ISO 3785:2023
(Main)Metallic materials — Designation of test specimen axes in relation to product texture
Metallic materials — Designation of test specimen axes in relation to product texture
This document specifies a method for designating test specimen axes in relation to product texture by means of an X-Y-Z orthogonal coordinate system. This document applies equally to unnotched and notched (or precracked) test specimens. This document is intended only for metallic materials with uniform texture that can be unambiguously determined. Test specimen orientation is decided before specimen machining, identified in accordance with the designation system specified in this document, and recorded.
Matériaux métalliques — Désignation des axes des éprouvettes en relation avec la texture du produit
Le présent document spécifie une méthode pour désigner les axes des éprouvettes en relation avec la texture du produit, au moyen d'un système orthogonal de coordonnées X-Y-Z. Le présent document s'applique aussi bien aux éprouvettes sans entaille qu'aux éprouvettes entaillées (ou préfissurées). Le présent document est destiné seulement aux matériaux métalliques de texture uniforme qui peut être déterminée sans ambiguïté. L'orientation de l'éprouvette est décidée avant usinage de l'éprouvette, identifiée conformément au système de désignation spécifié dans le présent document, et enregistrée.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 3785
Third edition
2023-05
Metallic materials — Designation
of test specimen axes in relation to
product texture
Matériaux métalliques — Désignation des axes des éprouvettes en
relation avec la texture du produit
Reference number
ISO 3785:2023(E)
© ISO 2023
---------------------- Page: 1 ----------------------
ISO 3785:2023(E)
COPYRIGHT PROTECTED DOCUMENT
© ISO 2023
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
© ISO 2023 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 3785:2023(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Designation system . 1
4.1 General . 1
4.2 Exception — not aligned . 1
4.3 Exception — no grain flow . 2
5 Designation of unnotched specimens . 2
5.1 General . 2
5.2 Sheet, plate, bar (flat rolled products). 2
5.2.1 Aligned, grain flow different in all three orthogonal directions . 2
5.2.2 Not aligned, grain flow different in all three orthogonal directions . 2
5.2.3 Aligned, equal cross-sectional grain flow . 2
5.2.4 Not aligned, equal cross-sectional grain flow . 2
5.3 Cylinders and thick-walled tubes. 3
5.4 Thin-walled tubes, helical grain flow . 3
5.5 Castings . 3
6 Designation of notched (or precracked) specimens . 3
6.1 General . 3
6.2 Aligned . 3
6.3 Not aligned . 3
6.4 No grain flow . 3
6.5 Welds . 3
6.6 Additive manufacturing . 4
7 Application of designation system in material specification . 4
7.1 General . 4
7.2 Non-uniform grain flow. 4
7.3 Specifications . 4
7.4 Comparisons . 4
Annex A (informative) Influence of mechanical working on material structure and
properties . 8
Bibliography . 9
iii
© ISO 2023 – All rights reserved
---------------------- Page: 3 ----------------------
ISO 3785:2023(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals,
Subcommittee SC 4, Fatigue, fracture and toughness testing, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 459/SC 1, Test methods for steel
(other than chemical analysis), in accordance with the Agreement on technical cooperation between ISO
and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 3785:2006), which has been technically
revised.
The main changes are as follows:
— a reference to Annex A was added in the Introduction;
— in 6.5 a reference to ISO 15653 was added;
— a new Subclause 6.6 (Additive manufacturing) was added.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
© ISO 2023 – All rights reserved
---------------------- Page: 4 ----------------------
ISO 3785:2023(E)
Introduction
The measured mechanical properties of a metallic product, especially those characterizing ductility
and toughness, such as elongation, reduction of area, fracture toughness and impact resistance, are
dependent on the test specimen location within the product and orientation with respect to the
product's principal directions of metal working, grain flow or otherwise-produced texture. This
document specifies a method for designating specimen orientation in relation to product texture.
Additional information on the influence of mechanical working on material structure and properties is
provided in Annex A.
v
© ISO 2023 – All rights reserved
---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 3785:2023(E)
Metallic materials — Designation of test specimen axes in
relation to product texture
1 Scope
This document specifies a method for designating test specimen axes in relation to product texture by
means of an X-Y-Z orthogonal coordinate system.
This document applies equally to unnotched and notched (or precracked) test specimens.
This document is intended only for metallic materials with uniform texture that can be unambiguously
determined.
Test specimen orientation is decided before specimen machining, identified in accordance with the
designation system specified in this document, and recorded.
2 Normative references
There are no normative references in this document.
3 Terms and definitions
No terms and definitions are listed in this document.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Designation system
4.1 General
The method for relating specimen axes to the characteristic directions of the pr
...
NORME ISO
INTERNATIONALE 3785
Troisième édition
2023-05
Matériaux métalliques — Désignation
des axes des éprouvettes en relation
avec la texture du produit
Metallic materials — Designation of test specimen axes in relation to
product texture
Numéro de référence
ISO 3785:2023(F)
© ISO 2023
---------------------- Page: 1 ----------------------
ISO 3785:2023(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2023
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
© ISO 2023 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 3785:2023(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application .1
2 Références normatives .1
3 Termes et définitions . 1
4 Système de désignation . 1
4.1 Généralités . 1
4.2 Exception — Désaxé . 1
4.3 Exception — Absence de fibrage . 2
5 Désignation des éprouvettes sans entaille . 2
5.1 Généralités . 2
5.2 Tôle, plaque, barre (produits plats laminés) . 2
5.2.1 Axé, fibrage différent dans les trois directions orthogonales . 2
5.2.2 Désaxé, fibrage différent dans les trois directions orthogonales . 2
5.2.3 Axé, fibrage équiaxe . 2
5.2.4 Désaxé, fibrage équiaxe . 2
5.3 Cylindres et tubes épais . 3
5.4 Tubes à paroi mince, fibrage hélicoïdal. 3
5.5 Pièces moulées . . 3
6 Désignation des éprouvettes entaillées (ou préfissurées) . 3
6.1 Généralités . 3
6.2 Axé . 3
6.3 Désaxé . 3
6.4 Absence de fibrage . 4
6.5 Soudures . . 4
6.6 Fabrication additive . 4
7 Application du système de désignation dans les spécifications de matériaux .4
7.1 Généralités . 4
7.2 Fibrage non uniforme . 4
7.3 Spécifications . 4
7.4 Comparaisons . 4
Annexe A (informative) Influence d'une mise en forme mécanique sur la structure et les
caractéristiques des matériaux .8
Bibliographie . 9
iii
© ISO 2023 – Tous droits réservés
---------------------- Page: 3 ----------------------
ISO 3785:2023(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document
a été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2
(voir www.iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion
de l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir: www.iso.org/iso/fr/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 164, Essais mécaniques des métaux,
sous-comité SC 4, Essais de fatigue, de fracture et de ténacité, en collaboration avec le Comité européen
de normalisation (CEN) comité technique CEN/TC 459/SC 1, Méthodes d'essai des aciers (autres que
l'analyse chimique), conformément à l'accord de coopération technique entre l'ISO et le CEN (Accord de
Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 3785:2006), qui a fait l'objet d'une
révision technique.
Les principaux changements sont les suivants:
— une référence à l'Annexe A a été ajoutée dans l'introduction;
— en 6.5, une référence à l'ISO 15653 a été ajoutée;
— un nouveau paragraphe 6.6 (Fabrication additive) a été ajouté.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes
se trouve à l’adresse www.iso.org/fr/members.html.
iv
© ISO 2023 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO 3785:2023(F)
Introduction
Les caractéristiques mécaniques mesurées d'un produit métallique, particulièrement celles
caractérisant la ductilité et la ténacité, telles que l'allongement, la striction, la ténacité à la rupture
et la résistance au choc, dépendent de la position des éprouvettes dans le produit et de l'orientation
des éprouvettes par rapport aux directions principales de mise en forme du métal, du fibrage ou
d'autres textures formées au sein du produit. Le présent document spécifie une méthode pour désigner
l'orientation des éprouvettes en relation avec la texture du produit.
Des informations supplémentaires sur l'influence du travail mécanique sur la structure et les propriétés
des matériaux sont fournies à l'Annexe A.
v
© ISO 2023 – Tous droits réservés
---------------------- Page: 5 ----------------------
NORME INTERNATIONALE ISO 3785:2023(F)
Matériaux métalliques — Désignation des axes des
éprouvettes en relation avec la texture du produit
1 Domaine d'application
Le présent document spécifie une méthode pour désigner les axes des éprouvettes en relation avec la
texture du produit, au moyen d'un système orthogonal de coordonnées X-Y-Z.
Le présent document s'applique aussi bien aux éprouvettes sans entaille qu'aux éprouvettes entaillées
(ou préfissurées).
Le présent document est destiné seulement aux matériaux métalliques de texture uniforme qui peut
être déterminée sans ambiguïté.
L'orientation de l'éprouvette est décidée avant usinage de l'éprouvette, identifiée conformément au
système de désignation spécifié dans le présent document, et enregistrée.
2 Références normatives
Le présent document ne contient aucune référence normative.
3 Termes et définitions
Aucun terme n’est défini dans le présent document.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
4 Système de désignation
4.1 Généralités
La méthode pour relier les axes des éprouvettes aux directions caractéristiques du produit utilise un
système orthogonal de coordonnées X-Y-Z pour les métaux mis en forme, pour lequel:
— la lettre X dénote toujours la direction de déformation principale (fibrage maximal dans le produit);
— la lettre Y dénote la direction de moindre déformation;
— la lettre Z dénote la direction perpendiculaire au plan X-Y.
4.2 Exception — Désaxé
Lorsque la direction de l'éprouvette ne coïncide pas avec les directions de fibrage caractéristiques du
produit, deux lettres sont utilisées, comme décrit pour les éprouvettes sans entaille en 5.2.2 et en 5.2.4
et pour les éprouvettes entaillées en 6.3.
1
© ISO 2023 – Tous droits réservés
---------------------- Page: 6 ----------------------
ISO 3785:2023(F)
4.3 Exception — Absence de fibrage
Lorsqu'il n'y a aucune direction de fibrage, comme
...
ISO/DIS FDIS 3785:
ISO/TC 164/SC 4
Secretariat: ANSI
Date: 2022(E)-12-19
2022-09-27
Third edition
Metallic materials — Designation of test specimen axes in relation
to product texture
Matériaux métalliques — Désignation des axes des éprouvettes en relation avec la texture du produit
FDIS stage
---------------------- Page: 1 ----------------------
ISO/DIS FDIS 3785:2022(E)
© ISO 2022
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this
publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical,
including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can
be requested from either ISO at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
Fax: +41 22 749 09 47
EmailE-mail: copyright@iso.org
Website: www.iso.orgwww.iso.org
Published in Switzerland
ii © ISO 2022 – All rights reserved
ii © ISO 2022 – All rights reserved
---------------------- Page: 2 ----------------------
ISO/DIS FDIS 3785:2022(E)
Contents Page
Foreword . v
Introduction . vi
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Designation system . 1
4.1 General . 1
4.2 Exception — not aligned . 1
4.3 Exception — no grain flow . 1
5 Designation of unnotched specimens . 2
5.1 General . 2
5.2 Sheet, plate, bar (flat rolled products) . 2
5.2.1 Aligned, grain flow different in all three orthogonal directions . 2
5.2.2 Not aligned, grain flow different in all three orthogonal directions . 2
5.2.3 Aligned, equal cross-sectional grain flow . 2
5.2.4 Not aligned, equal cross-sectional grain flow . 2
5.3 Cylinders and thick-walled tubes . 2
5.4 Thin-walled tubes, helical grain flow . 2
5.5 Castings . 2
6 Designation of notched (or precracked) specimens . 3
6.1 General . 3
6.2 Aligned . 3
6.3 Not aligned . 3
6.4 No grain flow . 3
6.5 Welds . 3
6.6 Additive manufacturing. 3
7 Application of designation system in material specification . 3
7.1 General . 3
7.2 Non-uniform grain flow . 4
7.3 Specifications . 4
7.4 Comparisons . 4
Annex A (informative) Influence of mechanical working on material structure and properties . 8
Bibliography . 9
Foreword iii
Introduction iv
1 Scope 1
2 Designation system 1
3 Designation of unnotched specimens 2
© ISO 2022 – All rights reserved iii
© ISO 2022 – All rights reserved iii
---------------------- Page: 3 ----------------------
ISO/DIS FDIS 3785:2022(E)
4 Designation of notched (or precracked) specimens 3
5 Application of designation system in material specification 4
Annex A (informative) Influence of mechanical working on material structure and properties 7
iv © ISO 2022 – All rights reserved
iv © ISO 2022 – All rights reserved
---------------------- Page: 4 ----------------------
ISO/DIS FDIS 3785:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directiveswww.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any
patent rights identified during the development of the document will be in the Introduction and/or on
the ISO list of patent declarations received (see www.iso.org/patentswww.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to the World
Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.htmlwww.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals,
Subcommittee SC 4, Fatigue, fracture and toughness testing, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC CEN/TC 459/SC 1, ECISS - European
Committee for Iron and Steel Standardization, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the first edition (ISO 3785:2006), which has been technically
revised.
The main changes are as follows:
— — A reference to Annex AAnnex A was added in the Introduction.;
— References to ISO 15653 and ISO/ASTM 52921 were moved from Clause 2 (Normative
references) to the Bibliography.
— A new Clause 3 (Terms and definition) was added.
— — In Clause 6.5 (Welds),6.5 a reference to ISO 15653 was added.;
— — A new Clause 6.6subclause 6.6 (Additive manufacturing) was added.
— Bibliography was added.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
Field Code Changed
© ISO 2022 – All rights reserved v
© ISO 2022 – All rights reserved v
---------------------- Page: 5 ----------------------
ISO/DIS FDIS 3785:2022(E)
Introduction
The measured mechanical properties of a metallic product, especially those characterizing ductility and
toughness, such as elongation, reduction of area, fracture toughness and impact resistance, are dependent
on the test specimen location within the product and orientation with respect to the product's principal
directions of metal working, grain flow or otherwise-produced texture. This International Standard
specifies a method for designating specimen orientation in relation to product texture.
Additional information on the influence of mechanical working on material structure and properties is
provided in Annex A.Annex A.
vi © ISO 2022 – All rights reserved
vi © ISO 2022 – All rights reserved
---------------------- Page: 6 ----------------------
DRAFT INTERNATIONAL STANDARD ISO/DIS 3785:2022(E)
Metallic materials — Designation of test specimen axes in relation
to product texture
1 Scope
This document specifies a method for designating test specimen axes in relation to product texture by
means of an X-Y-Z orthogonal coordinate system.
This document applies equally to unnotched and notched (or precracked) test specimens.
This document is intended only for metallic materials with uniform texture that can be unambiguously
determined.
Test specimen orientation is decided before specimen machining, identified in accordance with the
designation system specified in this document, and recorded.
2 Normative references
There are no normative references in this document.
3 Terms and definitions
No terms and definitions are listed in this document. For additive manufacturing, the terms and
definitions given in ISO/ASTM 52921-13(2019) apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— — ISO Online browsing platform: available at https://www.iso.org/obphttps://www.iso.org/obp
— — IEC Electropedia: available at https://www.electropedia.org/https://www.electropedia.org/
4 Designation system
4.1 General
The method for relating specimen axes to the characteristic directions of the product makes use of an X-
Y-Z orthogonal coordinate system for wrought metals:
— — the letter X always denotes the direction of principal deformation
...
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 3785
ISO/TC 164/SC 4
Metallic materials — Designation
Secretariat: ANSI
of test specimen axes in relation to
Voting begins on:
2023-01-04 product texture
Voting terminates on:
Matériaux métalliques — Désignation des axes des éprouvettes en
2023-03-01
relation avec la texture du produit
ISO/CEN PARALLEL PROCESSING
RECIPIENTS OF THIS DRAFT ARE INVITED TO
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
Reference number
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/FDIS 3785:2023(E)
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN-
DARDS TO WHICH REFERENCE MAY BE MADE IN
NATIONAL REGULATIONS. © ISO 2023
---------------------- Page: 1 ----------------------
ISO/FDIS 3785:2023(E)
FINAL
INTERNATIONAL ISO/FDIS
DRAFT
STANDARD 3785
ISO/TC 164/SC 4
Metallic materials — Designation
Secretariat: ANSI
of test specimen axes in relation to
Voting begins on:
product texture
Voting terminates on:
Matériaux métalliques — Désignation des axes des éprouvettes en
relation avec la texture du produit
COPYRIGHT PROTECTED DOCUMENT
© ISO 2023
ISO/CEN PARALLEL PROCESSING
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
RECIPIENTS OF THIS DRAFT ARE INVITED TO
ISO copyright office
SUBMIT, WITH THEIR COMMENTS, NOTIFICATION
OF ANY RELEVANT PATENT RIGHTS OF WHICH
CP 401 • Ch. de Blandonnet 8
THEY ARE AWARE AND TO PROVIDE SUPPOR TING
CH-1214 Vernier, Geneva
DOCUMENTATION.
Phone: +41 22 749 01 11
IN ADDITION TO THEIR EVALUATION AS
Reference number
Email: copyright@iso.org
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/FDIS 3785:2022(E)
Website: www.iso.org
LOGICAL, COMMERCIAL AND USER PURPOSES,
DRAFT INTERNATIONAL STANDARDS MAY ON
Published in Switzerland
OCCASION HAVE TO BE CONSIDERED IN THE
LIGHT OF THEIR POTENTIAL TO BECOME STAN
DARDS TO WHICH REFERENCE MAY BE MADE IN
ii
© ISO 2023 – All rights reserved
NATIONAL REGULATIONS. © ISO 2022
---------------------- Page: 2 ----------------------
ISO/FDIS 3785:2022(E)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Designation system . 1
4.1 General . 1
4.2 Exception — not aligned . 1
4.3 Exception — no grain flow . 2
5 Designation of unnotched specimens . 2
5.1 General . 2
5.2 Sheet, plate, bar (flat rolled products). 2
5.2.1 Aligned, grain flow different in all three orthogonal directions . 2
5.2.2 Not aligned, grain flow different in all three orthogonal directions . 2
5.2.3 Aligned, equal cross-sectional grain flow . 2
5.2.4 Not aligned, equal cross-sectional grain flow . 2
5.3 Cylinders and thick-walled tubes. 3
5.4 Thin-walled tubes, helical grain flow . 3
5.5 Castings . 3
6 Designation of notched (or precracked) specimens . 3
6.1 General . 3
6.2 Aligned . 3
6.3 Not aligned . 3
6.4 No grain flow . 3
6.5 Welds . 3
6.6 Additive manufacturing . 4
7 Application of designation system in material specification . 4
7.1 General . 4
7.2 Non-uniform grain flow. 4
7.3 Specifications . 4
7.4 Comparisons . 4
Annex A (informative) Influence of mechanical working on material structure and
properties . 8
Bibliography . 9
iii
© ISO 2022 – All rights reserved
---------------------- Page: 3 ----------------------
ISO/FDIS 3785:2022(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO's adherence to
the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals,
Subcommittee SC 4, Fatigue, fracture and toughness testing, in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC CEN/TC 459/SC 1, ECISS - European
Committee for Iron and Steel Standardization, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the first edition (ISO 3785:2006), which has been technically
revised.
The main changes are as follows:
— A reference to Annex A was added in the Introduction;
— In 6.5 a reference to ISO 15653 was added;
— A new subclause 6.6 (Additive manufacturing) was added.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
© ISO 2022 – All rights reserved
---------------------- Page: 4 ----------------------
ISO/FDIS 3785:2022(E)
Introduction
The measured mechanical properties of a metallic product, especially those characterizing ductility
and toughness, such as elongation, reduction of area, fracture toughness and impact resistance, are
dependent on the test specimen location within the product and orientation with respect to the
product's principal directions of metal working, grain flow or otherwise-produced texture. This
International Standard specifies a method for designating specimen orientation in relation to product
texture.
Additional information on the influence of mechanical working on material structure and properties is
provided in Annex A.
v
© ISO 2022 – All rights reserved
---------------------- Page: 5 ----------------------
FINAL DRAFT INTERNATIONAL STANDARD ISO/FDIS 3785:2022(E)
Metallic materials — Designation of test specimen axes in
relation to product texture
1 Scope
This document specifies a method for designating test specimen axes in relation to product texture by
means of an X-Y-Z orthogonal coordinate system.
This document applies equally to unnotched and notched (or precracked) test specimens.
This document is intended only f
...
PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 3785
ISO/TC 164/SC 4
Matériaux métalliques — Désignation
Secrétariat: ANSI
des axes des éprouvettes en relation
Début de vote:
2023-01-04 avec la texture du produit
Vote clos le:
Metallic materials — Designation of test specimen axes in relation to
2023-03-01
product texture
TRAITEMENT PARALLÈLE ISO/CEN
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 3785:2023(F)
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
TION NATIONALE. © ISO 2023
---------------------- Page: 1 ----------------------
ISO/FDIS 3785:2023(F)
PROJET
NORME ISO/FDIS
FINAL
INTERNATIONALE 3785
ISO/TC 164/SC 4
Matériaux métalliques — Désignation
Secrétariat: ANSI
des axes des éprouvettes en relation
Début de vote:
2023-01-04 avec la texture du produit
Vote clos le:
Metallic materials — Designation of test specimen axes in relation to
2023-03-01
product texture
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2023
TRAITEMENT PARALLÈLE ISO/CEN
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
LES DESTINATAIRES DU PRÉSENT PROJET SONT
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
INVITÉS À PRÉSENTER, AVEC LEURS OBSER-
VATIONS, NOTIFICATION DES DROITS DE PRO-
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
PRIÉTÉ DONT ILS AURAIENT ÉVENTUELLEMENT
ISO copyright office
CONNAISSANCE ET À FOURNIR UNE DOCUMEN-
TATION EXPLICATIVE.
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
Tél.: +41 22 749 01 11
INDUSTRIELLES, TECHNOLOGIQUES ET COM-
Numéro de référence
E-mail: copyright@iso.org
MERCIALES, AINSI QUE DU POINT DE VUE
ISO/FDIS 3785:2023(F)
Web: www.iso.org
DES UTILISATEURS, LES PROJETS DE NORMES
INTERNATIONALES DOIVENT PARFOIS ÊTRE
Publié en Suisse
CONSIDÉRÉS DU POINT DE VUE DE LEUR POSSI-
BILITÉ DE DEVENIR DES NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTA-
ii
© ISO 2023 – Tous droits réservés
TION NATIONALE. © ISO 2023
---------------------- Page: 2 ----------------------
ISO/FDIS 3785:2023(F)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application .1
2 Références normatives .1
3 Termes et définitions . 1
4 Système de désignation . 1
4.1 Généralités . 1
4.2 Exception — Désaxé . 1
4.3 Exception — Absence de fibrage . 2
5 Désignation des éprouvettes sans entaille . 2
5.1 Généralités . 2
5.2 Tôle, plaque, barre (produits plats laminés) . 2
5.2.1 Axé, fibrage différent dans les trois directions orthogonales . 2
5.2.2 Désaxé, fibrage différent dans les trois directions orthogonales . 2
5.2.3 Axé, fibrage équiaxe . 2
5.2.4 Désaxé, fibrage équiaxe . 2
5.3 Cylindres et tubes épais . 3
5.4 Tubes à paroi mince, fibrage hélicoïdal. 3
5.5 Pièces moulées . . 3
6 Désignation des éprouvettes entaillées (ou préfissurées) . 3
6.1 Généralités . 3
6.2 Axé . 3
6.3 Désaxé . 3
6.4 Absence de fibrage . 4
6.5 Soudures . . 4
6.6 Fabrication additive . 4
7 Application du système de désignation dans les spécifications de matériaux .4
7.1 Généralités . 4
7.2 Fibrage non uniforme . 4
7.3 Spécifications . 4
7.4 Comparaisons . 4
Annexe A (informative) Influence d'une mise en forme mécanique sur la structure et les
caractéristiques des matériaux .8
Bibliographie . 9
iii
© ISO 2023 – Tous droits réservés
---------------------- Page: 3 ----------------------
ISO/FDIS 3785:2023(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes
nationaux de normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est
en général confiée aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l'ISO participent également aux travaux.
L'ISO collabore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d'approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L'attention est attirée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l'élaboration du document sont indiqués dans l'Introduction et/ou dans la liste des déclarations de
brevets reçues par l'ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité à l'intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, de la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ainsi que des informations sur l'adhésion de l'ISO
aux principes de l'Organisation mondiale du commerce (OMC) dans le domaine des obstacles techniques
au commerce (OTC), voir www.iso.org/iso/foreword.html.
Le présent document a été élaboré par le comité technique ISO/TC 164, Essais mécaniques des métaux,
sous-comité SC 4, Essais de ténacité — Fracture (F), Pendulum (P), Déchirage (T), en collaboration avec
le comité technique du Comité Européen de Normalisation (CEN) CEN/TC 459/SC 1, ECISS — Comité
européen de normalisation du fer et de l'acier, conformément à l'accord sur la coopération technique
entre l'ISO et le CEN (accord de Vienne).
Cette troisième édition annule et remplace la première édition (ISO 3785:2006), qui a fait l'objet d'une
révision technique.
Les principaux changements sont les suivants :
— une référence à l'Annexe A a été ajoutée dans l'introduction ;
— à l'Article 6.5, une référence à la norme ISO 15653 a été ajoutée ;
— un nouveau paragraphe 6.6 (Fabrication additive) a été ajouté.
Tout commentaire ou question sur ce document doit être adressé à l'organisme national de
normalisation de l'utilisateur. Une liste complète de ces organismes peut être consultée à l'adresse
www.iso.org/members.html.
iv
© ISO 2023 – Tous droits réservés
---------------------- Page: 4 ----------------------
ISO/FDIS 3785:2023(F)
Introduction
Les caractéristiques mécaniques mesurées d'un produit métallique, particulièrement celles
caractérisant la ductilité et la ténacité, telles que l'allongement, la striction, la ténacité à la rupture et
la résistance au choc, dépendent de la position des éprouvettes dans le produit et de l'orientation des
éprouvettes par rapport aux directions principales de mise en forme du métal, du fibrage ou d'autres
textures formées au sein du produit. La présente Norme internationale spécifie une méthode pour
désigner l'orientation des éprouvettes en relation avec la texture du produit.
Des informations supplémentaires sur l'influence du travail mécanique sur la structure et les propriétés
des matériaux sont fournies à l'Annexe A.
v
© ISO 2023 – Tous droits réservés
---------------------- Page: 5 ----------------------
PROJET FINAL DE NORME INTERNATIONALE ISO/FDIS 3785:2023(F)
Matériaux métalliques — Désignation des axes des
éprouvettes en relation avec la texture du produit
1 Domaine d'application
La présente Norme internationale spécifie une méthode pour désigner les axes des éprouvettes en
relation avec la texture du produit, au moyen d'un système orthogonal de coordonnées X-Y-Z.
Le système s'applique aussi bien aux éprouvettes sans entaille qu'aux éprouvettes entaillées (ou
préfissurées).
La méthode est destinée seulement aux matériaux métalliques de texture uniforme qui peut être
déterminée sans ambiguïté.
L'orientation de l'éprouvette est décidée avant usinage de l'éprouvette, identifiée conformément au
système de désignation spécifié dans la présente Norme internationale, et enregistrée.
2 Références normatives
Il n'y a pas de références normatives dans ce document.
3 Termes et définitions
Aucun terme ni aucune définition ne figurent dans ce document.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes :
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
4 Système de désignation
4.1 Généralités
La méthode pour relier les axes des
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.