ASTM D5869-95(2002)

(Practice)

Standard Practice for Dark Oven Heat Exposure of Bituminous Materials

Standard Practice for Dark Oven Heat Exposure of Bituminous Materials

SCOPE
1.1 This practice establishes a procedure and conditions of temperature and time for heat exposure of bituminous materials in the presence of air.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
09-Dec-1995
ICS
75.140 - Waxes, bituminous materials and other petroleum products
91.100.50 - Binders. Sealing materials
Technical Committee
D08 - Roofing and Waterproofing
Drafting Committee
D08.02 - Steep Roofing Products and Assemblies
Current Stage
Ref Project

Relations

Replaces
ASTM D5869-95(2000)e1 - Standard Practice for Dark Oven Heat Exposure of Bituminous Materials
Effective Date
10-Dec-1995
Replaced By
ASTM D5869-04 - Standard Practice for Dark Oven Heat Exposure of Bituminous Materials
Effective Date
01-Jul-2004

Buy Standard

ASTM D5869-95(2002) - Standard Practice for Dark Oven Heat Exposure of Bituminous MaterialsASTM D5869-95(2002) - Standard Practice for Dark Oven Heat Exposure of Bituminous Materials
PreviousNext
Standard
ASTM D5869-95(2002) - Standard Practice for Dark Oven Heat Exposure of Bituminous Materials
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D 5869 – 95 (Reapproved 2002)
Standard Practice for
Dark Oven Heat Exposure of Bituminous Materials
This standard is issued under the fixed designation D 5869; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope 4.3 This practice permits the selection of the duration of
heat exposure from three specified time periods, which are 35,
1.1 This practice establishes a procedure and conditions of
90, and 180 6 0.25 consecutive days. The duration selected
temperature and time for heat exposure of bituminous materials
must be included in any report of results obtained by using this
in the presence of air.
practice.
1.2 The values stated in SI units are to be regarded as the
standard. The values given in parentheses are for information
NOTE 1—The time period to be used should be specified in any standard
only. that refers to this practice. European standards for polymer-modified
bituminous materials specify 180 days at 70°C. For research purposes,
1.3 This standard does not purport to address all of the
selection of other time periods is permitted, provided that the precise
safety concerns, if any, associated with its use. It is the
duration is stated in any report of results.
responsibility of the user of this standard to establish appro-
priate safety and health practices and determine the applica-
5. Significance and Use
bility of regulatory limitations prior to use.
5.1 Bituminous materials undergo changes in physical prop-
erties as a result of being subjected to heat. Bituminous
2. Referenced Documents
materials undergo changes in physical properties as they age in
2.1 ASTM Standards:
service. Since service conditions vary widely, any relationship
D 883 Terminology Relating to Plastics
between changes observed in this practice and changes in
D 1079 Terminology Relating to Roofing, Waterproofing,
service must be established by the user of this practice.
and Bituminous Materials
D 1566 Terminology Relating to Rubber
6. Apparatus
E 1 Specification for ASTM Thermometers
6.1 Oven—The oven shall have forced ventilation, shall be
E 145 Specification for Gravity-Convection and Forced-
electrically heated, and shall conform to the requirements of
Ventilation Ovens
Specification E 145, Type IIB. The oven shall be of sufficient
size to accommodate the size and number of specimens
3. Terminology
selected by the user of this practice.
3.1 Definitions—For definitions of terms used in this prac-
6.2 Thermometer—The thermometer shall be an ASTM
tice, refer to Terminologies D 883, D 1079, and D 1566.
partial immersion (general use) thermometer, conforming to
the requirements for thermometer 2°C (or 2°F) in accordance
4. Summary of Practice
with Specification E 1. (Partially immersed in the oven and
4.1 Specimens of bituminous materials are exposed to heat
read from the shaft extending outside the oven.)
in a dark forced-ventilation
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D2746/D2746M-18(2023)(Test Method)
Standard Test Method for Staining Tendency of Asphalt (Stain Index)

SIGNIFICANCE AND USE
4.1 This test method measures the tendency for oil components to separate spontaneously from asphalt. The separation of oil components can cause staining in asphalt roofing products and adjacent materials in storage and use.  
4.2 The stain index is related to the thermal stability of the asphalt. Higher stain index values indicate lower stability and greater tendency for staining.  
4.3 Use this procedure to determine the staining tendency of asphalt and to compare the results against a material for which the staining tendency is known.
SCOPE
1.1 This test method covers the determination of the staining tendency of asphalt and the assignment of a stain index proportional to the extent of staining observed.  
1.2 This test method is applicable to asphalts having ring-and-ball softening points of 85 °C [185 °F] or greater.  
Note 1: This test method may be modified for use with other bituminous materials with softening points less than 85 °C [185 °F] by using a different temperature than specified in Section 7 by agreement of the interested parties. The report of results from such a test may cite this method but must clearly state the temperature employed in the exception and acknowledge that the interpretation of results in Section 9 and the precision and bias stated in Section 10 may not apply.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D5869/D5869M-07a(2023)(Practice)
Standard Practice for Dark Oven Heat Exposure of Roofing and Waterproofing Materials

SIGNIFICANCE AND USE
5.1 Roofing and waterproofing materials and systems undergo changes in physical properties as a result of being subjected to heat. They also undergo changes in physical properties as they age in service. Since service conditions vary widely, any relationship between changes observed in this practice and changes in service must be established by the user of this practice.
SCOPE
1.1 This practice establishes a procedure and conditions of temperature and time for heat exposure of roofing and waterproofing materials and systems in the presence of air.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D4799/D4799M-17(2023)(Practice)
Standard Practice for Accelerated Weathering Test Conditions and Procedures for Bituminous Materials (Fluorescent UV, Water Spray, and Condensation Method)

SIGNIFICANCE AND USE
4.1 This weathering apparatus is used for comparing the weathering characteristics of bituminous materials against a control material for which the outdoor weathering characteristics are known. It is not possible to establish a precise correlation between accelerated and natural weathering because (1) there are geographical climatic variations, local weather variations, and variations in local pollutants, and (2) the relation between accelerated and natural weathering is material dependent. Acceleration factors differ between materials as well as between formulations of the same material. Guide G141 provides guidance regarding this issue.
Note 1: This practice can be used for other than bituminous materials, but the significance and use have not been evaluated.
SCOPE
1.1 This practice describes test conditions and procedures for fluorescent UV and condensation exposures conducted according to Practices G151 and G154 for bituminous roofing and waterproofing materials. (See Terminology G113.)  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4798/D4798M-11(2021)(Practice)
Standard Practice for Accelerated Weathering Test Conditions and Procedures for Bituminous Materials (Xenon-Arc Method)

SIGNIFICANCE AND USE
4.1 Tests conducted according to this practice are used to compare the weathering characteristics of bituminous materials versus a control material of known outdoor durability. It is not possible to establish a single relationship that is applicable to all materials between time in accelerated tests conducted according to this practice and time in natural weathering because (1) there are geographical climatic variations, local weather variations, and variations in local pollutants, and (2) the relation between accelerated and natural weathering is material dependent with differences in acceleration factors between materials as well as for different formulations of the same material. Guide G141 provides guidance regarding variability in outdoor and accelerated weathering tests and about the use of control materials.  
Note 1: It is recommended that outdoor weathering be used to validate the laboratory accelerated test in terms of performance ranking.
Note 2: This practice can be used for other than bituminous materials, but the significance and use have not been evaluated.
SCOPE
1.1 This practice covers test conditions and procedures for xenon-arc exposures according to Practices G151 and G155 for bituminous roofing and waterproofing materials. (See Terminology G113.)  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D5801-24(Test Method)
Standard Test Method for Toughness and Tenacity of Asphalt Materials

SIGNIFICANCE AND USE
4.1 This test method is useful in confirming that an asphalt cement has been modified with a material that provides a significant elastomeric component. Elastomer-modified asphalts can be characterized by their ability to be stretched to a large elongation while at the same time resisting further stretching. Toughness and tenacity are two parameters for measuring this ability.
Note 1: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method describes the procedure for measuring the toughness and tenacity of asphalt materials. Typically, the test method has been used to characterize elastomer-modified asphalts, although values for toughness and tenacity may be obtained for any type of polymer-modified or non-modified asphalt.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.2.1 Exception—Sample mass is given only in SI units. Sample mass as given in SI units should be regarded as standard. No other units of sample mass are included in this standard.  
1.3 Warning—Mercury has been designated by the United States Environmental Protection Agency and many state agencies as a hazardous material that can cause central nervous system, kidney, and liver damage. Mercury, or its vapor, may be hazardous to health and corrosive to materials. Caution should be taken when handling mercury and mercury-containing products. See the applicable Material Safety Data Sheet (MSDS) for details and EPA’s website—http://www.epa.gov/mercury/index.htm—for additional information. Users should be aware that selling mercury and/or mercury-containing products in your state may be prohibited by state law.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D5869/D5869M-07a(2023)(Practice)
Standard Practice for Dark Oven Heat Exposure of Roofing and Waterproofing Materials

SIGNIFICANCE AND USE
5.1 Roofing and waterproofing materials and systems undergo changes in physical properties as a result of being subjected to heat. They also undergo changes in physical properties as they age in service. Since service conditions vary widely, any relationship between changes observed in this practice and changes in service must be established by the user of this practice.
SCOPE
1.1 This practice establishes a procedure and conditions of temperature and time for heat exposure of roofing and waterproofing materials and systems in the presence of air.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    2 pages
    English language
    sale 15% off
ASTM
ASTM D2746/D2746M-18(2023)(Test Method)
Standard Test Method for Staining Tendency of Asphalt (Stain Index)

SIGNIFICANCE AND USE
4.1 This test method measures the tendency for oil components to separate spontaneously from asphalt. The separation of oil components can cause staining in asphalt roofing products and adjacent materials in storage and use.  
4.2 The stain index is related to the thermal stability of the asphalt. Higher stain index values indicate lower stability and greater tendency for staining.  
4.3 Use this procedure to determine the staining tendency of asphalt and to compare the results against a material for which the staining tendency is known.
SCOPE
1.1 This test method covers the determination of the staining tendency of asphalt and the assignment of a stain index proportional to the extent of staining observed.  
1.2 This test method is applicable to asphalts having ring-and-ball softening points of 85 °C [185 °F] or greater.  
Note 1: This test method may be modified for use with other bituminous materials with softening points less than 85 °C [185 °F] by using a different temperature than specified in Section 7 by agreement of the interested parties. The report of results from such a test may cite this method but must clearly state the temperature employed in the exception and acknowledge that the interpretation of results in Section 9 and the precision and bias stated in Section 10 may not apply.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D4799/D4799M-17(2023)(Practice)
Standard Practice for Accelerated Weathering Test Conditions and Procedures for Bituminous Materials (Fluorescent UV, Water Spray, and Condensation Method)

SIGNIFICANCE AND USE
4.1 This weathering apparatus is used for comparing the weathering characteristics of bituminous materials against a control material for which the outdoor weathering characteristics are known. It is not possible to establish a precise correlation between accelerated and natural weathering because (1) there are geographical climatic variations, local weather variations, and variations in local pollutants, and (2) the relation between accelerated and natural weathering is material dependent. Acceleration factors differ between materials as well as between formulations of the same material. Guide G141 provides guidance regarding this issue.
Note 1: This practice can be used for other than bituminous materials, but the significance and use have not been evaluated.
SCOPE
1.1 This practice describes test conditions and procedures for fluorescent UV and condensation exposures conducted according to Practices G151 and G154 for bituminous roofing and waterproofing materials. (See Terminology G113.)  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D7552-22(Test Method)
Standard Test Method for Determining the Complex Shear Modulus (G*) of Asphalt Mixtures Using Dynamic Shear Rheometer

SIGNIFICANCE AND USE
5.1 The complex shear modulus of asphalt mixtures is a fundamental property of the material. Test results at critical temperatures (Tcritical) are used for specifications for some mixes. Mixtures with stiffer binders, aged mixes, mixtures with higher amounts of fines (material finer than 75 µ), and mixtures with lower voids all tend to have higher complex shear modulus values than mixtures with less stiff binders, unaged mixes, mixtures with low levels of fines, and higher air voids. In general, mixtures with higher complex shear modulus values at a given service temperature will exhibit lower permanent deformation values than similar mixtures tested at the same temperature that have lower complex shear modulus values.  
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.
SCOPE
1.1 This test method covers the determination of the complex shear modulus of asphalt mixtures using torsion rectangular geometry on a dynamic shear rheometer (DSR). It is applicable to asphalt mixtures having complex shear modulus values greater than 1 × 104 Pa when tested over a range of temperatures from –40 °C to 76 °C at frequencies of 0.01 to 25 Hz and strains of 0.0005 % to 0.1 %. The determination of complex shear modulus is typically determined at 20 °C to 70 °C at 0.01 % strain at ten discrete frequency values covering 0.01 to 10 Hz. From these data, temperature or frequency master curves can be generated as required. This test method is intended for determining the complex shear modulus of asphalt mixtures as required for specification testing or quality control of asphalt mixture production.  
1.2 This test method is appropriate for laboratory-prepared and compacted mixtures, field-produced and laboratory-compacted mixtures or field cores, regardless of binder type or grade and regardless of whether RAP is used in the mixture. Due to the geometry of the specimens being tested this test method is not applicable to open-graded or SMA mixtures. It has been found to be appropriate for dense-graded mixtures, whether coarse- or fine-graded, with 19 mm or smaller nominal maximum aggregate size.  
1.3 Since a precision estimate for this standard has not been developed, the test method is to be used for research and informational purposes only. Therefore, this standard should not be used for acceptance or rejection of a material for purchasing purposes.  
1.4 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.5 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers...

  • Standard
    9 pages
    English language
    sale 15% off
  • Standard
    9 pages
    English language
    sale 15% off
ASTM
ASTM D6521-22(Practice)
Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV)

SIGNIFICANCE AND USE
5.1 This practice is designed to simulate the in-service oxidative aging that occurs in asphalt binders during pavement service. Residue from this conditioning practice may be used to estimate the physical or chemical properties of asphalt binders after several years of in-service aging in the field.  
5.2 Binders conditioned using this practice are normally used to determine specification properties in accordance with Specification D6373 or D8239, or AASHTO M 320.  
5.3 For asphalt binders of different grades or from different sources, there is no unique correlation between the time and temperature in this conditioning practice and in-service pavement age and temperature. Therefore, for a given set of in-service climatic conditions, it is not possible to select a single PAV conditioning time, temperature, and pressure that will predict the properties or the relative rankings of the properties of asphalt binders after a specific set of in-service exposure conditions.  
5.4 The relative degree of hardening of different asphalt binders varies with conditioning temperatures and pressures in the PAV. Therefore, two asphalt binders may age at a similar rate at one condition of temperature and pressure, but age differently at another condition. Hence, the relative rates of aging for a set of asphalts at PAV conditions may differ significantly from the actual in-service relative rates at lower pavement temperatures and ambient pressures.
SCOPE
1.1 This practice covers the conditioning of asphalt binders to simulate accelerated aging (oxidation) by means of pressurized air and elevated temperature. This is intended to simulate the changes in rheology which occur in asphalt binders during in-service oxidative aging, but may not accurately simulate the relative rates of aging. It is normally intended for use with residue from Test Method D2872 (RTFOT), which is designed to simulate plant aging.
Note 1: PAV conditioning has not been validated for materials containing particulate materials.  
1.2 The aging of asphalt binders during service is affected by ambient temperature and by mixture-associated variables, such as the volumetric proportions of the mix, the permeability of the mix, properties of the aggregates, and possibly other factors. This conditioning process is intended to provide an evaluation of the relative resistance of different asphalt binders to oxidative aging at selected elevated aging temperatures and pressures, but cannot account for mixture variables or provide the relative resistance to aging at in-service conditions.  
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.4 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard
Note 2: The quality of the results produced by this standard are dependent on the competence of the personnel performing the procedure and the capability, calibration, and maintenance of the equipment used. Agencies that meet the criteria of Specification D3666 are generally considered capable of competent and objective testing, sampling, inspection, etc. Users of this standard are cautioned that compliance with Specification D3666 alone does not completely ensure reliable results. Reliable results depend on many factors; following the suggestions of Specification D3666 or some similar acceptable guideline provides a means of evaluating and controlling some of those factors.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was de...

  • Standard
    7 pages
    English language
    sale 15% off
  • Standard
    7 pages
    English language
    sale 15% off