Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings

Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings

SIGNIFICANCE AND USE
This practice for preparation of test panels greatly increases the likelihood of achieving reproducible results in subsequent testing.
SCOPE
1.1 This practice covers a procedure for the preparation of accelerated and outdoor weathering test panels of bituminous coatings. It is considered suitable for the preparation of film thicknesses in the range from 0.25 to 2.54 mm (0.010 to 0.100 in.).
1.2 The values stated in SI units are to be regarded as standard.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (Warning-Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet (MSDS) for details and EPA's website, http://www.epa.gov/mercury/faq.htm, for additional information. Users should be aware that selling mercury and/or mercury-containing products into your state may be prohibited by state law.)

General Information

Status
Historical
Publication Date
14-Sep-2007
ICS
91.100.50 - Binders. Sealing materials
Technical Committee
D08 - Roofing and Waterproofing
Drafting Committee
D08.02 - Steep Roofing Products and Assemblies
Current Stage
Ref Project

Relations

Replaces
ASTM D1669-03 - Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings
Effective Date
15-Sep-2007
Replaced By
ASTM D1669-07(2013) - Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings
Effective Date
01-May-2013

Buy Standard

ASTM D1669-07 - Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous CoatingsASTM D1669-07 - Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings
PreviousNext
Standard
ASTM D1669-07 - Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D1669 − 07
StandardPractice for
Preparation of Test Panels for Accelerated and Outdoor
1
Weathering of Bituminous Coatings
This standard is issued under the fixed designation D1669; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision.Anumber in parentheses indicates the year of last reapproval.A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 3. Summary of Practice
3.1 Heated bituminous material is poured onto a clean,
1.1 This practice covers a procedure for the preparation of
accelerated and outdoor weathering test panels of bituminous heated, and masked aluminum panel. Care is taken to remove
air bubbles. The bitumen is leveled in a press before
coatings. It is considered suitable for the preparation of film
thicknesses in the range from 0.25 to 2.54 mm (0.010 to 0.100 solidifying, and the coated panel is then cooled, cleaned, and
measured for uniform thickness.
in.).
1.2 The values stated in SI units are to be regarded as
4. Significance and Use
standard.
4.1 This practice for preparation of test panels greatly
1.3 This standard does not purport to address all of the
increases the likelihood of achieving reproducible results in
safety concerns, if any, associated with its use. It is the
subsequent testing.
responsibility of the user of this standard to establish appro-
priate safety and health practices and determine the applica-
5. Apparatus
bility of regulatory limitations prior to use. (Warning—
5.1 Panel—A supporting metal panel on which the bitumi-
Mercury has been designated by EPAand many state agencies
nous coating is applied. It shall meet the following require-
as a hazardous material that can cause central nervous system,
ments:
kidney, and liver damage. Mercury, or its vapor, may be
5.1.1 Metal, Aluminum or Aluminum Alloy, as described in
hazardous to health and corrosive to materials. Caution should
3
Table2 of Specification B209 under Alloy 3003-H14.
be taken when handling mercury and mercury-containing
5.1.2 Finish—Mill finish and process cleaned.
products. See the applicable product Material Safety Data
5.1.3 Dimensions:
Sheet (MSDS) for details and EPA’s website, http://
5.1.3.1 Thickness—0.64 to 1.90 mm (0.025 to 0.075 in.).
www.epa.gov/mercury/faq.htm,foradditionalinformation.Us-
3 7
5.1.3.2 Width and Length—70 by 150 mm (2 ⁄4 by 5 ⁄8 in.)
ers should be aware that selling mercury and/or mercury-
or of a size that will allow a minimum bitumen film area of 50
containing products into your state may be prohibited by state
1
by 130 mm (2 by 5 ⁄8 in.).
law. )
5.1.4 Flatness—The maximum deviation from a true flat
surfaceforeitherlengthorwidthshallnotexceed0.0005times
2. Referenced Documents
thedimension.Flatnessshallbemeasuredonatrueflatsurface
2
2.1 ASTM Standards:
employingacurlinggaugeequippedwithadialwhichreadsin
B209Specification for Aluminum and Aluminum-Alloy
0.025 mm (0.001 in.) and having a foot loading of approxi-
4
Sheet and Plate
mately 100 g.
D5Test Method for Penetration of Bituminous Materials
5.1.5 Edges—The edges of the panels shall be free of burrs.
E1Specification for ASTM Liquid-in-Glass Thermometers
3
Thesolesourcesofsupplyoftheapparatus(panels)knowntothecommitteeat
this time are The Q-Panel Company, 26200 First St., Cleveland OH 44145; Atlas
1
ThispracticeisunderthejurisdictionofASTMCommitteeD08onRoofingand Electric Devices Co., 4114 N. Ravenswood Ave., Chicago, IL 60613; Advanced
Waterproofing and is the direct responsibility of Subcommittee D08.02 on Prepared Coating Technologies Inc., 273 Industrial Dr. (PO Box 401), Hillsdale MI 49242.
Roofings, Shingles and Siding Materials. If you are aware of alternative suppliers, please provide this information toASTM
Current edition approved Sept. 15, 2007. Published September 2007. Originally International Headquarters. Your comments will receive careful consideration at a
1
approved in 1959. Last previous edition approved in 2003 as D1669–03. DOI: meeting of the responsible technical committee, which you may attend.
4
10.1520/D1669-07. The sole source of supply of the apparatus (Model B-81) known to the
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or committee at this time is Federal Products Corp., 1112 Eddy St., Providence, RI
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM 02901. If you are aware of alternative suppliers, please provide this information to
Standards volume information, refer to the standard’s Document Summary page on ASTM International Headquarters. Your comments will receive careful consider-
1
the ASTM website. ation at a meeting of the responsible technical committee, which you may attend.
Copyright © ASTM International, 100 Barr Harbor Drive, P
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D2829/D2829M-07(2023)(Practice)
Standard Practice for Sampling and Analysis of Existing Built-Up Roof Systems

SIGNIFICANCE AND USE
5.1 This practice is for the sampling and analysis of existing built-up roof systems. For roofs under construction, use Practice D3617/D3617M.
SCOPE
1.1 This practice is a guide for removing test specimens from existing built-up roofing systems in the field and for determining the approximate quantities of the components of that specimen (Note 1). Components determined may be:  
1.1.1 Insulation components when they are part of the roof membrane system,  
1.1.2 Plies of roofing felt,  
1.1.3 Interply layers of bituminous material,  
1.1.4 Top coating, and  
1.1.5 Surfacing.  
Note 1: This procedure is for the investigation of existing roofs and is not intended for new construction inspection.  
1.2 This practice is applicable to both 914 mm [36 in.] and 1000 mm [393/8 in.] wide felt rolls.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precautionary information, see 6.3.2.1.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM C1305/C1305M-16(2023)(Test Method)
Standard Test Method for Crack Bridging Ability of Liquid-Applied Waterproofing Membrane

SIGNIFICANCE AND USE
5.1 This test method is used to indicate a waterproofing membrane's ability to maintain its integrity while bridging a preexisting crack in the substrate at low ambient temperatures, when the membrane is least likely to be flexible.
SCOPE
1.1 This test method covers a laboratory procedure for determining the ability of a waterproofing membrane to bridge a crack in the substrate.  
1.2 There are no ISO standards similar or equivalent to this ASTM standard.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1306/C1306M-08(2023)(Test Method)
Standard Test Method for Hydrostatic Pressure Resistance of a Liquid-Applied Waterproofing Membrane

SIGNIFICANCE AND USE
5.1 This test method is used as a screening tool to determine the hydrostatic pressure to which a liquid-applied waterproofing membrane may be subjected without failing when stretched over a crack in the substrate. This test method discriminates between a membrane that is very resistant to hydrostatic pressure and one that is not. Because of the variability inherent in this test method, it is not recommended that this test method be used to set a numerical standard for hydrostatic pressure resistance. No prediction of durability at lower hydrostatic pressures can be made when using the results of this test method.
SCOPE
1.1 This test method describes a laboratory procedure for determining the resistance of a waterproofing membrane to hydrostatic pressure.  
1.2 The committee with jurisdiction over this standard is not aware of any comparable standards published by other organizations.  
1.3 There are no ISO standards similar or equivalent to this ASTM standard.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D3805/D3805M-16(2023)(Guide)
Standard Guide for Application of Aluminum-Pigmented Asphalt Roof Coatings

SIGNIFICANCE AND USE
3.1 Asphalt-based, solvent-type, fibered or nonfibered, aluminum-pigmented roof coatings are used as a protective coating for solar reflection to prolong the life of roofing materials or where decorative qualities are desired.  
3.2 Suitable application of aluminum-pigmented asphalt roof coatings is an important factor in achieving a successful long-term coating. Suitable application is, in part, dependent upon appropriate specifications to guide the work. This guide can be useful in facilitating development of an appropriate specification for surface preparation and application of the roof coating.  
3.3 Designers/specifiers of coatings may use this guide in preparing the application portion of their specification. Contractors working directly for the building owner may also use this guide.  
3.4 This guide is not all-inclusive. Manufacturer's application instructions should be consulted and geographical “area practices” considered. Consult membrane manufacturer and coating manufacturer for acceptability of procedures and products.
SCOPE
1.1 This guide covers the application methods for Specification D2824/D2824M Aluminum-Pigmented Asphalt Roof Coatings, Nonfibered, and Fibered without Asbestos, for application on asphalt built-up roof membranes, modified bitumen roof membranes, bituminous base flashings, concrete surfaces, metal surfaces, emulsion coatings, and solvent-based coatings. This guide does not apply to the selection of a specific aluminum-pigmented asphalt roof coating type for use on specific projects. The fibered version of these coatings excludes the use of asbestos fibers.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Section 4.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM D1669/D1669M-07(2023)(Practice)
Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings

SIGNIFICANCE AND USE
4.1 This practice for preparation of test panels greatly increases the likelihood of achieving reproducible results in subsequent testing.
SCOPE
1.1 This practice covers a procedure for the preparation of accelerated and outdoor weathering test panels of bituminous coatings. It is considered suitable for the preparation of film thicknesses in the range from 0.25 to 2.54 mm [0.010 to 0.100 in.].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet (MSDS) for details and EPA's website, http://www.epa.gov/mercury/faq.htm, for additional information. Users should be aware that selling mercury or mercury-containing products, or both, in your state may be prohibited by state law.)  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1670/D1670M-11(2023)(Test Method)
Standard Test Method for Failure End Point in Accelerated and Outdoor Weathering of Bituminous Materials

SIGNIFICANCE AND USE
4.1 The extent of cracking or pitting of bituminous films is a measure of the extent of deterioration due to weathering. Failure due to cracking is more accurately determined electrically than visually.  
4.2 Failure determined by this test method will depend not only on the characteristics of the bituminous material and the extent of weathering, but also on the film thickness, and the amount and type of mineral filler present.  
4.3 Tests on a similar material of known weathering characteristics (a control) exposed at the same time as the test material is strongly recommended as a check on the validity of the test results.
SCOPE
1.1 This test method covers the use of a spark-generating apparatus for determination of failure due to cracking of bituminous materials undergoing accelerated or outdoor weathering on electrically conductive backings.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D8051/D8051M-16(2023)(Specification)
Standard Specification for Wax-Modified Asphalt Used in Roofing

ABSTRACT
This specification establishes the manufacturing process and physical requirements for wax-modified asphaltic products intended for built-up roof construction, construction of bituminous vapor retarder systems, adhering fleece-backed single-ply roof membranes, and adhering insulation boards used in various types of roof systems. The base asphalt shall be prepared from lightly oxidized petroleum asphalt, and the wax-modified asphalt shall incorporate one or more high melt-point synthetic waxes. Furthermore, the products shall be homogeneous and free of water.
SCOPE
1.1 This specification covers wax-modified asphaltic products intended for use in built-up roof construction, construction of bituminous vapor retarder systems, adhering fleece-backed single-ply roof membranes, and adhering insulation boards used in various types of roof systems. The specification is intended for general classification purposes only, and does not imply restrictions on roofing system design, such as the slope at which this asphalt may be used.  
1.2 These products have lower application temperatures compared to products specified by Specification D312/D312M.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM D3423/D3423M-15(2023)(Practice)
Standard Practice for Application of Emulsified Coal-Tar Pitch (Mineral Colloid Type)

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D5727/D5727M, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D2746/D2746M-18(2023)(Test Method)
Standard Test Method for Staining Tendency of Asphalt (Stain Index)

SIGNIFICANCE AND USE
4.1 This test method measures the tendency for oil components to separate spontaneously from asphalt. The separation of oil components can cause staining in asphalt roofing products and adjacent materials in storage and use.  
4.2 The stain index is related to the thermal stability of the asphalt. Higher stain index values indicate lower stability and greater tendency for staining.  
4.3 Use this procedure to determine the staining tendency of asphalt and to compare the results against a material for which the staining tendency is known.
SCOPE
1.1 This test method covers the determination of the staining tendency of asphalt and the assignment of a stain index proportional to the extent of staining observed.  
1.2 This test method is applicable to asphalts having ring-and-ball softening points of 85 °C [185 °F] or greater.  
Note 1: This test method may be modified for use with other bituminous materials with softening points less than 85 °C [185 °F] by using a different temperature than specified in Section 7 by agreement of the interested parties. The report of results from such a test may cite this method but must clearly state the temperature employed in the exception and acknowledge that the interpretation of results in Section 9 and the precision and bias stated in Section 10 may not apply.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D5869/D5869M-07a(2023)(Practice)
Standard Practice for Dark Oven Heat Exposure of Roofing and Waterproofing Materials

SIGNIFICANCE AND USE
5.1 Roofing and waterproofing materials and systems undergo changes in physical properties as a result of being subjected to heat. They also undergo changes in physical properties as they age in service. Since service conditions vary widely, any relationship between changes observed in this practice and changes in service must be established by the user of this practice.
SCOPE
1.1 This practice establishes a procedure and conditions of temperature and time for heat exposure of roofing and waterproofing materials and systems in the presence of air.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off