ASTM D6163-00e2

Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements

ABSTRACT
This specification covers Grades G (granule surfaced) and S (smooth surfaced) prefabricated bituminous sheet materials with glass fiber reinforcement that has been modified by styrene butadiene styrene (SBS) thermoplastic elastomer, and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes. This specification is intended as a material specification only, and does not address issues regarding the suitability of the specific roof constructions or application techniques. The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties, Hence, roof system design criteria such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, and others are factors beyond its scope. Material properties for which the sheet materials should adhere to are peak load before and after heat conditioning, elongation at peak load, ultimate elongation, tear strength, low temperature flexibility, dimensional stability, compound stability at specified temperatures, and granule embedment.
SCOPE
1.1 This specification covers prefabricated modified bituminous sheet materials with glass fiber reinforcement, with or without granules, that use styrene butadiene styrene (SBS) thermoplastic elastomer as the primary modifier and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes.
1.2 This specification is intended as a material specification only. Issues regarding the suitability of the specific roof constructions or application techniques are beyond this scope.
1.3 The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties. In-place roof system design criteria, such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, and others, are factors beyond the scope of this material specification.
1.4 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

General Information

• Status: Historical
• Publication Date: 09-Jul-2000
• ICS: 91.100.50 - Binders. Sealing materials
• Technical Committee: D08 - Roofing and Waterproofing
• Drafting Committee: D08.04 - Felts, Fabrics and Bituminous Sheet Materials

Relations

• Replaces: ASTM D6163-00e1 - Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements
• Effective Date: 10-Jul-2000
• Replaced By: ASTM D6163-00(2008) - Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements
• Effective Date: 01-Dec-2008
• Referred By: ASTM D7693/D7693M-15 - Standard Guide for Application of Heat Weldable Modified Bituminous Waterproofing Membranes Systems for New Concrete Decks
• Effective Date: 10-Jul-2000

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
e2
Designation: D 6163 – 00
Standard Specification for
Styrene Butadiene Styrene (SBS) Modified Bituminous
1
Sheet Materials Using Glass Fiber Reinforcements
This standard is issued under the fixed designation D 6163; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1
e NOTE—Table 2 was editorially corrected in October 2001.
2
e NOTE—Section 3, subsection 9.2, and Table 2 were editorially corrected in March 2008.
1. Scope 4. Classifications
1.1 This specification covers prefabricated modified bitumi- 4.1 Modified bituminous sheet materials reinforced with
nous sheet materials with glass fiber reinforcement, with or glass fiber, Type I, Type II, and Type III are covered by this
without granules, that use styrene butadiene styrene (SBS) specification.
thermoplastic elastomer as the primary modifier and are 4.2 The following grades are used to describe the material
intended for use in the fabrication of multiple ply roofing and surfacing:
waterproofing membranes. 4.2.1 Grade G—Granule surfaced.
1.2 This specification is intended as a material specification 4.2.2 Grade S—Smooth surfaced.
only. Issues regarding the suitability of the specific roof
5. Material and Manufacture
constructions or application techniques are beyond this scope.
5.1 In the process of manufacture, the reinforcement is
1.3 The specified tests and property limits used to charac-
terize the sheet materials are intended to establish minimum impregnated and coated on both sides with an SBS modified
bituminous coating. The SBS modified bituminous coating
properties. In-place roof system design criteria, such as fire
resistance, field strength, impact/puncture resistance, material shall be permitted to be compounded with a mineral stabilizer.
5.2 The Grade G sheet is surfaced on the weather side with
compatibility, uplift resistance, and others, are factors beyond
the scope of this material specification. mineralgranules,exceptforanyselvage.Topreventstickingin
the roll, the reverse side and any selvage shall be permitted to
1.4 The values stated in SI units are to be regarded as the
be covered with a fine mineral surfacing or any other surfacing
standard. The values given in parentheses are for information
only. that will not interfere with adhesion or bonding of the lap
during application.
2. Referenced Documents
5.3 Sheet material intended for application by heat welding
2
2.1 ASTM Standards: (torching) shall meet the minimum bottom coating requirement
D 1079 Terminology Relating to Roofing and Waterproof- found in Table 1.
ing
6. Physical Properties
D 5147 Test Methods for Sampling and Testing Modified
Bituminous Sheet Material 6.1 The sheet shall conform to the minimum physical
properties prescribed in Table 2.
3. Terminology
6.2 The finished product shall not crack nor be so sticky as
3.1 Definitions—For definitions of terms used in this speci- to cause tearing or other material damage upon being unrolled
fication, refer to Terminology D 1079. at any product temperature between 4 and 60°C (40 and
140°F).
1
This specification is under the jurisdiction of ASTM Committee D08 on 7. Dimensions, Mass, and Permissible Variations
Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.04
7.1 The finished product shall conform to the following
on Felts and Fabrics.
dimensions and variations:
Current edition approved July 10, 2000. Published September 2000. Originally
published as D 6163–97. Last previous edition D 6163–98a.
7.1.1 The width of the roll shall be as agreed between the
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
purchaser and the seller and shall not vary more than 1 %.
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
7.1.2 The area of the roll shall be no less than as agreed
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. between the purchaser and the seller.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
e2
D6163–00
TABLE 1 Dimensions and Masses of SBS Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements
Description Type I Type II Type III
Thickness, min, mm (mils),
Grade S 2.0 (80) 2.0 (80) 2.0 (80)
Grade G 2.4 (95) 2.7 (105) 3.0 (120)
2 2
Net mass/unit area, min, g/m (lbs/100 ft )
Grade S 2197 (45) 2197 (45) 2197 (45)
Grade G 3173 (65) 3661 (75) 3661 (75)
Bottom coating thickness, heat welding application
products, min, mm (mils)
Grade S 1.0 (40) 1.0 (40) 1.0 (40)
Grade G 1.0 (40) 1.0 (40
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
e2
Designation:D6163–98a Designation: D 6163 – 00
Standard Specification for
Styrene Butadiene Styrene (SBS) Modified Bituminous
1
Sheet Materials Using Glass Fiber Reinforcements
This standard is issued under the fixed designation D 6163; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1
e NOTE—Table 2 was editorially corrected in October 2001.
2
e NOTE—Section 3, subsection 9.2, and Table 2 were editorially corrected in March 2008.
1. Scope
1.1 This specification covers prefabricated modified bituminous sheet materials with glass fiber reinforcement, with or without
granules, whichthat use styrene butadiene styrene (SBS) thermoplastic elastomer as the primary modifier and are intended for use
in the fabrication of multiple ply roofing and waterproofing membranes.
1.2 This specification is intended as a material specification only. Issues regarding the suitability of the specific roof
constructions or application techniques are beyond this scope.
1.3 The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties.
In-place roof system design criteria, such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift
resistance, and others, are factors beyond the scope of this material specification.
1.4 The values stated in inch-poundSI units are to be regarded as the standard. The values given in parentheses are for
information only.
2. Referenced Documents
2
2.1 ASTM Standards:
D 1079Terminology Relating to Roofing, Waterproofing, and Bituminous Materials Terminology Relating to Roofing and
Waterproofing
2
D 5147Test Methods for Sampling andTesting Modified Bituminous Sheet Materials Used in Roofing andWaterproofing Test
Methods for Sampling and Testing Modified Bituminous Sheet Material
3. Terminology
3.1 Definitions— For definitions of terms used in this specification, refer to Terminology D 1079:
3.1.1elongation at 5% of maximum load, n—the elongation measured on the load-elongation curve at which point the load has
dropped to 5% of its maximum value. .
4. Classifications
4.1 Modified bituminous sheet materials reinforced with glass fiber, Type I, Type II, and Type III are covered by this
specification.
4.2 The following grades are used to describe the material surfacing:
4.2.1 Grade G—Granule surfaced.
4.2.2 Grade S—Smooth surfaced.
5. Material and Manufacture
5.1 In the process of manufacture, the reinforcement is impregnated and coated on both sides with an SBS modified bituminous
coating. The SBS modified bituminous coating mayshall be permitted to be compounded with a fine mineral stabilizer.
5.2 The Grade G sheet is surfaced on the weather side with mineral granules, except for any selvage. To prevent sticking in the
roll, the reverse side and any selvage mayshall be permitted to be covered with a fine mineral surfacing or any other surfacing that
will not interfere with adhesion or bonding of the lap during application.
1
This specification is under the jurisdiction ofASTM Committee D-08D08 on Roofing, Waterproofing, Roofing and Bituminous Materials Waterproofing and is the direct
responsibility of Subcommittee D08.04 on Felts and Fabrics.
Current edition approved Aug.July 10, 1998.2000. Published October 1998.September 2000. Originally published as D 6163–97. Last previous edition D 6163–98a.
2
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
, Vol 04.04.volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
e2
D6163–00
5.3 Sheet material intended for application by heat welding (torching) shall meet the minimum bottom coating requirement
found in Table 1.
6. Physical Properties
6.1 The sheet shall conform to the minimum physical properties prescribed in Table 2.
6.2 The finished product shall not crack nor be so sticky as to cause tearing or other material damage upon being unrolled at
any product temperature between 404 and 140°F (460°C (40 and 60°C). 140°F).
7. Dimensions, Mass, and Permissible Variations
7.1 The finished product shall conform to
...