ISO 8502-2:2005

Preparation of steel substrates before application of paints and related products — Tests for the assessment of surface cleanliness — Part 2: Laboratory determination of chloride on cleaned surfaces

ISO 8502-2:2005 describes a method for the determination of chloride-containing salts that are readily soluble in water and are present on a steel surface. The method is also applicable to previously coated surfaces. It will normally be used in a laboratory using washings sampled from surfaces on site. ISO 8502-2:2005 is applicable to the determination of salts that have been deposited on the steel surface before, during or after the cleaning operations. ISO 8502-2:2005 is not applicable to surfaces treated with chromate, nitrite or amine, which are commonly used as inhibitors in the water when wet blast-cleaning. This is because a chromate concentration of 10 mg/l or greater or a nitrite concentration of 20 mg/l or greater in the wash water interferes with the determination of the chloride. Also the amine inhibitors can form a hydroxide boundary layer (not water soluble) over the substrate and prevent the water from contacting the underlying salt for its removal. An iron(III) ion concentration of 10 mg/l also interferes with the determination, but the iron(III) ions are concentrated in the rust deposits, which are removed from the test solution by filtration.

Préparation des subjectiles d'acier avant application de peintures et de produits assimilés — Essais pour apprécier la propreté d'une surface — Partie 2: Recherche en laboratoire des chlorures sur les surfaces nettoyées

L'ISO 8502-2:2005 décrit une méthode de recherche des sels contenant des chlorures solubles dans l'eau et présents à la surface d'un subjectile d'acier. Cette méthode est également applicable à des surfaces qui ont déjà été revêtues. Elle doit être normalement utilisée dans un laboratoire sur des eaux de lavage échantillonnées à partir de surfaces in situ. L'ISO 8502-2:2005 est applicable à la recherche de sels ayant été déposés à la surface du subjectile avant, pendant ou après le nettoyage. L'ISO 8502-2:2005 ne s'applique pas aux surfaces traitées avec des chromates, des nitrites ou de l'amine, qui sont couramment utilisés comme inhibiteurs lorsqu'on pratique le sablage humide. En effet une concentration de chromates de 10 mg/l ou plus ou une concentration de nitrites de 20 mg/l ou plus dans l'eau de lavage interfère avec la recherche des chlorures. De plus, les inhibiteurs de l'amine peuvent entraîner la formation d'une couche limite d'hydroxyde (non soluble dans l'eau) sur le subjectile, empêchant ainsi l'eau de pouvoir atteindre le sel situé en dessous. Une concentration d'ions fer(III) de 10 mg/l interfère également avec la recherche des chlorures, mais les ions fer(III) sont concentrés dans les dépôts de rouille que l'on enlève de la solution d'essai par filtration.

General Information

• Status: Withdrawn
• Publication Date: 13-Oct-2005
• Withdrawal Date: 13-Oct-2005
• ICS: 25.220.10 - Surface preparation
• Technical Committee: ISO/TC 35/SC 12 - Preparation of steel substrates before application of paints and related products
• Drafting Committee: ISO/TC 35/SC 12/WG 2 - Surface cleanliness
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 10-Jan-2017

Relations

• Revised: ISO 8502-2:2017 - Preparation of steel substrates before application of paints and related products — Tests for the assessment of surface cleanliness — Part 2: Laboratory determination of chloride on cleaned surfaces
• Effective Date: 22-Jan-2011
• Consolidates: ISO/IEC TR 9126-3:2003 - Software engineering — Product quality — Part 3: Internal metrics
• Effective Date: 06-Jun-2022
• Revises: ISO 8502-2:1992 - Preparation of steel substrates before application of paints and related products — Tests for the assessment of surface cleanliness — Part 2: Laboratory determination of chloride on cleaned surfaces
• Effective Date: 15-Apr-2008

Standards Content (Sample)

МЕЖДУНАРОДНЫЙ ISO
СТАНДАРТ
8502-2
Второеиздание
2005-10-15
Исправленная версия
2006-01-15

Подготовка стальной поверхности
перед нанесением красок и
относящихся к ним продуктов.
Испытания для оценки чистоты
поверхности.
Часть 2.
Лабораторное определение
содержания хлорида на очищенных
поверхностях
Preparation of steel substrates before application of paints and related
products – Tests for the assessment of surface cleanliness –
Part 2: Laboratory determination of chloride on cleaned surfaces



Ответственность за подготовку русской версии несёт GOST R
(Российская Федерация) в соответствии со статьёй 18.1 Устава ISO
Ссылочный номер
ISO 8502-2:2005(R)
©
ISO 2005

---------------------- Page: 1 ----------------------
ISO 8502-2:2005(R)
Отказ от ответственности при работе в PDF
Настоящий файл PDF может содержать интегрированные шрифты. В соответствии с условиями лицензирования, принятыми
фирмой Adobe, этот файл можно распечатать или смотреть на экране, но его нельзя изменить, пока не будет получена
лицензия на интегрированные шрифты и они не будут установлены на компьютере, на котором ведется редактирование. В
случае загрузки настоящего файла заинтересованные стороны принимают на себя ответственность за соблюдение
лицензионных условий фирмы Adobe. Центральный секретариат ISO не несет никакой ответственности в этом отношении.
Adobe - торговый знак фирмы Adobe Systems Incorporated.
Подробности, относящиеся к программным продуктам, использованные для создания настоящего файла PDF, можно найти в
рубрике General Info файла; параметры создания PDF были оптимизированы для печати. Были приняты во внимание все
меры предосторожности с тем, чтобы обеспечить пригодность настоящего файла для использования комитетами-членами
ISO. В редких случаях возникновения проблемы, связанной со сказанным выше, просьба проинформировать Центральный
секретариат по адресу, приведенному ниже.


ДОКУМЕНТ ЗАЩИЩЕН АВТОРСКИМ ПРАВОМ


© ISO 2005
Все права сохраняются. Если не указано иное, никакую часть настоящей публикации нельзя копировать или использовать в
какой-либо форме или каким-либо электронным или механическим способом, включая фотокопии и микрофильмы, без
предварительного письменного согласия ISO, которое должно быть получено после запроса о разрешении, направленного по
адресу, приведенному ниже, или в комитет-член ISO в стране запрашивающей стороны.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Опубликовано в Швейцарии

ii © ISO 2005 – Все права сохраняются

---------------------- Page: 2 ----------------------
ISO 8502-2:2005(R)
Содержание       Страница

Предисловие .iv
Введение .v
1 Область применения .1
2 Нормативные ссылки .2
3 Принцип.2
4 Реактивы и материалы.2
5 Аппаратура.3
6 Проведение испытания.4
6.1 Холостое титрование.4
6.2 Промывка поверхности.4
6.3 Титрование промывных вод.4
7 Обработка результатов.4
8 Протокол испытания.5
Библиография.6

© ISO 2005 – Все права сохраняются iii

---------------------- Page: 3 ----------------------
ISO 8502-2:2005(R)
Предисловие
Международная организация по стандартизации (ISO) является всемирной федерацией национальных организаций
по стандартизации (комитетов-членов ISO). Разработка международных стандартов обычно осуществляется
техническими комитетами ISO. Каждый комитет-член ISO, заинтересованный в деятельности, для которой был
создан технический комитет, имеет право быть представленным в этом комитете. Международные организации,
правительственные и неправительственные, имеющие связи с ISO, также принимают участие в работах. ISO
непосредственно сотрудничает с Международной электротехнической комиссией (IEC) по всем вопросам
электротехнической стандартизации.
Международные стандарты разрабатываются в соответствии с правилами, приведенными в
Директивах ISO/IEC, Часть 2.
Основной задачей технических комитетов является подготовка международных стандартов. Проекты
международных стандартов, одобренные техническими комитетами, рассылаются комитетам-членам
на голосование. Их опубликование в качестве международных стандартов требует одобрения, по
меньшей мере, 75 % комитетов-членов, принимающих участие в голосовании.
Следует иметь в виду, что некоторые элементы настоящего документа могут быть объектом патентных прав.
ISO не должен нести ответственность за идентификацию какого-либо одного или всех патентных прав.
Международный стандарт ISO 8502-2 разработан Техническим комитетом ISO/ТC 35, Краски и лаки, Подкомитетом
SC 12, Подготовка стальной поверхности перед нанесением красок и относящихся к ним продуктов.
Настоящее второе издание отменяет и заменяет первое издание (ISO 8502-2:1992), которое было
подвергнуто техническому пересмотру.
ISO 8502 состоит из следующих частей под общим названием Подготовка стальной поверхности перед
нанесением красок и относящихся к ним продуктов. Испытания для оценки чистоты поверхности:
— Часть 1. Полевое испытание растворимых продуктов коррозии железа (отменен) [Технический отчет]
— Часть 2. Лабораторное определение содержания хлорида на очищенных поверхностях
— Часть 3. Оценка запыленности стальных поверхностей, подготовленных для нанесения краски
(метод липкой ленты)
— Часть 4. Руководство по оценке вероятности образования конденсата перед нанесением краски
— Часть 5. Измерение содержания хлорида на стальных поверхностях, подготовленных к окраске
(метод обнаружения ионов с помощью трубки)
⎯ Часть 6. Извлечение растворимых загрязнителей для анализа. Метод Бресла
⎯ Часть 8. Метод рефрактометрического определения содержания влаги в полевых условиях
⎯ Часть 9. Метод кондуктометрического определения содержания водорастворимых солей в
полевых условиях
⎯ Часть 10. Метод титриметрического определения содержания водорастворимого хлорида в
полевых условиях (отменен)
⎯ Часть 11. Метод турбидиметрического определения содержания водорастворимого -сульфата
в полевых условиях
⎯ Часть 12. Метод титриметрического определения содержания водорастворимых ионов
железа (II) в полевых условиях
В настоящую исправленную версию ISO 8502-2:2005 включены следующие поправки:
⎯ в 4.5 «0,0125 мг/л» было заменено на «0,0125 моль/л»;
-5 -2
— в 4.5.2 числитель формулы «2,8 × 10 » был изменен на «2,8 × 10 » и была добавлена единица
объема в то место пункта, в котором определяется, что «V - объем израсходованного раствора
нитрата ртути (II), в миллилитрах».
iv © ISO 2005 – Все права сохраняются

---------------------- Page: 4 ----------------------
ISO 8502-2:2005(R)
Введение
Характеристики защитных покрытий лаков, красок и других относящимися к ним продуктов, нанесенных
на сталь, существенно зависят от состояния поверхности стали непосредственно перед окраской.
Известно, что основными факторами, влияющими на эти характеристики, являются:
a) наличие ржавчины и прокатной окалины,
b) наличие поверхностных загрязнителей, включая соли, пыль, масла и смазки, и
c) профиль поверхности.
Международные стандарты ISO 8501, ISO 8502 и ISO 8503 были разработаны для обеспечения
методов оценки этих факторов, в то время как ISO 8504 обеспечивает руководство по методам
подготовки, которые пригодны для очистки стальной поверхности с указанием возможности получения
заданных уровней чистоты для каждого из этих методов.
Эти международные стандарты не содержат рекомендаций по системам защитных покрытий,
наносимых на стальную поверхность. Они также не содержат рекомендаций относительно требований
к качеству поверхности для специфических условий, хотя качество поверхности может оказывать
непосредственное влияние на выбор наносимого защитного покрытия и на его характеристики. Такие
рекомендации содержатся в других документах, таких как национальные стандарты и кодексы
установившейся практики. Пользователь этих международных стандартов должен убедиться, что
указанные качества:
⎯ cовместимы и приемлемы как для условий окружающей среды, воздействию которых будет
подвергаться сталь, так и для используемой защитной системы покрытия, и
⎯ находятся в пределах возможностей указанной методики очистки.
В четырех вышеуказанных международных стандартах рассматриваются следующие аспекты
подготовки стальной поверхности перед нанесением красок или относящихся к ним продуктов:
⎯ ISO 8501 визуальная оценка чистоты поверхности;
⎯ ISO 8502 испытания для оценки чистоты поверхности;
⎯ ISO 8503 характеристики шероховатости стальных поверхностей, подвергнутых струйной очистке;
⎯ ISO 8504 методы подготовки поверхности.
Каждый из этих международных стандартов разделен, в свою очередь, на несколько отдельных частей.
В настоящей части ISO 8502 описывается метод оценки хлоридсодержащих солей, которые легко
растворимы в воде и находятся на поверхности стали. Стальные поверхности, покрытые ржавчиной,
особенно при степени ржавления С или D (cм. ISO 8501-1), даже после струйной очистки до степени
подготовки Sa 3 (cм. ISO 8501-1) все еще могут быть загрязнены растворимыми солями и продуктами
коррозии. Эти вещества почти бесцветны и расположены в самой нижней части коррозионных раковин.
Если их не удалить перед окраской, возможны химические реакции в больших скоплениях ржавчины,
которые нарушают адгезию между поверхностью и нанесенным защитным покрытием. Даже если соль
легко растворима в воде, часто невозможно полностью удалить ее с поверхности с помощью простой
промывки, которая описана в этой методике. Этот метод, следовательно, не определяет общее
количество хлорида на поверхности, однако дает показатель уровня чистоты поверхности. Увеличение
времени промывки должно обеспечить удаление большей части соли.

© ISO 2005 – Все права сохраняются v

---------------------- Page: 5 ----------------------
МЕЖДУНАРОДНЫЙ СТАНДАРТ ISO 8502-2:2005(R)

Подготовка стальной поверхности перед нанесением
красок и относящихся к ним продуктов. Испытания для
оценки чистоты поверхности.
Часть 2.
Лабораторное определение содержания хлорида на
очищенных поверхностях
ПРЕДОС
...

INTERNATIONAL ISO
STANDARD 8502-2
Second edition
2005-10-15
Corrected version
2006-01-15

Preparation of steel substrates before
application of paints and related
products — Tests for the assessment of
surface cleanliness —
Part 2:
Laboratory determination of chloride on
cleaned surfaces
Préparation des subjectiles d'acier avant application de peintures et de
produits assimilés — Essais pour apprécier la propreté d'une surface —
Partie 2: Recherche en laboratoire des chlorures sur les surfaces
nettoyées




Reference number
ISO 8502-2:2005(E)
©
ISO 2005

---------------------- Page: 1 ----------------------
ISO 8502-2:2005(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2005
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland

ii © ISO 2005 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 8502-2:2005(E)
Contents Page
Foreword. iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Principle. 2
4 Reagents and materials . 2
5 Apparatus . 3
6 Procedure . 3
6.1 Blank titration. 3
6.2 Washing of the surface . 3
6.3 Wash-water titration . 4
7 Expression of results . 4
8 Test report . 5
Bibliography . 6

© ISO 2005 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 8502-2:2005(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 8502-2 was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee SC 12,
Preparation of steel substrates before application of paints and related products.
This second edition cancels and replaces the first edition (ISO 8502-2:1992), which has been technically
revised.
ISO 8502 consists of the following parts, under the general title Preparation of steel substrates before
application of paints and related products — Tests for the assessment of surface cleanliness:
 Part 1: Field test for soluble iron corrosion products (withdrawn) [Technical Report]
 Part 2: Laboratory determination of chloride on cleaned surfaces
 Part 3: Assessment of dust on steel surfaces prepared for painting (pressure-sensitive tape method)
 Part 4: Guidance on the estimation of the probability of condensation prior to paint application
 Part 5: Measurement of chloride on steel surfaces prepared for painting (ion detection tube method)
 Part 6: Extraction of soluble contaminants for analysis — The Bresle method
 Part 8: Field method for the refractometric determination of moisture
 Part 9: Field method for the conductometric determination of water-soluble salts
 Part 10: Field method for the titrimetric determination of water-soluble chloride (withdrawn)
 Part 11: Field method for the turbidimetric determination of water-soluble sulfate
 Part 12: Field method for the titrimetric determination of water-soluble ferrous ions
This corrected version of ISO 8502-2:2005 incorporates the following corrections:
 in 4.5 “0,012 5 mg/l” has been changed to “0,012 5 mol/l”;
−5 −2
 in 4.5.2 the numerator in the equation has been changed from “2,8 × 10 ” to “2,8 × 10 ” and the
volume unit has been added in the where clause, giving “V is the volume, in millilitres, of the
mercury(II) nitrate solution consumed.”
iv © ISO 2005 – All rights reserved

---------------------- Page: 4 ----------------------
ISO 8502-2:2005(E)
Introduction
The performance of protective coatings of paint and related products applied to steel is significantly affected
by the state of the steel surface immediately prior to painting. The principal factors that are known to influence
this performance are
a) the presence of rust and mill scale,
b) the presence of surface contaminants, including salts, dust, oils and greases, and
c) the surface profile.
ISO 8501, ISO 8502 and ISO 8503 have been prepared to provide methods of assessing these factors, while
ISO 8504 provides guidance on the preparation methods that are available for cleaning steel substrates,
indicating the capabilities of each in attaining specified levels of cleanliness.
These International Standards do not contain recommendations for the protective coating systems to be
applied to the steel surface. Neither do they contain recommendations for the surface quality requirements for
specific situations even though surface quality can have a direct influence on the choice of protective coating
to be applied and on its performance. Such recommendations are found in other documents such as national
standards and codes of practice. It will be necessary for the users of these International Standards to ensure
that the qualities specified are
 compatible and appropriate both for the environmental conditions to which the steel will be exposed and
for the protective coating system to be used, and
 within the capability of the cleaning procedure specified.
The four International Standards referred to above deal with the following aspects of preparation of steel
substrates before application of paints and related products:
 ISO 8501 on visual assessment of surface cleanliness;
 ISO 8502 on tests for the assessment of surface cleanliness;
 ISO 8503 on surface roughness characteristics of blast-cleaned steel substrates;
 ISO 8504 on surface preparation methods.
Each of these International Standards is in turn divided into separate parts. This part of ISO 8502 describes a
method for the assessment of chloride-containing salts that are readily soluble in water and are present on a
steel surface. Rusted steel substrates, particularly of rust grades C or D (see ISO 8501-1), even when blast
cleaned to preparation grade Sa 3 (see ISO 8501-1) can still be contaminated by soluble salts and corrosion
products. These compounds are almost colourless and are localized at the lowest point of the rust pits. If they
are not removed prior to painting, chemical reactions can result in large accumulations of rust that destroy the
adhesion between the substrate and the applied protective coating. Even if the salt is readily soluble in water,
it is often impossible to remove it completely from the surface by a simple washing such as that described in
this procedure. The method does not therefore determine the total amount of chloride on the surface but gives
an indication of the cleanliness level of the surface. Prolonging the washing time should remove a larger
proportion of the salt.
© ISO 2005 – All rights reserved v

---------------------- Page: 5 ----------------------
INTERNATIONAL STANDARD ISO 8502-2:2005(E)

Preparation of steel substrates before application of paints and
related products — Tests for the assessment of surface
cleanliness —
Part 2:
Laboratory determination
...

NORME ISO
INTERNATIONALE 8502-2
Deuxième édition
2005-10-15
Version corrigée
2006-01-15


Préparation des subjectiles d'acier avant
application de peintures et de produits
assimilés — Essais pour apprécier la
propreté d'une surface —
Partie 2:
Recherche en laboratoire des chlorures
sur les surfaces nettoyées
Preparation of steel substrates before application of paints and related
products — Tests for the assessment of surface cleanliness —
Part 2: Laboratory determination of chloride on cleaned surfaces




Numéro de référence
ISO 8502-2:2005(F)
©
ISO 2005

---------------------- Page: 1 ----------------------
ISO 8502-2:2005(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.


©  ISO 2005
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse

ii © ISO 2005 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 8502-2:2005(F)
Sommaire Page
Avant-propos. iv
Introduction . vi
1 Domaine d'application. 1
2 Références normatives . 1
3 Principe. 2
4 Réactifs et matériaux. 2
5 Appareillage . 3
6 Mode opératoire . 3
6.1 Essai à blanc . 3
6.2 Nettoyage de la surface . 3
6.3 Titrage des eaux de lavage . 4
7 Expression des résultats . 4
8 Rapport d'essai . 5
Bibliographie . 6

© ISO 2005 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 8502-2:2005(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 8502-2 a été élaborée par le comité technique ISO/TC 35, Peintures et vernis, sous-comité SC 12,
Préparation des subjectiles d'acier avant application de peintures et de produits assimilés.
Cette deuxième édition annule et remplace la première édition (ISO 8502-2:1992), dont elle constitue une
révision technique.
L'ISO 8502 comprend les parties suivantes, présentées sous le titre général Préparation des subjectiles
d'acier avant application de peintures et de produits assimilés — Essais pour apprécier la propreté d'une
surface:
 Partie 1: Essai in situ pour l'évaluation des produits de corrosion du fer solubles (annulée) [Rapport
technique]
 Partie 2: Recherche en laboratoire des chlorures sur les surfaces nettoyées
 Partie 3: Évaluation de la poussière sur les surfaces d'acier préparées pour la mise en peinture (méthode
du ruban adhésif sensible à la pression)
 Partie 4: Principes directeurs pour l'estimation de la probabilité de condensation avant application de
peinture
 Partie 5: Mesurage des chlorures sur les surfaces d'acier préparées pour la mise en peinture (méthode
du tube détecteur d'ions)
 Partie 6: Extraction des contaminants solubles en vue de l'analyse — Méthode de Bresle
 Partie 8: Méthode in situ pour la détermination réfractométrique de l'humidité
 Partie 9: Méthode in situ pour la détermination des sels solubles dans l'eau par conductimétrie
 Partie 10: Méthode in situ pour la détermination titrimétrique du chlorure hydrosoluble (annulée)
 Partie 11: Méthode in situ pour la détermination turbidimétrique des sulfates hydrosolubles
 Partie 12: Méthode in situ pour la détermination titrimétrique des ions ferreux hydrosolubles
iv © ISO 2005 – Tous droits réservés

---------------------- Page: 4 ----------------------
ISO 8502-2:2005(F)
Dans le présente version corrigée, les corrections suivantes ont été apportées:
 en 4.5 «0,012 5 mg/l» a été remplacé par «0,012 5 mol/l»
−5 −2
 en 4.5.2 dans le numérateur de l’équation, «2,8 × 10 » a été remplacé par «2,8 × 10 » et l’unité de
volume a été ajoutée dans la ligne suivante afin de lire «V est le volume de la solution de
nitrate de mercure(II) utilisée, en millilitres»
© ISO 2005 – Tous droits réservés v

---------------------- Page: 5 ----------------------
ISO 8502-2:2005(F)
Introduction
L'efficacité des revêtements de peintures et produits assimilés de protection appliqués sur de l'acier est
considérablement affectée par l'état du subjectile juste avant l'application de la peinture. Les principaux
facteurs connus affectant cette efficacité sont:
a) la présence de rouille et de calamine;
b) la présence d'agents contaminants tels que sels, poussières, huiles et graisses;
c) le profil de surface.
L'ISO 8501, l'ISO 8502 et l'ISO 8503 ont été élaborées afin de fournir des méthodes pour évaluer ces facteurs,
alors que l'ISO 8504 fournit des directives sur les méthodes de préparation existantes pour le nettoyage des
subjectiles d'acier avec les possibilités de chacune de parvenir aux niveaux de propreté spécifiés.
Ces Normes internationales ne proposent aucune recommandation pour les systèmes de revêtement de
protection à appliquer sur le subjectile d'acier. Elles ne proposent pas non plus de recommandations quant
aux exigences sur la qualité du subjectile dans des cas particuliers, bien que ce facteur puisse avoir une
influence directe sur le choix du revêtement à appliquer et sur son efficacité. On trouvera de telles
recommandations dans d'autres documents tels que les normes nationales ou les codes d'utilisation. Il est
nécessaire que les utilisateurs de ces Normes internationales s'assurent que les qualités spécifiées sont:
 compatibles et adaptées tant à l'environnement auquel le subjectile sera exposé qu'aux revêtements de
protection à utiliser;
 dans les limites de possibilités du mode de nettoyage spécifié.
Les quatre Normes internationales auxquelles il est fait référence ci-dessus traitent des aspects suivants de la
préparation des subjectiles d'acier:
 ISO 8501, de l'évaluation visuelle de la propreté d'un subjectile;
 ISO 8502, des essais pour apprécier la propreté d'un subjectile;
 ISO 8503, des caractéristiques de rugosité des subjectiles d'acier décapés;
 ISO 8504, des méthodes de préparation des subjectiles.
Chacune de ces Normes internationales est à son tour divisée en parties séparées. La présente partie de
l'ISO 8502 décrit une méthode de recherche de sels contenant des chlorures solubles dans l'eau et présents
à la surface du subjectile d'acier. Les subjectiles d'acier rouillés, particulièrement ceux d'un degré de rouille C
et D (voir l'ISO 8501-1), même lorsqu'ils ont été amenés à un degré de préparation Sa 3 (voir l'ISO 8501-1 et
l'ISO 8501-2), peuvent être encore contaminés par des sels solubles et des produits de corrosion. Ces
composés sont pratiquement incolores et sont localisés au fond des piqûres de rouille. S'ils ne sont pas
éliminés avant la mise en peinture, des réactions chimiques peuvent se produire, avec comme résultat des
amas de rouille qui vont nuire à l'adhérence entre le subjectile et le revêtement protecteur appliqué. Même si
le sel est très soluble dans l'eau, il est souvent impossible de l'enlever complètement de la surface par simple
lavage comme décrit dans le présent mode opératoire. La méthode ne permet donc pas de déterminer la
quantité totale des chlorures sur la surface mais donne une indication sur le niveau de propreté de la surface.
Un temps de lavage plus long permet généralement d'enlever une plus grande proportion du sel.
vi © ISO 2005 – Tous droits réservés

---------------------- Page: 6 ----------------------
NORME INTERNATIONALE ISO 8502-2:2005(F)

Préparation des subjectiles d'acier avant application de
peintures et de produits assimilés — Essais pour apprécier la
propreté d'une surface —
Partie 2:
Recherche en laboratoire des chlorures sur les surfaces
nettoyées
...