ASTM A1024/A1024M-02(2007)

Standard Specification for Steel Line Pipe, Black, Plain-End, Seamless

ABSTRACT
This specification covers standard requirements for seamless, black, plain-end steel pipes for use in the conveyance of fluids under pressure. A quantity of pipe of the same ordered diameter, heat, wall thickness, and grade shall be given. Heat and product analyses shall be performed wherein steel pipes shall conform to the required chemical composition for carbon, sulfur, and phosphorus. Steel samples shall undergo tension test and shall conform to tensile properties such as yield strength and tensile strength. Hydrostatic pressure test shall be performed for steel samples with specified wall thickness and test pressure. The entire outer surface of the steel pipe shall undergo nondestructive electric test and shall be inspected for longitudinal defects by either magnetic particle inspection, ultrasonic inspection, and electromagnetic inspection.
SCOPE
1.1 This specification covers seamless, black, plain-end steel pipe for use in the conveyance of fluids under pressure. Pipe in sizes NPS 1 to 26, inclusive, as given in ASME B36.10M is included. Pipe having other dimensions, in this size range, may be furnished provided such pipe complies with all other requirements of this specification.
1.2 It is intended that the pipe be capable of being circumferentially welded in the field when welding procedures in accordance with the requirements of the applicable pipeline construction code are used.
1.3 The values stated in either inch-pound units or in SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values in each system are not exact equivalents; therefore, each system is to be used independently of the other.

General Information

• Status: Historical
• Publication Date: 31-Oct-2007
• ICS: 23.040.10 - Iron and steel pipes
• Technical Committee: A01 - Steel, Stainless Steel and Related Alloys
• Drafting Committee: A01.09 - Carbon Steel Tubular Products

Relations

• Replaces: ASTM A1024/A1024M-02 - Standard Specification for Steel Line Pipe, Black, Plain-End, Seamless
• Effective Date: 01-Nov-2007
• Replaced By: ASTM A1024/A1024M-02(2012) - Standard Specification for Steel Line Pipe, Black, Plain-End, Seamless
• Effective Date: 01-Sep-2012

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A1024/A1024M −02(Reapproved 2007)
Standard Specification for
1
Steel Line Pipe, Black, Plain-End, Seamless
This standard is issued under the fixed designation A1024/A1024M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 2.3 ASME Standard:
4
ASME B36.10MWelded and SeamlessWrought Steel Pipe
1.1 This specification covers seamless, black, plain-end
steel pipe for use in the conveyance of fluids under pressure.
3. Terminology
Pipe in sizes NPS 1 to 26, inclusive, as given in ASME
3.1 Definitions—For terminology used in this specification,
B36.10M is included. Pipe having other dimensions, in this
refer to Terminology A941.
sizerange,maybefurnishedprovidedsuchpipecomplieswith
all other requirements of this specification.
3.2 Definitions of Terms Specific to This Standard:
3.2.1 lot, n—a quantity of pipe of the same ordered
1.2 It is intended that the pipe be capable of being circum-
diameter, heat, wall thickness, and grade as given in Table 1.
ferentially welded in the field when welding procedures in
accordance with the requirements of the applicable pipeline
3.2.2 seamless pipe, n—a tubular product made without a
construction code are used. welded seam; it is manufactured usually by hot working the
material, and if necessary, by subsequently cold-finishing the
1.3 The values stated in either inch-pound units or in SI
hot worked tubular product to produce the desired shape,
units are to be regarded separately as standard.Within the text,
dimensions, and properties.
the SI units are shown in brackets. The values in each system
3.2.3 specified outside diameter (OD), n—the outside diam-
are not exact equivalents; therefore, each system is to be used
eter specified in the purchase order or the outside diameter
independently of the other.
listedinASMEB36.10Mforthenominalpipesizespecifiedin
2. Referenced Documents
the purchase order.
2
2.1 ASTM Standards:
4. General Requirements
A370Test Methods and Definitions for Mechanical Testing
4.1 Pipe furnished under this specification shall conform to
of Steel Products
the applicable requirements of Specification A530/A530M
A450/A450MSpecification for General Requirements for
unless otherwise provided herein.
Carbon and Low Alloy Steel Tubes
A530/A530MSpecification for General Requirements for
5. Ordering Information
Specialized Carbon and Alloy Steel Pipe
A751Test Methods, Practices, and Terminology for Chemi-
5.1 Information items to be considered, if appropriate, for
cal Analysis of Steel Products
inclusion in the purchase order are as follows:
A941TerminologyRelatingtoSteel,StainlessSteel,Related
5.1.1 Specification designation and year of issue,
Alloys, and Ferroalloys
5.1.2 Quantity (feet or metres),
2.2 API Standard:
5.1.3 Grade (see Table 2 and 8.1.5),
API RP 5L3Recommended Practice for Conducting Drop- 5.1.4 Size (either nominal (NPS) or outside diameter and
3
Weight Tear Tests on Line Pipe
wall thickness),
5.1.5 Nominal length (see 14.3),
5.1.6 End finish (plain-end beveled or special, see 15.1),
1
This specification is under the jurisdiction ofASTM Committee A01 on Steel,
5.1.7 Impact test temperature (see 8.2.5),
Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee
5.1.8 Heat treatment condition (see 6.1),
A01.09 on Carbon Steel Tubular Products.
Current edition approved Nov. 1, 2007. Published January 2008. Originally
5.1.9 Carbon equivalent for over 0.800 in. [20.3 mm] wall
approved in 2002. Last previous edition approved in 2002 as A1024/A1024M–02,
thicknesses (see 7.4),
DOI: 10.1520/A1024_A1024M-02R07.
2 5.1.10 Reduced under thickness variation (see Table 5),
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on
4
the ASTM website. Available from American Society of Mechanical Engineers (ASME), ASME
3
Available from American Petroleum Institute (API), 1220 L. St., NW, International Headquarters, Three Park Ave., New York, NY 10016-5990, http://
Washington, DC 20005-4070, http://api-ec.api.org. www.asme.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
A1024/A1024M−02 (2007)
TABLE 1 Lot Size and Sample Size for Mechanical and
7. Chemical Composition
Toughness Testing
7.1 The steel for any grade, by heat and product analyses,
Pipe Size Lot Size Sample Size
shall contain no more than 0.24% carbon, 0.015% sulfur, and
...