ISO 5794-2:1982

Rubber compounding ingredients — Silica, precipitated, hydrated — Part 2: Test recipe and determination of physical properties in rubber

Ingrédients de mélange du caoutchouc — Silices hydratées précipitées — Partie 2: Formule d'essai et détermination des propriétés physiques dans le caoutchouc

General Information

• Status: Withdrawn
• Publication Date: 31-Oct-1982
• Withdrawal Date: 31-Oct-1982
• ICS: 83.040.20 - Rubber compounding ingredients
• Technical Committee: ISO/TC 45/SC 3 - Raw materials (including latex) for use in the rubber industry
• Drafting Committee: ISO/TC 45/SC 3 - Raw materials (including latex) for use in the rubber industry
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 05-Nov-1998

Relations

• Revised: ISO 5794-2:1998 - Rubber compounding ingredients — Silica, precipitated, hydrated — Part 2: Evaluation procedures in styrene-butadiene rubber
• Effective Date: 15-Apr-2008
• Consolidated By: ISO 1628-1:1998 - Plastics — Determination of the viscosity of polymers in dilute solution using capillary viscometers — Part 1: General principles
• Effective Date: 06-Jun-2022

Standards Content (Sample)

International Standard @ 579412
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION~MEX~YHAPO~HAR OPrAHH3AUMR no CTAH~APTH3AUMM*ORGANlSATlON INTERNATIONALE DE NORMALISATION
Rubber compounding ingredients - Silica, precipitated,
\
L
hydrated -
Part 2 : Test recipe and determination of physical
properties in rubber
Ingrédients de mélange du caoutchouc - Silices hydratées précipitées - Partie 2 : FormL.2 d'essai et détermination c
?S
propriétés physiques dans le caoutchouc
First edition - 1982-11-15
A
* UDC 546.284-31 : 678.023 Ref. No. IS0 5794/2-1982 (E)
8
51
Descriptors : rubber, styrene-butadiene rubber, silicon dioxide, tests, determination, physical properties, ingredients, test equipment.
N
O
v, Price based on '2 pages

---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
right to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 R94/2 was developed by Technical Committee
ISO/TC 45, Rubber and rubberproducfs, and was circulated to the member bodies in
February 1981.
It has been approved by the member bodies of the following countries
Hungary South Africa, Rep. of
Australia
India Spain
Austria
Belgium Italy Sri Lanka
Korea, Rep. of Sweden
Brazil
Canada Mexico Thailand
Czechoslovakia Netherlands United Kingdom
Egypt, Arab Rep. of Poland U SA
France Portugal USSR
Romania
Germany, F. R.
No member body expressed disapproval of the document.
0 International Organization for Standardization, 1982 O
Printed in Switzerland

---------------------- Page: 2 ----------------------
INTERNATIONAL STAN DARD IS0 57!34/2-1982 (E)
Rubber compounding ingredients - Silica, precipitated,
hydrated -
Part 2 : Test recipe and determination of physical
properties in rubber
1
Scope and field of application 3 Test recipe
This part of IS0 5794 specifies the test recipe, equipment, pro- The standard test recipe is given in the following table.
cedure and test methods for determining the physical proper-
ties of precipitated hydrated silica in a styrene-butadiene rubber
Reference material
--.-y
Material
I Parts by mass
mix.
number
SBR 1500 EST^)
IS0 579411 describes methods for chemical analysis of
precipitated hydrated silica, and IS0 5794/3 specifies its Silica
physical and chemical properties and properties in the rubber
Zinc oxide NBS 370d2)
mix.
Stearic acid NBS 37292)
TMTD3) NBS 374~2)
2 References
TBBS4) NBS 3842)
IS0 34, Rubber, vulcanized - Determination of tear strength
SuiDhur NBS 371f2)
(trouser, angle and crescent test pieces).
Total
IS0 37, Rubber, vulcanized - Determination of tensile stress-
1) See IS0 3257. A European equivalent to NBS standard reference
strain properties. material 386 has been developed by ANIC. This EST (European Stan-
dard Type) rubber is an SBR 1 500 type using a rosin acid emulsifier
and a staining stabilizer.
IS0 48, Vulcanized rubbers - Determination of hardness
2) NBS standard reference material number (National Bureau of
(Hardness beiween 30 and 85 IRHD).
Standards of the USA). Alternatively the ingredients shall be in accor-
dance with equivalent national standards.
IS0 289, Rubber, unvulcanized - Determination of Mooney
3) Tetramethylthiuramdisulphide.
viscosity. 1 )
4) N-ferf-butyl-2-benzothiazole sulphenamide.
IS0 2393, Rubber test mixes - Preparation, mixing and
vulcanization - Equipment and procedures.
4 Procedure
IS0 3257, Rubber compounding ingredients - Carbon black
4.1 Equipment and procedure
- Test recipe and method of evaluation in styrene-butadiene
rubbers.
Equipment and procedure for preparation, mixing and
vulcanization shall be in accordance with IS0 2393.
IS0 34
...

Norme internationale @ 579412
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONOMEXSlYHAPOnHAR OPïAHbi3AUbiR no CTAH~APT~3AUbiUOORGANIçATlON INTERNATIONALE DE NORMALISATION
Ingrédients de mélange du caoutchouc - Silices
c
hydratées précipitées -
Partie 2 : Formule d'essai et détermination des propriétés
physiques dans le caoutchouc
Rubber compounding ingredients - Silica, precipitated, hydrated - Part 2 : Test recipe and determination of physical properties
in rubber
Première édition - 1982-11-15
-
CDU 546.284-31 : 678.023 Réf. no : IS0 R94/2-1982 (FI
!il
'7 Descripteurs : caoutchouc, caoutchouc butadiène-styrène, silice, essai, détermination, propriété physique, ingrédient, matériel d'essai.
P
8
s;
O
2 Prix basé sur 2 pages

---------------------- Page: 1 ----------------------
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I'ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO.
La Norme internationale IS0 5794/2 a été élaborée par le comité technique ISO/TC 45,
€/astomères et produits à base d'élastomères, et a été soumise aux comités membres
en février 1981.
Les comités membres des pays suivants l'ont approuvée :
Afrique du Sud, Rép. d' Espagne Roumanie
Allemagne, R. F. France Royaume- Uni
Hongrie Sri Lanka
Australie
Autriche Inde Suède
Belgique Italie Tchécoslovaquie
Brésil Mexique T hail a n de
Canada Pays-Bas URSS
Corée, Rép. de Pologne USA
Égypte, Rép. arabe d' Portugal
Aucun comité membre ne l'a désapprouvée.
O Organisation internationale de normalisation, 1982 O
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORM E I NTE RN ATlON ALE IS0 !5794/2-1982 (FI
Ingrédients de mélange du caoutchouc - Silices
hydratées précipitées -
Partie 2 : Formule d'essai et détermination des propriétés
physiques dans le caoutchouc
IS0 5794, Caoutchouc - Ingrédients de mélange - Silices
1 Objet et domaine d'application
hydratées précipitées -
La présente partie de I'ISO 5794 spécifie la formule d'essai,
l'appareillage, le mode opératoire et les méthodes d'essai pour Partie 7 : Essais sur le produit brut.2)
la détermination, dans un mélange caoutchouc de butadiène- Partie 3 : Spécification.2)
styrène, des propriétés physiques des silices hydratées
précipitées.
3 Formule d'essai
L'ISO 579411 décrit des méthodes d'analyse chimique des
précipités hydratés de silice, et 1'1S0 5794/3 spécifie les
La formule d'essai normalisée est donnée dans le tableau
propriétés physiques et chimiques de ces produits, ainsi que
suivant.
leurs propriétés dans le mélange caoutchouc.
2 Références
Numéro de référence
Ingrédient
Parties en masse
du produit
IS0 34, Caoutchouc vulcanisé - Détermination de la
SBA 1500 EST')
résistance au déchirement (éprouvettes pantalon, angulaire et
Silice
croissan tl.
Oxyde de zinc NBS 370d2)
IS0 37, Caoutchouc vulcanisé - Essai de traction-
allongement.
Acide stéarique NBS 37292)
TMTD3) NBS 374~2)
L
IS0 48, Elastomères vulcanisés - Détermination de la dureté
(Dureté Comprise entre 30 et 85 DIDC).
TBBS4)
NBS 3842)
Soufre NBS 371f2)
IS0 289, Caoutchouc, non vulcanisé - Détermination de la
consistance Mooney. 1)
Total
I 148,9
I
1) Voir IS0 3257. Un équivalent du produit de référence NBS 386 a
IS0 2393, Mélanges d'essais à base d'élastomères -
été développé en Europe par ANIC. Ce caoutchouc EST (European
Préparation, mélangeage et vulcanisation - Appareillage et
Standard Type) est un SBR de type 1500 pour lequel on a employé un
mode opératoire.
émulsifiant acide à base de colophane et un stabilisant de teinte.
2) Numéro de référence du produit de référence NBS (National
IS0 3257, Ingrédients de mélange du caoutchouc - Noir de
Bureau of Standards des USA). Alternativement, les ingrédients doi-
carbone - Formule d'essai et méthode d'évaluation dans les
vent être des produits équivalents normalisés par les organismes natio-
caoutchoucs butadiène-styrène.
naux.
3) Disulfure de tétraméthylthiurame.
IS0 3417, Caoutchouc - Détermination des caractéristiques
de vulcanisation à raide du rhéomètre à disque oscillant. 4) N-terf-butyl-benzothiazolesulfénamide-2.
1) Actuellement au stade de projet. (Révision de I'ISO/R 289-1963.)
2) Actuellement au stade de projet.
1

---------------------- Page: 3 ----------------------
IS0 5794/2-1982 (FI
4 Mode opératoire 4.2.10 Conditionner le mélange pendant une durée comprise
entre 18 et 24 h.
4.1 A
...