ASTM B498/B498M-98(2002)
(Specification)Standard Specification for Zinc-Coated (Galvanized) Steel Core Wire for Aluminum Conductors, Steel Reinforced (ACSR)
Standard Specification for Zinc-Coated (Galvanized) Steel Core Wire for Aluminum Conductors, Steel Reinforced (ACSR)
ABSTRACT
This specification covers round, zinc-coated (galvanized), steel core wire with three classes of zinc coating used for mechanical reinforcement in the manufacture of aluminum conductors, steel-reinforced (ACSR). The wire is furnished in three classes of coating, namely: Class A, Class B, and Class C. The base metal shall be steel produced by the open-hearth, electric-furnace, or basic-oxygen process. The wire shall be cold drawn and coated with zinc to produce the desired properties and the the slab zinc used for coating shall be high-grade or better. The steel shall conform to the chemical composition requirements prescribed for carbon, manganese, phosphorus, sulfur, and silicon, as determined by chemical analysis. The following tests shall be performed: (1) tensile test to determine the mechanical properties such as ultimate tensile strength, elongation, and stress at extension, (2) wrap test, (3) coating test to determine conformity to the specified diameter and area density requirements, and (4) coating adherence test. Requirements for joints which may be made by electric butt-weld or flash-welding are detailed. The density and resistivity of galvanized steel wire are prescribed for the purposes of calculating mass per unit length, cross-sections, and so forth.
SCOPE
1.1 This specification covers round, zinc-coated, steel core wire with three classes of zinc coating used for mechanical reinforcement in the manufacture of aluminum conductors, steel-reinforced (ACSR).
1.2 This specification covers wire of diameter from 0.0500 to 0.1900 in. or 1.60 to 4.80 mm, inclusive.
1.3 The values stated in inch-pound units or SI units are to be regarded separately as standard. The values in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B 498/B 498M – 98 (Reapproved 2002)
Standard Specification for
Zinc-Coated (Galvanized) Steel Core Wire for Aluminum
Conductors, Steel Reinforced (ACSR)
This standard is issued under the fixed designation B 498/B 498M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 4. Classification
4.1 The wire is furnished in three classes of coating, Class
1.1 This specification covers round, zinc-coated, steel core
wire with three classes of zinc coating used for mechanical A, Class B, or Class C, as specified, in conformance with the
reinforcement in the manufacture of aluminum conductors, requirements of Section 10 and Table 1 or Table 2.
steel-reinforced (ACSR).
5. Ordering Information
1.2 This specification covers wire of diameter from 0.0500
5.1 Orders for material under this specification shall include
to 0.1900 in. or 1.60 to 4.80 mm, inclusive.
1.3 The values stated in inch-pound units or SI units are to the following information:
5.1.1 Quantity of each size,
be regarded separately as standard. The values in each system
are not exact equivalents; therefore, each system shall be used 5.1.2 Wire diameter in inches or millimetres (Section 14),
5.1.3 Class of coating (see 4.1),
independently of the other. Combining values from the two
systems may result in nonconformance with this specification. 5.1.4 Certification, if required (Section 19),
5.1.5 Test report, if required (Section 19), and
2. Referenced Documents
5.1.6 Package size (Section 20).
2.1 The following documents of the issue in effect on date
6. Materials and Manufacture
of material purchase form a part of this specification to the
extent referenced herein. 6.1 The base metal shall be steel produced by the open-
hearth, electric-furnace, or basic-oxygen process.
2.2 ASTM Standards:
A 90/A 90M Test Method for Weight [Mass] of Coating on 6.2 The wire shall be cold drawn and coated with zinc to
produce the desired properties.
Iron and Steel Articles with Zinc or Zinc-Alloy Coatings
A 370 Test Methods and Definitions for MechanicalTesting 6.3 The slab zinc used for coating shall be high-grade or
of Steel Products better, conforming to Specification B 6.
A 751 Test Methods, Practices, and Terminology for
7. Chemical Composition
Chemical Analysis of Steel Products
7.1 The steel shall conform to the requirements prescribed
B 6 Specification for Zinc
in Table 3.
B 193 Test Method for Resistivity of Electrical Conductor
7.2 Chemical analysis shall be conducted in accordance
Materials
with Test Methods, Practices, and Terminology A 751.
3. Terminology
8. Tensile Test
3.1 Definition:
8.1 The zinc-coated steel core wire shall conform to the
3.1.1 lot—unless otherwise specified in the contract or
tensile and elongation requirements prescribed in Table 4 and
order, a lot shall consist of all coils of wire of the same
Table 5.
diameter and unit lengths submitted for inspection at the same
8.2 Tensile tests shall be conducted in accordance with Test
time.
Methods and Definitions A 370, using the initial settings for
determining stress at 1 % extension given in Table 6 or Table
This specification is under the jurisdiction of ASTM Committee B01 on
7 of this specification.
Electrical Conductors and is the direct responsibility of Subcommittee B01.05 on
Conductors of Ferrous Metals. 8.3 Test Specimens—The test specimens shall be free of
Current edition approved Sept. 10, 1998. Published November 1998. Originally
bends or kinks other than the curvature resulting from the usual
published as B 498 – 69 to replace B 245 and B 261. Last previous edition
coiling operations.Any hand straightening necessary to permit
B 498 – 93.
insertion of the specimen in the jaws of the testing machine
Annual Book of ASTM Standards, Vol 01.06.
Annual Book of ASTM Standards, Vol 01.03. shall be performed by drawing between wood blocks or by
Annual Book of ASTM Standards, Vol 02.04.
some other equally satisfactory means.
Annual Book of ASTM Standards, Vol 02.03.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
B 498/B 498M – 98 (2002)
TABLE 1 Zinc Coating
12.2 Joints may be made at any stage of processing before
Area Density of Coating, min, oz/ft of final cold drawing by the electric butt-weld or flash-welding
Specified Diameter of Coated
Uncoated Wire Surface
process.
Wire, in.
Class A Class B Class C
12.3 Welding equipment and procedure shall be such that it
0.0500 to 0.599, incl 0.60 1.20 1.80
can be demonstrated that the tensile strength of a finished wire
0.0600 to 0.0749, incl 0.65 1.30 1.95
specimen containing the welded section shall not be less than
0.0750 to 0.0899, incl 0.70 1.40 2.10
96 % of the specified minimum stress at 1 % extension.
0.0900 to 0.1039, incl 0.75 1.50 2.25
0.1040 to 0.1199, incl 0.80 1.60 2.40
12.4 A welded section shall not be required to meet the
0.1200 to 0.1399, incl 0.85 1.70 2.55
stress at 1 % extension, elongation, and wrap tests.
0.1400 to 0.1799, incl 0.90 1.80 2.70
0.1800 to 0.1900, incl 1.00 2.00 3.00
13. Density and Resistivity
13.1 For the purposes of calculating mass per unit length,
TABLE 2 Zinc Coating
cross-sections, and so forth, the density of galvanized steel
Area Density of Coating, min, g/m of
3 3
wire at 20°C shall be taken as 0.281 lb/in. (7780 kg/m ).
Specified Diameter of Coated
Uncoated Wire Surface
Wire, mm
13.2 A maximum resistivity of galvanized steel wire is not
Class A Class B Class C
guaranteed, but a typical value of 0.191 57 V·mm /m may be
1.60 to 1.90, incl 210 420 630
used for purposes of calculation. For conversion to other units
Over 1.90 to 2.30, incl 220 440 660
Over 2.30 to 2.70, incl 230 460 690
of conductivity or resistivity, refer to Test Method B 193.
Over 2.70 to 3.10, incl 240 480 720
Over 3.10 to 3.50, incl 260 520 780
14. Dimensions and Permissible Variations
Over 3.50 to 3.90, incl 270 540 810
Over 3.90 to 4.50, incl 275 550 825
14.1 The specified diameter shall be expressed in decimal
Over 4.50 to 4.80, incl 300 600 900
fractionsofaninchtofourdecimalplacesorinmillimetresand
decimal fractions of a millimetre to two decimal places.
TABLE 3 Chemical Requirements
14.2 For diameter measurements and diameter tolerances,
Element Composition, % specified diameters shall be rounded to the closest 0.0005 in. or
0.01 mm.
Carbon 0.50 to 0.85
Manganese 0.50 to 1.10
14.3 Determine the greatest and least diameters each to the
Phosphorus, max 0.035
neareast 0.001 in. or 0.01 mm, at the same cross-section. The
Sulfur, max 0.045
Silicon 0.10 to 0.35 average of these two diameters shall not differ from the
specified diameter by more than the tolerances shown in Table
10 and Table 11.
9. Wrap Test
9.1 The material, as represented by the test specimens, shall
15. Workmanship, Finish, and Appearance
not fracture when the galvanized wire is wrapped at a rate not
15.1 The zinc coating shall be reasonably smooth, continu-
exceeding 15 turns/min in a close helix of at least eight turns
ous, of reasonably uniform thickness, and free from imperfec-
around a cylindrical mandrel with a diameter equal to two
tions not consistent with good commercial practice.
times the specified diameter of the wire under test, 65%.
10. Coating Test
16. Number of Tests and Retests
10.1 The material, as represented by the test specimens,
16.1 One test specimen shall be taken from each 5000 lbs or
shall conform to the coating requirements of Table 1 or Table
2500 kg. or fraction, thereof, in the inspection lot.
2. for the diameter and class of coating specified.
16.2 Each specimen shall be tested for compliance with
10.2 The coating test shall be conducted in accordance with
Sections 8, 9, 11, and 14. At least half of the specimens shall
Test Method A 90/A 90M.
be tested for compliance with Section 10.
11. Adherence of Coating Test 16.3 Should one or more of the
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.