ISO 6502-2:2025
(Main)Rubber — Measurement of vulcanization characteristics using curemeters — Part 2: Oscillating disc curemeter
Rubber — Measurement of vulcanization characteristics using curemeters — Part 2: Oscillating disc curemeter
This document specifies a method for determining selected vulcanization characteristics of a rubber compound by means of an oscillating disc curemeter.
Caoutchouc — Mesure des caractéristiques de vulcanisation à l'aide de rhéomètres — Partie 2: Rhéomètre à disque oscillant
Le présent document spécifie une méthode pour la détermination de certaines caractéristiques de vulcanisation d'un mélange de caoutchouc à l'aide d'un rhéomètre à disque oscillant.
General Information
Relations
Buy Standard
Standards Content (Sample)
International
Standard
ISO 6502-2
Second edition
Rubber — Measurement of
2025-07
vulcanization characteristics using
curemeters —
Part 2:
Oscillating disc curemeter
Caoutchouc — Mesure des caractéristiques de vulcanisation à
l'aide de rhéomètres —
Partie 2: Rhéomètre à disque oscillant
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 General .2
5.2 Dies .3
5.3 Die closure .5
5.4 Disc .5
5.5 Disc oscillation .7
5.6 Torque-measuring system .7
5.6.1 Measurement .7
5.6.2 Recording .7
5.7 Heating and temperature control .8
6 Calibration . 8
7 Test piece . 8
8 Vulcanization . 8
9 Conditioning . 8
10 Procedure . 9
10.1 Preparation for test .9
10.2 Loading the curemeter .9
11 Expression of results . 9
11.1 General .9
11.2 Torque values .9
11.3 Times to different percentages of full cure .9
11.4 Scorch time .10
11.5 Cure rate index .10
12 Test report . 10
Annex A (normative) Calibration schedule .11
Bibliography .13
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This second edition cancels and replaces the first edition (ISO 6502-2:2018), which has been technically
revised.
The main changes are as follows:
— an Introduction was added;
— the view direction was changed in Figure 3;
3 3
— the volume of the test piece was changed from 8 cm to 9 cm in Clause 7;
— the temperature accuracy was corrected to the temperature resolution in Table A.1.
A list of all parts in the ISO 6502 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
Introduction
An International Standard specifying requirements for the use of oscillating disc curemeters was
1)
established in 1977 as ISO 3417. Later, when various rotorless curemeters were developed and became
2)
popular, an International Standard for these instruments was produced as ISO 6502. However, owing
to the differences in geometry and construction of the various available instruments, ISO 6502 was not
able to specify such requirements in detail. In 1999, it became clear that a number of different rotorless
curemeters were available and that significant developments had taken place and were continuing to do
so. Hence, it was concluded that, rather than specify individual rotorless instruments, possibly restricting
future developments, a more general document was required. Accordingly, it was decided to provide general
guidance and assistance in the design and use of curemeters.
The previous edition of this document (ISO 6502-2:2018) replaced ISO 6502, which was split into subsequent
parts, covering oscillating disc curemeters (ISO 6502-2) and rotorless curemeters (ISO 6502-3). ISO 6502-1
covers the general principle required for the measurement of vulcanization characteristics using curemeters.
1) Withdrawn.
2) Withdrawn.
v
International Standard ISO 6502-2:2025(en)
Rubber — Measurement of vulcanization characteristics
using curemeters —
Part 2:
Oscillating disc curemeter
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine
the applicability of any other restrictions.
WARNING — Certain procedures specified in this document can involve the use or generation of
substances, or the generation of waste, that can constitute a local environmental hazard. Reference
should be made to appropriate documentation on safe handling and disposal after use.
1 Scope
This document specifies a method for determining selected vulcanization characteristics of a rubber
compound by means of an oscillating disc curemeter.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 6502-1:2025, Rubber — Measurement of vulcanization characteristics using curemeters — Part 1:
Introduction
ISO 18899:2013, Rubber — Guide to the calibration of test equipment
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6502-1 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Principle
4.1 A test piece of rubber is contained in a sealed test cavity under an initial positive pressure and
maintained at an elevated temperature. A biconical disc is embedded in the test piece and is oscillated
through a small rotary amplitude. This action exerts a shear strain on the test piece, a
...
Norme
internationale
ISO 6502-2
Deuxième édition
Caoutchouc — Mesure des
2025-07
caractéristiques de vulcanisation à
l'aide de rhéomètres —
Partie 2:
Rhéomètre à disque oscillant
Rubber — Measurement of vulcanization characteristics using
curemeters —
Part 2: Oscillating disc curemeter
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 1
5 Appareillage . 2
5.1 Généralités .2
5.2 Demi-chambres .3
5.3 Fermeture de la chambre .5
5.4 Disque .5
5.5 Oscillation du disque .7
5.6 Système de mesurage du couple .7
5.6.1 Mesurage .7
5.6.2 Enregistrement .7
5.7 Mesurage et contrôle de la température .8
6 Étalonnage . 8
7 Éprouvette . 8
8 Vulcanisation . 9
9 Conditionnement . 9
10 Mode opératoire . 9
10.1 Préparation pour l’essai .9
10.2 Chargement du rhéomètre .9
11 Expression des résultats . 9
11.1 Généralités .9
11.2 Valeurs du couple .9
11.3 Temps correspondant à différents pourcentages de vulcanisation complète .10
11.4 Temps de grillage .10
11.5 Indice de vitesse de vulcanisation .10
12 Rapport d’essai . 10
Annexe A (normative) Programme d’étalonnage .12
Bibliographie . 14
iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de document ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomère, sous-comité SC 2, Essais et analyses.
Cette deuxième édition annule et remplace la première édition (ISO 6502-2:2018), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— une introduction a été ajoutée;
— la direction de la vue a été modifiée à la Figure 3;
3 3
— le volume de l’éprouvette a été modifié de 8 cm à 9 cm dans l’Article 7;
— l'exactitude de température a été remplacée par résolution de température dans le Tableau A.1.
Une liste de toutes les parties de la série ISO 6502 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.
iv
Introduction
Une Norme internationale spécifiant les exigences pour l'utilisation de rhéomètres à disque oscillant a été
1)
établie en 1977 sous la référence ISO 3417 .
Plus tard, lorsque différents rhéomètres sans rotor ont été développés et sont devenus populaires, une
2)
Norme internationale pour ces instruments a été produite sous la référence ISO 6502 .
Cependant, en raison des différences de géométrie et de construction des divers instruments disponibles,
l’ISO 6502 n'était pas en mesure de spécifier ces exigences en détail. En 1999, il est apparu qu'un certain
nombre de rhéomètres différents étaient disponibles sur le marché, et que des progrès significatifs avaient
été réalisés et se poursuivaient. Plutôt que de se concentrer sur des instruments sans rotor en particulier,
ce qui aurait pu limiter les évolutions futures, il a été convenu qu'un document plus général était nécessaire.
Par conséquent, il a été décidé de fournir des lignes directrices ainsi qu'une aide à la conception et à l'emploi
des rhéomètres de façon générale.
La précédente édition du présent document (ISO 6502-2:2018) a remplacé l'ISO 6502, qui a été scindée en
plusieurs parties, couvrant les rhéomètres à disque oscillant (ISO 6502-2) et les rhéomètres sans rotor
(ISO 6502-3). L'ISO 6502-1 porte sur le principe général exigé pour le mesurage des caractéristiques de
vulcanisation à l'aide de rhéomètres.
1) Supprimée.
2) Supprimée.
v
Norme internationale ISO 6502-2:2025(fr)
Caoutchouc — Mesure des caractéristiques de vulcanisation à
l'aide de rhéomètres —
Partie 2:
Rhéomètre à disque oscillant
AVERTISSEMENT — Il convient que l'utilisateur du présent document connaisse bien les pratiques
courantes de laboratoire. Le présent document n'a pas pour but de traiter tous les problèmes de
sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l'utilisateur d'établir des pratiques
appropriées en matière d'hygiène et de sécurité, et de déterminer l'applicabilité de toute autre
condition réglementaire nationale.
AVERTISSEMENT — Certains modes opératoires spécifiés dans le présent document peuvent
impliquer l'utilisation ou la génération de substances, ou la génération de déchets, susceptibles
de constituer un danger environnemental localisé. Il convient de se référer à la documentation
appropriée relative à la manipulation et à l'élimination de ces substances en toute sécurité après
utilisation.
1 Domaine d’application
Le présent document spécifie une méthode pour la détermination de certaines caractéristiques de
vulcanisation d'un mélange de caoutchouc à l'aide d'un rhéomètre à disque oscillant.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
ISO 6502-1:2025, Caoutchouc — Mesure des caractéristiques de vulcanisation à l’aide de rhéomètres —
...
FINAL DRAFT
International
Standard
ISO/FDIS 6502-2
ISO/TC 45/SC 2
Rubber — Measurement of
Secretariat: JISC
vulcanization characteristics using
Voting begins on:
curemeters —
2025-04-11
Part 2:
Voting terminates on:
2025-06-06
Oscillating disc curemeter
Caoutchouc — Mesure des caractéristiques de vulcanisation à
l'aide de rhéomètres —
Partie 2: Rhéomètre à disque oscillant
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/FDIS 6502-2:2025(en) © ISO 2025
FINAL DRAFT
ISO/FDIS 6502-2:2025(en)
International
Standard
ISO/FDIS 6502-2
ISO/TC 45/SC 2
Rubber — Measurement of
Secretariat: JISC
vulcanization characteristics using
Voting begins on:
curemeters —
Part 2:
Voting terminates on:
Oscillating disc curemeter
Caoutchouc — Mesure des caractéristiques de vulcanisation à
l'aide de rhéomètres —
Partie 2: Rhéomètre à disque oscillant
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland Reference number
ISO/FDIS 6502-2:2025(en) © ISO 2025
ii
ISO/FDIS 6502-2:2025(en)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 General .2
5.2 Dies .3
5.3 Die closure .4
5.4 Disc .4
5.5 Disc oscillation .6
5.6 Torque-measuring system .6
5.6.1 Measurement .6
5.6.2 Recording .6
5.7 Heating and temperature control .7
6 Calibration . 7
7 Test piece . 7
8 Vulcanization . 7
9 Conditioning . 7
10 Procedure . 8
10.1 Preparation for test .8
10.2 Loading the curemeter .8
11 Expression of results . 8
11.1 General .8
11.2 Torque values .8
11.3 Times to different percentages of full cure .8
11.4 Scorch time .9
11.5 Cure rate index .9
12 Test report . 9
Annex A (normative) Calibration schedule .10
Bibliography .12
iii
ISO/FDIS 6502-2:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This second edition cancels and replaces the first edition (ISO 6502-2:2018), which has been technically
revised.
The main changes are as follows:
— an Introduction was added;
— the view direction was changed in Figure 3;
3 3
— the volume of the test piece was changed from 8 cm to 9 cm in Clause 7;
— the temperature accuracy was corrected to the temperature resolution in Table A.1.
A list of all parts in the ISO 6502 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
ISO/FDIS 6502-2:2025(en)
Introduction
An International Standard specifying requirements for the use of oscillating disc curemeters was
1)
established in 1977 as ISO 3417.
Later, when various rotorless curemeters were developed and became popular, an International Standard
2)
for these instruments was produced as ISO 6502.
However, owing to the differences in geometry and construction of the various available instruments, ISO
6502 was not able to specify such requirements in detail. In 1999, it became clear that a number of different
rotorless curemeters were available and that significant developments had taken place and were continuing
to do so. Hence, it was concluded that, rather than specify individual rotorless instruments, possibly
restricting future developments, a more general document was required. Accordingly, it was decided to
provide general guidance and assistance in the design and use of curemeters.
The previous edition of this document (ISO 6502-1:2018) replaced ISO 6502, which was split into subsequent
parts, covering oscillating disc curemeters (ISO 6502-2) and rotorless curemeters (ISO 6502-3). ISO 6502-1
covers the general principle required for the measurement of vulcanization characteristics using curemeters.
1) Withdrawn.
2) Withdrawn.
v
FINAL DRAFT International Standard ISO/FDIS 6502-2:2025(en)
Rubber — Measurement of vulcanization characteristics
using curemeters —
Part 2:
Oscillating disc curemeter
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine
the applicability of any other restrictions.
Certain procedures specified in this document can involve the use or generation of substances
...
ISO/FDIS 6502-2:2024(en)
ISO/TC 45/SC 2
Secretariat: JISC
Date: 2024-12-162025-03-27
Rubber — Measurement of vulcanization characteristics using
curemeters —
Part 2:
Oscillating disc curemeter
Caoutchouc — Mesure des caractéristiques de vulcanisation à l'aide de rhéomètres —
Partie 2: Rhéomètre à disque oscillant
FDIS stage
ISO/FDIS 6502-2:2025(en)
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication
may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying,
or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO
at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
EmailE-mail: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
ISO/DISFDIS 6502-2:20242025(en)
Contents
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 General . 2
5.2 Dies. 4
5.3 Die closure . 8
5.4 Disc . 8
5.5 Disc oscillation . 11
5.6 Torque-measuring system. 11
5.7 Heating and temperature control . 12
6 Calibration . 12
7 Test piece . 12
8 Vulcanization . 13
9 Conditioning . 13
10 Procedure . 13
10.1 Preparation for test . 13
10.2 Loading the curemeter . 13
11 Expression of results . 13
11.1 General . 13
11.2 Torque values . 13
11.3 Times to different percentages of full cure . 14
11.4 Scorch time . 14
11.5 Cure rate index . 14
12 Test report . 14
Annex A (normative) Calibration schedule . 16
Bibliography . 18
iii
ISO/FDIS 6502-2:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s)
which may be required to implement this document. However, implementers are cautioned that this may not
represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 2, Testing and analysis.
This second edition cancels and replaces the first edition (ISO 6502-2:2018), which has been technically
revised.
The main changes are as follows:
— — an Introduction was added;
— — the view direction was changed in Figure 3Figure 3;;
3 3
— — the volume of the test piece was changed from 8 cm to 9 cm in Clause 7Clause 7;;
— — the temperature accuracy was corrected to the temperature resolution in Table A.1Table A.1.
A list of all parts in the ISO 6502 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
Field Code Changed
iv
ISO/DISFDIS 6502-2:20242025(en)
Introduction
An International Standard specifying requirements for the use of oscillating disc curemeters was established
1 1)
in 1977 as ISO 3417, . . Later, when various rotorless curemeters were developed and became popular, an
2 2)
International Standard for these instruments was produced as ISO 6502, . However, owing to the
differences in geometry and construction of the various available instruments, ISO 6502 was not able to
specify such requirements in detail. In 1999, it became clear that a number of different rotorless curemeters
were available and that significant developments had taken place and were continuing to do so. Hence, it was
concluded that, rather than specify individual rotorless instruments, possibly restricting future developments,
a more general document was required. Accordingly, it was decided to provide general guidance and
assistance in the design and use of curemeters. ISO 6502 was divided into ISO 6502-1 and ISO 6502-3. ISO
3417 was incorporated into ISO 6502-2.
The previous edition of this document (ISO 6502-1:2018) replaced ISO 6502, which was split into subsequent
parts, covering oscillating disc curemeters (ISO 6502-2) and rotorless curemeters (ISO 6502-3). ISO 6502-1
covers the general principle required for the measurement of vulcanization characteristics using curemeters.
Withdrawn.
1)
Withdrawn.
Withdrawn.
2)
Withdrawn.
v
DRAFT International Standard ISO/DIS 6502-2:2024(en)
Rubber — Measurement of vulcanization characteristics using
curemeters — —
Part 2:
Oscillating disc curemeter
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine the
applicability of any other restrictions.
Certain procedures specified in this document can involve the use or generation of substances, or the
generation of waste, that can constitute a local environmental hazard. Reference should be made to
appropriate documentation on safe handling and disposal after use.
1 Scope
This document specifies a method for determining selected vulcanization characteristics of a rubber
compound by means of an oscillating disc curemeter.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 6502--1:2025, Rubber — Measurement of vulcanization characteristics using curemeters — Part 1:
Introduction
ISO 18899:2013, Rubber — Guide to the calibration of test equipment
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6502-1 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— — ISO Online browsing platform: available at https://www.iso.org/obp
— — IEC Electropedia: available at https://www.electropedia.org/
4 Principle
4.1 4.1 A test piece of rubber is contained in a sealed test cavity under an initial positive pressure and
maintained at an elevated temperature. A biconical disc is embedded in the test piece and is oscillated through
a small rotary amplitude. This action exerts a shear strain on the test piece, and the torque required to oscillate
the disc depends on the stiffness (shear modulus) of the rubber. The torque is recorded autographically as a
function of time.
ISO/FDIS 6502-2:2025(en)
4.2 4.2 The stiffness of the rubber test piece increases as vulcanization proceeds. The curve is
complete when the recorded torque rises either to an equilibrium value or to a maximum value (see
ISO 6502--1). If the torque continues to increase, vulcanization is considered to be complete after a given time.
The time required to obtain a vulcanization curve is a function of the test temperature and the characteristics
of the rubber compound.
4.3 4.3 The parameters that can be measured from the recorded curve of torque as a function of time,
i.e. M = f (t), are presented in ISO 6502--1:2025, Table 1.
5 Apparatus
5.1 General
The curemeter consists of a biconical disc in a temperature-controlled die cavity. The shaft of the disc is
secured in a drive shaft and oscillated through a small rotary amplitude (see Figure 1Figure 1).).
The torque applied to the disc represents the resistance of the rubber test piece to deformation and is recorded
autographically to yield a curve of torque versus time.
ISO/DISFDIS 6502-2:20242025(en)
Key
1 heater 6 upper platen
2 seal 7 calibrated temperature sensors
3 lower die 8 lower platen
4 upper die 9 biconical disc
ISO/FDIS 6502-2:2025(en)
5 cylinder rod
Figure 1 — Curemeter assembly
5.2 Dies
The dies shall be manufactured from a non-deforming tool steel having a minimum Rockwell hardness of
50 HRC or equivalent.
The geometry of the dies is shown in Figures 2Figures 2 a
...
PROJET FINAL
Norme
internationale
ISO/FDIS 6502-2
ISO/TC 45/SC 2
Caoutchouc — Mesure des
Secrétariat: JISC
caractéristiques de vulcanisation à
Début de vote:
l'aide de rhéomètres —
2025-04-11
Partie 2:
Vote clos le:
2025-06-06
Rhéomètre à disque oscillant
Rubber — Measurement of vulcanization characteristics using
curemeters —
Part 2: Oscillating disc curemeter
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
ISO/FDIS 6502-2:2025(fr) © ISO 2025
PROJET FINAL
ISO/FDIS 6502-2:2025(fr)
Norme
internationale
ISO/FDIS 6502-2
ISO/TC 45/SC 2
Caoutchouc — Mesure des
Secrétariat: JISC
caractéristiques de vulcanisation à
Début de vote:
l'aide de rhéomètres —
2025-04-11
Partie 2:
Vote clos le:
2025-06-06
Rhéomètre à disque oscillant
Rubber — Measurement of vulcanization characteristics using
curemeters —
Part 2: Oscillating disc curemeter
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse Numéro de référence
ISO/FDIS 6502-2:2025(fr) © ISO 2025
ii
ISO/FDIS 6502-2:2025(fr)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 1
5 Appareillage . 2
5.1 Généralités .2
5.2 Demi-chambres .3
5.3 Fermeture de la chambre .5
5.4 Disque .5
5.5 Oscillation du disque .7
5.6 Système de mesurage du couple .7
5.6.1 Mesurage .7
5.6.2 Enregistrement .7
5.7 Mesurage et contrôle de la température .8
6 Étalonnage . 8
7 Éprouvette . 8
8 Vulcanisation . 9
9 Conditionnement . 9
10 Mode opératoire . 9
10.1 Préparation pour l’essai .9
10.2 Chargement du rhéomètre .9
11 Expression des résultats . 9
11.1 Généralités .9
11.2 Valeurs du couple .9
11.3 Temps correspondant à différents pourcentages de vulcanisation complète .10
11.4 Temps de grillage .10
11.5 Indice de vitesse de vulcanisation .10
12 Rapport d’essai . 10
Annexe A (normative) Programme d’étalonnage .12
Bibliographie . 14
iii
ISO/FDIS 6502-2:2025(fr)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de document ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d'élastomère, sous-comité SC 2, Essais et analyses.
Cette deuxième édition annule et remplace la première édition (ISO 6502-2:2018), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— une introduction a été ajoutée;
— la direction de la vue a été modifiée à la Figure 3;
3 3
— le volume de l’éprouvette a été modifié de 8 cm à 9 cm dans l’Article 7;
— l'exactitude de température a été remplacée par résolution de température dans le Tableau A.1.
Une liste de toutes les parties de la série ISO 6502 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.
iv
ISO/FDIS 6502-2:2025(fr)
Introduction
Une Norme internationale spécifiant les exigences pour l'utilisation de rhéomètres à disque oscillant a été
1)
établie en 1977 sous la référence ISO 3417 .
Plus tard, lorsque différents rhéomètres sans rotor ont été développés et sont devenus populaires, une
2)
Norme internationale pour ces instruments a été produite sous la référence ISO 6502 .
Cependant, en raison des différences de géométrie et de construction des divers instruments disponibles,
l’ISO 6502 n'était pas en mesure de spécifier ces exigences en détail. En 1999, il est apparu qu'un certain
nombre de rhéomètres différents étaient disponibles sur le marché, et que des progrès significatifs avaient
été réalisés et se poursuivaient. Plutôt que de se concentrer sur des instruments sans rotor en particulier,
ce qui aurait pu limiter les évolutions futures, il a été convenu qu'un document plus général était nécessaire.
Par conséquent, il a été décidé de fournir des lignes directrices ainsi qu'une aide à la conception et à l'emploi
des rhéomètres de façon générale.
La précédente édition du présent document (ISO 6502-1:2018) a remplacé l'ISO 6502, qui a été scindée en
plusieurs parties, couvrant les rhéomètres à disque oscillant (ISO 6502-2) et les rhéomètres sans rotor
(ISO 6502-3). L'ISO 6502-1 porte sur le principe général exigé pour le mesurage des caractéristiques de
vulcanisation à l'aide de rhéomètres.
1) Supprimée.
2) Supprimée.
v
-------
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.