform sampling in accordance with statistical rules (see ISO 2859-1).
Ensure throughout sampling and specimen preparation that handling imposes the minimum possible tensile stress
so as to prevent incorrect extension of the textile fabric.
7.2 Selection of the laboratory sample
Select the laboratory sample from a test lot to be representative of properties of the textile fabric. Check the
representative nature of sampling from the start or end of a textile fabric.
Take the laboratory sample from across the full fabric width.
7.3 Sampling of the test specimens from the laboratory sample
Before sampling the test specimens from the laboratory samples, condition the laboratory samples free from
tension, for at least 18 h on a smooth horizontal surface with free access of air exposed to the standard atmosphere
specified in clause 6.
For woven fabrics, take the specimens so that they each contain different warp and weft threads.
Take the test specimens at least 100 mm from the edge distributed across the entire laboratory sample. Take a
sufficient number of test specimens (at least three) to be in accordance with statistical notes (see 7.1).
For patterned fabrics or fabrics with textured surface, take care that the test specimens contain all characteristic
parts of the pattern, ensuring that the parts of the pattern likely to be sensitive to abrasion are contained in the test
specimens.
7.4 Dimensions of specimens and auxiliary materials
7.4.1 Dimensions of the test specimens
The dimensions of the test specimen shall be at least 140 mm in diameter or length and width.
© ISO
7.4.2 Dimensions of abradant
+5
The diameter of the abradant shall be 38 mm.
7.4.3 Dimensions of the test specimen felt substrate
+5
The diameter of the test specimen felt substrate shall be 140 mm.
7.4.4 Dimensions of the abradant foam backing
+5
The diameter of the abradant foam backing shall be 38 mm.
7.5 Preparation and mounting of the test specimens and cutting-out and mounting of
the auxiliary materials
7.5.1 Preparation
Stamp or cut out the test specimens from the laboratory sample. Give particular attention to the clean status of the
cut edges to prevent the occurrence of unwa
...

NORME ISO
INTERNATIONALE 12947-4
Première édition
1998-12-15
Textiles — Détermination de la résistance
à l’abrasion des étoffes par la méthode
Martindale —
Partie 4:
Évaluation du changement d’aspect
Textiles — Determination of the abrasion resistance of fabrics by the
Martindale method —
Part 4: Assessment of appearance change
A
Numéro de référence
Sommaire Page
1 Domaine d’application .1
2 Références normatives .1
3 Définitions .1
4 Principe.2
5 Appareillage et matériaux .2
6 Atmosphère de conditionnement et d'essai .2
7 Échantillonnage et préparation des éprouvettes .2
8 Mode opératoire de l'essai d'abrasion.4
9 Résultats.4
10 Rapport d'essai .5
Annexe A (normative) Préparation des éprouvettes provenant d'étoffes spécifiques .6
Bibliographie.8
©  ISO 1998
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet [e-mail]
Imprimé en Suisse
ii
© ISO
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI, Partie 3.
Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour
vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités
membres votants.
La Norme internationale ISO 12947-4 a été élaborée par le comité technique ISO/TC 38, Textiles.
L'ISO 12947 comprend les parties suivantes, présentées sous le titre général Textiles — Détermination de la
résistance à l'abrasion des étoffes par la méthode Martindale:
 Partie 1: Appareillage d'essai d'abrasion de Martindale
 Partie 2: Détermination de la détérioration de l'éprouvette
 Partie 3: Détermination de la perte de masse
 Partie 4: Évaluation du changement d'aspect
L’annexe A fait partie intégrante de la présente partie de l’ISO 12947.
iii
NORME INTERNATIONALE  © ISO ISO 12947-4:1998(F)
Textiles — Détermination de la résistance à l’abrasion des étoffes
par la méthode Martindale —
Partie 4:
Évaluation du changement d’aspect
1 Domaine d’application
La présente partie de l'ISO 12947 s'applique pour l'évaluation du changement d'aspect des éprouvettes, de tous les
types de textiles, y compris les nontissés mais pas d'étoffes pour lesquelles il est indiqué une faible résistance à
l'abrasion dans la spécification de performance finale. La méthode décrite diffère sensiblement de celles figurant
dans l’ISO 12947-2 et l’ISO 12947-3.
NOTE D'autres observations d'introduction sont indiquées dans l'ISO 12947-1.
2 Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente partie de l’ISO 12947. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s'appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente partie de l’ISO 12947 sont invitées à rechercher la possibilité d’appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s'applique. Les membres de l’ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 105-A02:1993, Textiles — Essais de solidité des teintures — Partie A02: Échelle de gris pour l'évaluation des
dégradations.
ISO 139:1973, Textiles — Atmosphères normales de conditionnement et d'essai.
1)
ISO 2859-1:— ,
Règles d'échantillonnage pour les contrôles par attributs — Partie 1: Plans d'échantillonnage pour
les contrôles lot par lot, indexés d'après le niveau de qualité acceptable (NQA).
ISO 12947-1:1998, Textiles — Détermination de la résistance à l'abrasion des étoffes par la méthode Martindale —
Partie 1: Appareillage d'essai d'abrasion de Martindale.
3 Définitions
Pour les besoins de la présente partie de l'ISO 12947, les définitions données dans l'ISO 12947-1 s'appliquent.

1) À publier. (Révision de l’ISO 2859-1:1989)
© ISO
4 Principe
Une éprouvette de forme circulaire est soumise à une charge définie et à l'action de frottement d'un élément abrasif
(étoffe normalisée) selon un mouvement de translation formant une courbe de Lissajous. En même temps, le
porte-éprouvette avec l'abrasif tourne librement autour de son propre axe perpendiculairement au plan de
l'éprouvette. La résistance à l'abrasion de l'étoffe est déterminée à partir du changement d'aspect.
Les essais sont effectués en utilisant uniquement la masse du porte-éprouvette et de la tige, soit (198 – 2) g.
La modification de la surface de l'éprouvette d'essai est évaluée et comparée à une éprouvette non soumise à essai
de la même étoffe, au moyen de l'une des deux méthodes suivantes:
a) essai d'abrasion selon un nombre convenu de frottements et évaluation de la modification de surface, le cas
échéant;
b) essai d'abrasion jusqu'à obtention de la modification de surface convenue et détermination de l'intervalle
d'essai dans lequel le changement s'est produit.
5 Appareillage et matériaux
L'appareillage d'essai et les matériaux auxiliaires sont spécifiés dans l'ISO 12947-1.
6 Atmosphère de conditionnement et d'essai
Utiliser l'atmosphère tempérée normalisée de conditionnement et d'essai des textiles définie dans l'ISO 139,
c'est-à-dire: une température de (20 – 2) °C et une humidité relative de (65 – 5) %.
7 Échantillonnage et préparation des éprouvettes
7.1 Généralités
Effectuer l'échantillonnage conformément aux règles statistiques (voir ISO 2859-1).
Pendant toute la durée d'échantillonnage et de préparation des éprouvettes, veiller à ce que les manipulations des
éprouvettes provoquent le moins de tension possible afin de ne pas allonger inutilement l'étoffe.
7.2 Sélection de l'échantillon pour laboratoire
Sélectionner l'échantillon pour laboratoire dans un lot d'essai représentatif des propriétés de l'étoffe. Vérifier la
représentativité de l'échantillonnage au début ou à la fin d'une étoffe.
Prélever l'échantillon pour laboratoire sur toute la largeur de l'étoffe.
7.3 Échantillonnage des éprouvettes prélevées dans l'échantillon pour laboratoire
Avant de procéder à l'échantillonnage des éprouvettes dans les échantillons pour laboratoire, conditionner les
échantillons, sans exercer de tension, sur une surface horizontale lisse, pendant au moins 18 h dans l'atmosphère
normalisée spécifiée à l'article 6 avec une circulation libre de l'air.
Pour les étoffes tissées, effectuer le prélèvement de manière que chaque éprouvette contienne des fils de chaîne et
de trame différents.
Prélever les éprouvettes réparties uniformément dans tout l'échantillon pour laboratoire, à au moins 100 mm du
bord. Prélever un nombre suffisant d'éprouvettes (au moins trois) pour respecter les règles statistiques (voir 7.1).
Pour les étoffes à dessin ou à surface texturée, veiller à ce que les éprouvettes contiennent tous les éléments
caractéristiques du dessin et en particulier les parties susceptibles de réagir à l'abrasion.
© ISO
7.4 Dimensions des éprouvettes et des matériaux auxiliaires
7.4.1 Dimensions des éprouvettes
Le diamètre ou le côté des éprouvettes doit être d'au moins 140 mm.
7.4.2 Dimensions de l'abrasif
+5
Le diamètre de l'abrasif doit être de 38 mm.
( )
7.4.3 Dimensions du support d'éprouvette en feutre
+5
Le diamètre du support d'éprouvette en feutre doit être de 140 mm.
( 0 )
7.4.4 Dimensions de la sous-couche en mousse de l’abrasif
+5
Le diamètre de la sous-couche en mousse de l'abrasif doit être de 38 mm.
( 0 )
7.5 Préparation et montage des éprouvettes, et prélèvement et montage des matériaux
auxiliaires
7.5.1 Préparation
Découper les éprouvettes dans l'échantillon pour laboratoire. Veiller tout particulièrement à ce que les bords soient
nettement découpés pour éviter toute perte involontaire de matériau lors des manipulations ultérieures.
Préparer les matériaux auxiliaires de la même façon à partir des pièces disponibles de tissu, de feutre ou de
mousse.
N
...