Magnesium and magnesium alloys -- Wrought magnesium alloys

ISO 3116:2007 specifies the chemical composition and mechanical properties of magnesium alloys for wrought products in the form of bars and solid sections, tubes and hollow sections, forgings, and plate and sheet.

Magnésium et alliages de magnésium -- Alliages de magnésium corroyés

General Information

Status
Replaced
Publication Date
15-Apr-2007
Withdrawal Date
15-Apr-2007
Current Stage
6060 - International Standard published
Start Date
26-Mar-2007
Completion Date
16-Apr-2007
Ref Project

RELATIONS

Buy Standard

Standard
ISO 3116:2007 - Magnesium and magnesium alloys -- Wrought magnesium alloys
English language
12 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (sample)

INTERNATIONAL ISO
STANDARD 3116
Fourth edition
2007-04-15
Magnesium and magnesium alloys —
Wrought magnesium alloys
Magnésium et alliages de magnésium — Alliages de magnésium
corroyés
Reference number
ISO 3116:2007(E)
ISO 2007
---------------------- Page: 1 ----------------------
ISO 3116:2007(E)
PDF disclaimer

This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but

shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In

downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat

accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.

Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation

parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In

the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.

COPYRIGHT PROTECTED DOCUMENT
© ISO 2007

All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,

electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or

ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2007 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 3116:2007(E)
Contents Page

Foreword............................................................................................................................................................ iv

Introduction ........................................................................................................................................................ v

1 Scope ......................................................................................................................................................1

2 Normative references ............................................................................................................................1

3 Designation ............................................................................................................................................1

4 Requirements.........................................................................................................................................2

5 Sampling.................................................................................................................................................2

6 Test pieces .............................................................................................................................................3

7 Test methods..........................................................................................................................................3

8 Retests ....................................................................................................................................................3

9 Rounding of results...............................................................................................................................3

Annex A (informative) List of national designations corresponding to the ISO designation ...................10

Annex B (informative) Physical properties of wrought magnesium alloys.................................................11

Annex C (informative) Heat-treatment schedules for wrought magnesium alloys ....................................12

© ISO 2007 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO 3116:2007(E)
Foreword

ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies

(ISO member bodies). The work of preparing International Standards is normally carried out through ISO

technical committees. Each member body interested in a subject for which a technical committee has been

established has the right to be represented on that committee. International organizations, governmental and

non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the

International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.

International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.

The main task of technical committees is to prepare International Standards. Draft International Standards

adopted by the technical committees are circulated to the member bodies for voting. Publication as an

International Standard requires approval by at least 75 % of the member bodies casting a vote.

Attention is drawn to the possibility that some of the elements of this document may be the subject of patent

rights. ISO shall not be held responsible for identifying any or all such patent rights.

ISO 3116 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee

SC 5, Magnesium and alloys of cast or wrought magnesium.

This fourth edition cancels and replaces the third edition (ISO 3116:2001), which has been technically revised.

The reason for this fourth edition is to clarify that requirements for chemical composition relate to cast

analysis, and to adjust elongation values for some alloys and tempers.
iv © ISO 2007 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 3116:2007(E)
Introduction

This International Standard classifies the commercially available magnesium alloys into a number of grades

suitable for the application to which they might be put.

Some of the alloys referenced in this International Standard can be the subject of a patent or of patent

applications and their listing herein is not to be construed in any way as the granting of a licence under such

patent rights.
© ISO 2007 – All rights reserved v
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 3116:2007(E)
Magnesium and magnesium alloys — Wrought magnesium
alloys
1 Scope

This International Standard specifies the chemical composition and mechanical properties of magnesium

alloys for wrought products in the form of bars and solid sections, tubes and hollow sections, forgings, and

plate and sheet.
2 Normative references

The following referenced documents are indispensable for the application of this document. For dated

references, only the edition cited applies. For undated references, the latest edition of the referenced

document (including any amendments) applies.
ISO 31-0:1992, Quantities and units — Part 0: General principles

ISO 2092, Light metals and their alloys — Code of designation based on chemical symbols

ISO 6892, Metallic materials — Tensile testing at ambient temperature
EN 515, Aluminium and aluminium alloys — Wrought products — Temper designations
3 Designation
3.1 Material
The material shall be designated by symbols as given in Tables 1 to 11.
The material symbol designations are in accordance with ISO 2092.

NOTE A list of national designations corresponding to this International Standard is given in Annex A and a table of

physical properties of the listed alloys is given in Annex B.
3.2 Temper designation
The following symbols shall be used for temper designation:
⎯ O: annealed;
⎯ F: as fabricated;

⎯ H×8: fully hardened (strain hardened to give maximum ultimate tensite strength);

⎯ H×4: half hardened (strain hardened to give an ultimate tensile strength approximately midway between

that of annealed and H×8 temper);
© ISO 2007 – All rights reserved 1
---------------------- Page: 6 ----------------------
ISO 3116:2007(E)

⎯ H×2: quarter hardened (strain hardened to give an ultimate tensile strength approximately midway

between that of annealed and H×4 temper);

⎯ T5: cooled from an elevated temperature shaping process and then artificially aged;

⎯ T6: solution heat treated and then artificially aged.
The temper designations are in accordance with EN 515.
3.3 Designations of product form
The following symbols shall be used for product form:
⎯ B: bars and solid sections;
⎯ T: tubes and hollow sections;
⎯ F: forgings;
⎯ P: plate and sheet.
3.4 Designation for ordering
EXAMPLE

An order for magnesium bars, conforming to this International Standard, of magnesium alloy ISO-WD 21150, delivered in

the as-fabricated condition (F) is as follows:
ISO 3116 - ISO-MgAl3Zn1 (A) (or WD21150) - F - B
Tonnage and dimensions are to be specified in addition.
4 Requirements
4.1 Chemical composition

The chemical composition of wrought magnesium alloys, taken as cast analysis at the time the material is

cast, shall conform to the requirements for the appropriate material given in Table 1.

4.2 Mechanical properties

The minimum values of the mechanical properties of wrought products in magnesium alloys in the defined

temper conditions shall be as given in Tables 2 to 11.
4.3 Frequency of testing

The frequency of testing shall be subject to an agreement between the manufacturer and the purchaser.

5 Sampling

Conditions for sampling, formation of batches and frequency of verification shall be subject to an agreement

between the manufacturer and the purchaser.
2 © ISO 2007 – All rights reserved
---------------------- Page: 7 ----------------------
ISO 3116:2007(E)
6 Test pieces

Test pieces shall be taken in the longitudinal direction. For rolled flat products of thickness > 0,6 mm, test

pieces may be taken in the long transverse direction.
7 Test methods
7.1 Chemical composition

The determination of the alloying elements given in Table 1 shall be performed in accordance with normal

practice.
7.2 T
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.