Standard Test Method for Cyclic Pressure Strength of Reinforced, Thermosetting Plastic Pipe

SIGNIFICANCE AND USE
5.1 The values obtained by this test method are applicable only to conditions that specifically duplicate the procedures used.  
5.2 After the regression characteristics of a pipe material and manufacturing process have been determined by this test method, one pressure may be used for quality-control purposes. This pressure shall be one of the points used in the original determination and be agreed upon between the individuals concerned.  
5.3 This test method deals with cyclic internal pressure performance of a pipe and omits creep and nonrecoverable deformation measurements.  
5.4 For determination of the cyclic hydrostatic design basis using data from this test method see Practice D2992.  
5.5 In the application of the following test requirements and recommendations it is assumed that test specimens of a given sample of pipe are truly representative of that material and manufacturing process. In tests conducted to show the effect of temperature and pressures on the life span of the pipe, great care must be taken to ensure that the specimens being tested are representative of the group being studied. Departure from this assumption could introduce discrepancies that are greater than those introduced by departure from the details of the procedure outlined in this test method.
SCOPE
1.1 This test method covers the determination of the failure characteristics of reinforced plastic pipe when subjected to cyclic internal hydraulic pressure. It is limited to pipe in which the ratio of outside diameter to wall thickness is 10:1 or more.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
Note 1: There is no known ISO equivalent to this standard.

General Information

• Status: Historical
• Publication Date: 30-Apr-2015
• ICS: 23.040.20 - Plastics pipes
• Technical Committee: D20 - Plastics
• Drafting Committee: D20.23 - Reinforced Thermosetting Resin Piping Systems and Chemical Equipment

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D2143 − 15
Standard Test Method for
Cyclic Pressure Strength of Reinforced, Thermosetting
1
Plastic Pipe
This standard is issued under the fixed designation D2143; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 3. Terminology
3.1 Definitions of Terms Specific to This Standard:
1.1 This test method covers the determination of the failure
3.1.1 failure—the transmission of the test fluid through the
characteristics of reinforced plastic pipe when subjected to
pipe wall in any manner, whether it be wall fracture, localized
cyclic internal hydraulic pressure. It is limited to pipe in which
leaking, or weeping at a distance greater than one diameter
the ratio of outside diameter to wall thickness is 10:1 or more.
from the end closure (specimens failing within one diameter of
1.2 The values stated in inch-pound units are to be regarded
the end closure shall be discarded).
as the standard. The values in parentheses are for information
3.1.2 failure detector—a devise that measures the electrical
only.
resistance between the test fluid and a conductive material,
1.3 This standard does not purport to address all of the
wrapped around the circumference of the test specimen, and
safety concerns, if any, associated with its use. It is the
which will indicate failure when 1) the resistance is lowered to
responsibility of the user of this standard to establish appro-
a range from 10 to 20 meg-ohm or 2) for the case of municipal
priate safety, health, and environmental practices and deter-
water, when the first drop of fluid has passed through the wall
mine the applicability of regulatory limitations prior to use.
of the specimen.
NOTE 1—There is no known ISO equivalent to this standard.
3.1.3 localized leaking—failure that occurs as small frac-
tures (one or more in a test specimen) that permit the test fluid
1.4 This international standard was developed in accor-
to be transferred at a rate that is measured by the failure
dance with internationally recognized principles on standard-
detector.
ization established in the Decision on Principles for the
Development of International Standards, Guides and Recom-
3.1.4 weeping—a general transmission of the test fluid
mendations issued by the World Trade Organization Technical
through the pipe, without visible fracture, at a sufficient rate to
Barriers to Trade (TBT) Committee.
be measured by the failure dectector, or in the case of larger
magnitudes of fluid transmission appear to be moisture con-
2. Referenced Documents densation on the specimen.
2
3.1.5 wall fracture—failure by a break in the pipe wall
2.1 ASTM Standards:
causing immediate loss of test fluid and continued loss at
D618 Practice for Conditioning Plastics for Testing
essentially no pressure.
D2992 Practice for Obtaining Hydrostatic or Pressure De-
sign Basis for “Fiberglass” (Glass-Fiber-Reinforced
4. Summary of Test Method
Thermosetting-Resin) Pipe and Fittings
4.1 This test method consists of exposing pipe specimens to
D3567 Practice for Determining Dimensions of “Fiberglass”
(Glass-Fiber-Reinforced Thermosetting Resin) Pipe and cyclic internal pressures at several different pressure levels and
Fittings measuring the cycles to failure at these different levels. Test
temperatures are obtained by circulating salt water or munici-
pal water through the specimens.
1
This test method is under the jurisdiction ofASTM Committee D20 on Plastics
5. Significance and Use
and is the direct responsibility of Subcommittee D20.23 on Reinforced Plastic
Piping Systems and Chemical Equipment.
5.1 The values obtained by this test method are applicable
Current edition approved May 1, 2015. Published June 2015. Originally
only to conditions that specifically duplicate the procedures
approved in 1963. Last previous edition approved in 2010 as D2143 – 00(2010).
used.
DOI: 10.1520/D2143-15.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
5.2 After the regression characteristics of a pipe material
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
and manufacturing process have been determined by this test
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. method,onepressuremaybeusedforquality-controlpurposes.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D2143 − 15
This pressure shall be one of the points used in the original a
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D2143 − 00 (Reapproved 2010) D2143 − 15 An American National Standard
Standard Test Method for
Cyclic Pressure Strength of Reinforced, Thermosetting
1
Plastic Pipe
This standard is issued under the fixed designation D2143; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope Scope*
1.1 This test method covers the determination of the failure characteristics of reinforced plastic pipe when subjected to cyclic
internal hydraulic pressure. It is limited to pipe in which the ratio of outside diameter to wall thickness is 10:1 or more.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
NOTE 1—There is no similar or equivalent ISO known ISO equivalent to this standard.
2. Referenced Documents
2
2.1 ASTM Standards:
D618 Practice for Conditioning Plastics for Testing
D2992 Practice for Obtaining Hydrostatic or Pressure Design Basis for “Fiberglass” (Glass-Fiber-Reinforced Thermosetting-
Resin) Pipe and Fittings
D3567 Practice for Determining Dimensions of “Fiberglass” (Glass-Fiber-Reinforced Thermosetting Resin) Pipe and Fittings
3. Terminology
3.1 Definitions of Terms Specific to This Standard:
3.1.1 failure—the transmission of the test fluid through the pipe wall in any manner, whether it be wall fracture, localized
leaking, or weeping at a distance greater than one diameter from the end closure (specimens failing within one diameter of the end
closure shall be discarded).
3.1.2 failure detector—a devise that measures the electrical resistance between the test fluid and a conductive material, wrapped
around the circumference of the test specimen, and which will indicate failure when 1) the resistance is lowered to a range from
10 to 20 meg-ohm or 2) for the case of municipal water, when the first drop of fluid has passed through the wall of the specimen.
3.1.3 localized leaking—failure that occurs as small fractures (one or more in a test specimen) that permit the test fluid to be
transferred at a rate that is measured by the failure detector.
3.1.4 weeping—a general transmission of the test fluid through the pipe, without visible fracture, at a sufficient rate to be
measured by the failure dectector, or in the case of larger magnitudes of fluid transmission appear to be moisture condensation on
the specimen.
3.1.5 wall fracture—failure by a break in the pipe wall causing immediate loss of test fluid and continued loss at essentially no
pressure.
4. Summary of Test Method
4.1 This test method consists of exposing pipe specimens to cyclic internal pressures at several different pressure levels and
measuring the cycles to failure at these different levels. Test temperatures are obtained by circulating salt water or municipal water
through the specimens.
1
This test method is under the jurisdiction of ASTM Committee D20 on Plastics and is the direct responsibility of Subcommittee D20.23 on Reinforced Plastic Piping
Systems and Chemical Equipment.
Current edition approved Nov. 1, 2010May 1, 2015. Published March 2011June 2015. Originally approved in 1963. Last previous edition approved in 20052010 as
ε1
D2143 – 00(2005)(2010). . DOI: 10.1520/D2143-00R10.10.1520/D2143-15.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D2143 − 15
5. Significance and Use
5.1 The values obtained by this test method are applicable only to conditions that specifically duplicate the procedures used.
5.2 After the regression characteristics of a pipe material and manufacturing process have been determined by this test method,
one pressure may be used for quality-c
...