ISO 13428:2024

Geosynthetics — Determination of the protection efficiency of a geosynthetic against impact damage

This document describes an index test for the determination of the protection efficiency of a geosynthetic on a hard surface, exposed to the impact load of a hemispherical object. The index test measures the change in thickness of a thin lead plate lying between the geosynthetic and a rigid support. It is also used as a performance test, by using the real rigid surface to protect and the real sequence of geosynthetics. The test is applicable to all geosynthetics with apertures smaller than 15 mm (maximum size).

Géosynthétiques — Détermination de l'efficacité de protection d'un géosynthétique contre l'effet d'un impact

Le présent document décrit un essai de caractérisation permettant de déterminer l’efficacité de la protection offerte par un produit géosynthétique sur une surface dure, soumis à l’impact d’un objet hémisphérique. Cet essai de caractérisation mesure la variation d’épaisseur d’une mince plaque de plomb placée entre le géosynthétique et un support rigide. Il peut être converti en essai de performance en utilisant la surface rigide réelle à protéger et la séquence réelle de géosynthétiques. L’essai est applicable à tous les produits géosynthétiques dont l’ouverture de maille est inférieure à 15 mm (dimension maximale).

General Information

• Status: Published
• Publication Date: 02-Oct-2024
• ICS: 59.080.70 - Geotextiles
• Technical Committee: ISO/TC 221 - Geosynthetics
• Drafting Committee: ISO/TC 221 - Geosynthetics
• Current Stage: 6060 - International Standard published
• Start Date: 03-Oct-2024
• Due Date: 12-Sep-2025
• Completion Date: 03-Oct-2024

Relations

• Revises: ISO 13428:2005 - Geosynthetics — Determination of the protection efficiency of a geosynthetic against impact damage
• Effective Date: 06-Jun-2022

Standards Content (Sample)

International
Standard
ISO 13428
Second edition
Geosynthetics — Determination
2024-10
of the protection efficiency of a
geosynthetic against impact damage
Géosynthétiques — Détermination de l'efficacité de protection
d'un géosynthétique contre l'effet d'un impact
Reference number
© ISO 2024
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Test specimens . 3
5.1 Sampling .3
5.2 Number and dimensions of test specimens .3
5.3 Conditioning.3
6 Apparatus . 3
6.1 General .3
6.2 Probe .3
6.3 Specimen support .3
6.4 Lead plate .4
6.5 Thickness gauge .5
7 Test procedure . 5
8 Calculation . 6
9 Test report . 7
Annex A (informative) Performance testing . 8
Bibliography . 9

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO [had/had not] received notice of
(a) patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 221 Geosynthetics, in collaboration with
the European Committee for Standardization (CEN) Technical Committee CEN/TC 189, Geosynthetics, in
accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement).
This second edition cancels and replaces the first edition (ISO 13428:2005), which has been technically
revised.
The main changes are as follows:
— the normative references have been updated;
— Figure 1 has been corrected;
— the thickness of lead plate has been modified to 2,0 mm.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
International Standard ISO 13428:2024(en)
Geosynthetics — Determination of the protection efficiency of
a geosynthetic against impact damage
1 Scope
This document describes an index test for the determination of the protection efficiency of a geosynthetic on
a hard surface, exposed to the impact load of a hemispherical object.
The index test measures the change in thickness of a thin lead plate lying between the geosynthetic and a
rigid support.
It is also used as a performance test, by using the real rigid surface to protect and the real sequence of
geosynthetics.
The test is applicable to all geosynthetics with apertures smaller than 15 mm (maximum size).
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 554, Standard atmospheres for conditioning and/or testing — Specifications
ISO 9862, Geosynthetics — Sampling and preparation of test specimens
ISO 9863-1, Geosynthetics — Determination of thickness at specified pressures — Part 1: Single layers
ISO 9864, Geosynthetics — Test method for the determination of mass per unit area of geotextiles and geotextile-
related products
ISO 10318-1, Geosynthetics — Part 1: Terms and definitions
EN 12588, Lead and lead alloys — Rolled lead sheet for building purposes
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 10318-1 and the following apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
lead plate thickness
s
thickness of the thin plate used to assess the effect of impact
Note 1 to entry: Plate thickness is expressed in millimeters.

3.2
initial lead plate thickness
s
i
lead plate thickness (3.1) under an applied pressure of 2 kPa
Note 1 to entry: Initial plate thickness is expressed in millimetres.
3.3
residual lead plate thickness
s
r
lead plate thickness (3.1) after an impact, in the centre of the impact area
Note 1 to entry: Residual lead plate thickness is expressed in millimetres.
3.4
probe
hemispherical mass used to produce the impact on the geosynthetic specimen
Note 1 to entry: The probe is shown in Figure 3.
3.5
nominal thickness
t
n
thickness of the specimen when subjected to an applied normal stress of 2 kPa, measured in accordance
with ISO 9863-1
Note 1 to entry: Nominal thickness is expressed in millimetres.
4 Principle
A geosynthetic test specimen is subjected to an impact load produced by a rigid probe with a hemispherical
head. The probe hits the specimen with a known energy.
The specimen lies on a rigid support, consisting of a thick steel plate of set characteristics and dimensions.
A thin lead plate is placed between the steel plate and the specimen.
This test is relevant for applications like geonets protecting the coating of steel pipelines and geocomposites
or geospacers protecting the geomembrane placed on the back face of a concrete retaining wall, where
stones dumped during backfilling can cause an impact of the same type that is simulated in the test.
The standard index-test procedures may be modified to be used for a performance test, as described in
Annex A.
The five specimens are each subjected to one impact. A single lead plate may be used for all five specimens.
The residual lead plate thickness is measured in the impacted areas and the average residual thickness is
calculated.
The impact energy is given by Formula (1):
E = F × h (1)
where
E is the impact energy, in joules;
F is the weight of the probe, in newtons;
h is the distance between top surface of the specimen and bottom point of the probe before releasing
the trigger, in metres.
5 Test specimens
5.1 Sampling
Take specimens in accordance with ISO 9862.
5.2 Number and dimensions of test specimens
Cut five specimens for each face from the test sample. A new set of specimens is required for each test.
Specimens shall meet the following criteria:
— the shape of the specimen shall be square (see Figure 2);
— the minimum size of the specimen shall be 60 mm × 60 mm (see Figure 2).
5.3 Conditioning
The test specimens shall be conditioned in the standard atmosphere for testing at (20 ± 2) °C and (65 ± 5) %
relative humidity in accordance with ISO 554.
The specimens may be considered to be conditioned when the change in mass in successive weighings made
at intervals of not less than 2 h does not exceed 0,25 % of the mass of the test specimen.
Either conditioning or testing, or both, in the standard atmosphere may only be omitted when it can be
shown that results obtained for the same specific type of product (both structure and polymer type) are not
affected by changes in temperature and humidity exceeding the limits. This information shall be included in
the test report.
6 Apparatus
6.1 General
NOTE See Figure 1.
6.2 Probe
The probe is made of a steel cylinder with a hemispherical head of (20 ± 0,5 mm) diameter. It is fixed to a
triggering system (Figure 3).
NOTE The probe can move inside a large tube, e.g. acrylic glass, to provide protection for the operator. For
performance tests, mass and diameter of the probe and the falling height are varied in order to model the real situation.
For index tests, the falling height shall be (1 000 ± 10) mm and the mass of the probe shall be (1 000 ± 2) g.
6.3 Specimen support
The specimen support is shown in Figure 2 with all the relevant dimensions.
It consists of a (40 mm ± 0,5 mm) thick steel plate, as shown in Figure 2. The steel plate shall have minimum
dimensions equal to or exceeding those of the specimens.
The steel plate shall be put on
...

Norme
internationale
ISO 13428
Deuxième édition
Géosynthétiques — Détermination
2024-10
de l'efficacité de protection d'un
géosynthétique contre l'effet d'un
impact
Geosynthetics — Determination of the protection efficiency of a
geosynthetic against impact damage
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2024
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 2
5 Éprouvettes. 3
5.1 Échantillonnage .3
5.2 Nombre et dimensions des éprouvettes .3
5.3 Conditionnement .3
6 Appareillage . 3
6.1 Généralités .3
6.2 Poinçon .3
6.3 Support d’éprouvette .3
6.4 Plaque de plomb .4
6.5 Instrument de mesure d’épaisseur .5
7 Mode opératoire d’essai . 6
8 Calculs . 7
9 Rapport d’essai . 8
Annexe A (informative) Essais de performance . 9
Bibliographie . 10

iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO, participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/CEI, Partie 1. Il convient en particulier de prendre note des différents
critères d’approbation requis pour les différents types de document ISO. Le présent document a
été rédigé conformément aux règles de rédaction définies dans les Directives ISO/CEI, Partie 2 (see
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en œuvre du présent document peut impliquer l’utilisation d’un
ou de plusieurs brevets. L’ISO ne prend pas position en ce qui concerne la preuve, la validité ou l’applicabilité
de tout droit de propriété intellectuelle revendiqué à cet égard. À la date de publication du présent document,
l’ISO n’a pas été notifié de l’existence d’un ou de plusieurs brevets pouvant être requis dans le cadre de sa
mise en œuvre. Toutefois, les exécutants sont avertis du fait qu’il ne s’agit pas forcément des dernières
informations disponibles, qui peuvent être obtenues depuis la base de données des brevets disponible à
l’adresse www.iso.org/patents. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié de tels
droits de propriété et averti de leur existence.
Toutes les appellations commerciales mentionnées dans le présent document sont données pour information,
par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, de la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir le lien suivant : www.iso.org/iso/foreword.html.
Le présent document a été élaboré par le comité technique ISO/TC 221, Produits géosynthétiques, en
collaboration avec le comité technique CEN/TC 189, Géosynthétiques, du Comité européen de normalisation
(CEN), conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Cette seconde édition annule et remplace la première édition (ISO 13428:2005), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes :
— les références normatives ont été mise à jour ;
— la Figure 1 a été corrigée ;
— l’épaisseur de la plaque de plomb a été modifiée à 2,0 mm.
Il convient d’adresser tout commentaire ou toute question à propos du présent document à l’organisme
de normalisation national de l’utilisateur. Une liste complète de ces organismes est disponible à l’adresse
www.iso.org/members.html.
iv
Norme internationale ISO 13428:2024(fr)
Géosynthétiques — Détermination de l'efficacité de
protection d'un géosynthétique contre l'effet d'un impact
1 Domaine d’application
Le présent document décrit un essai de caractérisation permettant de déterminer l’efficacité de la protection
offerte par un produit géosynthétique sur une surface dure, soumis à l’impact d’un objet hémisphérique.
Cet essai de caractérisation mesure la variation d’épaisseur d’une mince plaque de plomb placée entre le
géosynthétique et un support rigide.
Il peut être converti en essai de performance en utilisant la surface rigide réelle à protéger et la séquence
réelle de géosynthétiques.
L’essai est applicable à tous les produits géosynthétiques dont l’ouverture de maille est inférieure à 15 mm
(dimension maximale).
2 Références normatives
Les documents suivants sont mentionnés dans le texte d’une manière telle que tout ou partie de leur contenu
constitue les exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document auquel il est fait référence s’applique (y compris
les éventuels amendements).
ISO 554, Atmosphères normales de conditionnement et/ou d'essai — Spécifications
ISO 9862, Géosynthétiques — Échantillonnage et préparation des éprouvettes
ISO 9863-1, Géosynthétiques — Détermination de l'épaisseur à des pressions spécifiées — Partie 1: Couches
individuelles
ISO 9864, Géosynthétiques — Méthode d'essai pour la détermination de la masse surfacique des géotextiles et
produits apparentés
ISO 10318-1, Géosynthétiques — Partie 1 : Termes et définitions
EN 12588, Plomb et alliages de plomb — Feuilles de plomb laminé pour le bâtiment
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l’ISO 10318-1 ainsi que les
termes et définitions suivants s’appliquent.
L’ISO et la CEI tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes :
— Plateforme de consultation en ligne (OBP) de l’ISO : disponible à l’adresse https:// www .iso .org/ obp
— Glossaire Electropedia de la CEI : disponible à l’adresse https:// www .electropedia .org/

3.1
épaisseur de la plaque de plomb
s
épaisseur de la plaque mince de plomb
Note 1 à l'article: l’épaisseur de la plaque est exprimée en millimètres.
3.2
épaisseur initiale de la plaque de plomb
s
i
épaisseur de la plaque de plomb (3.1) sous une pression de 2 kPa
Note 1 à l'article: l’épaisseur initiale de la plaque est exprimée en millimètres.
3.3
épaisseur résiduelle de la plaque de plomb
s
r
épaisseur de la plaque de plomb (3.1) après un impact, mesurée au centre de la zone d’impact
Note 1 à l'article: l’épaisseur résiduelle de la plaque de plomb est exprimée en millimètres.
3.4
poinçon
masse hémisphérique utilisée pour produire l’impact sur l’éprouvette de géosynthétique
Note 1 à l'article: le poinçon est représenté à la Figure 3.
3.5
épaisseur nominale
t
n
épaisseur de l’éprouvette soumise à une contrainte normale de 2 kPa, mesurée conformément à l’ISO 9863-1
Note 1 à l'article: l’épaisseur nominale est exprimée en millimètres.
4 Principe
Une éprouvette de géosynthétique est soumise à un impact produit par un poinçon rigide à tête
hémisphérique. Le poinçon frappe l’éprouvette avec une énergie connue.
L’éprouvette repose sur un support rigide, constitué d’une plaque épaisse d’acier dont les caractéristiques
et les dimensions sont définies. Une plaque mince de plomb est placée entre la plaque d’acier et l’éprouvette.
Cet essai est pertinent pour des applications telles que les géofilets protégeant le revêtement des pipelines
en acier et les géocomposites ou géoespaceurs protégeant la géomembrane placée sur la face arrière d'un
mur de soutènement en béton, où les pierres déversées lors du remblayage peuvent provoquer un impact du
même type que celui simulé lors de l’essai.
Les procédures d'essai de caractérisation de la norme peuvent être modifiées pour être utilisées comme
essais de performance, comme décrit à l'Annexe A.
Chacune des cinq éprouvettes est soumise à un impact. Une seule plaque de plomb peut être utilisée pour les
cinq éprouvettes.
L’épaisseur résiduelle de la plaque de plomb est mesurée dans les zones d’impact et l’épaisseur résiduelle
moyenne est calculée.
L’énergie d’impact est donnée par la Formule (1) :
E = F × h (1)
où
E est l’énergie d’impact, en joules ;
F est le poids du poinçon, en newtons ;
h est la distance entre la surface supérieure de l’éprouvette et la pointe inférieure du poinçon avant de
relâcher le dispositif de déclenchement, en mètres.
5 Éprouvettes
5.1 Échantillonnage
Prélever les éprouvettes conformément à l’ISO 9862.
5.2 Nombre et dimensions des éprouvettes
Découper cinq éprouvettes pour chaque face de l’échantillon. Un nouveau jeu d’éprouvettes est nécessaire
pour chaque essai.
Les éprouvettes doivent répondre aux critères suivants :
— l’éprouvette doit être de forme carrée (voir la Figure 2) ;
— les dimensions minimales de l’éprouvette doivent être de 60 mm × 60 mm (voir la Figure 2).
5.3 Conditionnement
Les éprouvettes doivent être conditionnées en atmosphère normale d’essai à (20 ± 2) °C et (65 ± 5) %
d’humidité relative, conformément à l’ISO 554.
Les éprouvettes peuvent être considérées comme étant conditionnées lorsque leur variation de masse entre
pesées successives effectuées à intervalles d’au moins 2 h ne dépasse pas 0,25 % de leur masse.
Le conditionnement et
...