ASTM A414/A414M-10
(Specification)Standard Specification for Steel, Sheet, Carbon, and High-Strength, Low-Alloy for Pressure Vessels
Standard Specification for Steel, Sheet, Carbon, and High-Strength, Low-Alloy for Pressure Vessels
ABSTRACT
This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Tensile and yield strengths shall be determined after a tension test of the sheets. The material shall be furnished without removing the hot-rolled oxide or scale. When required, the material may be specified to be pickled or blast cleaned. When specified to be pickled or blast cleaned, the material shall be furnished oiled. When required, pickled or blast-cleaned material may be specified to be furnished dry.
SCOPE
1.1 This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Welding and brazing technique is of fundamental importance and shall be in accordance with commercial practices.
1.2 The following grades are included in this specification:
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A414/A414M −10
StandardSpecification for
Steel, Sheet, Carbon, and High-Strength, Low-Alloy for
1
Pressure Vessels
This standard is issued under the fixed designationA414/A414M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* be used independently of the other. Combining values from the
two systems may result in nonconformance with the specifi-
2
1.1 This specification covers hot-rolled carbon steel sheet
cation.
for pressure vessels involving fusion welding or brazing.
1.5 Tolerances are found in General Requirements Specifi-
Welding and brazing technique is of fundamental importance
cationsA568/A568MandA635/A635M.TheappropriateGen-
and shall be in accordance with commercial practices.
eral Requirements specification is applied based on the thick-
1.2 The following grades are included in this specification:
ness and width of the product ordered.
Mechanical Requirements
2. Referenced Documents
Grade Yield Strength, min Tensile Strength, min
3
ksi MPa ksi MPa
2.1 ASTM Standards:
A370 Test Methods and Definitions for Mechanical Testing
A 25 170 45 310
of Steel Products
B 30 205 50 345
C 33 230 55 380
A568/A568M Specification for Steel, Sheet, Carbon,
D 35 240 60 415
Structural,andHigh-Strength,Low-Alloy,Hot-Rolledand
E 38 260 65 450
F 42 290 70 485
Cold-Rolled, General Requirements for
G 45 310 75 515
A635/A635M Specification for Steel, Sheet and Strip,
H 45 310 75 515
Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon,
Structural, High-Strength Low-Alloy, and High-Strength
1.3 Hot-rolled carbon steel sheet is generally furnished in
Low-Alloy with Improved Formability, General Require-
cut lengths and to decimal thickness only. Coils may be
ments for
furnished, provided tension test specimens are taken to repre-
A941 TerminologyRelatingtoSteel,StainlessSteel,Related
sent the middle of the slab as required by 6.1.3. The purchaser
Alloys, and Ferroalloys
should recognize this may require cutting the coils to obtain
test samples and results in half-size coils. The sheet is
3. Terminology
furnished to the following size limits:
3.1 Definitions—For definitions of other terms used in this
Width, in. [mm]
specification refer to Terminology A941.
Thickness, in. [mm] Over 12 [Over 300]
3.2 Definitions of Terms Specific to This Standard:
3.2.1 lot, n—all coils of one thickness and width combina-
0.270 to 0.230 [7.0 to 6.0] sheet (coils only)
Under 0.230 to 0.057 [6.0 to 1.5] sheet
tion from one heat and one rolling on the hot mill, up to 100
tons [90 tonnes] total mass.
1.4 The values stated in either inch-pound units or SI units
are to be regarded separately as standard. Within the text, the
4. Ordering Information
SI units are shown in brackets. The values stated in each
system are not exact equivalents; therefore, each system shall 4.1 Orders for material under this specification shall include
the following information, as required, to describe the material
adequately:
4.1.1 Designationorspecificationnumber,dateofissue,and
1
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
grade,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
A01.19 on Steel Sheet and Strip.
Current edition approved April 1, 2010. Published April 2010. Originally
3
approved in 1971. Last previous edition approved in 2009 as A414/A414M – 09. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
DOI: 10.1520/A0414_A0414M-10. contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
2
For ASME Boiler and Pressure Vessel Code applications see related Specifi- Standards volume information, refer to the standard’s Document Summary page on
cation SA-414 in Section 11 of that Code. the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A414/A414M−10
TABLE 2 Limits on Unspecified Elements (See 5.1.1)
4.1.1.1 Grade H may be substituted for Grade G upon
A
agreement between the purchaser and producer, Copper, max % Heat analysis 0.40
Product analysis 0.43
4.1.2 Copper bearing steel, when required,
A
Nickel, max % Heat analysis 0.40
4.1.3 Special requirements, if required,
Product analysis 0.43
A,B
4.1.3.1 Charpy impact properties may be specified for Chromium, max % Heat analysis 0.30
Product analysis 0.34
Grade H at the time of order,
A,B
Molybdenum, max % Heat analysis 0.12
4.1.3.2 Strength levels at other than room temperature may
Product analysis 0.1
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A414/A414M–09 Designation: A414/A414M – 10
Standard Specification for
Steel, Sheet, Carbon, for Pressure VesselsSteel, Sheet,
1
Carbon, and High-Strength, Low-Alloy for Pressure Vessels
This standard is issued under the fixed designationA414/A414M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
2
1.1 This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Welding
and brazing technique is of fundamental importance and shall be in accordance with commercial practices.
1.2 The following grades are included in this specification:
Mechanical Requirements
Grade Yield Strength, min Tensile Strength, min
ksi MPa ksi MPa
A 25 170 45 310
B 30 205 50 345
C 33 230 55 380
D 35 240 60 415
E 38 260 65 450
F 42 290 70 485
G 45 310 75 515
H 45 310 75 515
1.3 Hot-rolled carbon steel sheet is generally furnished in cut lengths and to decimal thickness only. Coils may be furnished,
provided tension test specimens are taken to represent the middle of the slab as required by 5.1.46.1.3. The purchaser should
recognize this may require cutting the coils to obtain test samples and results in half-size coils. The sheet is furnished to the
following size limits:
Width, in. [mm]
Thickness, in. [mm] Over 12 [Over 300]
0.270 to 0.230 [7.0 to 6.0] sheet (coils only)
Under 0.230 to 0.057 [6.0 to 1.5] sheet
1.4 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.5 Tolerances are found in General Requirements Specifications A568/A568M and A635/A635M. The appropriate General
Requirements specification is applied based on the thickness and width of the product ordered.
2. Referenced Documents
3
2.1 ASTM Standards: ASTM Standards:
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A568/A568M Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled,
General Requirements for
A635/A635M Specification for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural,
High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General Requirements for Specification
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.19
on Steel Sheet and Strip.
Current edition approved Nov.April 1, 2009.2010. Published December 2009.April 2010. Originally approved in 1971. Last previous edition approved in 20072009 as
A414/A414M – 079. DOI: 10.1520/A0414_A0414M-109.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SA-414 in Section 11 of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A414/A414M – 10
for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural, High-Strength Low-Alloy, and
High-Strength Low-Alloy with Improved Formability, General Requirements for
A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
3. Terminology
3.1 Definitions: For definitions of other terms used in this specification refer to Terminology A941.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 lot, n—all coils of one thickness and width combination from one heat and one rolling on the hot mill, up to 100 tons [90
tonnes] total mass.
4. Ordering Information
3.1Orders for material under this specification shall include the following information, as required, to describe the material
adequately:
3.1.1Designation or specification number, date of issue, and grade,
3.1.2Copper bearing
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation:A414/A414M–09 Designation: A414/A414M – 10
Standard Specification for
Steel, Sheet, Carbon, for Pressure VesselsSteel, Sheet,
1
Carbon, and High-Strength, Low-Alloy for Pressure Vessels
This standard is issued under the fixed designationA414/A414M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
2
1.1 This specification covers hot-rolled carbon steel sheet for pressure vessels involving fusion welding or brazing. Welding
and brazing technique is of fundamental importance and shall be in accordance with commercial practices.
1.2 The following grades are included in this specification:
Mechanical Requirements
Grade Yield Strength, min Tensile Strength, min
ksi MPa ksi MPa
A 25 170 45 310
B 30 205 50 345
C 33 230 55 380
D 35 240 60 415
E 38 260 65 450
F 42 290 70 485
G 45 310 75 515
H 45 310 75 515
1.3 Hot-rolled carbon steel sheet is generally furnished in cut lengths and to decimal thickness only. Coils may be furnished,
provided tension test specimens are taken to represent the middle of the slab as required by 5.1.46.1.3. The purchaser should
recognize this may require cutting the coils to obtain test samples and results in half-size coils. The sheet is furnished to the
following size limits:
Width, in. [mm]
Thickness, in. [mm] Over 12 [Over 300]
0.270 to 0.230 [7.0 to 6.0] sheet (coils only)
Under 0.230 to 0.057 [6.0 to 1.5] sheet
1.4 Thevaluesstatedineitherinch-poundunitsorSIunitsaretoberegardedseparatelyasstandard.Withinthetext,theSIunits
are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used
independently of the other. Combining values from the two systems may result in nonconformance with the specification.
1.5 Tolerances are found in General Requirements Specifications A568/A568M and A635/A635M. The appropriate General
Requirements specification is applied based on the thickness and width of the product ordered.
2. Referenced Documents
3
2.1 ASTM Standards: ASTM Standards:
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A568/A568M Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled,
General Requirements for
A635/A635M Specification for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural,
High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, General Requirements for Specification
1
This specification is under the jurisdiction ofASTM CommitteeA01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of SubcommitteeA01.19
on Steel Sheet and Strip.
Current edition approved Nov.April 1, 2009.2010. Published December 2009.April 2010. Originally approved in 1971. Last previous edition approved in 20072009 as
A414/A414M – 079. DOI: 10.1520/A0414_A0414M-109.
2
For ASME Boiler and Pressure Vessel Code applications see related Specification SA-414 in Section 11 of that Code.
3
For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1
---------------------- Page: 1 ----------------------
A414/A414M – 10
for Steel, Sheet and Strip, Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Structural, High-Strength Low-Alloy, and
High-Strength Low-Alloy with Improved Formability, General Requirements for
A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
3. Terminology
3.1 Definitions: For definitions of other terms used in this specification refer to Terminology A941.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 lot, n—all coils of one thickness and width combination from one heat and one rolling on the hot mill, up to 100 tons [90
tonnes] total mass.
4. Ordering Information
3.1Orders for material under this specification shall include the following information, as required, to describe the material
adequately:
3.1.1Designation or specification number, date of issue, and grade,
3.1.2Copper bearing
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.