ISO 182-3:2025

Plastics - Determination of the tendency of compounds and products based on vinyl chloride homopolymers and copolymers to evolve hydrogen chloride and any other acidic products at elevated temperatures - Part 3: Conductometric method

This document specifies a method for the determination of the thermal stability at elevated temperature of compounds and products based on vinyl chloride homopolymers and copolymers (in the following text abbreviated as PVC) which undergo dehydrochlorination (the evolution of hydrogen chloride). This document is applicable to the characterization of PVC compounds and products, especially with regard to the effectiveness of their heat-stabilizing systems. It is applicable to coloured PVC compounds and products where a discolouration test under the action of heat can be unsatisfactory. This document is applicable to compounded PVC materials and products. It can be applicable to polymers in powder form under appropriate conditions, depending on the agreement between the interested parties. This document does not apply to PVC compounds in the form of dry blends, since such materials might not be sufficiently homogeneous. This document does not apply to PVC compounds and products which evolve other decomposition products, in addition to hydrogen chloride, at elevated temperatures that can affect the conductivity of water when they are absorbed into it. NOTE In this case, ISO 182-4 [2] provides the suitable method for the determination of chloride ion (Cl−) in the absorbing solution. This document can also be applied to other plastics materials which can evolve hydrogen chloride or other hydrogen halides when heated under the conditions prescribed by the relevant specifications, or as agreed upon between the interested parties.

Plastiques — Détermination de la tendance des compositions et produits à base d’homopolymères et de copolymères du chlorure de vinyle à dégager du chlorure d’hydrogène et éventuellement d’autres produits acides à températures élevées — Partie 3: Méthode conductimétrique

Le présent document spécifie une méthode pour la détermination de la stabilité thermique à températures élevées des compositions et produits à base d’homopolymères et de copolymères du chlorure de vinyle (PVC dans le texte qui suit), qui sont sujets à une déhydrochloruration (dégagement de chlorure d’hydrogène). Le présent document s’applique à la caractérisation des compositions et produits à base de PVC, en particulier en ce qui concerne l’efficacité de leurs systèmes de stabilisation à la chaleur. Il est applicable aux compositions et produits à base de PVC colorés, lorsqu’un essai de décoloration sous l’action de la chaleur peut être insatisfaisant. Le présent document est applicable aux matériaux et produits composés de PVC. Il peut être applicable aux polymères sous forme de poudres dans des conditions appropriées en fonction de l’accord entre les parties intéressées. Le présent document ne s’applique pas aux compositions de PVC sous forme de mélanges secs, ces matériaux pouvant ne pas être suffisamment homogénéisés. Le présent document ne s’applique pas aux compositions et produits à base de PVC qui dégagent, à températures élevées, des produits de décomposition en plus du chlorure d’hydrogène pouvant avoir une incidence sur la conductivité de l’eau lorsqu’ils y sont absorbés. NOTE Dans ce cas, l’ISO 182-4 [2] fournie la méthode appropriée pour la détermination des ions chlorures (Cl−) dans la solution absorbante. Le présent document peut aussi être appliqué à d’autres matériaux plastiques pouvant dégager du chlorure d’hydrogène ou d’autres halogénures d’hydrogène lorsqu’ils sont chauffés dans des conditions particulières prescrites dans les spécifications appropriées ou convenues entre les parties intéressées.

General Information

• Status: Published
• Publication Date: 21-Oct-2025
• ICS: 83.080.20 - Thermoplastic materials
• Technical Committee: ISO/TC 61/SC 9 - Thermoplastic materials
• Drafting Committee: ISO/TC 61/SC 9/WG 20 - Poly(vinyl chloride)
• Current Stage: 6060 - International Standard published
• Start Date: 22-Oct-2025
• Due Date: 21-May-2026
• Completion Date: 22-Oct-2025

Relations

• Consolidates: ISO 5286:2023 - Flight performance of civil small and light fixed-wing unmanned aircraft systems (UAS) - Test methods
• Effective Date: 05-Apr-2025
• Revises: ISO 182-3:2023 - Plastics - Determination of the tendency of compounds and products based on vinyl chloride homopolymers and copolymers to evolve hydrogen chloride and any other acidic products at elevated temperatures - Part 3: Conductometric method
• Effective Date: 07-Jan-2025

Overview

ISO 182-3:2025 - Plastics: Determination of the tendency of PVC compounds and products to evolve hydrogen chloride at elevated temperatures - Part 3: Conductometric method.
This ISO method specifies a conductometric test to evaluate the thermal stability of vinyl chloride homopolymers and copolymers (PVC) that undergo dehydrochlorination (HCl evolution). It is intended for characterization of compounded PVC materials and products, and for assessing the effectiveness of heat‑stabilizing systems where discoloration tests are unsuitable.

Key topics and requirements

• Test principle: A sample is heated in a nitrogen stream; evolved HCl is absorbed in demineralized water and quantified by the change in the water’s conductivity. The measured parameter is the stability time (ts) - the time for a defined conductivity change.
• Reagents and gas purity: Use analytical‑grade reagents. Nitrogen purity: < 6 ppm O2 and < 0.1 ppm CO2; gas flow validation includes passing N2 through demineralized water at (7.2 ± 0.1) L/h with no conductivity change.
• Absorbing medium: Demineralized water with conductivity ≤ 5 µS/cm.
• Apparatus: Dehydrochlorination cells (Cell A reusable, Cell B disposable), measurement cell, conductance meter/electrodes, heated bath or block (capable of 170–210 °C, maintained to ±0.1 °C), flowmeter and drying agent for N2.
• Sample handling: Clauses detail preparation for plastisols, pellets, films, coatings, cable insulation, etc.; dry blends are excluded because of likely inhomogeneity.
• Limitations: Not applicable to materials that evolve other decomposition products that alter water conductivity-ISO 182-4 is recommended in that case for chloride ion determination.
• Accuracy and comparability: The document includes precision data (repeatability and reproducibility) and a comparison with the pH‑meter method in ISO 182-2.

Applications and users

• Quality control and R&D of PVC formulations to verify heat‑stabilizer performance.
• Materials selection for coloured PVC products where visual discoloration tests are unreliable.
• Cable and wire manufacturers, extrusion and moulding labs assessing thermal ageing and HCl release.
• Independent testing laboratories performing standardized assessments for compliance, material specifications, and supplier verification.
• Regulatory and safety evaluations where quantifying HCl evolution is necessary for end‑use risk assessment.

Related standards

• ISO 182-2: pH‑meter method (comparison referenced)
• ISO 182-4: Determination of chloride ion in absorbing solutions (when other decomposition products interfere)
• Normative references used in ISO 182-3: ISO 565, ISO 4793, ISO 6353-2

Keywords: ISO 182-3:2025, conductometric method, PVC thermal stability, dehydrochlorination, hydrogen chloride evolution, heat‑stabilizers, conductometry, PVC testing.

Standards Content (Sample)

International
Standard
ISO 182-3
Third edition
Plastics — Determination of
2025-10
the tendency of compounds and
products based on vinyl chloride
homopolymers and copolymers to
evolve hydrogen chloride and any
other acidic products at elevated
temperatures —
Part 3:
Conductometric method
Plastiques — Détermination de la tendance des compositions et
produits à base d’homopolymères et de copolymères du chlorure
de vinyle à dégager du chlorure d’hydrogène et éventuellement
d’autres produits acides à températures élevées —
Partie 3: Méthode conductimétrique
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 2
5 Reagents . 2
6 Apparatus . 2
7 Preparation of test samples . 7
7.1 General .7
7.2 PVC plastisols . .7
7.3 PVC pellets, extrudates, mouldings, thick sheet, etc. .7
7.4 PVC film and sheet .7
7.5 PVC coatings .7
7.6 Cable and conductor insulation or sheating .7
8 Number of tests . 7
9 Temperatures for dehydrochlorination . 7
10 Test procedure . 8
10.1 Preparation of test portion .8
10.2 Preliminary operations .8
10.3 Special precautions when using dehydrochlorination cell A .8
10.4 Preparation of the measurement cell .8
10.5 Decomposition of the test portion .8
11 Expression of results . 9
12 Test report . 9
13 Precision . 9
13.1 General .9
13.2 Repeatability .10
13.3 Reproducibility .10
13.4 Comparison with the pH-meter method (ISO 182-2) .10
13.5 Factors affecting the stability time .10
13.6 Conclusions . 12
Annex A (informative) Cleaning of the apparatus .13
Annex B (informative) Calculation of repeatability and reproducibility — Conductometric and
pH-meter methods . 14
Annex C (informative) Interlaboratory test.16
Bibliography .18

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 9, Thermoplastic
materials, in collaboration with the European Committee for Standardization (CEN) Technical Committee
CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 182-3:2023), of which it constitutes a minor
revision.
The changes are as follows:
— the reference to ISO 182-4 in the Scope has been placed in a Note;
— the unit min has been added to m, r, and R in Clause 13;
— the code for stability time in Table 1 has been corrected to t ;
s
— the unit of t in Table 2 has been corrected to min.
s
A list of all parts in the ISO 182 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
International Standard ISO 182-3:2025(en)
Plastics — Determination of the tendency of compounds
and products based on vinyl chloride homopolymers and
copolymers to evolve hydrogen chloride and any other acidic
products at elevated temperatures —
Part 3:
Conductometric method
WARNING — The use of this document can involve hazardous materials, operations and equipment.
This document does not purport to address all of the safety problems associated with its use. It is the
responsibility of the user of this document to establish appropriate safety and health practices and
determine the applicability of regulatory limitations prior to use.
1 Scope
1.1 This document specifies a method for the determination of the thermal stability at elevated
temperature of compounds and products based on vinyl chloride homopolymers and copolymers (in the
following text abbreviated as PVC) which undergo dehydrochlorination (the evolution of hydrogen chloride).
1.2 This document is applicable to the characterization of PVC compounds and products, especially with
regard to the effectiveness of their heat-stabilizing systems.
It is applicable to coloured PVC compounds and products where a discolouration test under the action of
heat can be unsatisfactory.
1.3 This document is applicable to compounded PVC materials and products. It can be applicable to
polymers in powder form under appropriate conditions, depending on the agreement between the interested
parties.
This document does not apply to PVC compounds in the form of dry blends, since such materials might not
be sufficiently homogeneous.
1.4 This document does not apply to PVC compounds and products which evolve other decomposition
products, in addition to hydrogen chloride, at elevated temperatures that can affect the conductivity of
water when they are absorbed into it.
[2] −
NOTE In this case, ISO 182-4 provides the suitable method for the determination of chloride ion (Cl ) in the
absorbing solution.
1.5 This document can also be applied to other plastics materials which can evolve hydrogen chloride or
other hydrogen halides when heated under the conditions prescribed by the relevant specifications, or as
agreed upon between the interested parties.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.

ISO 565, Test sieves — Metal wire cloth, perforated metal plate and electroformed sheet — Nominal sizes of
openings
ISO 4793, Laboratory sintered (fritted) filters — Porosity grading, classification and designation
ISO 6353-2, Reagents for chemical analysis — Part 2: Specifications — First series
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
stability time
t
s
time, measured by reference to a predetermined change in the conductivity of absorbing demineralized
water, required for a certain amount of hydrogen chloride to be evolved when a prescribed mass of PVC
compound or product is maintained at an elevated temperature under the test conditions specified in this
document
4 Principle
A test portion of the PVC compound or product is maintained at an agreed temperature in a nitrogen gas
stream and the hydrogen chloride evolved is absorbed in a given amount of demineralized water. The amount
of hydrogen chloride evolved is determined in relation to the recorded change in conductivity of the water.
5 Reagents
During the test, use only reagents of recognized analytical grade in accordance with ISO 6353-2.
5.1 Pure nitrogen, containing less than 6 ppm oxygen and less than 0,1 ppm carbon dioxide by volume.
The purity shall be such that when the gas is passed through demineralized water (see 5.2) for 1 h at a rate
of (7,2 ± 0,1) l/h, the conductivity of the water remains unchanged.
The gas shall be dried by passing it through a suitable drying agent, and the flow-rate through the
dehydrochlorination cell adjusted by means of a needle valve and measured using a suitable flowmeter.
5.2 Demineralized water, with a conductivity not higher than 5 µS/cm.
6 Apparatus
The general arrangement of the apparatus is shown in Figure 1.
6.1 Dehydrochlorination cells.
6.1.1 Glass Cell A (re-usable), with shape and dimensions as shown in Figure 2.
A recommended procedure for cleaning the cell is given in Annex A.
6.1.2 Glass Cell B (disposable), with shape and dimensions as shown in Figure 3.

NOTE Other types of cell can be employed if it has been proved that the results obtained are equivalent to those
obtained with one of the cells described in 6.1.1 and 6.1.2.
6.2 Test portion holder, for use with cell A. The test portion shall be supported on a porous sintered-
glass disc grade P 100, as specified in ISO 4793, 10 mm in diameter.
To prevent blocking of the porous disc, it is advisable to place a thin, soft layer of glass wool between it and
the test portion.
A recommended procedure for cleaning the disc support is given in Annex A.
Key
1 N cylinder with pure nitrogen
2 flowmeter
3 heating bath/heating block including temperature controller (resolution 0,1 °C)
4 PVC test portion
5 dehydrochlorination cell (details see Figure 2 and 3)
6 thermometer (resolution 0,1 °C)
7 magnetic stirrer (in case using heating oil bath)
8 absorbing solution
9 measuring electrode(s)
10 conductance meter
Figure 1 — General arrangement of apparatus

Dimensions in millimetres
Key
1 spurs
2 17 coils
3 sintered-glass disc, 10 mm diameter (removable)
Figure 2 — Cell A (re-usable) for dehydrochlorination of PVC samples

Dimensions in millimetres
Key
1 disposable glass
2 nitrogen inlet tube
3 sample
Figure 3 — Cell B (disposable) for dehydrochlorination of PVC samples
6.3 Glass connection tube, for use with cell A, connecting the dehydrochlorination cell to the
measurement cell and having dimensions as shown in Figure 4. The connection tube is secured to cell A by
two springs fixed to hooks on the ground-glass joints. The tube shall be provided with an insulating jacket.

-------------------
...

Norme
internationale
ISO 182-3
Troisième édition
Plastiques — Détermination de
2025-10
la tendance des compositions et
produits à base d’homopolymères
et de copolymères du chlorure
de vinyle à dégager du chlorure
d’hydrogène et éventuellement
d’autres produits acides à
températures élevées —
Partie 3:
Méthode conductimétrique
Plastics — Determination of the tendency of compounds and
products based on vinyl chloride homopolymers and copolymers
to evolve hydrogen chloride and any other acidic products at
elevated temperatures —
Part 3: Conductometric method
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 2
3 Termes et définitions . 2
4 Principe. 2
5 Réactifs . 2
6 Appareillage . 2
7 Préparation des échantillons pour essai . 7
7.1 Généralités .7
7.2 Plastisols de PVC .7
7.3 Granulés de PVC, extrudats, pièces moulées, plaques épaisses, etc .7
7.4 Films et feuilles de PVC .7
7.5 Revêtements de PVC .7
7.6 Isolation et revêtements de câbles et de conducteurs .7
8 Nombre d’essais . 7
9 Températures pour la déhydrochloruration . 8
10 Mode opératoire d’essai . 8
10.1 Préparation de la prise d’essai.8
10.2 Opérations préliminaires .8
10.3 Précautions spéciales lors de l’utilisation de la cellule de déhydrochloruration A .8
10.4 Préparation de la cellule de mesure .8
10.5 Décomposition de la prise d’essai .9
11 Expression des résultats . 9
12 Rapport d’essai . 9
13 Fidélité . 9
13.1 Généralités .9
13.2 Répétabilité .10
13.3 Reproductibilité .10
13.4 Comparaison avec la méthode au pH-mètre (ISO 182-2) .10
13.5 Facteurs ayant une incidence sur le temps de stabilité .10
13.6 Conclusions . 13
Annexe A (informative) Nettoyage de l’appareillage . 14
Annexe B (informative) Calcul de la répétabilité et de la reproductibilité — Méthode
conductimétrique et méthode au pH-mètre .15
Annexe C (informative) Essai interlaboratoires . 17
Bibliographie . 19

iii
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux
de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général
confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n'avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l'adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 9, Matériaux
thermoplastiques, en collaboration avec le comité technique CEN/TC 249, Plastiques, du Comité européen de
normalisation (CEN) conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de
Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 182-3:2023), dont elle constitue une
révision mineure.
Les modifications sont les suivantes:
— dans le Domaine d’application, la référence à l’ISO 182-4 a été mise dans une Note;
— l'unité min a été ajoutée à m, r et R à l'Article 13;
— dans le Tableau 1, le sigle utilisé pour le temps de stabilité a été modifié en t ;
s
— dans le Tableau 2, l’unité de t a été modifié en min.
s
Une liste de toutes les parties de la série ISO 182 se trouve sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
Norme internationale ISO 182-3:2025(fr)
Plastiques — Détermination de la tendance des compositions
et produits à base d’homopolymères et de copolymères du
chlorure de vinyle à dégager du chlorure d’hydrogène et
éventuellement d’autres produits acides à températures
élevées —
Partie 3:
Méthode conductimétrique
AVERTISSEMENT — L’utilisation du présent document peut impliquer l’exécution d’opérations et
l’utilisation de matières et d’équipements dangereux. Le présent document n’a pas pour but de traiter
tous les problèmes de sécurité éventuels qui sont liés à son utilisation. Il incombe à l’utilisateur du
présent document de mettre en place des pratiques appropriées en matière d’hygiène et de sécurité
et de déterminer l’applicabilité des limites réglementaires avant de l’utiliser.
1 Domaine d’application
1.1 Le présent document spécifie une méthode pour la détermination de la stabilité thermique à
températures élevées des compositions et produits à base d’homopolymères et de copolymères du chlorure
de vinyle (PVC dans le texte qui suit), qui sont sujets à une déhydrochloruration (dégagement de chlorure
d’hydrogène).
1.2 Le présent document s’applique à la caractérisation des compositions et produits à base de PVC, en
particulier en ce qui concerne l’efficacité de leurs systèmes de stabilisation à la chaleur.
Il est applicable aux compositions et produits à base de PVC colorés, lorsqu’un essai de décoloration sous
l’action de la chaleur peut être insatisfaisant.
1.3 Le présent document est applicable aux matériaux et produits composés de PVC. Il peut être applicable
aux polymères sous forme de poudres dans des conditions appropriées en fonction de l’accord entre les
parties intéressées.
Le présent document ne s’applique pas aux compositions de PVC sous forme de mélanges secs, ces matériaux
pouvant ne pas être suffisamment homogénéisés.
1.4 Le présent document ne s’applique pas aux compositions et produits à base de PVC qui dégagent, à
températures élevées, des produits de décomposition en plus du chlorure d’hydrogène pouvant avoir une
incidence sur la conductivité de l’eau lorsqu’ils y sont absorbés.
[2] −
NOTE Dans ce cas, l’ISO 182-4 fournie la méthode appropriée pour la détermination des ions chlorures (Cl )
dans la solution absorbante.
1.5 Le présent document peut aussi être appliqué à d’autres matériaux plastiques pouvant dégager du
chlorure d’hydrogène ou d’autres halogénures d’hydrogène lorsqu’ils sont chauffés dans des conditions
particulières prescrites dans les spécifications appropriées ou convenues entre les parties intéressées.

2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
ISO 565, Tamis de contrôle — Tissus métalliques, tôles métalliques perforées et feuilles électroformées —
Dimensions nominales des ouvertures
ISO 4793, Filtres frittés de laboratoire — Échelle de porosité — Classification et désignation
ISO 6353-2, Réactifs pour analyse chimique — Partie 2: Spécifications — Première série
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en normalisation,
consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
3.1
temps de stabilité
t
s
durée, mesurée par référence à une variation prédéterminée de la conductivité d’une solution absorbante
d’eau déminéralisée, nécessaire au dégagement d’une certaine quantité de chlorure d’hydrogène, lorsqu’une
masse prescrite d’une composition ou d’un produit à base de PVC est maintenue à une température élevée
dans les conditions d’essai spécifiées dans le présent document
4 Principe
Une prise d’essai de la composition ou du produit à base de PVC est maintenue à une température convenue,
dans un courant d’azote gazeux, et le chlorure d’hydrogène dégagé est absorbé par un volume donné d’eau
déminéralisée. La quantité de chlorure d’hydrogène dégagée est déterminée par enregistrement de la
variation de la conductivité de l’eau.
5 Réactifs
Au cours de l’essai, utiliser uniquement des réactifs de qualité analytique reconnue selon l’ISO 6353-2.
5.1 Azote pur, contenant moins de 6 ppm d’oxygène et moins de 0,1 ppm de dioxyde de carbone en volume.
La pureté doit être telle qu’après 1 h de barbotage du gaz dans l’eau déminéralisée (voir 5.2), à un débit de
(7,2 ± 0,1) l/h, la conductivité de l’eau reste inchangée.
Le gaz doit être desséché en le faisant passer à travers un agent déshydratant approprié et le débit dans la
cellule de déhydrochloruration doit être réglé par une vanne à pointeau et mesuré au moyen d’un débitmètre
approprié.
5.2 Eau déminéralisée, avec une conductivité non supérieure à 5 µS/cm.
6 Appareillage
La Figure 1 donne une représentation générale de l’appareillage.

6.1 Cellules de déhydrochloruration.
6.1.1 Cellule en verre A (réutilisable), ayant la forme et les dimensions indiquées à la Figure 2.
Un mode opératoire recommandé pour le nettoyage de cette cellule est fourni dans l’Annexe A.
6.1.2 Cellule en verre B (consommable), ayant la forme et les dimensions indiquées à la Figure 3.
NOTE D’autres types de cellules peuvent être employés à condition de démontrer que les résultats obtenus sont
équivalents à ceux obtenus par l’une des cellules décrites en 6.1.1 et 6.1.2.
6.2 Support de la prise d’essai, pour la cellule A. La prise d’essai doit être posée sur une pastille en verre
fritté poreuse, de porosité P 100, comme spécifié dans l’ISO 4793, de 10 mm de diamètre.
Pour éviter l’encrassement de la pastille poreuse, il est conseillé de placer un tampon de laine de verre mince
et doux entre la prise d’essai et la pastille.
Un mode opératoire recommandé pour le nettoyage de ce support est fourni dans l’Annexe A.
Légende
1 bouteille de N avec azote pur
2 débitmètre
3 bain chauffant/bloc chauffant comprenant un régulateur thermique (résolution de 0,1 °C)
4 prise d’essai de PVC
5 cellule de déhydrochloruration (voir les Figures 2 et 3 pour plus de détails)
6 thermomètre (résolution de 0,1 °C)
7 agitateur magnétique (en cas d’utilisation d’un bain d’huile chauffant)
8 solution absorbante
9 électrode(s) de mesure
10 conductimètre
Figure 1 — Représentation générale de l’appareillage

Dimensions en millimètres
Légende
1 ergot
2 17 spires
3 pastille en verre fritté, de 10 mm de diamètre (amovible)
Figure 2 — Cellule A (réutilisable) pour la déhydrochloruration des échantillons de PVC

Dimensions en millimètres
Légende
1 verre consommable
2 tube d’entrée d’azote
3 échantillon
Figure 3 — Cellule B (consommable) pour la déhydrochloruration des échantillons de PVC
6.3 Tube en verre de raccordement, pour la cellule A, raccordant la cellule de déhydrochloruration
à la cellule de mesure et ayant les dimensions indiquées à la Figure 4. Le tube de raccordement est fixé à
la cellule A par deux ressorts fixés aux ergots sur les joints en verre rodé. Le tube doit être pourvu d’une
chemise isolante.
Dimensions en millimètres
Légende
1, 2 ergots
Figure 4 — Tubes en verre pour raccorder la cellule de déhydrochloruration à la cellule de mesure
(à utiliser pour la cellule A)
6.4 Bain chauffant (par exemple bain d’huile)/bloc chauffant (par exemple bloc métallique)
incluant un régulateur thermique d’une capacité d’au moins 10 l. Le bain/bloc doit être capable de
fonctionner su
...