ISO 9073-12:2002

Textiles — Test methods for nonwovens — Part 12: Demand absorbency

ISO 9073-12 describes a method for the evaluation of the absorbency of fabrics when one side is in contact with a liquid and the fabric is under mechanical pressure. This test is designed to allow comparison of absorbent materials such as nonwovens and is not intended to simulate in-use conditions of finished products. Demand absorbency is also called demand wettability.

Textiles — Méthodes d'essai pour nontissés — Partie 12: Absorption par contact unifacial

L'ISO 9073-12 décrit une méthode pour l'évaluation du pouvoir absorbant d'une étoffe soumise à une pression mécanique alors qu'une face est en contact avec un liquide. Cet essai vise à permettre de comparer des matériaux absorbants tels que les nontissés, et n'est pas destiné à simuler les conditions d'utilisation de produits finis. NOTE Le terme anglais «demand absorbency» est également connu sous le terme «demand wettability».

General Information

• Status: Published
• Publication Date: 29-Oct-2002
• ICS: 59.080.30 - Textile fabrics
• Technical Committee: ISO/TC 38 - Textiles
• Drafting Committee: ISO/TC 38 - Textiles
• Current Stage: 9093 - International Standard confirmed
• Start Date: 12-Jun-2025
• Completion Date: 12-Feb-2026

Overview

ISO 9073-12:2002 - Textiles - Test methods for nonwovens - Part 12: Demand absorbency defines a laboratory method to evaluate the demand absorbency (also called demand wettability) of fabrics and nonwoven materials. The test measures how much liquid a sample absorbs when one face is in contact with a liquid under a defined mechanical pressure. It is intended for comparative assessment of absorbent materials and not to simulate in-use conditions of finished products.

Key topics and technical requirements

• Principle: A test piece is placed on a specified porous plate connected by a siphon to a liquid reservoir. Absorption is recorded as the decrease in reservoir mass versus time.
• Measured outputs:
  • Maximum absorbed mass (A) - mass of liquid absorbed when mass change stabilizes.
  • Demand absorbency capacity (DAC) - A divided by sample mass (g/g).
  • Maximum absorption rate (MAR) - maximum absorption rate calculated over a 1 s period (g/s); special rules for very fast materials.
• Apparatus highlights:
  • Porous glass plate: ~60 mm diameter, 4 ± 1 mm thick, porosity rating 2 (4 µm–90 µm), target flow 2.5–3.5 g/s (see calibration Annex A).
  • Reservoir and siphon assembly with specified tube diameters and alignment.
  • Electronic balance accurate to 0.01 g and a data acquisition system capable of ≥4 readings/s (higher rates for very fast-absorbing materials).
  • Hydrophobic foam and cylindrical weight providing an imposed pressure of ~2.50 kPa (total weight ≈ 605 g).
• Procedure essentials: Cut conditioned 55 mm test pieces (five replicates), affix to foam/weight, start data acquisition, record reservoir mass until absorption stabilizes (mass change <1% over previous 5 s), compute A, DAC, MAR.
• Reporting: Include A vs. t data and curves, DAC and MAR individual results and statistics, test liquid identification (surface tension and temperature), any deviations.

Applications and users

ISO 9073-12 is used for:

• Comparative evaluation in R&D and quality control of nonwovens, wipes, absorbent hygiene components, medical textiles, filtration media and other absorbent substrates.
• Supplier qualification, material selection, benchmarking and product development where quantitative absorbency metrics (DAC, MAR) are required.

Typical users:

• Textile testing laboratories, nonwoven manufacturers, product R&D teams, standards and conformity assessment bodies.

Related standards

• Other parts of ISO 9073 (e.g., Part 1 mass per unit area; Part 6 absorption; Part 8 liquid strike-through).
• ISO 139 (conditioning atmospheres) and ISO 3696 (water for analytical use) are normative references used by this test method.

Keywords: ISO 9073-12:2002, demand absorbency, nonwovens test methods, DAC, MAR, absorbency testing, porous plate siphon, textile testing.

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 9073-12
First edition
2002-11-01
Textiles — Test methods for nonwovens —
Part 12:
Demand absorbency
Textiles — Méthodes d'essai pour nontissés —
Partie 12: Absorption par contact unifacial

Reference number
©
ISO 2002
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not
be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this
file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this
area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.

©  ISO 2002
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body
in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Printed in Switzerland
ii © ISO 2002 – All rights reserved

Contents Page
Foreword . iv
1 Scope. 1
2 Normative references. 1
3 Terms and definitions. 1
4 Principle . 2
5 Apparatus. 2
6 Assembly of the apparatus . 3
7 Preparation and conditioning of test pieces . 4
8 Procedure. 4
9 Expression of the results . 5
10 Test report. 8
Annex A (normative) Determination of flow through the porous medium using the data acquisition
system . 9
Annex B (informative) MAR calculation explanation . 11
Annex C (informative) Precision . 12

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
The main task of technical committees is to prepare International Standards. Draft International Standards adopted
by the technical committees are circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this part of ISO 9073 may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 9073-12 was prepared by Technical Committee ISO/TC 38, Textiles.
ISO 9073 consists of the following parts, under the general title Textiles — Test methods for nonwovens:
 Part 1: Determination of mass per unit area
 Part 2: Determination of thickness
 Part 3: Determination of tensile strength and elongation
 Part 4: Determination of tear resistance
 Part 6: Absorption
 Part 7: Determination of bending length
 Part 8: Determination of liquid strike-through time (simulated urine)
 Part 9: Determination of drape coefficient
 Part 10: Generation of lint and other particles in the dry state
 Part 11: Run-off
 Part 12: Demand absorbency
Annex A forms a normative part of this part of ISO 9073. Annexes B and C are for information only.

iv © ISO 2002 – All rights reserved

INTERNATIONAL STANDARD ISO 9073-12:2002(E)

Textiles — Test methods for nonwovens —
Part 12:
Demand absorbency
1 Scope
This part of ISO 9073 describes a method for the evaluation of the absorbency of fabrics when one side is in
contact with a liquid and the fabric is under mechanical pressure.
This test is designed to allow comparison of absorbent materials such as nonwovens and is not intended to
simulate in-use conditions of finished products.
NOTE Demand absorbency is also called demand wettability.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this part of ISO 9073. For dated references, subsequent amendments to, or revisions of, any of these publications
do not apply. However, parties to agreements based on this part of ISO 9073 are encouraged to investigate the
possibility of applying the most recent editions of the normative documents indicated below. For undated
references, the latest edition of the normative document referred to applies. Members of ISO and IEC maintain
registers of currently valid International Standards.
ISO 139:1973, Textiles — Standard atmospheres for conditioning and testing
ISO 3696:1987, Water for analytical laboratory use — Specification and test methods
3 Terms and definitions
For the purposes of this part of ISO 9073 the following terms and definitions apply.
3.1
maximum absorbed mass
A
f
mass of liquid absorbed, in grams, at time T , when the absorbed mass variation in the previous 5 s time period is
f
lower than 1 % of the absorbed mass corresponding to T
f
3.2
demand absorbency capacity
DAC
maximum absorbed mass of liquid, A , divided by the mass of the test piece, m, expressed in grams per gram
f
3.3
maximum absorption rate
MAR
maximum change in liquid absorbed mass per time interval, expressed in grams per second
NOTE The MAR is calculated over a 1 s time period from data recorded with sampling intervals of 0,25 s or less. The
maximum absorption rate is observed at the point of inflexion of the curve absorbed mass of liquid versus time.
4 Principle
The method measures the demand absorbency of a fabric under constant mechanical pressure. The test piece is
placed on a specified porous plate, which is connected by a siphon to a liquid reservoir. The level in the reservoir is
set below the upper surface of the porous plate. The demand absorbency is measured in terms of the change in
mass of the reservoir with time.
5 Apparatus
See Figure 1.
Dimensions in millimetres
Key
1 Cylindrical weight 5 Reservoir
2 Foam piece 6 Electronic balance
3 Sample 7 Data system
4 Porous glass plate
Figure 1 — Siphon assembly
2 © ISO 2002 – All rights reserved

5.1 Plain porous glass plate, diameter (60 ± 1) mm set into the top of a funnel which has a minimum outlet
diameter of (7,0 ± 0,2) mm. The plate (4 ± 1) mm thick has a porosity rating of 2 (4 µm to 90 µm) and a flow rate of
2,5 g/s to 3,5 g/s under the conditions specified in the calibration procedure (see annex A).
5.2 Glass reservoir, cylindrical, with a diameter W 80 mm.
5.3 Siphon assembly, consisting of a glass U-tube and a flexible silicone rubber tube each with an internal
diameter of (8,0 ± 0,2) mm (see Figure 1).
5.4 Electronic balance, to weigh the reservoir and its content, capable of determining the mass to an accuracy
of 0,01 g.
5.5 Data acquisition system, that allows the change of mass of the reservoir to be recorded against time (e.g.
microprocessing device, data analysis and printing device). If this is a digital system it shall be able to take
readings at least four times per second.
NOTE High absorbent rate materials may need readings taken eight times per second. (See 9.4, note 1.)
5.6 Hydrophobic polyether-polyurethane foam piece, (55 ± 1) mm in diameter and (2,0 ± 0,5) mm thick, with
20 regular open cells per centimetre and a density of (28 ± 3) kg/m .
5.7 Cylindrical weight, (60 ± 1) mm in diameter. The total mass of the weight and the foam piece shall be
(605 ± 5) g, which corresponds to an imposed pressure on the test piece of (2,50 ± 0,05) kPa.
5.8 Test liquid, normally demineralized water (in accordance with ISO 3696), but other appropriate liquids can
be used. The liquid used shall be specified and identified in the test report and used at temperature of (20 ± 2) ºC.
5.9 Cleaning product, e.g. sulfochromic acid (1/3 K Cr O at 50 g/l and 2/3 H SO at 95 %) or equivalent.
2 2 7 2 4
5.10 Spirit level.
6 Assembly of the apparatus
6.1 The layout of the apparatus is shown in Figure 1. The components shall be assembled according to the
dimensions given.
6.2 The hydrophobic foam (5.6) is attached to the bottom of the cylindrical weight (5.7) using hydrophobic
double-sided tapes so that the foam can be changed from time to time.
6.3 In order that the apparatus be filled with liquid without the ent
...

NORME ISO
INTERNATIONALE 9073-12
Première édition
2002-11-01
Textiles — Méthodes d'essai
pour nontissés —
Partie 12:
Absorption par contact unifacial
Textiles — Test methods for nonwovens —
Part 12: Demand absorbency
Numéro de référence
©
ISO 2002
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier peut
être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence autorisant
l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées acceptent de fait la
responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute responsabilité en la
matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info du
fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir l'exploitation de
ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation, veuillez en informer le
Secrétariat central à l'adresse donnée ci-dessous.

©  ISO 2002
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous quelque
forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit de l'ISO à
l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.ch
Imprimé en Suisse
ii © ISO 2002 – Tous droits réservés

Sommaire Page
Avant-propos . iv
1 Domaine d'application . 1
2 Références normatives. 1
3 Définitions. 1
4 Principe . 2
5 Appareillage. 2
6 Montage de l'appareillage . 3
7 Préparation et conditionnement des éprouvettes . 4
8 Mode opératoire . 4
9 Expression des résultats. 5
10 Rapport d'essai. 8
Annexe A (normative) Détermination du débit au travers de la plaque poreuse à l'aide du système
d'acquisition de données . 9
Annexe B (informative) Explication du calcul de la MAR . 11
Annexe C (informative) Précision . 12

Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 3.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur publication
comme Normes internationales requiert l'approbation de 75 % au moins des comités membres votants.
L'attention est appelée sur le fait que certains des éléments de la présente partie de l'ISO 9073 peuvent faire l'objet
de droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne pas
avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 9073-12 a été élaborée par le comité technique ISO/TC 38, Textiles.
L'ISO 9073 comprend les parties suivantes, présentées sous le titre général Textiles — Méthodes d'essai pour
nontissés:
 Partie 1: Détermination de la masse surfacique
 Partie 2: Détermination de l’épaisseur
 Partie 3: Détermination de la résistance à la traction et de l’allongement
 Partie 4: Détermination de la résistance à la déchirure
 Partie 6: Absorption
 Partie 7: Détermination de la longueur de flexion
 Partie 8: Détermination du temps de transpercement des liquides (urine artificielle)
 Partie 9: Détermination du coefficient de drapé
 Partie 10: Relargage de peluches et d'autres particules à l'état sec
 Partie 11: Écoulement sur plan incliné
 Partie 12: Absorption par contact unifacial
L’annexe A de la présente partie de l’ISO 9073 est donnée uniquement à titre d’information.
iv © ISO 2002 – Tous droits réservés

NORME INTERNATIONALE ISO 9073-12:2002(F)

Textiles — Méthodes d'essai pour nontissés —
Partie 12:
Absorption par contact unifacial
1 Domaine d'application
La présente partie de l'ISO 9073 décrit une méthode pour l’évaluation du pouvoir absorbant d’une étoffe soumise à
une pression mécanique alors qu’une face est en contact avec un liquide.
Le présent essai vise à permettre de comparer des matériaux absorbants tels que les nontissés, et n'est pas
destiné à simuler les conditions d'utilisation de produits finis.
NOTE Le terme anglais «demand absorbency» est également connu sous le terme «demand wettability».
2 Références normatives
Les documents normatifs suivants contiennent des dispositions qui, par suite de la référence qui y est faite,
constituent des dispositions valables pour la présente partie de l'ISO 9073. Pour les références datées, les
amendements ultérieurs ou les révisions de ces publications ne s'appliquent pas. Toutefois, les parties prenantes
aux accords fondés sur la présente partie de l'ISO 9073 sont invitées à rechercher la possibilité d'appliquer les
éditions les plus récentes des documents normatifs indiqués ci-après. Pour les références non datées, la dernière
édition du document normatif en référence s'applique. Les membres de l'ISO et de la CEI possèdent le registre des
Normes internationales en vigueur.
ISO 139:1973, Textiles — Atmosphères normales de conditionnement et d'essai
ISO 3696:1987, Eau pour laboratoire à usage analytique — Spécification et méthodes d'essai
3 Définitions
Pour les besoins de la présente partie de l’ISO 9073, les termes et définitions suivants s'appliquent.
3.1
masse maximale absorbée
A
f
masse de liquide absorbée, en grammes, au moment T , lorsque la variation de la masse absorbée au cours de la
f
période de 5 s précédente est inférieure à 1 % de la masse absorbée correspondant à T
f
3.2
capacité d'absorption par contact unifacial
DAC
masse maximale absorbée de liquide, A, divisée par la masse de l’éprouvette, m, exprimée en grammes par
f
gramme
3.3
vitesse maximale d'absorption
MAR
variation maximale de la masse de liquide absorbée par intervalle de temps, exprimée en grammes par seconde
NOTE La MAR est calculée sur une période de 1 s à partir des données enregistrées avec des intervalles de temps de
mesure de 0,25 s ou moins. La vitesse maximale d'absorption est observée au point d'inflexion de la courbe représentative de
la masse absorbée de liquide en fonction du temps.
4 Principe
La méthode permet de mesurer le pouvoir d'absorption par contact unifacial d'une étoffe soumise à une pression
mécanique constante. L’éprouvette est placée sur une plaque poreuse spécifiée, raccordée par un siphon à un
réservoir contenant le liquide. Le niveau du réservoir est situé au-dessous de la surface supérieure de la plaque
poreuse. Le pouvoir d'absorption par contact unifacial est mesuré par la variation de la masse du réservoir en
fonction du temps.
5 Appareillage
Voir la Figure 1.
5.1 Plaque en verre poreux, de (60 ± 1) mm de diamètre, placée à la partie supérieure d'un entonnoir
possédant un diamètre minimal d’embout de (7,0 ± 0,2) mm. La plaque, de (4 ± 1) mm d'épaisseur, possède un
degré de porosité de 2 (40 µm à 90 µm) et est susceptible de délivrer un débit de 2,5 g/s à 3,5 g/s dans les
conditions spécifiées dans la procédure d'étalonnage (voir l'annexe A).
5.2 Réservoir en verre, cylindrique, d'au moins 80 mm de diamètre.
5.3 Siphon, composé d’un tube de verre en U et d’un tuyau souple en caoutchouc de silicone, tous deux ayant
un diamètre intérieur de (8,0 ± 0,2) mm (voir la Figure 1).
5.4 Balance électronique, pour peser le réservoir et son contenu, capable de déterminer la masse avec une
précision de 0,01 g.
5.5 Système d'acquisition de données, permettant d'enregistrer le changement de masse du réservoir en
fonction du temps (par exemple un dispositif avec microprocesseur, analyse de données et imprimante). S'il s'agit
d'un système numérique, il doit être capable de recueillir des données au moins quatre fois par seconde.
NOTE Avec des matériaux à vitesse d'absorption élevée, il peut être nécessaire de recueillir des données huit fois par
seconde. (Voir 9.4, note 1.)
5.6 Pièce en mousse de polyéther-polyuréthanne hydrophobe, de (55 ± 1) mm de diamètre et de
(2,0 ± 0,5) mm d'épaisseur, avec 20 cellules ordinaires ouvertes par centimètre et une densité de (28 ± 3) kg/m .
5.7 Poids cylindrique, de (60 ± 1) mm de diamètre. La masse totale du poids et de la pièce en mousse doit être
de (605 ± 5) g, ce qui correspond à une pression imposée sur l’éprouvette de (2,50 ± 0,05) kPa.
5.8 Liquide d'essai, normalement de l'eau déminéralisée (conformément à l'ISO 3696), mais d'autres liquides
adéquats peuvent être utilisés. Le liquide employé doit être spécifié et décrit dans le rapport d'essai et utilisé à une
température de (20 ± 2) °C.
5.9 Produit de nettoyage, par exemple de l'acide sulfochromique (1/3 K Cr O à 50 g/l et 2/3 H SO à 95 %)
2 2 7 2 4
ou équivalent.
5.10 Niveau à bulle.
2 © ISO 2002 – Tous droits réservés

6 Montage de l'appareillage
6.1 Le schéma de montage de l'appareillage est représenté à la Figure 1. Les pièces doivent être assemblées
conformément aux dimensions spécifiées.
Dimensions en millimètres
Légende
1 Poids cylindrique 5 Réservoir
2 Pièce en mousse 6 Balance électronique
3 Échantillon 7 Système d'acquisition de données
4 Plaque en verre poreux
Figure 1 — Schéma de montage de l’appareillage

6.2 La mousse hydrophobe (5.6) est fixée à la base du poids cylindrique (5.7) avec des rubans adhésifs
hydrophobes à double face, de manière à pouvoir remplacer la mousse périodiquement.
6.3 Pour remplir l'appareillage avec le liquide sans formation de bulles d'air, s'assurer que tous les tubes sont
remplis, puis les connecter, sous l’eau, à l'entonnoir supporta
...