SIST EN 13445-8:2014/A1:2015
(Main)Unfired pressure vessels - Part 8: Additional requirements for pressure vessels of aluminium and aluminium alloys
Unfired pressure vessels - Part 8: Additional requirements for pressure vessels of aluminium and aluminium alloys
This Part 8 of this EN 13445 specifies requirements for unfired pressure vessels and their parts made of aluminium and aluminium alloys in addition to the general requirements for unfired pressure vessels under EN 13445:2009 Parts 1 to 5. This European Standard specifies unfired pressure vessels for loads up to 500 full cycles.
NOTE Cast materials are not included in this version. Details regarding cast materials will be subject to an amendment to or a revision of this European Standard.
Unbefeuerte Druckbehälter - Teil 8: Zusätzliche Anforderungen an Druckbehälter aus Aluminium und Aluminiumlegierungen
Der vorliegende Teil 8 dieser EN 13445 legt zusätzlich zu den allgemeinen Anforderungen an unbefeuerte Druckbehälter nach EN 13445-1:2009 bis EN 13445-5:2009, Anforderungen an aus Aluminium und Aluminium-legierungen hergestellte unbefeuerte Druckbehälter und deren Bauteile fest. Diese Europäische Norm gilt für unbefeuerte Druckbehälter für Druckbelastungen bis zu 500 vollen Lastzyklen.
ANMERKUNG Gusswerkstoffe sind in der vorliegenden Fassung nicht enthalten. Einzelheiten zu Gusswerkstoffen werden in einer Ergänzung bzw. Überarbeitung dieser Europäischen Norm aufgenommen.
Récipients sous pression non soumis à la flamme - Partie 8: Exigences complémentaires pour les récipients sous pression en aluminium et alliages d'aluminium
La présente partie 8 de l’EN 13445 spécifie les exigences relatives aux récipients sous pression non soumis à la flamme et à leurs composants en aluminium et alliages d’aluminium, en complément des exigences générales énoncées dans les parties 1 à 5 de l’EN 13445:2009. La présente Norme européenne concerne les récipients sous pression non soumis à la flamme pouvant aller jusqu’à 500 cycles complets de chargement.
NOTE Les matériaux moulés ne sont pas inclus pour l’instant. Des détails relatifs aux matériaux moulés feront l’objet d’un amendement ou d’une révision de la présente Norme européenne.
Neogrevane tlačne posode - 8. del: Dodatne zahteve za tlačne posode iz aluminija in aluminijevih zlitin
Ta del tega evropskega standarda določa zahteve v skladu z Direktivo EU 97/23/ES o tlačni opremi (PED) za uvedbo tehničnih dobavnih pogojev, in sicer v obliki:
– harmoniziranih evropskih standardov za material;
– evropske odobritve za materiale (EAM);
– posebne ocene materialov (PMA)
za kovinske materiale za tlačno opremo v vseh oblikah proizvodov. Ta standard ne zajema dodajnih materialov za varjenje.
OPOMBA: Ta standard je bil razvit predvsem na podlagi jekla. Kljub temu se lahko uporablja tudi za druge materiale, vendar je treba upoštevati posebne vidike zadevnega materiala
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST EN 13445-8:2014/A1:2015
01-marec-2015
1HRJUHYDQHWODþQHSRVRGHGHO 'RGDWQH]DKWHYH]DWODþQHSRVRGHL]DOXPLQLMD
LQDOXPLQLMHYLK]OLWLQ
Unfired pressure vessels - Part 8: Additional requirements for pressure vessels of
aluminium and aluminium alloys
Unbefeuerte Druckbehälter - Teil 8: Zusätzliche Anforderungen an Druckbehälter aus
Aluminium und Aluminiumlegierungen
Récipients sous pression non soumis à la flamme - Partie 8: Exigences complémentaires
pour les récipients sous pression en aluminium et alliages d'aluminium
Ta slovenski standard je istoveten z: EN 13445-8:2014/A1:2014
ICS:
23.020.30 7ODþQHSRVRGHSOLQVNH Pressure vessels, gas
MHNOHQNH cylinders
SIST EN 13445-8:2014/A1:2015 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN 13445-8:2014/A1:2015
---------------------- Page: 2 ----------------------
SIST EN 13445-8:2014/A1:2015
EUROPEAN STANDARD
EN 13445-8:2014/A1
NORME EUROPÉENNE
EUROPÄISCHE NORM
December 2014
ICS 23.020.30
English Version
Unfired pressure vessels - Part 8: Additional requirements for
pressure vessels of aluminium and aluminium alloys
Récipients sous pression non soumis à la flamme - Partie 8: Unbefeuerte Druckbehälter - Teil 8: Zusätzliche
Exigences complémentaires pour les récipients sous Anforderungen an Druckbehälter aus Aluminium und
pression en aluminium et alliages d'aluminium Aluminiumlegierungen
This amendment A1 modifies the European Standard EN 13445-8:2014; it was approved by CEN on 18 October 2014.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for inclusion of this
amendment into the relevant national standard without any alteration. Up-to-date lists and bibliographical references concerning such
national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.
This amendment exists in three official versions (English, French, German). A version in any other language made by translation under the
responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United
Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2014 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 13445-8:2014/A1:2014 E
worldwide for CEN national Members.
---------------------- Page: 3 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
Contents Page
Foreword .3
1 Modification to Clause 2 .4
2 Modification to subclause 5.1 .5
3 Modification of subclause 5.2 .5
4 Modification of subclause 5.3 .6
5 Modification of subclause 5.4 .6
6 Modification of subclause 5.5 .6
7 Modification of subclause 5.6 .6
8 Modification of subclause 6.2 .7
9 Modification to subclause 6.3 .7
10 Modification to subclause 6.5 .8
11 Modification to subclause 6.6.4 .8
12 New subclause 6.7 Flat ends .8
13 New subclause 6.8 Design by experiment .8
14 New subclause 6.9 Port-hole-extruded tubes .8
15 New subclause 7.3 Tolerances .9
16 Modification to current Sub-Clause 7.3 “Welding procedure specification (WPS)” (to
become subclause 7.4) .9
17 Modification to current subclause 7.8 “Production test, reference criteria” (to become
subclause 7.9) .9
18 Modification to current subclause 7.9 “Extent of testing” (to become subclause 7.10) . 10
19 Modification to current subclause 7.12 “Heat treatment after forming” (to become
subclause 7.13) . 10
20 Modification to current subclause 7.13 “Sampling of formed products” (to become
subclause 7.14) . 11
21 Modification to current subclause 7.14 “Tests” (to become subclause 7.15) . 11
22 Modification to current subclause 7.15 “Post weld heat treatment (PWHT)” (to become
subclause 7.16) . 11
23 Modification to subclause 8.3 . 11
24 Modification to subclause 8.4 . 15
25 Modification to subclause 8.5 . 16
26 New Annex A Allowable design strength values . 16
27 Update of Annex ZA. 22
28 Update of bibliography . 23
2
---------------------- Page: 4 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
Foreword
This document (EN 13445-8:2014/A1:2014) has been prepared by Technical Committee CEN/TC 54 “Unfired
pressure vessels”, the secretariat of which is held by BSI.
This Amendment to the European Standard EN 13445-8:2014 shall be given the status of a national standard,
either by publication of an identical text or by endorsement, at the latest by June 2015, and conflicting national
standards shall be withdrawn at the latest by June 2015.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
This document has been prepared under a mandate given to CEN by the European Commission and the
European Free Trade Association, and supports essential requirements of EU Directive 97/23/EC.
For relationship with EU Directive 97/23/EC, see informative Annex ZA, which is an integral part of this
document.
This document includes the text of the amendment itself. The corrected pages of EN 13445-8 will be
published in July 2015 as Issue 2 of the standard.
This document was submitted to the Formal Vote with the reference EN 13445-8:2009/FprA1.
According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece,
Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom.
3
---------------------- Page: 5 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
1 Modification to Clause 2
Replace normative references with the following:
EN 485-2:2013, Aluminium and aluminium alloys — Sheet, strip and plate — Part 2: Mechanical properties
EN 573-3:2013, Aluminium and aluminium alloys — Chemical composition and form of wrought products —
Part 3: Chemical composition and form of products
EN 586-2:1994, Aluminium and aluminium alloys — Forgings — Part 2: Mechanical properties and additional
property requirements
EN 754-2:2013, Aluminium and aluminium alloys — Cold drawn rod/bar and tube — Part 2: Mechanical
properties
EN 755 (all parts), Aluminium and aluminium alloys — Extruded rod/bar, tube and profiles
EN 764-5:2002, Pressure Equipment — Part 5: Compliance and Inspection Documentation of Materials
EN 10204:2004, Metallic products — Types of inspection documents
EN 12392:2000, Aluminium and aluminium alloys — Wrought products — Special requirements for products
intended for the production of pressure equipment
EN 13445-1:2009, Unfired pressure vessels — Part 1: General
EN 13445-2:2009, Unfired pressure vessels — Part 2: Materials
EN 13445-3:2009, Unfired pressure vessels — Part 3: Design
EN 13445-4:2009, Unfired pressure vessels — Part 4: Fabrication
EN 13445-5:2009, Unfired pressure vessels — Part 5: Inspection and testing
EN ISO 3452-1:2013, Non-destructive testing — Penetrant testing — Part 1: General principles (ISO 3452-
1:2013)
EN ISO 3834-2:2005, Quality requirements for fusion welding of metallic materials — Part 2: Comprehensive
quality requirements (ISO 3834-2:2005)
EN ISO 3834-3:2005, Quality requirements for fusion welding of metallic materials — Part 3: Standard quality
requirements (ISO 3834-3:2005)
EN ISO 4063:2010, Welding and allied processes — Nomenclature of processes and reference numbers (ISO
4063:2009, Corrected version 2010-03-01)
EN ISO 6520-1:2007, Welding and allied processes — Classification of geometric imperfections in metallic
materials — Part 1: Fusion welding (ISO 6520-1:2007)
EN ISO 9606-2:2004, Qualification test of welders — Fusion welding — Part 2: Aluminium and aluminium
alloys (ISO 9606-2:2004)
EN ISO 10042:2005, Welding — Arc-welded joints in aluminium and its alloys — Quality levels for
imperfections (ISO 10042:2005)
4
---------------------- Page: 6 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
EN ISO 11666:2010, Non-destructive testing of welds — Ultrasonic testing — Acceptance levels (ISO
11666:2010)
EN ISO 15614-2:2005, Specification and qualification of welding procedures for metallic materials — Welding
procedure test — Part 2: Arc welding of aluminium and its alloys (ISO 15614-2:2005)
EN ISO 16826:2014, Non-destructive testing — Ultrasonic testing — Examination for discontinuities
perpendicular to the surface (ISO 16826:2012)
EN ISO 17635:2010, Non-destructive testing of welds — General rules for metallic materials (ISO
17635:2010)
EN ISO 17636-1:2013, Non-destructive testing of welds — Radiographic testing — Part 1: X- and gamma-ray
techniques with film (ISO 17636-1:2013)
EN ISO 17636-2:2013, Non-destructive testing of welds — Radiographic testing — Part 2: X- and gamma-ray
techniques with digital detectors (ISO 17636-2:2013)
EN ISO 17637:2011, Non-destructive testing of welds — Visual testing of fusion-welded joints (ISO
17637:2003)
EN ISO 17640:2010, Non-destructive testing of welds — Ultrasonic testing — Techniques, testing levels, and
assessment (ISO 17640:2010)
EN ISO 23277:2009, Non-destructive testing of welds — Penetrant testing of welds — Acceptance levels (ISO
23277:2006)
CR ISO/TR 15608:2013, Welding — Guidelines for a metallic materials grouping system
(ISO/TR 15608:2013)
ISO 857-1:1998, Welding and allied processes — Vocabulary — Part 1: Metal welding processes
2 Modification to subclause 5.1
Add before the first paragraph:
Materials for pressure-bearing parts compliant with the requirements of this European Standard shall be
accompanied by inspection documents in accordance with EN 10204:2004.
The type of inspection document shall be in accordance with EN 764-5:2002 and include a declaration of
compliance to the material specification.
3 Modification of subclause 5.2
Replace the last paragraph, starting with “Aluminium and aluminium alloys.” until “.defined by the material
specification.” by the following:
Aluminium and aluminium alloys used for parts of pressure vessels that are not subject to cold forming (e.g.
straight flanges and nozzles) shall have a specified minimum elongation after fracture of ≥ 10 % in the
longitudinal or transverse direction as defined by the material specification, measured on a gauge length as
defined in eq. (5.2-1).
5
---------------------- Page: 7 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
4 Modification of subclause 5.3
Replace the complete text of subclause 5.3 by the following:
EN 13445-2:2009, Annex B, is not applicable. All materials of Table 5.6-1 are suitable for any minimum metal
temperature without impact testing.
NOTE See also EN 1252-1 and EN 12392:2000, 8.4.
5 Modification of subclause 5.4
In the NOTE replace 4.2.1.2 of EN 13445-2:2009 by EN 13445-2:2009, 4.2.1.2.
6 Modification of subclause 5.5
Replace the text by the following:
The chemical composition shall be in accordance with the material specification.
It is recommended that the material to be used for welded components be produced from rolling or extrusion
ingots with hydrogen level no greater than 0,2 ml per 100 g aluminium, measured on liquid metal during
casting (see EN 12392:2000, 5.1.3).
EN 12392:2000, 4.1, recommends a maximum lead content not exceeding 150 μg/g.
7 Modification of subclause 5.6
Replace the text of the first and second paragraph by the following:
Annex A of EN 13445-2:2009 is not applicable for pressure vessels of aluminium and its alloys. The allowable
materials for the construction of aluminium alloy pressure vessels shall be according to Table 5.6-1 below.
Any product form available in EN 12392:2000 for a material in Table 5.6-1 at an acceptable temper is
acceptable for construction to this European Standard, as long as the requirements of 5.2 and 5.5 are fulfilled.
Other materials not defined here may be used by agreement by the parties concerned (see EN 13445-2:2009,
4.1.4) if they meet the requirements of 5.2 and 5.5 and a particular material appraisal is produced (see
EN 764-4:2002).
Change the heading of Table 5.6.1 by the following:
Table 5.6-1 — Grouping system based on CR ISO/TR 15608:2013 and allowable materials of
construction based on EN 12392:2000 using the EN AW numbers according to EN 573-3:2013
Delete the NOTE before Table 5.6-1.
6
---------------------- Page: 8 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
8 Modification of subclause 6.2
Replace the complete text of subclause 6.2 with the following:
NOTE 1 Also see EN 13445-2:2009, 4.2.2.
nd
EN 13445-2:2009, 4.2.2.1, 2 paragraph, is not applicable for aluminium and its alloys.
Design strength values are given in Tables A.2 to A.5 in Annex A. Design temperatures that exceed the
respective temperature limit in Annex A are not permitted.
For materials of group 22.4 temperatures above 80 °C may result in grain boundary precipitation of Al -Mg .
3 2
These materials may be used at temperatures above 80 °C up to 200 °C only for non-corrosive service.
NOTE 2 For further material properties see EN 12392:2000.
For welded parts and heat treated parts after forming only the values equivalent to the O temper shall be used
for design when 6 000 series flanges, etc. are welded. These values are not quoted in EN 12392:2000 and so
the tabulated values for f shown in Table 6.3-2 shall be used for design. The weld area shall be based on the
O temper but the flange strength away from the weld (2t) may be based on the actual temper (T4 or T6).
For aluminium and aluminium alloys values of 0,2 % proof stress (or 1 % proof stress for material
group 21-1 000 series aluminium) for temperatures above 20 °C shall be established by linear interpolation
between two adjacent values in Annex A or in EN 12392:2000 except that for alloys 5083 and 5086 the
respective value at 50 °C may be used for 65 °C.
For material of group 22.4: For short periods, higher temperatures (e.g. when defrosting refrigerating plant) up
to 150 °C are permissible provided that the pressure is reduced to half the working pressure for a period up to
8 h and to atmospheric pressure for a period up to 24 h.
9 Modification to subclause 6.3
rd st
In Table 6.3-1, 3 column, 1 line, replace [R / 1,05] by [R / 1,05] (add a space in the index between
p1,0,20 p1,0, 20
1,0 and 20).
In the heading of Table 6.3-2 replace Aluminium by aluminium (lower case letter).
7
---------------------- Page: 9 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
10 Modification to subclause 6.5
Replace the first paragraph by the following:
Fatigue design for over 500 full equivalent pressure cycles is not covered by this Part 8 for aluminium and
aluminium alloy pressure vessels. For the determination of 500 full equivalent pressure cycles see EN 13445-
3:2009, 5.4.2
11 Modification to subclause 6.6.4
Replace the second sentence by the following:
Permanent backing strips are permitted for circumferential seams and for shell or head closure plates (see
EN 13445-3:2009, Table A, reference E 7) only under the following conditions:
12 New subclause 6.7 Flat ends
Add a new subclause 6.7:
6.7 Flat ends
The requirements of Clause 10 of EN 13445-3:2009 shall apply with the following additions/exclusions:
— Joint types E 5 and E 14 in Table A-3 of EN 13445-3:2009:
Only the first term of equation (10.4-10) shall be considered.
— Joint types E 6, E 7, and E 15 in Table A-3 of EN 13445-3:2009:
For values of C and C higher than 0,45 in equation (10.4-10) the value of 0,45 may be taken.
1 2
— Joint types E 10, E 11, E 17, and E 19 in Table A-3 of EN 13445-3:2009:
For values of C and C higher than 0,5 in equation (10.4-10) the value of 0,5 may be taken.
1 2
13 New subclause 6.8 Design by experiment
Add a new subclause 6.8:
6.8 Design by experiment
When a plate-and-fin structure is to be designed by experimental method, the procedure shall be based on the
principles laid down in Annex T of EN 13445-3:2009, however, with the following modifications:
— A test piece shall be subject to a pressure load until the required pressure P is reached or the test piece
B
is destroyed.
— PS shall be determined by P , divided by 4.
B
14 New subclause 6.9 Port-hole-extruded tubes
Add a new subclause 6.9:
6.9 Port-hole-extruded tubes
Port-hole-extruded tubes in accordance with the EN 755-series may be used up to and including DN 25,
provided that a joint efficiency of 0,7 is applied. When these tubes are subject to a combined pressure-leak-
test for the entire length the joint efficiency may be set to a factor of 1. If this test is carried out:
8
---------------------- Page: 10 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
by the tube manufacturer, the test pressure shall be
e
n
P = ⋅0,95⋅R (6.9-1)
T px
D
e
by the pressure vessel manufacturer, the test pressure shall be
P =1,43⋅PS (6.9-2)
T
The combined pressure-leak test for achieving a joint efficiency factor of 1 is to be carried out before
integration in the piping system either using helium or a gas mixture containing helium, depending on the
application. It does not replace the pressure test as specified in Clauses 8.6 and 8.7.
15 New subclause 7.3 Tolerances
Add a new subclause 7.3 and re-number the current paragraphs 7.3 to 7.15 to become 7.4 to 7.16:
7.3 Tolerances
The requirements of EN 13445-4:2009, 5.4, shall apply with the following modification:
For the dished end tolerances of the circumference C the following limit deviations are applicable:
for outer diameters D ≤ 300 mm: +/- 4 mm;
e
for outer diameters D with 300 mm < D ≤ 4000 mm: +/- 10 mm;
e e
for outer diameters D > 4000 mm the tolerance shall be +/- 10 mm or more if agreed before
e
fabrication commences.
16 Modification to current Sub-Clause 7.3 “Welding procedure specification (WPS)”
(to become subclause 7.4)
Replace EN ISO 4063:2000 by EN ISO 4063:2010.
17 Modification to current subclause 7.8 “Production test, reference criteria” (to
become subclause 7.9)
Replace the complete text by the following:
The requirements in 8.2 of EN 13445-4:2009 are not applicable.
Production test plates are required for pressure vessels manufactured according to this European Standard in
the case of a joint coefficient z of 0,85 < z ≤ 1,0. If a joint coefficient of 0,85 or less is specified by the designer
no production test plates are required.
Requirements for impact testing are not relevant to aluminium materials.
9
---------------------- Page: 11 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
a) There is a strict relationship between the WPS and the mechanical properties obtained in the procedure
approval test for aluminium materials 21, 22.1, 22.3 and 22.4. Because of the tolerance of these
aforementioned aluminium materials to weld procedural variables, production tests are not required if all
of the following conditions are met:
— The quality requirements for welding according to EN ISO 3834-2:2005 or EN ISO 3834-3:2005 are
fulfilled.
— The welding process is fully mechanised (see ISO 857-1) ensuring that the welding procedure is
applied consistently.
— There is no requirement in the WPS for preheating or post weld heat treatment (PWHT).
≤ 30 mm.
— The wall thickness e
n
b) Otherwise, for vessels made of aluminium permitted by Clause 5 of this standard, the following shall
apply:
1) for longitudinal welds, one test plate per vessel in the case of joint coefficient 1,0;
2) one test plate per 200 m of longitudinal welds in hemispherical heads in the case of joint coefficient
1,0;
3) one test plate per year where the circumferential welds are welded to a procedure involving joggle
joints or permanent backing strips.
After 10 consecutive test plates have successfully passed the tests, testing may be reduced to the following:
4) one test plate per 200 m of longitudinal welds in the case of joint coefficient 1,0;
5) one test plate per 1500 m of longitudinal welds in hemispherical heads in the case of joint coefficient
1,0;
6) one test plate per year where the circumferential welds are welded to a procedure involving joggle
joints or permanent backing strips.
The testing of the production test plate shall consider the parameters for the post-weld heat treatment(s) of
the pressure vessel.
18 Modification to current subclause 7.9 “Extent of testing” (to become subclause
7.10)
In the first sentence replace Table 7.9-1 by Table 7.10-1.
Re-number the heading of the Table from 7.9-1 to 7.10-1.
19 Modification to current subclause 7.12 “Heat treatment after forming” (to become
subclause 7.13)
In 7.12.1 (to become 7.13.1) replace Table 7.12-1 by Table 7.13-1 and re-number the heading of the Table
from 7.12-1 to 7.13-1.
In 7.12.2 (to become 7.13.2) replace Table 7.12-2 by Table 7.13-2 and re-number the heading of the Table
from 7.12-2 to 7.13-2.
10
---------------------- Page: 12 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
In 7.12.3 (to become 7.13.3) replace Table 7.12-3 by Table 7.13-3 and re-number the heading of the Table
from 7.12-3 to 7.13-3.
20 Modification to current subclause 7.13 “Sampling of formed products” (to
become subclause 7.14)
In 7.13.1 (to become 7.14.1) replace the complete text by the following:
The requirements in 9.5.1 of EN 13445-4:2009 are not applicable for pressure vessels of aluminium and its
alloys.
No mechanical tests with respect to forming are required for
— cold-formed plates and tubes for which heat treatment is not required by Table 7.13-1 and Table 7.13-2;
— cold-formed and heat-treated cylindrical and conical shell sections.
21 Modification to current subclause 7.14 “Tests” (to become subclause 7.15)
In 7.14.1 (to become 7.15.1):
In the second sentence replace 7.13.2 by 7.14.2.
In 7.14.2 (to become 7.15.2):
In the NOTE replace 7.3 by 7.4.
22 Modification to current subclause 7.15 “Post weld heat treatment (PWHT)” (to
become subclause 7.16)
Under item c) replace Table 7.12-3 by Table 7.13-3.
23 Modification to subclause 8.3
Modify Table 8.3-1 as follows:
> 150 mm or e > 16 mm” by “d > 150 mm and e > 16 mm”.
In Line 3a replace “d
i i
> 150 mm or e > 16 mm” by “d > 150 mm and e > 16 mm”.
In Line 3b replace “d
i i
< 150 mm and e < 16 mm” by “d < 150 mm or e < 16 mm”.
In Line 4 replace “d
i i
In Line 8 in columns 1, 2 and 3 replace each NA by NP.
In Line 10 in columns 1 and 2 replace each NA by NP.
In Line 11 in columns 1 and 2 replace each NA by NP.
In Line 11 in column 3 replace 0 by NA.
In Line 13 & 14 in columns 1 and 2 replace each NA by NP.
≤ 200 mm and e ≤ 25 mm” by “d ≤ 200 mm or e ≤ 25 mm”.
In Line 16 replace “d
i i
11
---------------------- Page: 13 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
In Line 21 delete the reference to Footnote f after Permanent attachments.
In the list of footnotes to Table 8.3-1:
In the explanation to Footnote e replace see 6.6.2b by 6.6.2.5 b).
In the explanation to Footnote f replace No RT or UT for weld throat thickness ≤ 16 mm. by (deleted).
In the explanation to Footnote i replace 6.6.2 by 6.6.2.4.
In the explanation to Footnote j replace
(i.e. RT & UT, & PT); also see Table 6.6.2-1 of EN 13445-5:2009 for other circumstances for the use of both
techniques.
by
(i.e. volumetric testing (RT or UT) and surface testing (PT)).
Replace the explanation to Footnote n by the following:
NA means “testing not applicable”, NP means “type of joint not permitted”.
In the explanation to Footnote p add after the first sentence:
The NDT requirements shall, however, not be less than those specified in this table.
The modified Table 8.3-1 would thus appear as depicted below:
12
---------------------- Page: 14 ----------------------
SIST EN 13445-8:2014/A1:2015
EN 13445-8:2014/A1:2014 (E)
Table 8.3-1 — Extent of non-destructive testing
Testing group 1 2 3 4
21, 22.1
Parent
21, 22.1 21, 22.1
21, 22.1 to 22.4
materials to 22.4 to 22.4,
to 22.4 (except
o
l m n
except 23.1 and 23.1
EN AW 5454)
a b
Type of weld Testing Extent Extent Extent Extent
p p p
Full 1 Longitudinal joint RT or UT 100 % (100–10) % 10 % 0
penetration
PT 0 0 0 0
butt weld
c
2a Circumferential joint on a shell RT or UT 25 % (25–10) % 10% 0
PT 0 0 0 0
2b Circumferential joint on a shell RT or UT 25 % (25–10) % 10 % 0
k
with backing strip
PT 0 0 0 0
k
2c Circumferential joggle joint RT or UT 25 % (25–10) % 10 % 0
PT 0 0 0 0
c
3a Circumferential joint on a nozzle RT or UT 25% (25–10)% 10% 0
with d > 150 mm and e >
i
PT 0 0 0 0
16 mm
3b Circumferential joint on a nozzle RT or UT 25 % (25–10) % 10 % 0
with d > 150 mm and e >
i
PT 0 0 0 0
k
16 mm with backing strip
4 Circumferential joint on a nozzle RT or UT 0 0 0 0
d
with d < 150 mm or e < 16 mm
i
PT 50 % (50–10) % 10 % 0
p p
5 All welds in shells, heads and in RT or UT 100 % 100 % 10 % 0
hemispherical heads to shells
PT 0 0 0 0
p
6 Assembly of a conical shell with RT or UT 25 % (25–10) % 10 % 0
a cylindrical shell angle ≤ 30°
PT 0 0 0 0
7 Assembly of a conical shell with RT or UT 100 % (100–25) % 10 % 10 %
d
a cylindrical shell angle > 30°
PT 0 0 10% 0
p
Fillet weld, 8 Circumferential lapped joint RT or UT NP NP NP 0
k
lapped joints head to shell
PT NP NP NP 0
p
Assembly of 9 With full penetration RT or UT 25 % (25–10) % 10 % 0
p p
a flat head or
PT 0 0 0 0
tube sheet,
10 With partial penetration, if a RT or UT NP NP 10 % 0
with a
> 16 mm (as defined in
PT NP NP 0 0
cylin
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.