ASTM D7505/D7505M-17(2023)

(Specification)

Standard Specification for Self-Adhesive Polyester Fabric Reinforced Polymer-Modified Asphalt Steep Slope Roll Roofing Surfaced with Mineral Granules

Standard Specification for Self-Adhesive Polyester Fabric Reinforced Polymer-Modified Asphalt Steep Slope Roll Roofing Surfaced with Mineral Granules

ABSTRACT
This specification covers prefabricated, self-adhesive, polyester fabric reinforced, polymer-modified asphalt surfaced roll roofing products, with granule surfacing, designed for steep slope applications. These products use polymer modifiers in their top and bottom coatings and have an adhesive bottom layer which is exposed by removal of a peel-away protective release paper or film sheet. The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties. The minimum physical properties required for the sheet include thickness, peak load, elongation, tear strength, adhesion to plywood, side lap integrity, thermal stability, and granule loss.
SCOPE
1.1 This specification covers prefabricated, self-adhesive, polyester fabric reinforced, polymer-modified asphalt surfaced roll roofing products, with granule surfacing, designed for steep slope applications. These products use polymer modifiers in their top and bottom coatings. These products have an adhesive bottom layer which is exposed by removal of a peel-away protective release paper or film sheet.  
1.2 The specified tests and property limits used to characterize the sheet materials are intended to establish minimum properties. In-place roof system design criteria such as fire resistance, field strength, impact/puncture resistance, material compatibility, uplift resistance, and others, are factors beyond the scope of this material specification. Factors regarding the suitability of specific roof constructions or application techniques are beyond this scope.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
30-Apr-2023
ICS
91.100.50 - Binders. Sealing materials
Technical Committee
D08 - Roofing and Waterproofing
Drafting Committee
D08.02 - Steep Roofing Products and Assemblies
Current Stage
Ref Project

Relations

Refers
ASTM D4977/D4977M-20 - Standard Test Method for Granule Adhesion to Mineral-Surfaced Roofing by Abrasion
Effective Date
01-May-2020
Refers
ASTM D1079-20 - Standard Terminology Relating to Roofing and Waterproofing
Effective Date
01-May-2020

Buy Standard

ASTM D7505/D7505M-17(2023) - Standard Specification for Self-Adhesive Polyester Fabric Reinforced Polymer-Modified Asphalt Steep Slope Roll Roofing Surfaced with Mineral GranulesASTM D7505/D7505M-17(2023) - Standard Specification for Self-Adhesive Polyester Fabric Reinforced Polymer-Modified Asphalt Steep Slope Roll Roofing Surfaced with Mineral Granules
PreviousNext
Technical specification
ASTM D7505/D7505M-17(2023) - Standard Specification for Self-Adhesive Polyester Fabric Reinforced Polymer-Modified Asphalt Steep Slope Roll Roofing Surfaced with Mineral Granules
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: D7505/D7505M − 17 (Reapproved 2023)
Standard Specification for
Self-Adhesive Polyester Fabric Reinforced Polymer-Modified
Asphalt Steep Slope Roll Roofing Surfaced with Mineral
1
Granules
This standard is issued under the fixed designation D7505/D7505M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 2. Referenced Documents
2
1.1 This specification covers prefabricated, self-adhesive, 2.1 ASTM Standards:
polyester fabric reinforced, polymer-modified asphalt surfaced D903 Test Method for Peel or Stripping Strength of Adhe-
roll roofing products, with granule surfacing, designed for sive Bonds
steep slope applications. These products use polymer modifiers D1079 Terminology Relating to Roofing and Waterproofing
in their top and bottom coatings. These products have an D4977/D4977M Test Method for Granule Adhesion to
adhesive bottom layer which is exposed by removal of a Mineral-Surfaced Roofing by Abrasion
peel-away protective release paper or film sheet. D5147/D5147M Test Methods for Sampling and Testing
Modified Bituminous Sheet Material
1.2 The specified tests and property limits used to charac-
terize the sheet materials are intended to establish minimum
3. Terminology
properties. In-place roof system design criteria such as fire
3.1 Definitions:
resistance, field strength, impact/puncture resistance, material
3.1.1 For definitions of terms used in this specification, refer
compatibility, uplift resistance, and others, are factors beyond
to Terminology D1079.
the scope of this material specification. Factors regarding the
3.1.2 ultimate elongation, n—the elongation measured on
suitability of specific roof constructions or application tech-
the load-elongation curve at which point the load has dropped
niques are beyond this scope.
to 5 % of its maximum value, after the peak load has been
1.3 The values stated in either SI units or inch-pound units
reached.
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each
4. Materials and Manufacture
system shall be used independently of the other. Combining
4.1 In the process of manufacture, the reinforcing mat is
values from the two systems may result in nonconformance
permitted to be impregnated with asphalt or modified asphalt
with the standard.
and is coated on its top and bottom sides with polymer-
1.4 This standard does not purport to address all of the
modified asphalt coatings. The polymer-modified asphalt coat-
safety concerns, if any, associated with its use. It is the
ings are permitted to be compounded with a mineral stabilizer.
responsibility of the user of this standard to establish appro-
The coating on the bottom side shall feature self-adhesive
priate safety, health, and environmental practices and deter-
properties.
mine the applicability of regulatory limitations prior to use.
4.2 The sheet is surfaced on the weather side with mineral
1.5 This international standard was developed in accor-
granules, except for any selvage.
dance with internationally recognized principles on standard-
ization established in the Decision on Principles for the
5. Physical Properties
Development of International Standards, Guides and Recom-
5.1 The sheet shall conform to the minimum physical
mendations issued by the World Trade Organization Technical
properties prescribed in Table 1.
Barriers to Trade (TBT) Committee.
5.2 The finished product shall not crack nor be so sticky as
to cause tearing or other material damage upon being unrolled
1
This specification is under the jurisdiction of ASTM Committee D08 on
Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.02
2
on Steep Roofing Products and Assemblies. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved May 1, 2023. Published May 2023. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
approved in 2010. Last previous edition approved in 2017 as D7505/D7505M – 17. Standards volume information, refer to the standard’s Document Summary page on
DOI:10.1520/D7505_D7505M-17R23. the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D7505/D7505M − 17 (2023)
TABLE 1 Physical Properties of Self-Adhesive Polyester Fabric Reinforced Polymer Modified Asphalt Steep S
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM C1306/C1306M-08(2023)(Test Method)
Standard Test Method for Hydrostatic Pressure Resistance of a Liquid-Applied Waterproofing Membrane

SIGNIFICANCE AND USE
5.1 This test method is used as a screening tool to determine the hydrostatic pressure to which a liquid-applied waterproofing membrane may be subjected without failing when stretched over a crack in the substrate. This test method discriminates between a membrane that is very resistant to hydrostatic pressure and one that is not. Because of the variability inherent in this test method, it is not recommended that this test method be used to set a numerical standard for hydrostatic pressure resistance. No prediction of durability at lower hydrostatic pressures can be made when using the results of this test method.
SCOPE
1.1 This test method describes a laboratory procedure for determining the resistance of a waterproofing membrane to hydrostatic pressure.  
1.2 The committee with jurisdiction over this standard is not aware of any comparable standards published by other organizations.  
1.3 There are no ISO standards similar or equivalent to this ASTM standard.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D3805/D3805M-16(2023)(Guide)
Standard Guide for Application of Aluminum-Pigmented Asphalt Roof Coatings

SIGNIFICANCE AND USE
3.1 Asphalt-based, solvent-type, fibered or nonfibered, aluminum-pigmented roof coatings are used as a protective coating for solar reflection to prolong the life of roofing materials or where decorative qualities are desired.  
3.2 Suitable application of aluminum-pigmented asphalt roof coatings is an important factor in achieving a successful long-term coating. Suitable application is, in part, dependent upon appropriate specifications to guide the work. This guide can be useful in facilitating development of an appropriate specification for surface preparation and application of the roof coating.  
3.3 Designers/specifiers of coatings may use this guide in preparing the application portion of their specification. Contractors working directly for the building owner may also use this guide.  
3.4 This guide is not all-inclusive. Manufacturer's application instructions should be consulted and geographical “area practices” considered. Consult membrane manufacturer and coating manufacturer for acceptability of procedures and products.
SCOPE
1.1 This guide covers the application methods for Specification D2824/D2824M Aluminum-Pigmented Asphalt Roof Coatings, Nonfibered, and Fibered without Asbestos, for application on asphalt built-up roof membranes, modified bitumen roof membranes, bituminous base flashings, concrete surfaces, metal surfaces, emulsion coatings, and solvent-based coatings. This guide does not apply to the selection of a specific aluminum-pigmented asphalt roof coating type for use on specific projects. The fibered version of these coatings excludes the use of asbestos fibers.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Section 4.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM C1305/C1305M-16(2023)(Test Method)
Standard Test Method for Crack Bridging Ability of Liquid-Applied Waterproofing Membrane

SIGNIFICANCE AND USE
5.1 This test method is used to indicate a waterproofing membrane's ability to maintain its integrity while bridging a preexisting crack in the substrate at low ambient temperatures, when the membrane is least likely to be flexible.
SCOPE
1.1 This test method covers a laboratory procedure for determining the ability of a waterproofing membrane to bridge a crack in the substrate.  
1.2 There are no ISO standards similar or equivalent to this ASTM standard.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D2829/D2829M-07(2023)(Practice)
Standard Practice for Sampling and Analysis of Existing Built-Up Roof Systems

SIGNIFICANCE AND USE
5.1 This practice is for the sampling and analysis of existing built-up roof systems. For roofs under construction, use Practice D3617/D3617M.
SCOPE
1.1 This practice is a guide for removing test specimens from existing built-up roofing systems in the field and for determining the approximate quantities of the components of that specimen (Note 1). Components determined may be:  
1.1.1 Insulation components when they are part of the roof membrane system,  
1.1.2 Plies of roofing felt,  
1.1.3 Interply layers of bituminous material,  
1.1.4 Top coating, and  
1.1.5 Surfacing.  
Note 1: This procedure is for the investigation of existing roofs and is not intended for new construction inspection.  
1.2 This practice is applicable to both 914 mm [36 in.] and 1000 mm [393/8 in.] wide felt rolls.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precautionary information, see 6.3.2.1.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D1670/D1670M-11(2023)(Test Method)
Standard Test Method for Failure End Point in Accelerated and Outdoor Weathering of Bituminous Materials

SIGNIFICANCE AND USE
4.1 The extent of cracking or pitting of bituminous films is a measure of the extent of deterioration due to weathering. Failure due to cracking is more accurately determined electrically than visually.  
4.2 Failure determined by this test method will depend not only on the characteristics of the bituminous material and the extent of weathering, but also on the film thickness, and the amount and type of mineral filler present.  
4.3 Tests on a similar material of known weathering characteristics (a control) exposed at the same time as the test material is strongly recommended as a check on the validity of the test results.
SCOPE
1.1 This test method covers the use of a spark-generating apparatus for determination of failure due to cracking of bituminous materials undergoing accelerated or outdoor weathering on electrically conductive backings.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D1669/D1669M-07(2023)(Practice)
Standard Practice for Preparation of Test Panels for Accelerated and Outdoor Weathering of Bituminous Coatings

SIGNIFICANCE AND USE
4.1 This practice for preparation of test panels greatly increases the likelihood of achieving reproducible results in subsequent testing.
SCOPE
1.1 This practice covers a procedure for the preparation of accelerated and outdoor weathering test panels of bituminous coatings. It is considered suitable for the preparation of film thicknesses in the range from 0.25 to 2.54 mm [0.010 to 0.100 in.].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning—Mercury has been designated by EPA and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable product Material Safety Data Sheet (MSDS) for details and EPA's website, http://www.epa.gov/mercury/faq.htm, for additional information. Users should be aware that selling mercury or mercury-containing products, or both, in your state may be prohibited by state law.)  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D8051/D8051M-16(2023)(Specification)
Standard Specification for Wax-Modified Asphalt Used in Roofing

ABSTRACT
This specification establishes the manufacturing process and physical requirements for wax-modified asphaltic products intended for built-up roof construction, construction of bituminous vapor retarder systems, adhering fleece-backed single-ply roof membranes, and adhering insulation boards used in various types of roof systems. The base asphalt shall be prepared from lightly oxidized petroleum asphalt, and the wax-modified asphalt shall incorporate one or more high melt-point synthetic waxes. Furthermore, the products shall be homogeneous and free of water.
SCOPE
1.1 This specification covers wax-modified asphaltic products intended for use in built-up roof construction, construction of bituminous vapor retarder systems, adhering fleece-backed single-ply roof membranes, and adhering insulation boards used in various types of roof systems. The specification is intended for general classification purposes only, and does not imply restrictions on roofing system design, such as the slope at which this asphalt may be used.  
1.2 These products have lower application temperatures compared to products specified by Specification D312/D312M.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM D3423/D3423M-15(2023)(Practice)
Standard Practice for Application of Emulsified Coal-Tar Pitch (Mineral Colloid Type)

ABSTRACT
This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways. The procedure for preparation of (1) old asphalt surfaces, (2) new asphalt surfaces, and (3) emulsion, and the procedure for application of emulsion for the first coat and second coat are detailed. When sand addition to the top coat of the emulsion is necessary, the sand shall meet the prescribed sieve size requirements. Application precautions including weather conditions, pavement and air temperatures, drying time, and emulsion freezing are also provided.
SCOPE
1.1 This practice covers the application of mineral-colloid-stabilized, emulsified coal-tar pitch meeting the requirements of Specification D5727/D5727M, as a weather protection and aliphatic-solvent-resistant sealer for use on bituminous pavements of airports, parking lots, and driveways.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D2746/D2746M-18(2023)(Test Method)
Standard Test Method for Staining Tendency of Asphalt (Stain Index)

SIGNIFICANCE AND USE
4.1 This test method measures the tendency for oil components to separate spontaneously from asphalt. The separation of oil components can cause staining in asphalt roofing products and adjacent materials in storage and use.  
4.2 The stain index is related to the thermal stability of the asphalt. Higher stain index values indicate lower stability and greater tendency for staining.  
4.3 Use this procedure to determine the staining tendency of asphalt and to compare the results against a material for which the staining tendency is known.
SCOPE
1.1 This test method covers the determination of the staining tendency of asphalt and the assignment of a stain index proportional to the extent of staining observed.  
1.2 This test method is applicable to asphalts having ring-and-ball softening points of 85 °C [185 °F] or greater.  
Note 1: This test method may be modified for use with other bituminous materials with softening points less than 85 °C [185 °F] by using a different temperature than specified in Section 7 by agreement of the interested parties. The report of results from such a test may cite this method but must clearly state the temperature employed in the exception and acknowledge that the interpretation of results in Section 9 and the precision and bias stated in Section 10 may not apply.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D3462/D3462M-23(Specification)
Standard Specification for Asphalt Shingles Made from Glass Felt and Surfaced with Mineral Granules

ABSTRACT
This specification deals with the standards for asphalt roofing in shingle form, composed of glass felt or felts impregnated and coated on both sides with asphalt, and surface on the weather side with minerals. Physical requirements of the shingles such as behavior on melting, tear strength, wind resistance, fire resistance, softening point, and pliability shall be measured immediately after packaging or at a reasonable time. Physical and performance requirements after application and during in-service use are however beyond the scope of this specification.
SCOPE
1.1 This specification covers asphalt roofing in shingle form, composed of glass felt or felts impregnated and coated on both sides with asphalt, and surfaced on the weather side with mineral granules. This specification is designed for the evaluation of products as manufactured. The test methods, physical requirements, and minimum masses are to be measured immediately after packaging or at a reasonable time, as agreed upon between buyer and seller, after manufacture and before installation. Physical and performance requirements after application and during in-service use of the products described herein are beyond the scope of this material specification.  
1.2 Shingles meeting this specification are intended to be applied with a headlap of not less than 51 mm [2 in.].  
1.3 The shingles shall be supplied with a factory-applied self-sealing adhesive or be designed to be locked together during installation of the shingles.  
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.5 The following safety hazards caveat pertains only to the test method described in this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
  • Technical specification
    4 pages
    English language
    sale 15% off