ASTM A636-08(2013)

(Specification)

Standard Specification for Nickel Oxide Sinter

Standard Specification for Nickel Oxide Sinter

ABSTRACT
This specifications covers standards for Grade 75 nickel oxide sinter to be used for alloying in iron and steel melting. The material shall adhere to specified nickel, cobalt, copper, iron, and sulfur contents. Guidelines for sampling and treatment of materials for chemical analysis are given.
SCOPE
1.1 This specification covers one grade of nickel oxide sinter, designated as 75 used for alloying in iron and steel melting.

General Information

Status
Historical
Publication Date
31-Mar-2013
ICS
77.150.40 - Nickel and chromium products
Technical Committee
A01 - Steel, Stainless Steel and Related Alloys
Drafting Committee
A01.18 - Castings
Current Stage
Ref Project

Relations

Replaces
ASTM A636-08 - Standard Specification for Nickel Oxide Sinter
Effective Date
01-Apr-2013
Replaced By
ASTM A636-08(2018) - Standard Specification for Nickel Oxide Sinter
Effective Date
01-Sep-2018
Referred By
ASTM A1025/A1025M-10(2020) - Standard Specification for Ferroalloys and Other Alloying Materials, General Requirements
Effective Date
01-Apr-2013

Buy Standard

ASTM A636-08(2013) - Standard Specification for Nickel Oxide SinterASTM A636-08(2013) - Standard Specification for Nickel Oxide Sinter
PreviousNext
Technical specification
ASTM A636-08(2013) - Standard Specification for Nickel Oxide Sinter
English language
2 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)


NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A636 −08 (Reapproved 2013)
Standard Specification for
Nickel Oxide Sinter
This standard is issued under the fixed designation A636; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 5. Sampling for Chemical Analysis
1.1 This specification covers one grade of nickel oxide 5.1 The material shall be sampled in accordance with
sinter, designated as 75 used for alloying in iron and steel procedures outlined below:
melting. 5.1.1 The sample shall be taken by cutting across the entire
stream at regular intervals during the time of movement of the
2. Referenced Documents
mass being sampled. The quantity to be taken at each interval
2.1 ASTM Standards: and the number of such intervals shall be so proportioned that
the total quantity taken shall amount to not less than 0.40 % of
A1025 Specification for Ferroalloys and Other Alloying
Materials, General Requirements the total material being sampled.
5.2 Treatment of Sample:
3. General Conditions for Delivery
5.2.1 In the case of nickel oxide sinter 75, the sample
3.1 Materials furnished to this specification shall conform to
representing each shipment or lot shall be reduced in amount
the requirements of Specification A1025, including any supple-
using a riffle splitter or other suitable mechanical splitter to
mentary requirements that are indicated in the purchase order.
1000 g.This 1000-g sample shall be placed in an oven at 250°F
Failure to comply with the general requirements of Specifica- 1
(121°C) for ⁄2 h to remove any traces of moisture, and then
tion A1025 constitutes nonconformance with this specification.
pulverized to pass an 80-mesh screen using appropriate equip-
In case of conflict between the requirements of this specifica-
ment to avoid sample contamination. Approximately 250 g of
tion and Specification A1025, this specification shall prevail.
this pulverized material shall be split out for copper and sulfur
assays, using a riffle splitter or other suitable mechanical
4. Chemical Requirements
splitter. The unused portion of individual shipment (or lot)
4.1 The chemical requirements are shown in Table 1.
samples whose copper and sulphur assays are within specifi-
cation shall be combined by weight into two, three, or four lot
composites. Approximately 250 g
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM A494/A494M-22(Specification)
Standard Specification for Castings, Nickel and Nickel Alloy

ABSTRACT
This specification covers nickel, nickel-copper, nickel-copper-silicon, nickel-molybdenum, nickel-chromium, and nickel-molybdenum-chromium alloy castings for corrosion resistant service. The castings shall be heat treated. When Class 1 is specified, grades CY40 and M25S shall be supplied in the as-cast condition. When Class 2 is specified, grades CY40 and M25S shall be supplied in the solution treated condition. When Class 3 is specified, grade M25S shall be supplied in the age-hardened condition. The chemical composition requirements of the alloys are presented. The tensile property requirements including the heat treatment procedure for the castings are presented in detail. It is required that one tension test shall be made from each master heat except for grades M25S and CY5SnBiM when the master heat is used to pour the castings. One tension test shall be made from each melt except for grades M25S and CY5SnBiM. Test results shall conform to the specified tensile requirements.
SCOPE
1.1 This specification covers nickel, nickel-copper, nickel-copper-silicon, nickel-molybdenum, nickel-chromium, and nickel-molybdenum-chromium alloy castings for corrosion-resistant service.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    8 pages
    English language
    sale 15% off
  • Technical specification
    8 pages
    English language
    sale 15% off
ASTM
ASTM A636-08(2018)(Specification)
Standard Specification for Nickel Oxide Sinter

ABSTRACT
This specifications covers standards for Grade 75 nickel oxide sinter to be used for alloying in iron and steel melting. The material shall adhere to specified nickel, cobalt, copper, iron, and sulfur contents. Guidelines for sampling and treatment of materials for chemical analysis are given.
SCOPE
1.1 This specification covers one grade of nickel oxide sinter, designated as 75, used for alloying in iron and steel melting.  
1.2 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM A560/A560M-12(2018)(Specification)
Standard Specification for Castings, Chromium-Nickel Alloy

ABSTRACT
This guide covers standard specification for chromium-nickel alloy castings intended for heat-resisting and elevated-temperature corrosion applications, such as structural members, containers, supports, hangers, spacers, and the like, in corrosive environments. The alloy for the castings shall be made by electric-arc or induction-furnace process. Heat treatment shall be performed wherein the material shall conform to the required chemical composition for carbon, manganese, silicon, sulfur, phosphorus, nitrogen, nitrogen + carbon, iron, titanium, aluminum, columbium, chromium, and nickel. Tensile and Charpy requirements of the alloy used for the casting shall conform to the specified values of tensile strength, yield point, elongation, and unnotched Charpy impact. Mechanical tests like tension test and impact test, if required, shall be made from each melt.
SCOPE
1.1 This specification covers chromium-nickel alloy castings intended for heat-resisting and elevated-temperature corrosion applications, such as structural members, containers, supports, hangers, spacers, and the like, in corrosive environments up to 2000 °F [1090 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B572-24(Specification)
Standard Specification for Heat and Corrosion Resistant High Temperature Alloy Bar or Rod

ABSTRACT
This specification covers alloys UNS N06002, UNS N06230, UNS N12160, and UNS R30556 in the form of rod for heat resisting and general-corrosive service. The material shall conform to the required chemical composition for nickel, iron, chromium, cobalt, molybdenum, tungsten, carbon, silicon, manganese, phosphorus, sulfur, columbium, tantalum, aluminum, zirconium, lanthanum, nitrogen, boron, and titanium. The mechanical properties of the material at room temperature shall conform to the prescribed values of tensile strength, yield strength, and elongation. The alloys shall undergo chemical analysis and mechanical testing, sampling for chemical analysis, and sampling for mechanical testing.
SCOPE
1.1 This specification2 covers alloys in the form of bar or rod that are typically used for (though not limited to) heat resisting and general-corrosive service.  
1.2 Alloys that can currently be certified to this specification are UNS N06002, UNS N06230, UNS N12160, and UNS R30556.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B804-02(2024)(Specification)
Standard Specification for UNS N08367 and UNS N08926 Welded Pipe

ABSTRACT
This guide covers UNS N08367 and UNS N08926 welded pipe for general corrosion applications. The joints of the specimens shall be double or single welded and full penetration welded made. The welds shall be made either manually or automatically by an electric process involving the deposition of filler metal according to the class specified. The weld surface on either side of the weld shall be flush with the base plate. The contour of the reinforcement shall be reasonably smooth and free of irregularities. The deposited metal shall be fused uniformly into the plate surface. Transverse tension tests shall be made across the welded joint to assure that it must have the same minimum ultimate tensile strength as the specified minimum ultimate tensile strength of the plate. Transverse guided weld bend test shall be used to check cracks or other imperfections. The pipe shall be furnished with smooth ends, free of burrs and injurious defects and shall have a workmanlike finish.
SCOPE
1.1 This specification covers UNS N08367 and UNS N08926 welded pipe for general corrosion applications. (Although no restrictions are placed on the sizes of pipe that may be furnished under this specification, commercial practice is commonly limited to sizes not less than 8 in. nominal diameter.)  
1.2 Six classes of pipe are covered as follows:  
1.2.1 Class 1 pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed.  
1.2.2 Class 2 pipe shall be double welded by processes employing filler metal in all passes. No radiography is required.  
1.2.3 Class 3 pipe shall be double welded by processes employing filler metal in all passes except the inside root weld may be made without the addition of filler metal. Welds are to be completely radiographed.  
1.2.4 Class 4 pipe shall be double welded by processes employing filler metal in all passes except the inside root weld may be made without the addition of filler metal. No radiography is required.  
1.2.5 Class 5 pipe shall be single welded by processes employing filler metal in all passes except that the pass exposed to the inside pipe surface may be made without the addition of filler metal. Welds are to be completely radiographed.  
1.2.6 Class 6 pipe shall be single welded by processes employing filler metal in all passes except that the pass exposed to the inside pipe surface may be made without the addition of filler metal. No radiography is required.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The following safety hazards caveat pertains only to the test methods portion, Section 13, of this standard: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B160-24(Specification)
Standard Specification for Nickel Rod and Bar

ABSTRACT
This specification covers nickel (UNS N02200), low carbon nickel (UNS N02201), and solution strengthened nickel (UNS N02211) in the form of hot-worked, cold-worked, or annealed rods and bars of round, square, hexagonal, or rectangular solid section. The material shall conform to the chemical composition limits specified for nickel, copper, iron, manganese, carbon, silicon, and sulfur. Mechanical requirements including tensile strength, yield strength, and elongation are given for specific conditions and diameter or distance between parallel surfaces. Chemical analysis, tension test, and hardness test shall be performed.
SCOPE
1.1 This specification2 covers nickel (UNS N02200),3 low-carbon nickel (UNS N02201),3 and solution-strengthened nickel (UNS N02211) in the form of hot-worked and cold-worked rod and bar in the conditions shown in Table 1.    
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B166-24(Specification)
Standard Specification for Nickel-Chromium-Aluminum Alloy, Nickel-Chromium-Iron Alloys, Nickel-Chromium-Cobalt-Molybdenum Alloy, Nickel-Iron-Chromium-Tungsten Alloy, and Nickel-Chromium-Molybdenum-Copper Alloy Rod, Bar, and Wire

ABSTRACT
This specification covers nickel-chromium-iron alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, N06045, and N06696) and nickel-chromium-cobaltmolybdenum alloy (UNS N06617) in the form of hot-finished and cold-worked rounds, squares, hexagons, rectangles, and cold-worked wire. The material shall conform to the composition limits specified in a reference material. The material shall be uniform in quality and condition, smooth, commercially straight or flat, and free of injurious imperfections. Mechanical properties of the alloys like tensile strength, yield strength, elongation, and hardness shall be determined by tension and hardness tests.
SCOPE
1.1 This specification2 covers nickel-chromium-aluminum alloy, nickel-chromium-iron alloys,3 nickel-chromium-cobalt-molybdenum alloy, nickel-iron-chromium-tungsten alloy, and nickel-chromim-molybdenum-copper alloy in the form of hot-finished and cold-worked rounds, squares, hexagons, rectangles, and cold-worked wire.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary caveat pertains only to the test methods portion, Section 12, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    9 pages
    English language
    sale 15% off
  • Technical specification
    9 pages
    English language
    sale 15% off
ASTM
ASTM B573-24(Specification)
Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys Bar or Rod

ABSTRACT
This specification covers rods of nickel-molybdenum-chromium-iron alloys with UNS Nos. N10003 and N10242 for use in general corrosive service. Specimens shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (diameter, length, out-of-roundness, weight, and straightness), mechanical (tensile and yield strengths, and elongation), and chemical composition requirements.
SCOPE
1.1 This specification2 covers nickel-molybdenum-chromium-iron alloys in the form of bar or rod. The alloys are typically for general corrosive service but not limited to this usage.  
1.2 Alloys that can currently be certified to this specification are UNS N10003 and UNS N10242.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    4 pages
    English language
    sale 15% off
  • Technical specification
    4 pages
    English language
    sale 15% off
ASTM
ASTM B473-24(Specification)
Standard Specification for Nickel-Iron-Chromium-Molybdenum-Copper Alloy Bar and Wire

ABSTRACT
This specification covers UNS N08020, UNS N08026, and UNS N08024 nickel alloy bar and wire. The alloys shall be furnished in the stabilized-annealed condition, solution-annealed condition, or annealed condition. The material shall conform to the requirements as to chemical composition prescribed. The material shall conform to the applicable requirements as to mechanical properties prescribed. Chemical analysis and tension test shall be made to conform to the requirements specified.
SCOPE
1.1 This specification2 covers UNS N08020 bar and wire other than required for reforging.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM B637-23(Specification)
Standard Specification for Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service

ABSTRACT
This specification covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for high-temperature service. Chemical analysis shall be performed on the alloy and shall conform to the chemical composition requirement in carbon, manganese, silicon, phosphorus, sulfur, chromium, cobalt, molybdenum, columbium, tantalum, titanium, aluminum, zirconium, boron, iron, copper, and nickel. The material shall follow recommended annealing treatment, solution treatment, stabilizing treatment, and precipitation hardening treatment. Tension testing, hardness testing and stress-rupture testing shall be performed on the material and shall comply to the required tensile strength, yield strength, elongation, reduction in area, and Brinell hardness.
SCOPE
1.1 This specification2 covers hot- and cold-worked precipitation-hardenable nickel alloy rod, bar, forgings, and forging stock for moderate or high temperature service (Table 1).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off