ASTM D2383-14
(Practice)Standard Practice for Testing Plasticizer Compatibility in Poly(Vinyl Chloride) (PVC) Compounds Under Humid Conditions
Standard Practice for Testing Plasticizer Compatibility in Poly(Vinyl Chloride) (PVC) Compounds Under Humid Conditions
SIGNIFICANCE AND USE
5.1 This practice provides an accelerated method for determining the stability of PVC compounds with respect to plasticizer compatibility under humid conditions.
5.2 The temperatures and humidity employed in this test can represent actual use conditions, but are intended primarily for rating materials.
SCOPE
1.1 This practice defines the conditions for the exposure and qualitative evaluation of poly(vinyl chloride) (PVC) compounds for plasticizer compatibility under humid conditions. Change in appearance is used for judging compatibility.
1.2 The text of this practice references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of this practice.
1.3 The values stated in SI units are to be regarded as standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Note 1—There is no known ISO equivalent to this practice.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D2383 − 14
Standard Practice for
Testing Plasticizer Compatibility in Poly(Vinyl Chloride)
1
(PVC) Compounds Under Humid Conditions
This standard is issued under the fixed designation D2383; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 3. Terminology
1.1 This practice defines the conditions for the exposure and 3.1 General—Definitions are in accordance with Terminol-
qualitative evaluation of poly(vinyl chloride) (PVC) com- ogy D883 and abbreviations with Terminology D1600, unless
pounds for plasticizer compatibility under humid conditions. otherwise indicated.
Change in appearance is used for judging compatibility.
4. Summary of Practice
1.2 The text of this practice references notes and footnotes
4.1 Specimens are suspended over water in closed contain-
that provide explanatory material. These notes and footnotes
ers and aged at either 60°C or 80°C. The specimens are
(excluding those in tables and figures) shall not be considered
removed from the containers at specified intervals and their
as requirements of this practice.
appearance is rated in accordance with 10.1 and recorded.
1.3 The values stated in SI units are to be regarded as
5. Significance and Use
standard.
5.1 This practice provides an accelerated method for deter-
1.4 This standard does not purport to address all of the
mining the stability of PVC compounds with respect to
safety concerns, if any, associated with its use. It is the
plasticizer compatibility under humid conditions.
responsibility of the user of this standard to establish appro-
priate safety and health practices and determine the applica-
5.2 Thetemperaturesandhumidityemployedinthistestcan
bility of regulatory limitations prior to use.
represent actual use conditions, but are intended primarily for
rating materials.
NOTE 1—There is no known ISO equivalent to this practice.
6. Apparatus
2. Referenced Documents
6.1 Screw-Cap Glass Jars or Capped Metal Containers,
2
2.1 ASTM Standards:
large enough to avoid contact between specimens and between
D883 Terminology Relating to Plastics
the specimens and 1 cm of deionized water.The covers shall be
D1600 Terminology forAbbreviatedTerms Relating to Plas-
provided on the inside with hooks of a corrosion-resistant
tics
metal such as stainless steel, nichrome or nickel.
D1755 Specification for Poly(Vinyl Chloride) Resins
6.2 Forced-Ventilation Laboratory Oven, Type II, Grade A,
E145 Specification for Gravity-Convection and Forced-
in accordance with Specification E145.
Ventilation Ovens
7. Materials
1
This practice is under the jurisdiction ofASTM Committee D20 on Plastics and 7.1 Distilled Water—Freshly prepared distilled or deionized
is the direct responsibility of Subcommittee D20.15 on Thermoplastic Materials
water.
(Section D20.15.07).
Current edition approved March 1, 2014. Published March 2014. Originally
8. Specimen Preparation (Note 2)
approved in 1969. Last previous edition approved in 2009 as D2383 - 09. DOI:
10.1520/D2383-14.
8.1 Cut test specimens with one side having a surface area
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or 2
of 25 cm from a 0.5-mm (0.02-in.) thick smooth surface
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
plastic sheet (60.05 mm (0.002-in.)) Punch a small hole near
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. the edge for hanging the specimen.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D2383 − 14
NOTE 2—For use as a control in testing the relative performance of
9.5 Replace the specimens in the original containers and
plasticizers, the following clear formulation may be employed.
continue the test for the specified period of time.
Parts
10. Ratings
General-Purpose PVC Resin:
Type GP 40000 as defined in Specification D1755. 100 10.1 The following visual and tactile ratings are used for
judging plasticizer compatibility:
Plasticizer:
10.1.1 None (Dry)—No evidence of exudation.
Di-2-ethylhexyl phthalate 50
10.1.2 Slight (Tacky)—Slight exudation resulting in a sticky
Stabilizer:
specimen surface.
Weatherable BaZn 1
10.1.3 Moderate (Greasy)—Thin film of exuded plasticizer
NOTE 3—The test compound suggested in Note 2 will not exude under
covers specimen surface. The film will appear to be greasy,
either test temperature specified in 9.2.
oily, or waxy.
10.1.4 Heavy (Wet)—Droplets of exu
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D2383 − 09 D2383 − 14
Standard Practice for
Testing Plasticizer Compatibility in Poly(Vinyl Chloride)
1
(PVC) Compounds Under Humid Conditions
This standard is issued under the fixed designation D2383; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This practice defines the conditions for the exposure and qualitative evaluation of poly(vinyl chloride) (PVC) compounds
for plasticizer compatibility under humid conditions. Change in appearance is used for judging compatibility.
1.2 The text of this practice references notes and footnotes that provide explanatory material. These notes and footnotes
(excluding those in tables and figures) shall not be considered as requirements of this practice.
1.3 The values stated in SI units are to be regarded as standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
NOTE 1—There is no known ISO equivalent to this practice.
2. Referenced Documents
2
2.1 ASTM Standards:
D883 Terminology Relating to Plastics
D1600 Terminology for Abbreviated Terms Relating to Plastics
D1755 Specification for Poly(Vinyl Chloride) Resins
E145 Specification for Gravity-Convection and Forced-Ventilation Ovens
3. Terminology
3.1 General—Definitions are in accordance with Terminology D883 and abbreviations with Terminology D1600, unless
otherwise indicated.
4. Summary of Practice
4.1 Specimens are suspended over water in closed containers and aged at either 60°C or 80°C. The specimens are removed from
the containers at specified intervals and their appearance is rated in accordance with 10.1 and recorded.
5. Significance and Use
5.1 This practice provides an accelerated method for determining the stability of PVC compounds with respect to plasticizer
compatibility under humid conditions.
5.2 The temperatures and humidity employed in this test can represent actual use conditions, but are intended primarily for
rating materials.
6. Apparatus
6.1 Screw-Cap Glass Jars or Capped Metal Containers, large enough to avoid contact between specimens and between the
specimens and 1 cm of deionized water. The covers shall be provided on the inside with hooks of a corrosion-resistant metal such
as stainless steel, nichrome or nickel.
1
This practice is under the jurisdiction of ASTM Committee D20 on Plastics and is the direct responsibility of Subcommittee D20.15 on Thermoplastic Materials (Section
D20.15.07).
Current edition approved Sept. 1, 2009March 1, 2014. Published September 2009March 2014. Originally approved in 1969. Last previous edition approved in 20012009
as D2383 - 97D2383 - 09.(2001). DOI: 10.1520/D2383-09.10.1520/D2383-14.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
D2383 − 14
6.2 Forced-Ventilation Laboratory Oven, Type II, Grade A, in accordance with Specification E145.
7. Materials
7.1 Distilled Water—Freshly prepared distilled or deionized water.
8. Specimen Preparation (Note 2)
2
8.1 Cut test specimens with one side having a surface area of 25 cm from a 0.5-mm (0.02-in.) thick smooth surface plastic sheet
(60.05 mm (0.002-in.)) Punch a small hole near the edge for hanging the specimen.
2
---------------------- Page: 2 ----------------------
D2383 − 14
NOTE 2—For use as a control in testing the relative performance of plasticizers, the following clear formulation may be employed.
Parts
General-Purpose PVC Resin:
Type GP 40000 as defined in Specification D1755. 100
Plasticizer:
Di-2-ethylhexyl phthalate 50
Stabilizer:
Weatherable BaZn 1
NOTE 3—The test compound suggested in Note 2 will not exude under either test temperature specified in 9.2.
9. Procedure
9.1 Suspend the specimens from hooks over 1-1.3 cm of distilled w
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.