ASTM D6222/D6222M-16(2023)
(Specification)Standard Specification for Atactic Polypropylene (APP) Modified Bituminous Sheet Materials Using Polyester Reinforcements
Standard Specification for Atactic Polypropylene (APP) Modified Bituminous Sheet Materials Using Polyester Reinforcements
ABSTRACT
This specification covers prefabricated modified bituminous sheet materials with polyester fabric reinforcement, with or without granules, that use atactic polypropylene (APP) as the primary modifier and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes. This specification is not intended for (1) issues regarding the suitability of specific roof constructions or application techniques and (2) in-place roof system design criteria such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, the need for field applied coatings, and others. Type I and II modified bituminous sheet materials reinforced with polyester fabric, with granule surfacing (Grade G) and smooth surfacing (Grade S) are covered by this specification The APP modified bituminous coating shall be permitted to be compounded with a mineral stabilizer. To prevent sticking in the roll, the reverse side and any selvage shall be permitted to be covered with a fine mineral surfacing or any other surfacing that will not interfere with adhesion or bonding of the lap. The sheet shall conform to the minimum physical properties prescribed for: peak load, elongation, ultimate elongation, tear strength, low temperature flexibility, dimensional stability, compound stability, granule embedment, water absorption, moisture content, and low temperature unrolling. The finished product shall conform to the requirements prescribed for net mass and dimensions such as width of roll, area of roll, selvage width, thickness, and bottom side coating thickness. The specified ultimate elongation, high temperature stability, and low temperature unrolling test methods shall be used.
SCOPE
1.1 This specification covers prefabricated modified bituminous sheet materials reinforced with polyester fabric, with or without granules, that use atactic polypropylene (APP) as the primary modifier and are intended for use in the fabrication of multiple ply roofing and waterproofing membranes.
Note 1: Many modified bituminous sheets are currently marketed with polyester mat reinforced with glass yarns to improve processing in the manufacture of the finished modified bitumen product and to reduce distortions that may be introduced during production. These glass yarns are typically a small percentage of the reinforcement and do not contribute to the physical properties of the finished product so much as to make these products be classified by Specification D6223/D6223M.
1.2 This specification is intended as a material specification only. Issues regarding the suitability of specific roof constructions or application techniques are beyond the scope of this specification.
1.3 The specified tests and property limits used to characterize the sheet materials covered by this specification are intended to establish minimum properties. In-place roof system design criteria such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, the need for field applied coatings, and others, are factors beyond the scope of this material specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.5 The following precautionary statement pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with international...
General Information
Relations
Standards Content (Sample)
This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D6222/D6222M − 16 (Reapproved 2023)
Standard Specification for
Atactic Polypropylene (APP) Modified Bituminous Sheet
Materials Using Polyester Reinforcements
This standard is issued under the fixed designation D6222/D6222M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope environmental practices and determine the applicability of
regulatory limitations prior to use.
1.1 This specification covers prefabricated modified bitumi-
1.6 This international standard was developed in accor-
nous sheet materials reinforced with polyester fabric, with or
dance with internationally recognized principles on standard-
without granules, that use atactic polypropylene (APP) as the
ization established in the Decision on Principles for the
primary modifier and are intended for use in the fabrication of
Development of International Standards, Guides and Recom-
multiple ply roofing and waterproofing membranes.
mendations issued by the World Trade Organization Technical
NOTE 1—Many modified bituminous sheets are currently marketed with
Barriers to Trade (TBT) Committee.
polyester mat reinforced with glass yarns to improve processing in the
manufacture of the finished modified bitumen product and to reduce
distortions that may be introduced during production. These glass yarns 2. Referenced Documents
are typically a small percentage of the reinforcement and do not contribute
2.1 ASTM Standards:
to the physical properties of the finished product so much as to make these
D1079 Terminology Relating to Roofing and Waterproofing
products be classified by Specification D6223/D6223M.
D5147/D5147M Test Methods for Sampling and Testing
1.2 This specification is intended as a material specification
Modified Bituminous Sheet Material
only. Issues regarding the suitability of specific roof construc-
D5636/D5636M Test Method for Low-Temperature Unroll-
tions or application techniques are beyond the scope of this
ing of Felt or Sheet Roofing and Waterproofing Materials
specification.
D6223/D6223M Specification for Atactic Polypropylene
1.3 The specified tests and property limits used to charac-
(APP) Modified Bituminous Sheet Materials Using a
terize the sheet materials covered by this specification are
Combination of Polyester and Glass Fiber Reinforcements
intended to establish minimum properties. In-place roof system
design criteria such as fire resistance, field strength, impact/ 3. Terminology
puncture resistance, material compatibility, uplift resistance,
3.1 Definitions:
the need for field applied coatings, and others, are factors
3.1.1 For definitions of terms used in this specification, refer
beyond the scope of this material specification.
to Terminology D1079.
1.4 The values stated in either SI units or inch-pound units
4. Classification
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each
4.1 Type I and II modified bituminous sheet materials
system shall be used independently of the other. Combining
reinforced with polyester fabric, are covered by this specifica-
values from the two systems may result in non-conformance
tion (see Table 1).
with the standard.
4.2 The following grades are used to describe the material
1.5 The following precautionary statement pertains only to
surfacing:
the test method portion, Section 9, of this specification: This
4.2.1 Grade G—Granule surfacing.
standard does not purport to address all of the safety concerns,
4.2.2 Grade S—Smooth surfacing.
if any, associated with its use. It is the responsibility of the user
of this standard to establish appropriate safety, health, and 5. Materials and Manufacture
5.1 In the process of manufacture, the reinforcement is
saturated with APP modified asphalt and is impregnated and
This specification is under the jurisdiction of ASTM Committee D08 on
Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.04
on Felts, Fabrics and Bituminous Sheet Materials. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved Feb. 1, 2023. Published February 2023. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 1998. Last previous edition approved in 2016 as D6222/D6222M – 16. Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/D6222_D6222M-16R23. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
D6222/D6222M − 16 (2023)
TABLE 1 Physical Properties of APP Modified Bituminous Sheet
7. Dimensions, Mass, and Permissible Variations
A
Materials Using Polyester Reinforcements
7.1 The finished product shall conform to the following
Property Type I Type II
dimensions and variations:
Peak load at 23 °C ± 2 °C [73.4 °F ± 3.6 °F]
7.1.1 The width of the roll shall be as agreed upon between
MD and XMD, before and after heat
conditioning, min, kN/m [lbf/in.] 8.8 [50] 14 [80]
the purchaser and the supplier and shall not vary more than
1 %.
Elongation at 23 °C ± 2 °C [73.4 °F ± 3.6 °F]
7.1.2 The area of the roll shall be no less than as agreed
MD and XMD, before and after heat
conditioning, at peak load,
upon between the purchaser and the supplier.
min, % 23 40
7.1.3 The selvage width shall be within 6 mm [ ⁄4 in.] of the
Peak load at –18 °C ± 2 °C [0 °F ± 3.6 °F] nominal selvage width and shall be not less than 76 mm [3 in.]
MD and XMD, min, kN/m [lbf/in.] 10.5 [60] 15.8 [90]
in width from the edge of the sheet.
Elongation at –18 °C ± 2 °C [0 °F ± 3.6 °F]
7.2 The mass and thickness of the finished product shall be
MD and XMD, at peak load,
as prescribed in Table 2.
min, % 10 15
8. Workmanship, Finish, and Appearance
Ultimate elongation at
23 °C ± 2 °C [73.4 °F ± 3.6 °F], MD and XMD,
8.1 The finished product shall be completely coated in a
min, % 30 50
continuous, unbroken film and shall be free of such defects as
Tear strength at 23 °C ± 2 °C
holes, tears, cracks, wrinkles or permanent deformations,
[73.4 °F ± 3
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.