Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe

Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe

ABSTRACT
This specification covers UNS N06625, N06219, and N08825 nickel-alloy welded pipe in the annealed condition. The pipe shall be manufactured from flat-rolled alloy by an automatic welding process with no additional filler metal. The pipe material shall be cold-worked, annealed, and nondestructively tested. The pipe shall be furnished with oxide removed. The material shall conform to the composition required by the specification. The pipe shall be subjected to tensile, yield, elongation, transverse guided bend, and nondestructive test requirements. Nondestructive test includes hydrostatic, pneumatic, eddy current, ultrasonic, leak, and electric testing. Acceptable size limit of cracks or other defect after bending test is specified.
SCOPE
1.1 This specification covers welded UNS N06625,* UNS N06219* and UNS N08825* pipe in the annealed condition (temper) for general corrosion applications.
1.2 This specification covers pipe sizes in schedules shown in the Permissible Variations in Outside Diameter and Wall Thickness for Welded Pipe table of Specification B 775.
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.
1.4 The following precautionary caveat pertains only to the test methods portion, Section , of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

Status
Historical
Publication Date
30-Apr-2005
ICS
77.120.40 - Nickel, chromium and their alloys
Technical Committee
B02 - Nonferrous Metals and Alloys
Drafting Committee
B02.07 - Refined Nickel and Cobalt and Their Alloys
Current Stage
Ref Project

Relations

Replaces
ASTM B705-03 - Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe
Effective Date
01-May-2005
Replaced By
ASTM B705-05(2009) - Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe
Effective Date
01-Oct-2009
Referred By
ASTM B366/B366M-23 - Standard Specification for Factory-Made Wrought Nickel and Nickel Alloy Fittings
Effective Date
01-May-2005
Referred By
ASTM B775/B775M-22 - Standard Specification for General Requirements for Nickel and Nickel Alloy Welded Pipe
Effective Date
01-May-2005

Buy Standard

ASTM B705-05 - Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded PipeASTM B705-05 - Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe
PreviousNext
Technical specification
ASTM B705-05 - Standard Specification for Nickel-Alloy (UNS N06625, N06219 and N08825) Welded Pipe
English language
3 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: B 705 – 05
Standard Specification for
Nickel-Alloy (UNS N06625, N06219 and N08825) Welded
1
Pipe
This standard is issued under the fixed designation B 705; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
3
1. Scope* 2.2 ASME Boiler and Pressure Vessel Code
Section IX Welding and Brazing Qualifications
1.1 This specification covers welded UNS N06625,* UNS
N06219* and UNS N08825* pipe in the annealed condition
3. General Requirement
(temper) for general corrosion applications.
3.1 Material furnished in accordance with this specification
1.2 This specification covers pipe sizes in schedules shown
shall conform to the applicable requirements of the current
in the Permissible Variations in Outside Diameter and Wall
edition of Specification B 775 unless otherwise provided
Thickness for Welded Pipe table of Specification B 775.
herein.
1.3 The values stated in inch-pound units are to be regarded
as the standard. The values given in parentheses are for
4. Definition of Terms
information only.
4.1 Class 1—Welded, cold-worked, annealed, and nonde-
1.4 The following precautionary caveat pertains only to the
structively tested in accordance with 9.1.
test methods portion, Section 8, of this specification: This
4.2 Class 2—Welded, cold-worked, annealed, and nonde-
standard does not purport to address all of the safety concerns,
structively tested in accordance with 9.2.
if any, associated with its use. It is the responsibility of the user
4.3 Grade 1—Annealed condition, relevant for UNS
of this standard to become familiar with all hazards including
N06625.
those identified in the appropriate Material Safety Data Sheet
4.4 Grade 2—Solution annealed condition, relevant for
for this product/material as provided by the manufacturer, to
UNS N06625.
establish appropriate safety and health practices, and deter-
mine the applicability of regulatory limitations prior to use.
5. Ordering Information
5.1 It is the responsibility of the purchaser to specify all
2. Referenced Documents
requirements that are necessary for the safe and satisfactory
2
2.1 ASTM Standards:
performance of material ordered under this specification.
B 751 Specification for General Requirements for Nickel
Examples of such requirements include, but are not limited to,
and Nickel Alloy Welded Tube
the following:
B 775 Specification for General Requirements for Nickel
5.1.1 Alloy name or UNS number,
and Nickel Alloy Welded Pipe
5.1.2 ASTM designation,
B 880 SpecificationforGeneralRequirementsforChemical
5.1.3 Dimensions:
Check Analysis Limits for Nickel, Nickel Alloys, and
5.1.3.1 Pipe size,
Cobalt Alloys
5.1.3.2 Length (specific or random),
5.1.4 Class (see 3),
5.1.5 Grade if UNS N06625 is specified. If neither grade of
N06625 is specified, grade 1 will be supplied.
1
This specification is under the jurisdiction of ASTM Committee B02 on
5.1.6 Quantity (feet or number of pieces),
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
5.1.7 Certification— State if certification is required,
B02.07 on Refined Nickel and Cobalt and Their Alloys.
5.1.8 Samples for Product (Check) Analysis—State whether
Current edition approved May 1, 2005. Published June 2005. Originally
approved in 1982. Last previous edition approved in 2003 as B 705 – 03. samples for product (check) analysis should be furnished (7.2),
* New designation established in accordance with Practice E 527 and SAE
and
J 1086, Practice for Numbering Metals and Alloys (UNS).
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
3
Standards volume information, refer to the standard’s Document Summary page on Available from American Society of Mechanical Engineers (ASME), ASME
the ASTM website. International Headquarters, Three Park Ave., New York, NY 10016-5990.
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1

---------------------- Page: 1 ----------------------
B705–05
TABLE 2 Mechanical Property Requirements
5.1.9 Purchaser Inspection—If purchaser wishes to witness
tests or inspection of material at place of manufacture, the Elonga-
Yield Strength tionin2
purchase order must so state indicating which tests or inspec-
Tensile Strength
Alloy Grade 0.2 % Offset, in.or50
min, psi (MPa)
tions are to be witnesses.
min, psi (MPa) mm, min,
%
6. Material and Manufacture
UNS N06625 1 (annealed) 120 000 (827) 60 000 (414) 30
UNS N06625 2 (solution 100 00 (690)
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM B704-23(Specification)
Standard Specification for Welded Nickel Alloy Tubes

ABSTRACT
This specification covers welded tubes made of UNS N06625, UNS N06219 and UNS N08825 alloys for use in boilers, heat exchangers and condensers for general corrosion prevention in either low or high-temperature environments. This standard contains information on manufacturing, chemical composition, mechanical properties and dimensional requirements for the welded tubes.
SCOPE
1.1 This specification covers welded UNS N06219, UNS N06625, UNS N08642, UNS N08825, and UNS N08827 nickel alloy boiler, heat exchanger, and condenser tubes for general corrosion resisting and low or high-temperature service.  
1.2 This specification covers tubes 1/8 in. to 5 in. (3.18 mm to 127 mm), inclusive, in outside diameter and 0.015 in. to 0.500 in. (0.38 mm to 12.70 mm), inclusive, in wall thickness. Specification B751 lists the dimensional requirements of these sizes. Tubes having other dimensions may be furnished provided such tubing complies with all other requirements of this specification.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B39-79(2023)(Specification)
Standard Specification for Nickel

ABSTRACT
This specification covers refined nickel primarily produced from ore or matte or similar raw material. Chemical analysis shall be performed on the metal and shall conform to the chemical composition requirements in nickel, cobalt, copper, carbon, iron, sulfur, phosphorus, manganese, silicon, arsenic, lead, antimony, bismuth, tin, and zinc. The principal commercial forms are cathodes, briquettes, and pellets. Cathodes shall be sampled using template drilling procedure.
SCOPE
1.1 This specification covers refined nickel primarily produced from ore or matte or similar raw material. The principal commercial forms are cathodes, briquettes, and pellets.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B924-02(2022)(Specification)
Standard Specification for Seamless and Welded Nickel Alloy Condenser and Heat Exchanger Tubes With Integral Fins

ABSTRACT
This specification covers seamless and welded nickel alloy tubing with either or both external and internal surfaces have been modified by cold forming. The cold forming process produces an enhanced surface for improved heat transfer in the tubing that makes these ideal for use in surface condensers, evaporators, heat exchangers and other similar heat transfer apparatus. The material properties and manufacturing conditions of the seamless and welded materials should conform accordingly.
SCOPE
1.1 This specification2 describes seamless and welded nickel alloy tubing on which the external or internal surface, or both, has been modified by a cold forming process to produce an integral enhanced surface, for improved heat transfer. The tubes are used in surface condensers, evaporators, heat exchangers and similar heat transfer apparatus in unfinned end diameters up to and including 1 in. (25.4 mm).  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following precautionary statement pertains to the test method portion only: Section 10 of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory requirements prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM B725-22(Specification)
Standard Specification for Welded Nickel and Nickel Copper Alloy Pipe

ABSTRACT
This specification covers UNS N02200 nickel alloy and UNS N02201 and N04400 low carbon nickel alloy welded pipes intended for general corrosive service and for mechanical applications. Each pipe should either be welded and annealed or welded and stress relieved and made from the flat-rolled alloys by an automatic welding process without any filler metal additions. The pipes should also be cold worked after welding to ensure the development of optimum corrosion resistance in the weld area and base metal during the final heat treatment.
SCOPE
1.1 This specification covers nickel (UNS N02200), low carbon nickel (UNS N02201) and nickel copper alloy (UNS N04400) in the form of welded and annealed or welded and stress relieved pipe intended for general corrosive service and for mechanical applications.  
1.2 This specification covers outside diameter and nominal wall pipe in Schedules 5S, 10S, and 40S through 30-in. nominal pipe size shown in ANSI B36.19 (see Table 1) and Specification B775 (see Table 1). Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 The following precautionary caveat pertains only to the test methods portion, Section 13, of this specification: This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    6 pages
    English language
    sale 15% off
  • Technical specification
    6 pages
    English language
    sale 15% off
ASTM
ASTM B726-02(2021)(Specification)
Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy (UNS N06333) Welded Tube

ABSTRACT
This specification covers UNS N06333 alloy welded tubes intended for heat-resisting applications and general corrosive service. Each tube should be made from the flat-rolled alloy by an automatic welding process without any filler metal additions and subsequently furnished annealed with the oxide removed. Descaling is not necessary when the final heat treatment is performed in a protective atmosphere. A flattening test and a flange test will be performed on each end of one tube per lot.
SCOPE
1.1 This specification covers alloy UNS N06333 in the form of welded tube intended for heat-resisting applications and general corrosive service.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    2 pages
    English language
    sale 15% off
ASTM
ASTM B710-20ae1(Specification)
Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Welded Pipe

ABSTRACT
This specification covers UNS N08330 and N08332 high-temperature alloy welded pipes for heat-resisting applications and general corrosive service. The pipes should be made from the flat-rolled alloys by an automatic welding process without any filler metal additions. After welding, the materials should be cold worked, either in weld and base metal or in weld metal only, then annealed. Each end of one pipe per lot will be subjected to a flattening test.
SCOPE
1.1 This specification2 covers alloys UNS N08330 and UNS N08332 in the form of welded pipe intended for heat-resisting applications and general-corrosive service.  
1.2 The pipe covered is nominal pipe sizes up to and including size 12, with the nominal wall thicknesses given as Schedules 5S, 10S, 40S, and 80S. Table 2 of Specification B775 is based on Table A1 of ANSI B36.19 and gives the nominal dimension of these sizes. Table 3 of Specification B775 lists the dimensional requirements of these sizes. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification.  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B1015-20(Practice)
Standard Practice for Form and Style of Standards Relating to Refined Nickel and Cobalt and Their Alloys

SCOPE
1.1 This practice covers the form and style for specifications under the jurisdiction of ASTM Subcommittee B02.07 Refined Nickel and Cobalt and Their Alloys. Anyone preparing new or revising existing specifications for this subcommittee shall follow the practices and procedures outlined herein.  
1.2 This practice is a supplement to the current edition of Form and Style for ASTM Standards (Form Manual)2. If there is a conflict between the documents, then this should be brought to the attention of B02.07. Until the conflict is resolved, the more stringent requirement of the two documents takes precedent.  
1.3 The word “specifications” will be used throughout this document to describe B02.07 standards because the majority of B02.07 standards are categorized as such. Nevertheless, the instruction herein applies to any standards under the jurisdiction of B02.07.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    13 pages
    English language
    sale 15% off
ASTM
ASTM B729-20(Specification)
Standard Specification for Seamless Nickel-Iron-Chromium-Molybdenum-Copper Nickel Alloy Pipe and Tube

ABSTRACT
This specification covers UNS N08020, UNS N08026 and UNS N08024 nickel-alloy seamless, cold-worked or hot-finished pipe and tube intended for general corrosive service. The product of UNS N08020 alloy, UNS N08026 alloy, and UNS N08024 alloy shall be furnished in the stabilized-annealed condition, solution-annealed condition, and annealed condition, respectively. The tensile strength, yield strength, and elongation requirements are specified. Hydrostatic and nondestructive electric tests shall be conducted on the each pipe or tube.
SCOPE
1.1 This specification covers UNS N08020, UNS N08026, and UNS N08024 seamless, cold-worked or hot finished pipe and tube intended for general corrosive service.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 The following safety hazards caveat pertains only to the test methods portion, Section 10, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    3 pages
    English language
    sale 15% off
  • Technical specification
    3 pages
    English language
    sale 15% off
ASTM
ASTM B719-20(Specification)
Standard Specification for Nickel-Chromium-Molybdenum-Cobalt-Tungsten-Iron-Silicon Alloy Bar

ABSTRACT
This specification covers the standard for hot-finished and cold-finished UNS N06333 alloy bars and flats proposed for use in heat resisting applications and general corrosive service. Materials shall conform to mechanical properties of the material such as tensile strength, yield strength, elongation, and hardness. Each specimen will be subjected to a chemical analysis, tension, Brinell hardness, and Rockwell hardness test.
SCOPE
1.1 This specification covers wrought alloy UNS N06333 in the form of hot-finished and cold-finished bars and flats intended for heat resisting applications and general corrosive service.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM B78-90(2019)(Test Method)
Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating

SIGNIFICANCE AND USE
2.1 This test method is used by producers of electrical heating alloys to measure the cyclic oxidation resistance of these alloys.  
2.2 Because of the effect of environment, design, and use, the life values obtained from this test method may not correlate with that of an appliance or industrial heating unit.
SCOPE
1.1 This test method covers the determination of the resistance to oxidation of iron-chromium-aluminum electrical heating alloys at elevated temperatures under intermittent heating using a constant-temperature cycle test. This test is used for internal comparative purposes only.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off