Standard Guide for Substrates Used in Testing Building Seals and Sealants

SIGNIFICANCE AND USE
4.1 The guide provides recommendations for substrates and methods of surface preparation to be used in comparative tests of building seals and sealants.
SCOPE
1.1 This guide describes the recommended standard substrates and their recommended surface preparation for use in standard tests of building seals and sealants.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
31-Dec-2013
Current Stage
Ref Project

Relations

Buy Standard

Guide
ASTM C1375-00(2014) - Standard Guide for Substrates Used in Testing Building Seals and Sealants
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: C1375 − 00 (Reapproved 2014)
Standard Guide for
Substrates Used in Testing Building Seals and Sealants
This standard is issued under the fixed designation C1375; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 6. Glass Substrate
1.1 This guide describes the recommended standard sub- 6.1 The glass used shall be float glass, which conforms to
strates and their recommended surface preparation for use in Specification C1036, Type I, Class 1, q3. This corresponds to
standard tests of building seals and sealants.
a glass that is formed on a float line, is transparent, clear, and
intended for architectural fenestration applications.
1.2 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
6.2 Float glass has two surfaces, which are not necessarily
responsibility of the user of this standard to establish appro-
identical in surface chemistry. There is a tin side, which was in
priate safety and health practices and determine the applica-
contact with a batch of molten tin, and an air side, which did
bility of regulatory limitations prior to use.
not have this intimate contact. These two surfaces may or may
not have the same adhesion properties with a given sealant. It
2. Referenced Documents
is best to test both surfaces for control of testing. If only one
2.1 ASTM Standards:
surface is to be tested, however, it is preferred to use the air
C33 Specification for Concrete Aggregates
side as this is likely a more consistent surface.
C150 Specification for Portland Cement
6.3 Determination of Air Side Versus Tin Side:
C305 Practice for Mechanical Mixing of Hydraulic Cement
6.3.1 Clean the glass as described in 6.4.
Pastes and Mortars of Plastic Consistency
6.3.2 Expose the substrate to the radiation from a short
C566 Test Method forTotal Evaporable Moisture Content of
wavelength UV light source of approximately 254 nm. The tin
Aggregate by Drying
sidewillfluoresceanddisplayahazywhitereflectance.Theair
C717 Terminology of Building Seals and Sealants
side will not show this effect under the same UV light.
C1036 Specification for Flat Glass
(Warning—Protect eyes and skin from exposure to UV light
when using a UV light source.)
3. Terminology
6.4 Surface Preparation—The substrate should be cleaned
3.1 Definitions—The terms used in this guide are in accor-
thoroughlywithasolutionof50 %isopropylalcohol(IPA)and
dance with Terminology C717.
50 % deionized or distilled water and wiped with a clean, lint
4. Significance and Use
free, soft cloth or paper towel. Prepared specimens must be
used within the same working day. Check surfaces for clean-
4.1 The guide provides recommendations for substrates and
liness by running distilled or deionized water over the glass
methods of surface preparation to be used in comparative tests
surface held in a vertical position. Cleaned parts must pass
of building seals and sealants.
water-break inspection as indicated by maintenance of a
5. Comparison to Other Standards continuous film of water on the surface for not less than 30 s.
Panels failing the water-break inspection should be recleaned
5.1 The ASTM committee with jurisdiction over this stan-
1 until the surface can maintain the continuous film of water.
dard is not aware of any comparable standards published by
other organizations.
7. Aluminum Substrates
7.1 The aluminum shall be one of two materials, depending
ThisguideisunderthejurisdictionofASTMCommitteeC24onBuildingSeals
on the test sample configuration:
and Sealants and is the direct responsibility of SubcommitteeC24.10
onSpecifications, Guides and Practices.
7.1.1 For tests requiring a sheet, less than 6 mm thick, the
Current edition approved Jan. 1, 2014. Published January 2014. Originally
sheet shall be made of aluminum alloy 5005-H34.
approved in 1997. Last previous edition approved in 2009 as C1375 – 00(2009).
7.1.2 For tests requiring a thicker plate, 6 mm or greater, the
DOI: 10.1520/C1375-00R14.
For referenced ASTM standards, visit the ASTM website, www.astm.org, or plate shall be made of aluminum alloy 6063-T5.
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
7.2 The aluminum for either a sheet or plate shall have a
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. clear, Class II anodized finish conforming toAA-M12C22A31
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
C1375 − 00 (2014)
(refer to Aluminum Association Circular 45). The anodized
1 part Type III Portland Cement
2parts+2MC Sand
surface shall be sealed using a hot water process.
0.5 part – 2 MC Water
7.3 Surface Preparation—The substrate should be cleaned
where MC is the moisture content of the sand expressed as a decimal as
thoroughlywithasolutionof50 %isopropylalcohol(IPA)and
determined in 8.3.2.
50 % dionized or distilled water and wiped with a clean, soft,
8.4.2 For example, if 1000 g total mortar are required to fill
lint-free cloth or paper towel. At the request of the
the mold, and the MC of the sand has been determined to be
manufacturer, cleaning with methyl ethyl ketone or similar
0.10, then the total weight of sand added must be increased by
solvent may precede the isopropyl wash. Panels must pass the
10 % or 57.1 g and the amount of water actually added must be
water-break free test described in 6.4. Prepared substrates must
reduced by the same amount. The recipe now becomes:
be used within the same working day.
1 part = 286 g Type III Portland Cement
2parts+2MC=571+57.1= 628.1 g wet sand
8. Mortar Substrates
0.5 part – 2 MC = 143 – 57.1 = 85.9 g actual water
1000 g total recipe
...