ISO 5082:1982
(Main)Textiles — Woven fabrics — Determination of breaking strength — Grab method
Textiles — Woven fabrics — Determination of breaking strength — Grab method
Textiles — Tissus — Détermination de la force de rupture — Méthode d'arrachement
General Information
Relations
Buy Standard
Standards Content (Sample)
International Standard 5082
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONOME~YHAPOAHAR OPrAHH3AlAHR Il0 CTAHAAPTH3A~MH~RGANlSATlON INTERNATIONALE DE NORMALISATION
Textiles - Woven fabrics - Determination of breaking
19
strength - Grab method
Textiles - Tissus - Détermination de la force de rupture - Méthode d'arrachement
First edition - 1982-12-01
üi UDC Wï.064 : 677.017.424.23 Ref. No. ISO!W2-1982(E)
-
Descriptors : textiles, woven fabrics, tests, tension tests, determination, tensile strength, test specimen conditioning, test equipment.
s Price based on 7 pages
---------------------- Page: 1 ----------------------
Fo rew o rd
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 5082 was developed by Technical Committee ISO/TC 38,
Textiles, and was circulated to the member bodies in September 1981.
It has been approved by the member bodies of the following countries :
South Africa, Rep. of
Belgium Israel
Italy Spain
Canada
Sri Lanka
China Japan
Korea, Rep. of Sweden
Czechoslovakia
Switzerland
Egypt, Arab Rep. of Netherlands
New Zealand Turkey
Finland
United Kingdom
Hungary Norway
Poland Yugoslavia
India
Iraq Portugal
Romania
Ireland
The member bodies of the following countries expressed disapproval of the document
on technical grounds :
France
USA
USSR
O International Organization for Standardization, 1982 0
Printed in Switzerland
---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD IS0 5082-1982 (E)
Determination of breaking
Textiles - Woven fabrics -
strength - Grab method
1 Scope and field of application 2 References
IS0 139, Textiles - Standard atmospheres for conditioning
1 .I This International Standard specifies a method, known
and testing.
as the "grab" method, for the determination of the breaking
strength of woven textile fabrics.
IS0 2602, Statistical interpretation of test results - Estimation
of the mean - Confidence interval.
NOTE - The determination of breaking strength using the "strip"
IS0 5081 .I) There is no simple relationship between
method is given in
results given by grab tests and those given by strip tests because the
3 Definitions
amount of assistance provided by the adjacent yarns depends on the
type of weave, construction, mobility of yarns, and other factors.
For the purpose of this International Standard, the following
definitions apply.
1.2 The method is applicable to unimpregnated fabrics and
to fabrics that have been impregnated with sizing or stiffening
3.1 breaking strength : The maximum tensile force ob-
materials, but not to fabrics coated with rubber or plastics.2)
sewed during a test in which the specimen is stretched until it
breaks.
1.3 The method provides for the determination of the break-
ing strength of specimens in equilibrium with the standard at-
3.2 grab test : A breaking strength test in which only the
mosphere for testing and of specimens in the wet state.
centre part of the width of the specimen is gripped in the jaws.
1.4 The method authorizes the use of the following types of
3.3 nominal gauge length : The length of a specimen
testing machine in common use for measuring the breaking under specified pre-tension, measured from nip to nip of the
strength of fabrics :
jaws of the holding clamps in their starting position.
ai constant-rate-of-specimen-extension (CRE) (see
3.4 time-to-break : The interval, measured in suitable units
clause 5 and annex A, clause A.1);
such as seconds, during which the specimen is under a
(generally increasing) tension, i.e. absorbing the energy sup-
b) constant-rate-of-traverse (CRT) (see clause 5 and
plied before the breaking force is reached.
annex A, clause A.2);
NOTE - Time-to-break does not include the time required to remove
constant-rate-of-load (CRL) (see clause 5 and annex A,
c)
slack from the specimen. On machines supplied with an autographic
clause A.3).
recorder, the time-to-break is indicated by the time elapsing after the
pen registers the initial force sustained by the specimen until the pen
The three types of testing machine do not necessarily give the
registers the maximum force.
same results for the same fabric. The type of tester to be used
must, therefore, be agreed upon by all parties interested in the
test results, and must be reported. As it has been found that
4 Principle
the breaking strengths obtained on different types of tester
agree best when the time-to-break is the same, the method
4.1 Breaking strength
provides for testing at a specific time-to-break (see 4.2) and
rates of extension, traverse, or loading are not specified.
An increasing force is applied (until break occurs) by a suitable
mechanical means that indicates the maximum force up to
NOTE - When the time-to-break has been the same, excellent ex-
break. The testing machine is operated at such a rate that the
perimental agreement has been reported between results obtained with
average time-to-break of a group of specimens falls within
CRE and CRT testers, but results given by CRL testers have in some
cases been reported to differ somewhat from the other results. specified time limits.
II IS0 5081, Textiles - Woven fabrics - Determination of breaking strength and elongation (Strip method).
2) The determination of breaking strength and elongation at break of fabrics coated with rubber or plastics is dealt with in IS0 1421, Determination
of breaking strength and elongation at break of fabrics coated with rubber or plastics.
1
---------------------- Page: 3 ----------------------
IS0 5082-1982 (E)
rates can be obtained most readily by means of a continuously
4.2 Time-to-break
variable drive, but satisfactory results can be obtained by
means of a series of steps, provided that the latter are small
Unless otherwise agreed upon by the parties interested in the
test results, the specified period for the average time-to-break enough. The ratio between the rates produced by consecutive
steps should not exceed 125 : 100.
shall be either 20 tr 3 s or 30 I 5 s.
5.2 Equipment in which specimens can be immersed in
5 Apparatus
water preparatory to wet testing (see 8.4).
5.1 Tensile testing machine meeting the following re-
5.3 Equipment for cutting specimens.
quirements :
5.1.1 Type
5.4 Stop-watch or interval-timer.
The type of machine shall be one of those described in annex
5.5 Distilled or de-ionized water for wetting out
A, as mutually agreed upon by the parties interested in the test
specimens.
resu Its.
5.1.2 Machine requirements
Wetting agent or surfactant, non-ionic.
5.6
O
The tensile testing machine shall include a pair of clamps
suitable for gripping the specimen, and a force-indicating
6 Atmospheres for testing
mechanism which will indicate (or record) continuously the
force applied to the specimen.
6.1 Standard atmosphere for testing
5.1.3 Accuracy of recorder
The standard temperate atmosphere for testing has a relative
humidity (RH) of 65 * 2 % at a temperature of 20 & 2 OC.
The dynamic response rate of the recorder shall be sufficiently
The standard tropical atmosphere for testing has the same
rapid to ensure that the maximum error of the indicated force at
relative humidity and a temperature of 27 I 2 OC (see
any point in the range in which the machine is used does not
IS0 139).
exceed 1 %. Before use, verify the accuracy of the graduated
scale of the apparatus dynamically.
6.2 Pre-conditioning atmosphere
5.1.4 Gauge length
Suitable atmospheres and procedures for pre-conditioning are
The testing machine shall be capable of testing specimens that
specified in IS0 139.
have a nominal gauge length of 75 mm.
NOTE - Air at 20 OC and 65 % RH has a water vapour pressure of
1 515 Pa* and when heated to 47 + 2 OC will produce an atmosphere
5.1.5 Jaws
having an RH of 12,3 % to 16.7 %. Air at the maximum permissible
of 22 OC and 67 YO RH has a vapour pressure of 1 700 Pa, and
limits
The central points of the two jaws of the machine shall be in the
e
when heated to 50 OC has an RH in the range of 14.3 YO to 19,4 %. If it
line of pull, the front edges shall be at right angles to the line of
is desired to keep the RH below 10 % and not to exceed a temperature
pull, and their clamping faces shall be so aligned as to maintain
of 50 OC, the original air must have a water vapour pressure below
specimens in a plane. The jaws of the clamps shall be capable
1 230 Pa (equivalent to 53 YO RH at 20 OC or 30 % RH at 27 OC).
of holding the specimens without slippage and without causing
apparent damage.
7 Samples
The size of one jaw of each clamp shall be 25 mm x 25 mm;
the other jaw of each clamp shall be at least as large as its mate.
7.1 Both bulk samples and laboratory samples shall be taken
The gripping faces of the jaws shall, preferably, be smooth and
in one of the following ways, as appropriate :
flat, but when the specimens under test cannot be satisfactorily
held with unlined flat faced jaws, jaws with lined or engraved
a) according to the directions given in the relevant material
faces may be used. (Suitable lining materials include paper,
specification;
felt, leather, plastics, and sheet rubber.)
b) if directions for sampling are not included in the
5.1.6 Rates of operation
material specification, according to the procedures ap-
proved by IS0 for textile products;
All testing machines shall include facilities for producing such
different constant rates of operation as will allow specimens to
c) if neither a) nor b) is applicable, according to the
be broken in the applicable average time-to-break, i.e. unless
method given in annex B.
otherwise agreed (see 4.2) 20 I 3 s or 30 I 5 s. Different
li 1 Pa = 1 N/m2
2
---------------------- Page: 4 ----------------------
IS0 5082-1982 (E)
8.4.2 The wet test specimens shall be laid on the surface of
7.2 Laboratory samples shall be conditioned as follows :
distilled or de-ionized water at a temperature between 17 and
30 OC, until they sink under their own weight, but if this period
7.2.1 Except in the case of heat-sensitive materials, the
exceeds 2 h, they shall be forcibly immersed in the water for at
laboratory samples from which specimens are to be taken shall
least a further 1 h.
be pre
...
38
= J internationale
Norm
INTERNATIONAL ORGANIZA >N FOR STANDARDIZATlON*MEWYHAPO)lHAfl OPrAHHBAUMR il0 CTAHLlAPTH3AUHM*ORGANlSATlON INTERNATIONALE DE NORh
Textiles - Tissus - Détermination de la force de
I)
-
Méthode d'arrachement
rupture -
ics - Determination of breaking strength - Grab method
Textiles - Woven fa,
Première éditior - 1982-12-01
- G CDU 677.064:6; '. O1 7.424.23
Réf. no : IS0 5082-1
SI
Descripteurs : textile, su, essai, essai de traction, détermination, résistance à la traction, préparation de spécimen d'essai, matéri
c
s
Prix basé SU
---------------------- Page: 1 ----------------------
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO.
La Norme internationale IS0 5082 a été élaborée par le comité technique ISO/TC 38,
Textiles, et a été soumise aux comités membres en septembre 1981.
Les comités membres des pays suivants l'ont approuvée :
Afrique du Sud, Rép. d' Iraq Roumanie
Belgique Irlande Royaume-Uni
Israël Sri Lanka
Canada
Chine Italie Suède
Corée, Rép. de Japon Suisse
Égypte, Rép. arabe d' Norvège Tchécoslovaquie
Nouvelle-Zélande Turquie
Espagne
Finlande Pays-Bas Yougoslavie
Hongrie Pologne
Inde Portugal
Les comités membres des pays suivants l'ont désapprouvée pour des raisons techni-
ques :
France
URSS
USA
4
---------------------- Page: 2 ----------------------
NORME INTER ATIONALE IS0 5082 982 (FI
c
Tissus - Détermination de la force de
Textiles
rupture Méthode d'arrachement
f
constaté que les valeurs de la force de rupture déterr iées sur
les différents appareils sont plus concordantes IorsqL la durée
d'essai de rupture est la même, la méthode prescrit e durée
d'essai de rupture spécifique (voir 4.21, et les vitesses allonge-
ment de l'éprouvette, de déplacement de la pince de ction et
d'accroissement de la force ne sont pas spécifiées.
rce de rupture par la méthode «sur
NOTE - Lorsque la durée d'essai de rupture est la même es essais
1.1) Il n'y a pas de relation simple
expérimentaux montrent une excellente concordance entr es résul-
sai d'arrachement et ceux obtenus
tats obtenus au moyen de l'appareil à vitesse constante d'a ngement
ue la force de rupture additionnelle
de l'éprouvette et celui à vitesse constante de déplacement ! la pince
d'armure, de la construction, de la
au moyen de l'appareil à vi se cons-
de traction, mais ceux obtenus
tante d'accroissement de la force montrent que, dans cert s cas, 11s
res types
diffèrent quelque peu de ceux obtenus au moyen des deux t
d'appareils.
2 Références
itionne-
IS0 139, Textiles - Atmosphères normales de CO
ment et d'essai.
IS0 2602, Interprétation statistique de résultats d sais -
Estimation de la moyenne - Intervalle de confiance
1.4 La méthod l'utilisation des types d'appareils sui-
nt utilisés pour la détermination de la
3 Définitions
force de rupture
Dans le cadre de la présente Norme internationale, défini-
tions suivantes sont applicables.
,
3.1 force de rupture : Force maximale observé1
l'essai de traction au cours duquel l'éprouvette
jusqu'à sa rupture.
3.2 essai d'arrachement : Essai de résistance à
dans lequel seule la partie centrale de la largeur de I't
est serrée dans les mâchoires de l'appareil.
3.3 longueur nominale d'essai : Longueur de I'é
sous une tension préalable spécifiée, mesurée entre If
res des pinces mises en position de démarrage de I'
force de rupture et de l'allongement de rupture (Méthode sur bande).
l'allongement à la rupture des tissus revêtus de caoutchouc ou de plastique fa
de plastique - Détermination de la résistance à la rupture et de l'allongement i
---------------------- Page: 3 ----------------------
IS0 5082-1982 (FI
3.4 durée d’essai de rupture : Intervalle de temps, mesuré 5.1.5 Mâchoires
dans une unité appropriée telle que la seconde, durant lequel
l‘éprouvette est soumise à une tension (généralement crois- La ligne passant par le centre des deux mâchoires de l‘appareil
doit être dans l‘alignement du sens de traction, les bords exté-
sante), c’est-à-dire absorbe l’énergie fournie avant que la force
rieurs des mâchoires doivent être perpendiculaires au sens de
de rupture ne soit atteinte.
traction et leurs faces de serrage doivent être alignées de
manière que les éprouvettes soient maintenues dans un même
NOTE - La durée d‘essai de rupture ne comprend pas le temps néces-
saire à la mise sous tension préalable de l’éprouvette. Sur les appareils
plan. Les mâchoires des pinces doivent permettre le serrage des
munis d‘un enregistreur graphique, la durée d’essai de rupture est indi-
éprouvettes sans les laisser glisser et sans les endommager de
quée par le temps s’écoulant entre le moment où la plume enregistre la
façon apparente.
force initiale supportée par l’éprouvette et le moment où la plume enre-
gistre la force maximale.
Les dimensions de l’une des mâchoires de chaque pince doi-
vent être de 25 mm x 25 mm; l‘autre mâchoire de chaque
pince doit être au moins aussi large que celle avec laquelle elle
4 Principe
est couplée. Les faces de serrage des mâchoires doivent être,
de préférence, lisses et plates, mais lorsque les éprouvettes
soumises à l’essai ne peuvent être maintenues de façon satisfai-
4.1 Résistance de rupture
sante dans les mâchoires lisses des pinces, des mâchoires dont
les faces sont garnies ou gravées ou corrodées peuvent être uti-
Application d’une force croissante (jusqu’à ce qu’il y ait rup-
lisées. (Pour le garnissage des faces des mâchoires, il est possi-
ture) au moyen d’un dispositif mécanique approprié qui indique
ble d’utiliser du papier, du feutre, du cuir, des feuilles de caout-
la force maximale provoquant la rupture. L‘appareil d’essai doit
chouc.)
permettre d’opérer à une vitesse telle que la durée moyenne
d’essai de rupture d’un certain nombre d’éprouvettes se situe
dans les limites de la durée spécifiée.
5.1.6 Vitesses d‘essai
4.2 Durée d’essai de rupture
Tous les appareils d‘essai doivent être munis de dispositifs per-
mettant d’opérer à différentes vitesses, de manière que les
À moins d’un autre accord entre les parties intéressées aux
éprouvettes essayées puissent être rompues dans la durée
résultats de l’essai, la durée moyenne d‘essai de rupture spéci-
moyenne d’essai de rupture spécifiée, c’est-à-dire, sauf autre
fiée est de 20 f. 3 s ou de 30 k 5 s.
accord (voir 4.21, 20 f 3 s ou 30 _+ 5 s. Les différentes vites-
ses peuvent être obtenues aisément au moyen de variateurs de
vitesse, mais on obtient des résultats satisfaisants au moyen
5 Appareillage d’une série de paliers successifs, pourvu que le dernier soit suf-
fisamment petit. La variation de vitesse produite par l’emploi de
deux paliers successifs ne doit pas excéder 125 : 100.
5.1 Appareil d’essai de traction correspondant aux spécifi-
cations suivantes :
Récipient pour l‘immersion des éprouvettes dans
5.2
5.1.1 Type l‘eau, en vue de l‘essai au mouillé (voir 8.4).
Le type d’appareil à utiliser doit être l‘un de ceux décrits dans
5.3 Matériel nécessaire au prélèvement des éprouvet-
l’annexe A, selon accord préalable entre les parties intéressées
tes.
aux résultats de l’essai.
5.1.2 Caractéristiques de l‘appareil
5.4 Compte-secondes ou chronomètre.
L’appareil d’essai de traction doit comprendre une paire de pin-
ces permettant une fixation convenable de l’éprouvette et un
Eau distillée ou déionisée, pour le mouillage des éprou-
5.5
dispositif indiquant (ou enregistrant), d’une manière continue,
vettes.
la force appliquée à l’éprouvette.
5.6 Agent mouillant ou surfactif, non ionique.
5.1.3 Précision d‘enregistrement
La vitesse d’enregistrement doit être suffisamment rapide pour
que l‘erreur maximale sur l’enregistrement de la force en tout
6 Atmosphères d‘essai
point du champ d’application de l‘appareil n’excède pas 1 %.
Avant utilisation, vérifier la précision de l’échelle graduée de
l‘appareil d’une manière dynamique.
6.1 Atmosphère normale d’essai
L’atmosphère tempérée normale d‘essai a une humidité relative
5.1.4 Longueur d‘essai
de 65 f 2 % à une température de 20 f 2 OC. L’atmosphère
tropicale normale d‘essai a la même humidité relative et une
L’appareil doit permettre d‘essayer des éprouvettes ayant une
longueur nominale d’essai de 75 mm. température de 27 _+ 2 OC (voir IS0 f31.
2
---------------------- Page: 4 ----------------------
6.2 Atmosphèi de conditionnement préalable
Les atmosphères e es modes de conditionnement convena-
bles sont spécifiés Ins I'ISO 139.
vent être aussi représentatives que possible de
Deux éprouvettes ne doivent pas contenir les mê
NOTE - L'air à la ten Brature de 20 OC et ayant une humidité relative
de 65 % a une pressic en vapeur d'eau de 1 515 Pa* et, lorsqu'il est
chauffé à 47 f 2 OC, mne une atmosphère ayant une humidité rela-
tive de 12,3 % à 16.7 . L'air aux conditions limites possibles de 22 OC
et 67 YO d'humidité re1 ive a une pression en vapeur d'eau de 1 700 Pa
et, lorsqu'il est chauR à 50 OC, a une humidité relative de 14,3 % à
19,4 %. Si l'on désire aintenir l'humidité relative au-dessous de 10 %
température de 50 OC, l'atmosphère originale
et ne pas dépasser Ur
doit avoir une pressioi tn vapeur d'eau au-dessous de 1 230 Pa (équi-
doivent être effectués dans l'atmosphère normale
B relative à 20 OC ou à 30 YO d'humidité relative
valant à 53 YO d'hurnic
A 27 OC).
8.2 Dimensions
7 Échantillon
7.1 Leséchantillc j globaux et les échantillons pour labora-
toire doivent être p levés de l'une des manières suivantes, la
mieux appropriée :
8.3 Préparation
a) selon les dir :tives données dans les spécifications du
Sur chaque éprouvette, des lignes doivent 6
matériau essayé
distance de 38 mm de chaque bord, parall
chaîne ou au sens trame, selon le cas, et sur
b) si les directi 8s pour l'échantillonnage ne sont pas don-
de l'éprouvette.
nées dans les pécifications du matér
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.