ISO 4649:2024

Rubber, vulcanized or thermoplastic — Determination of abrasion resistance using a rotating cylindrical drum device

This document specifies two methods for the determination of the resistance of rubber to abrasion by means of a rotating cylindrical drum device. The methods involve determination of the volume loss due to the abrasive action of rubbing a test piece over a specified grade of abrasive sheet. Method A is for a non-rotating test piece and method B is for a rotating test piece. For each method, the result can be reported as a relative volume loss or an abrasion resistance index. These test methods are suitable for comparative testing, quality control, specification compliance testing, referee purposes and research and development work. No close relation between the results of this abrasion test and service performance can be inferred. NOTE The abrasion loss is often more uniform using the rotating test piece because the whole surface of the test piece is in contact with the abrasive sheet over the duration of the test. However, there is considerable experience using the non-rotating test piece.

Caoutchouc vulcanisé ou thermoplastique — Détermination de la résistance à l'abrasion à l'aide d'un dispositif à tambour tournant

Le présent document spécifie deux méthodes de détermination de la résistance du caoutchouc à l'abrasion à l'aide d'un dispositif à tambour tournant. Les méthodes consistent à déterminer la perte de volume d'une éprouvette de caoutchouc soumise à une action abrasive par frottement sur une qualité spécifiée de toile abrasive. La méthode A utilise une éprouvette fixe et la méthode B utilise une éprouvette tournante. Pour chaque méthode, le résultat peut être exprimé en perte de volume relative ou par un indice de résistance à l'abrasion. Ces deux méthodes d'essai conviennent aux essais comparatifs, de contrôle de la qualité, de conformité aux spécifications, aux besoins d'arbitrage et aux travaux de recherche et de développement. On ne peut déduire aucune relation entre les résultats de cet essai d'abrasion et les performances en service. NOTE L'utilisation de l'éprouvette tournante conduit souvent à une perte par abrasion plus uniforme dans la mesure où toute la surface de l'éprouvette est en contact avec la toile abrasive pendant toute la durée de l'essai. Cependant, il existe une expérience considérable acquise en utilisant l'éprouvette fixe.

General Information

• Status: Published
• Publication Date: 31-Jul-2024
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2 - Testing and analysis
• Current Stage: 6060 - International Standard published
• Start Date: 01-Aug-2024
• Due Date: 20-Feb-2026
• Completion Date: 01-Aug-2024

Relations

• Revises: ISO 4649:2017 - Rubber, vulcanized or thermoplastic — Determination of abrasion resistance using a rotating cylindrical drum device
• Effective Date: 25-Feb-2023

Standards Content (Sample)

International
Standard
ISO 4649
Fifth edition
Rubber, vulcanized or
2024-08
thermoplastic — Determination of
abrasion resistance using a rotating
cylindrical drum device
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
résistance à l'abrasion à l'aide d'un dispositif à tambour tournant
Reference number
© ISO 2024
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Apparatus and materials . 4
6 Calibration . 5
7 Test pieces . 5
7.1 Type and preparation .5
7.2 Number .6
7.3 Time interval between vulcanization or forming and testing .6
7.4 Conditioning.6
8 Test temperature . 6
9 Procedure . 6
9.1 General test procedure .6
9.2 Comparison against standard reference compounds or user-defined reference
compounds .7
9.3 Density .8
10 Expression of results . 8
10.1 General .8
10.2 Relative volume loss, ΔV .8
rel
10.3 Abrasion resistance index .8
11 Precision . 9
12 Test report . 9
Annex A (normative) Suitable abrasive sheet. 10
Annex B (normative) Standard and user-defined reference compounds .11
Annex C (normative) Calibration schedule .15
Annex D (informative) Precision and bias . 17
Bibliography . 19

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This fifth edition cancels and replaces the fourth edition (ISO 4649:2017), which has been technically
revised.
The main changes are as follows:
— Addition of requirement to report the abrasive sheet cleaning method used.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
Introduction
Various types of laboratory test equipment for wear resistance of rubber compound have been developed
depending on the products to which rubber compounds have been applied in the past. Methods and
equipment are briefly introduced in ISO 23794 and the test method using a rotating cylindrical drum device
is described in detail in this document.
Because factors such as the grade of abrasive sheet, the type of adhesive used in the manufacture of the
sheet and contamination and wear caused by previous testing lead to variations in the absolute values of
abrasion loss, all tests are comparative. Runs with a reference compound are included so that the results
can be expressed either as a relative volume loss compared to a calibrated abrasive sheet or as an abrasion
resistance index compared to a reference compound.
This document describes two methods and specifies two standard reference compounds that can be chosen
freely, although some combinations are more frequently used in practice. Considerable experience has been
accumulated using the relative volume loss calculation in 10.2 for method A with reference compound no. 1
and method B with reference compounds no. 1 and no. 2.
When using standard reference compound no. 1 with a non-rotating test piece, a very important part of the
method is the preparation of the abrasive sheet and its calibration.
Relative volume loss can be calculated for either test method with another reference compound, if the
defined mass loss is known.
v
International Standard ISO 4649:2024(en)
Rubber, vulcanized or thermoplastic — Determination of
abrasion resistance using a rotating cylindrical drum device
WARNING 1 — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine
the applicability of any other restrictions.
WARNING 2 — Certain procedures specified in this document might involve the use or generation of
substances or the generation of waste, that could constitute a local environmental hazard. Reference
should be made to appropriate documentation on safe handling and disposal after use.
1 Scope
This document specifies two methods for the determination of the resistance of rubber to abrasion by means
of a rotating cylindrical drum device.
The methods involve determination of the volume loss due to the abrasive action of rubbing a test piece over a
specified grade of abrasive sheet. Method A is for a non-rotating test piece and method B is for a rotating test
piece. For each method, the result can be reported as a relative volume loss or an abrasion resistance index.
These test methods are suitable for comparative testing, quality control, specification compliance testing,
referee purposes and research and development work. No close relation between the results of this abrasion
test and service performance can be inferred.
NOTE The abrasion loss is often more uniform using the rotating test piece because the whole surface of the test
piece is in contact with the abrasive sheet over the duration of the test. However, there is considerable experience
using the non-rotating test piece.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 48-4, Rubber, vulcanized or thermoplastic — Determination of hardness — Part 4: Indentation hardness by
durometer method (Shore hardness)
ISO 2230, Rubber products — Guidelines for storage
ISO 2393, Rubber test mixes — Preparation, mixing and vulcanization — Equipment and procedures
ISO 2781, Rubber, vulcanized or thermoplastic — Determination of density
ISO 18899:2013, Rubber — Guide to the calibration of test equipment
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.

-----------
...

Norme
internationale
ISO 4649
Cinquième édition
Caoutchouc vulcanisé ou
2024-08
thermoplastique — Détermination
de la résistance à l'abrasion à l'aide
d'un dispositif à tambour tournant
Rubber, vulcanized or thermoplastic — Determination of
abrasion resistance using a rotating cylindrical drum device
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2024
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Principes . 2
5 Appareillage et matériaux . 4
6 Étalonnage . 5
7 Éprouvettes. 6
7.1 Type et préparation .6
7.2 Nombre .6
7.3 Délai entre vulcanisation ou mise en œuvre et essai .6
7.4 Conditionnement .6
8 Température d'essai . 6
9 Mode opératoire . 6
9.1 Mode opératoire général.6
9.2 Comparaison avec les mélanges de référence normalisés ou ceux définis par l'utilisateur.7
9.3 Masse volumique .8
10 Expression des résultats . 8
10.1 Généralités .8
10.2 Perte de volume relative, ΔVrel .8
10.3 Indice de résistance à l'abrasion .9
11 Fidélité . 9
12 Rapport d'essai . 9
Annexe A (normative) Toile abrasive appropriée .11
Annexe B (normative) Mélanges de référence normalisés et définis par l'utilisateur .12
Annexe C (normative) Programme d'étalonnage .16
Annexe D (informative) Fidélité et biais. 19
Bibliographie .21

iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomères, sous-comité SC 2, Essais et analyses.
Cette cinquième édition annule et remplace la quatrième édition (ISO 4649:2017), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— Ajout d‘une exigence relative à la déclaration de la méthode de nettoyage des toiles abrasives utilisée.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
Introduction
Divers types d'équipements d'essai de laboratoire pour la résistance à l'usure du mélange de caoutchouc ont
été développés en fonction des produits auxquels les mélanges de caoutchouc ont été appliqués par le passé.
Les méthodes et les équipements sont introduits brièvement dans l’ISO 23794 et la méthode d'essai utilisant
un dispositif à tambour tournant est décrite en détail dans le présent document.
Étant donné que des facteurs tels que la qualité de toile abrasive et l'adhésif utilisés dans la fabrication de la
toile ainsi que la contamination et l'usure dues aux essais antérieurs entraînent des variations des valeurs
absolues de la perte par abrasion, tous les essais sont comparatifs. Des essais avec des mélanges de référence
sont inclus pour que les résultats puissent être exprimés soit en perte de volume relative par rapport à une
toile abrasive étalonnée, soit par un indice de résistance à l'abrasion par rapport à un mélange de référence.
Le présent document décrit deux méthodes et spécifie deux mélanges de référence qui peuvent être choisis
librement, bien que certaines combinaisons soient plus fréquemment utilisées dans la pratique. Une
expérience considérable a été accumulée en utilisant le calcul de la perte de volume relative en 10.2 pour
la méthode A avec le mélange de référence normalisé n° 1 et la méthode B avec les mélanges de référence
normalisé n° 1 et n° 2.
Lors de l'utilisation du mélange de référence normalisé n° 1 avec une éprouvette fixe, une partie extrêmement
importante de cette méthode réside dans la préparation de la toile abrasive et de son étalonnage.
La perte relative de volume peut être calculée pour l'une ou l'autre méthode d'essai avec un autre mélange
de référence, si la perte de masse définie est connue.

v
Norme internationale ISO 4649:2024(fr)
Caoutchouc vulcanisé ou thermoplastique — Détermination
de la résistance à l'abrasion à l'aide d'un dispositif à tambour
tournant
AVERTISSEMENT 1 — Il convient que l'utilisateur du présent document connaisse bien les pratiques
courantes de laboratoire. Le présent document n'a pas pour but de traiter tous les problèmes de
sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur d'établir des pratiques
appropriées en matière d'hygiène et de sécurité, et déterminer si des restrictions supplémentaires
s’appliquent.
AVERTISSEMENT 2 — Certains modes opératoires spécifiés dans le présent document peuvent
impliquer l'utilisation ou la génération de substances ou de déchets pouvant représenter un danger
environnemental local. Il convient de se référer à la documentation appropriée concernant la
manipulation et l'élimination après usage en toute sécurité.
1 Domaine d’application
Le présent document spécifie deux méthodes de détermination de la résistance du caoutchouc à l'abrasion à
l'aide d'un dispositif à tambour tournant.
Les méthodes consistent à déterminer la perte de volume d'une éprouvette de caoutchouc soumise à
une action abrasive par frottement sur une qualité spécifiée de toile abrasive. La méthode A utilise une
éprouvette fixe et la méthode B utilise une éprouvette tournante. Pour chaque méthode, le résultat peut être
exprimé en perte de volume relative ou par un indice de résistance à l'abrasion.
Ces deux méthodes d'essai conviennent aux essais comparatifs, de contrôle de la qualité, de conformité aux
spécifications, aux besoins d'arbitrage et aux travaux de recherche et de développement. On ne peut déduire
aucune relation entre les résultats de cet essai d'abrasion et les performances en service.
NOTE L'utilisation de l'éprouvette tournante conduit souvent à une perte par abrasion plus uniforme dans
la mesure où toute la surface de l'éprouvette est en contact avec la toile abrasive pendant toute la durée de l'essai.
Cependant, il existe une expérience considérable acquise en utilisant l'éprouvette fixe.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références d
...