(Main)Copper and copper alloys - Determination of impurities in pure copper - ET AAS method
Copper and copper alloys - Determination of impurities in pure copper - ET AAS method
This European Standard specifies two different electrothermal atomization atomic absorption spectrometric meth-ods (ET AAS) for the determination of silver, arsenic, bismuth, cadmium, cobalt, chromium, iron, manganese, nickel, lead, antimony, selenium, tin, tellurium and zinc in copper (greater than 99,85 %) in the form of unwrought, wrought and cast products.
The standard specifies two methods depending on range of impurity concentrations, see Table 1.
Method B (method of additions) is applicable to products containing impurity elements at concentrations below 1,0 µg/g. This method uses special ET AAS equipment fitted with background correction by means of the Zeemann effect.
Kupfer und Kupferlegierungen - Bestimmung der Verunreinigungen in reinem Kupfer - Elektrothermales Atomabsorptionsspektrometrie-Verfahren (ET-AAS)
Diese Europäische Norm legt zwei verschiedene atomabsorptionsspektrometrische Verfahren mit elektrothermischer
Atomisierung (ET AAS) zur Bestimmung von Silber, Arsen, Bismut, Cadmium, Cobalt, Chrom, Eisen,
Mangan, Nickel, Blei, Antimon, Selen, Zinn, Tellur und Zink in Kupfer (> 99,85 %) fest, die als Gussstücke oder als
plastisch oder nicht plastisch geformte Produkte vorliegen.
Diese Norm legt zwei Verfahren, abhängig von dem Konzentrationsbereich der Verunreinigungen, fest; siehe
Tabelle 1.
Cuivre et alliages de cuivre - Dosage des impuretés dans le cuivre pur - Méthode par spectrométrie d'absorption atomique électrothermique (ET-AAS)
La présente Norme européenne spécifie deux méthodes différentes par spectrométrie d’absorption atomique avec atomisation électrothermique (ET-AAS) pour le dosage de l’argent, de l’arsenic, du bismuth, du cadmium, du cobalt, du chrome, du fer, du manganese, du nickel, du plomb, de l’antimoine, du sélénium, de l’étain, du tellure et du zinc dans le cuivre (pureté supérieure a 99,85 %) sous la forme de produits non corroyés, corroyés et coulés.
La norme spécifie deux méthodes en fonction du domaine de teneurs en impuretés (voir le Tableau 1).
Tableau 1
Domaine de teneurs en µg/g
Élément Méthode A Méthode B
de a (inclus) de a (inclus)
Ag 1 30 0,02 1,0
As 1 20 0,04 1,0
Bi 1 5 0,09 1,0
Cd 1 5 0,001 1,0
Co 1 10 0,04 1,0
Cr 1 10 0,04 1,0
Fe 1 10 0,01 1,0
Mn 1 10 0,02 1,0
Ni 1 30 0,01 1,0
Pb 1 10 0,01 1,0
Sb 1 10 0,2 1,0
Se 1 10 0,05 1,0
Sn 1 10 0,02 1,0
Te 1 10 0,05 1,0
Zn 1 10 0,01 1,0
La méthode B (méthode par ajouts) est applicable aux produits contenant des impuretés a des teneurs inférieures a 1,0 µg/g. Cette méthode utilise un équipement d’absorption électrothermique spécial muni d’un systeme de correction du fond utilisant l’effet Zeemann.
Baker in bakrove zlitine – Določevanje nečistoč v čistem bakru – Metoda ET AAS
General Information
Standards Content (Sample)
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Copper and copper alloys - Determination of impurities in pure copper - ET AAS methodCuivre et alliages de cuivre - Dosage des impuretés dans le cuivre pur - Méthode par spectrométrie d'absorption atomique électrothermique (ET-AAS)Kupfer und Kupferlegierungen - Bestimmung der Verunreinigungen in reinem Kupfer - Elektrothermales Atomabsorptionsspektrometrie-Verfahren (ET-AAS)Ta slovenski standard je istoveten z:EN 14935:2006SIST EN 14935:2006en77.120.30ICS:SLOVENSKI
STANDARDSIST EN 14935:200601-september-2006
EUROPEAN STANDARDNORME EUROPÉENNEEUROPÄISCHE NORMEN 14935June 2006ICS 77.120.30 English VersionCopper and copper alloys - Determination of impurities in purecopper - ET AAS methodCuivre et alliages de cuivre - Dosage des impuretés dans lecuivre pur - Méthode par spectrométrie d'absorptionatomique électrothermiqueKupfer und Kupferlegierungen - Bestimmung derVerunreinigungen in reinem Kupfer - ElektrothermalesAtomabsorptionsspektrometrie-Verfahren (ET-AAS)This European Standard was approved by CEN on 15 May 2006.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the Central Secretariat or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the officialversions.CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMITÉ EUROPÉEN DE NORMALISATIONEUROPÄISCHES KOMITEE FÜR NORMUNGManagement Centre: rue de Stassart, 36
B-1050 Brussels© 2006 CENAll rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 14935:2006: E
EN 14935:2006 (E) 2 Contents Page Foreword.3 1 Scope.4 2 Normative references.4 3 Principle.5 4 Reagents and materials.5 5 Apparatus.9 6 Sampling.9 7 Procedure.10 8 Expression of results.15 9 Precision.16 10 Test report.17 Annex A (informative)
Matrix modifiers.18 Bibliography.19
EN 14935:2006 (E) 3 Foreword This document (EN 14935:2006) has been prepared by Technical Committee CEN/TC 133 “Copper and copper alloys”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by December 2006, and conflicting national standards shall be withdrawn at the latest by December 2006. Within its programme of work, Technical Committee CEN/TC 133 requested CEN/TC 133/WG 10 "Methods of analysis" to prepare the following standard: EN 14935:2006, Copper and copper alloys — Determination of impurities in pure copper — ET AAS method According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following coun-tries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Esto-nia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EN 14935:2006 (E) 4 1 Scope This European Standard specifies two different electrothermal atomization atomic absorption spectrometric meth-ods (ET AAS) for the determination of silver, arsenic, bismuth, cadmium, cobalt, chromium, iron, manganese, nickel, lead, antimony, selenium, tin, tellurium and zinc in copper (greater than 99,85 %) in the form of unwrought, wrought and cast products. The standard specifies two methods depending on range of impurity concentrations, see Table 1. Table 1
Concentration range in µg/g Element Method A Method B
from up to andincluding from up to and including
Ag 1 30 0,02 1,0
As 1 20 0,04 1,0
Bi 1
5 0,09 1,0
Cd 1
5 0,001 1,0
Co 1 10 0,04 1,0
Cr 1 10 0,04 1,0
Fe 1 10 0,01 1,0
Mn 1 10 0,02 1,0
Ni 1 30 0,01 1,0
Pb 1 10 0,01 1,0
Sb 1 10 0,2 1,0
Se 1 10 0,05 1,0
Sn 1 10 0,02 1,0
Te 1 10 0,05 1,0
Zn 1 10 0,01 1,0
Method B (method of additions) is applicable to products containing impurity elements at concentrations below 1,0 µg/g. This method uses special ET AAS equipment fitted with background correction by means of the Zeemann effect. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 1811-1, Copper and copper alloys — Selection and preparation of samples for chemical analysis — Part 1: Sampling of cast unwrought products ISO 1811-2, Copper and copper alloys — Selection and preparation of samples for chemical analysis — Part 2: Sampling of wrought products and castings NOTE Informative references to documents used in the preparation of this standard, and cited at the appropriate places in the text, are listed in the Bibliography.
EN 14935:2006 (E) 5 3 Principle Dissolution of a test portion in nitric acid followed, after suitable dilution, by injection into electrothermal atomization equipment of an atomic absorption spectrometer with a suitable background corrector. Measurement of the absorption of the following lines emitted by the relevant hollow-cathode or electrodeless discharge lamps, see Table 2. Table 2 Element Wave length
nm
Ag 328,1
As 193,7
Bi 223,1
Cd 228,8
Co 240,7
Cr 357,9
Fe 248,3
Mn 279,5
Ni 232,0
Pb 283,3
Sb 217,6
Se 196,0
Sn 224,6
Te 214,3
Zn 213,9
4 Reagents and materials 4.1 General During the analysis, use only reagents of recognized analytical grade and only distilled water or water of equivalent purity. 4.2 Hydrochloric acid, HCl (ρ = 1,19 g/ml). 4.3 Nitric acid, HNO3 (ρ = 1,40 g/ml). 4.4 Nitric acid solution, 1 + 1 Dilute 500 ml of nitric acid (4.3) in 500 ml of water. 4.5 Nitric acid solution, 1 + 3 Dilute 250 ml of nitric acid (4.3) in 750 ml of water. 4.6 Pure sodium hydroxide, NaOH 1 mol/l.
EN 14935:2006 (E) 6 4.7 Sulfuric acid, H2SO4 0,5 mol/l. 4.8 Hydrofluoric acid, HF (ρ = 1,13 g/ml). 4.9 Metal stock solutions, containing 1,000 g/l element. NOTE All these stock solutions have limited life (3 months max.) and should be cold and dark stored. 4.9.1 Silver a) Weigh (1 ± 0,001) g of silver (Ag ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solu-tion (4.4). Heat gently until the silver has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. b) Weigh 1,5748 g of pure silver nitrate (AgNO3) and dissolve it in 100 ml of water previously acidified with 20 ml of nitric acid solution (4.4). Transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.2 Arsenic a) Weigh 0,660 g of pure arsenic trioxide (As2O3) and transfer it into a 250 ml PTFE beaker. Add 50 ml of sodium hydroxide (4.6) and, after complete dissolution, add 150 ml of sulfuric acid (4.7). Transfer the solution quantita-tively into a 500 ml one-mark volumetric flask, dilute to the mark with water and mix well. b) Weigh 4,1650 g of pure sodium arsenate (Na2HAsO4 ⋅ 7H2O) and dissolve it in 200 ml of water. Transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.3 Bismuth Weigh (1 ± 0,001) g of bismuth (Bi ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the bismuth has been completely dissolved and then bring to the boiling point until the ni-trous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.4 Cadmium Weigh (1 ± 0,001) g of cadmium (Cd ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solu-tion (4.4). Heat gently until the cadmium has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.5 Cobalt Weigh (1 ± 0,001) g of cobalt (Co ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the cobalt has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.6 Chromium Weigh (1 ± 0,001) g of chromium (Cr ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solu-tion (4.4). Heat gently until the chromium has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.7 Iron Weigh (1 ± 0,001) g of iron (Fe ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the iron has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well.
EN 14935:2006 (E) 7 4.9.8 Manganese Weigh (1 ± 0,001) g of manganese (Mn ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid so-lution (4.4). Heat gently until the manganese has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.9 Nickel Weigh (1 ± 0,001) g of nickel (Ni ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the nickel has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.10
Lead Weigh (1 ± 0,001) g of lead (Pb ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the lead has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.11
Antimony Weigh (1 ± 0,001) g of antimony (Sb ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 25 ml of hydrochloric acid (4.2) and 50 ml of nitric acid solution (4.4). Heat gently until the antimony has been completely dissolved. Cool to room temperature. Transfer the solution quantitatively into a 1 000 ml of one-mark volumetric flask. Add 100 ml of hydrocloric acid (4.2). Dilute to the mark with water and mix well. 4.9.12
Selenium Weigh (1 ± 0,001) g of selenium (Se ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solu-tion (4.4). Heat gently until the selenium has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.13
Tin Weigh (1 ± 0,001) g of tin (Sn ≥ 99,90 %) and transfer it into a 250 ml PTFE beaker. Add 40 ml of nitric acid solu-tion (4.4) and 2 ml of hydrofluoric acid (4.8). After dissolution, transfer it quantitatively into a 1 000 ml plastics one-mark volumetric flask containing 500 ml of water. Dilute to the mark with water and mix well. 4.9.14
Tellurium Weigh (1 ± 0,001) g of tellurium (Te ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the tellurium has been completely dissolved and then bring to the boiling point until the ni-trous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well. 4.9.15
Zinc Weigh (1 ± 0,001) g of zinc (Zn ≥ 99,90 %) and transfer it into a 250 ml beaker. Add 40 ml of nitric acid solution (4.4). Heat gently until the zinc has been completely dissolved and then bring to the boiling point until the nitrous fumes have been expelled. Cool to room temperature, transfer the solution quantitatively into a 1 000 ml one-mark volumetric flask, dilute to the mark with water and mix well.
EN 14935:2006 (E) 8 4.10 Diluted metal stock solutions 4.10.1 Metal stock solutions 0,05 g/l element Group A: Bismuth and Cadmium Transfer individually 5,00 ml of the metal stock solution (4.9.3 and 4.9.4) into two 100 ml one-mark volumetric flasks. Dilute to the mark with water and mix well. 1 ml of each of these solutions contains 0,05 mg of the corresponding element. Discard these solutions after the normal analysis time (8 h max.). 4.10.2 Metal stock solutions 0,1 g/l element Group B: Arsenic, Cobalt, Chromium, Iron, Manganese, Lead, Antimony, Selenium, Tin, Tellurium and Zinc. Transfer individually 10,00 ml of the metal stock solution (4.9.2, 4.9.5 to 4.9.8 and 4.9.10 to 4.9.15) into twelve 100 ml one-mark volumetric flasks. For tin provide 100 ml plastics one-mark volumetric flasks. Dilute to the mark with water and mix well. 1 ml of each of these solutions contains 0,10 mg of the corresponding element. Discard these solutions after the normal analysis time (8 h max.). 4.10.3 Metal stock solutions 0,2 g/l element Group C: Silver and Nickel. Transfer individually 20,00 ml of the metal stock solution (4.9.1 and 4.9.9) into two 100 ml one-mark volumetric flasks. Dilute to the mark with water and mix well. 1 ml of each of these solutions contains 0,20 mg of the corresponding element. Discard these solutions after the normal analysis time (8 h max.). 4.11 Multi-element standard solution This solution may contain a maximum of four elements. Select up to four elements of interest and transfer 2,50 ml of the metal stock solutions (see 4.10) into the same 100 ml one-mark volumetric flask. If tin is present, use a plastics 100 ml one-mark volumetric flask. Dilute to the mark with water and mix well. 1 ml of this solution contains: Group A: 0,001 25 mg of the corresponding elements; Group B: 0,002 5 mg of the corresponding elements; Group C: 0,005 mg of the corresponding elements. Discard these solutions after the normal analysis time (8 h max.). 4.12 Metal stock solutions 0,02 g/l element 4.12.1 General Transfer individually 5,00 ml of each of the metal stock solutions (4.9.1 to 4.9.15) into 250 ml one-mark volumetric flasks. For tin, use plastics 250 ml one-mark volumetric flasks. Dilute to the mark with water and mix well. 1 ml of each of these solutions contains 0,02 mg of the corresponding element. Discard these solutions after the normal analysis time (8 h max.).
EN 14935:2006 (E) 9 4.12.2 Multi-element standard solution 100 µg/l element This solution may contain a maximum of four elements. Select up to four elements of interest and transfer 10,00 ml of the metal stock solutions (see 4.12.1) into the same 500 ml one-mark volumetric flask. Dilute to the mark with water and mix well. Transfer 25,00 ml of this solution into a 100 ml one-mark volumetric flask, dilute to the mark with water and mix well. If tin is present use
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.