ISO 3384-1:2019

Rubber, vulcanized or thermoplastic — Determination of stress relaxation in compression — Part 1: Testing at constant temperature

This document specifies two procedures for determining the decrease in counterforce exerted by a test piece of vulcanized or thermoplastic rubber which has been compressed to a constant deformation and maintained thus at a predetermined test temperature. The counterforce can be determined either by means of a continuous-measurement system or by a discontinuous-measurement one. Two test methods are specified, method A and method B. In method A the compression and all measurements of counterforce are made at test temperature and in method B the compression and all measurements of counterforce are made at standard laboratory temperature. Method A and method B do not give the same results, as in method B the shrinkage of the material from the test temperature to standard laboratory temperature is included in the result. Two forms of test piece are specified in this document: cylindrical test pieces and rings. Comparison of results is valid only when made on test pieces of similar size and shape. The use of ring test pieces is particularly suitable for the determination of stress relaxation in liquid environments. This document deals only with testing at constant ambient or elevated temperature. Testing at temperatures below standard laboratory temperature is not specified. The methods have been used for low‑temperature testing, but their reliability under these conditions is not proven.

Caoutchouc vulcanisé ou thermoplastique — Détermination de la relaxation de contrainte en compression — Partie 1: Essais à température constante

Le présent document spécifie deux modes opératoires de détermination de la diminution de la force de réaction exercée par une éprouvette de caoutchouc vulcanisé ou thermoplastique comprimée sous déformation constante et maintenue ainsi à une température d'essai prédéterminée. La force de réaction peut être déterminée au moyen d'un système de mesure continue ou d'un système de mesure discontinue. Deux méthodes d'essai sont spécifiées, la méthode A et la méthode B. Dans la méthode A, la compression et tous les mesurages de force de réaction sont réalisés à la température d'essai et dans la méthode B, la compression et tous les mesurages de force de réaction sont réalisés à la température normale de laboratoire. La méthode A et la méthode B ne donnent pas les mêmes résultats, car dans la méthode B, la rétraction thermique du matériau lors du passage de la température d'essai à la température normale de laboratoire est inclus dans le résultat. Deux formes d'éprouvette sont spécifiées dans le présent document: éprouvettes cylindriques et annulaires. La comparaison des résultats n'est valable que si elle est faite pour des éprouvettes de taille et de forme similaires. L'utilisation d'éprouvettes annulaires convient tout particulièrement à la détermination de la relaxation de contrainte dans des environnements liquides. Le présent document traite uniquement des essais à température constante, ambiante ou élevée. Les essais à des températures inférieures à la température normale de laboratoire ne sont pas spécifiés. Les méthodes ont été mises en œuvre pour des essais à basse température, mais leur fiabilité n'est toutefois pas prouvée dans ces conditions.

General Information

• Status: Withdrawn
• Publication Date: 13-Aug-2019
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 2 - Visco-elastic properties
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 08-Mar-2024

Relations

• Revised: ISO 3384-1:2024 - Rubber, vulcanized or thermoplastic — Determination of stress relaxation in compression — Part 1: Testing at constant temperature
• Effective Date: 04-Feb-2023
• Revises: ISO 3384-1:2011 - Rubber, vulcanized or thermoplastic — Determination of stress relaxation in compression — Part 1: Testing at constant temperature
• Effective Date: 10-Dec-2016
• Revises: ISO 3384-1:2011/Amd 1:2013 - Rubber, vulcanized or thermoplastic — Determination of stress relaxation in compression — Part 1: Testing at constant temperature — Amendment 1: Revised calibration schedule
• Effective Date: 10-Dec-2016

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 3384-1
Second edition
2019-08
Rubber, vulcanized or
thermoplastic — Determination of
stress relaxation in compression —
Part 1:
Testing at constant temperature
Caoutchouc vulcanisé ou thermoplastique — Détermination de la
relaxation de contrainte en compression —
Partie 1: Essais à température constante
Reference number
ISO 3384-1:2019(E)
©
ISO 2019

---------------------- Page: 1 ----------------------
ISO 3384-1:2019(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2019
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting
on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address
below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Fax: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii © ISO 2019 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 3384-1:2019(E)

Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 2
4 Principle . 2
5 Apparatus . 2
6 Calibration . 4
7 Test piece . 4
7.1 Type and preparation of test pieces . 4
7.1.1 General. 4
7.1.2 Cylindrical test pieces . 4
7.1.3 Ring test pieces. 4
7.2 Measurement of dimensions of test pieces . 4
7.3 Number of test pieces . 5
7.4 Time interval between forming and testing . 5
7.5 Conditioning of test pieces . 5
8 Duration, temperature and test liquid . 5
8.1 Duration of test .
...

NORME ISO
INTERNATIONALE 3384-1
Deuxième édition
2019-08
Caoutchouc vulcanisé ou
thermoplastique — Détermination
de la relaxation de contrainte en
compression —
Partie 1:
Essais à température constante
Rubber, vulcanized or thermoplastic — Determination of stress
relaxation in compression —
Part 1: Testing at constant temperature
Numéro de référence
ISO 3384-1:2019(F)
©
ISO 2019

---------------------- Page: 1 ----------------------
ISO 3384-1:2019(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2019
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
Fax: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii © ISO 2019 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 3384-1:2019(F)

Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d'application . 1
2 Références normatives . 1
3 Termes et définitions . 2
4 Principe . 2
5 Appareillage . 3
6 Étalonnage . 4
7 Éprouvette . 4
7.1 Type et préparation des éprouvettes . 4
7.1.1 Généralités . 4
7.1.2 Éprouvettes cylindriques . 4
7.1.3 Éprouvettes annulaires . 4
7.2 Mesurage des dimensions des éprouvettes . . 5
7.3 Nombre d'éprouvettes . 5
7.4 Délai entre fabrication et essais . 5
7.5 Conditionnement des éprouvettes . 5
8 Durée, température et liquide d'essai . 6
8.1 Durée de l'essai .
...