ISO 1872-2:1989
(Main)Plastics — Polyethylene (PE) and ethylene copolymer thermoplastics — Part 2: Preparation of test specimens and determination of properties
Plastics — Polyethylene (PE) and ethylene copolymer thermoplastics — Part 2: Preparation of test specimens and determination of properties
Plastiques — Thermoplastiques à base de polyéthylène (PE) et de copolymères d'éthylène — Partie 2: Préparation des éprouvettes et détermination des caractéristiques
Plastične mase - Polietilenski (PE) in kopolimerni etilenski plastomeri - 2. del: Priprava preskušancev in določitev lastnosti
General Information
Relations
Buy Standard
Standards Content (Sample)
I NTER NAT1 ON AL
IS0
STANDARD
1872-2
First edition
1989-11-01
Plastics - Polyethylene (PE) and ethylene
copolymer thermoplastics -
Part 2 :
Preparation of test specimens and determination of
properties
Plastiques - Thermoplastiques a base de polyéthylène (PE) et de copolymères
d'éthylène -
Partie 2 : Préparation des éprouvettes et détermination des caractéristiques
Reference number
IS0 1872-2 : 1989 (E)
---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. IS0 J
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 1872-2 was prepared by Technical Committee ISO/TC 61,
Plastics.
Together with IS0 1872-1 : 1986, it cancels and replaces International Standard
IS0 1872 :1972.
IS0 1872 consists of the following parts, under the general title Plastics -
Polyethylene (PEI and ethylene copolymer thermoplastics :
- Part I: Designation
-
Part 2: Preparation of test specimens and determination of properties
Annex A of this part of IS0 1872 is for information only.
O IS0 1989
All rights reserved. No part of this publication may be reproduced or utilized in any form or by any
means, electronic or mechanical, including photocopying and microfilm, without permission in
writing from the publisher.
International Organization for Standardization
Case postale 56 0 CH-I21 1 Genève 20 0 Switzerland
Printed in Switzerland
---------------------- Page: 2 ----------------------
IS0 1872-2 : 1989 (E)
INTERNATIONAL STANDARD
Plastics - Polyethylene (PE) and ethylene copolymer
thermoplastics -
Part 2 :
Preparation of test specimens and determination of properties
1 Scope ' were valid. All standards are subject to revision, and parties to
agreements based on this part of IS0 1872 are encouraged to
L This part of 1872 specifies for moulding investigate the possibility of applying the most recent editions
Members Of IEC and ISo
test specimens of polyethylene materials under specified mould- Of the standards indicated below.
maintain registers of currently valid International Standards.
ing conditions and methods for measuring their properties.1)
IS0 62 : 1980, Plastics - Determination of water absorption.
1.2 No figures are quoted for these properties. Those
required for the designation of polyethylene materials for IS0 75 : 1987, Plastics and ebonite - Determination of
moulding and extrusion are given in Is0 1872-1. Other proper-
temperature of deflection under load.
ties are determined by the appropriate methods referred to in
IS0 1872 and values may be obtained from manu-
this part of
IS0 175 : 1981, Plastics - Determination of the effects of
facturers' literature. Values should only be compared if the pro-
liquid chemicals, including water.
cedures described herein for preparing the test specimens and
for determining the properties are followed.
IS0 178 : 1975, Plastics - Determination of flexuralproperties
of rigid plastics.
1.3 The values determined in accordance with this part of
179 : 1982, plastics - Determination of Charpy impact
IS0 1872 will not necessarily be identical to those obtained
strength of rigid materials.
using specimens of different dimensions andior prepared by
different procedures. They may also be influenced by colorants
IS0 180 : 1982, Plastics - Determination of lzod impact
and other additives. The values obtained for the properties of a
strength of rigid materials.
moulding depend on the moulding compound, the shape, the
test method and the state of anisotropy. The last-mentioned
291 : 19n, plastics -
atmospheres for con-
\/
depends on the gating and the moulding conditions, for exam-
ditioning and testing.
ple temperature, pressure and injection rate. Any subsequent
treatment must also be considered, for example conditioning or
IS0 293 : 1986, Plastics - Compression moulding test
annealing.
Specimens of thermoplastic materials.
IS0 294 : 1975, Plastics - Injection moulding test specimens
1.4 The thermal history and the internal stresses of the speci-
mens may strongly influence the thermal and mechanical pro- of thermoplastic materials.
perties and the resistance to environmental stress cracking, but
exert less effect on the electrical properties, which depend
IS0 306 : 1987, Plastics - Thermoplastic materials - Deter-
mainly on the chemical composition of the moulding com-
mination of Vicat softening temperature.
pound.
ISOiR 527 : 1966, Plastics - Determination of tensile proper-
ties.
2 Normative references
IS0 537 : 1980, Plastics - Testing with the torsion pendulum.
The following standards contain provisions which, through
reference in this text, constitute provisions of this part of IS0 868 : 1985, Plastics and ebonite - Detemination of in-
IS0 1872. At the time of publication, the editions indicated dentation hardness by means of a durometer (Shore hardness).
1 i Preferred methods and temperatures in this part of IS0 1872 will become mandatory at the next five-year revision.
1
---------------------- Page: 3 ----------------------
IS0 1872-2 : 1989 (E)
IS0 899 : 1981, Plastics - Determination of tensile creep. IEC Publication 243 : 1967, Recommended methods of test for
electric strength of solid insulating materials at power frequen-
cies.
IS0 974 : 1980, Plastics - Determination of the brittleness
temperature by impact.
IEC Publication 250 : 1969, Recommended methods for the
determination of the permittivity and dielectric dissipation fac-
IS0 1133 : 1981, Plastics - Determination of the melt flow
tor of electrical insulating materials at power, audio and radio
rate of thermoplastics.
frequencies including metre wavelengths.
IS0 1183 : 1987, Plastics - Methods for determining the den-
sity and relative density of non-cellular plastics.
3 Preparation of test specimens
IS0 1628-3 : - 11, Plastics - Determination of viscosity num-
Two methods of preparation of test specimens are described :
ber and limiting viscosity number - Part 3: Polyethylenes and
compression moulding and injection moulding.
polypropylenes .
3.1 Compression moulding
IS0 1872-1 : 1986, Plastics - Polyethylene (PE) and ethylene
copolymer thermoplastics - Part 1 : Designation.
Specimens shall be prepared either by stamping or by machin-
ing from a compression-moulded sheet (see IS0 2818). Full
IS0 2039-1 : 1987, Plastics - Determination of hardness -
,.
details of compression moulding of sheet are given in IS0 293
Part I: Ball indentation method.
but for polyethylene materials the following additional points
-,
shall apply:
IS0 2039-2 : 1987, Plastics - Determination of hardness -
Part 2: Rockwell hardness.
M
...
SLOVENSKI STANDARD
SIST ISO 1872-2:1996
01-marec-1996
3ODVWLþQHPDVH3ROLHWLOHQVNL 3( LQNRSROLPHUQLHWLOHQVNLSODVWRPHULGHO
3ULSUDYDSUHVNXãDQFHYLQGRORþLWHYODVWQRVWL
Plastics -- Polyethylene (PE) and ethylene copolymer thermoplastics -- Part 2:
Preparation of test specimens and determination of properties
Plastiques -- Thermoplastiques à base de polyéthylène (PE) et de copolymères
d'éthylène -- Partie 2: Préparation des éprouvettes et détermination des caractéristiques
Ta slovenski standard je istoveten z: ISO 1872-2:1989
ICS:
83.080.20 Plastomeri Thermoplastic materials
SIST ISO 1872-2:1996 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST ISO 1872-2:1996
---------------------- Page: 2 ----------------------
SIST ISO 1872-2:1996
I NTER NAT1 ON AL
IS0
STANDARD
1872-2
First edition
1989-11-01
Plastics - Polyethylene (PE) and ethylene
copolymer thermoplastics -
Part 2 :
Preparation of test specimens and determination of
properties
Plastiques - Thermoplastiques a base de polyéthylène (PE) et de copolymères
d'éthylène -
Partie 2 : Préparation des éprouvettes et détermination des caractéristiques
Reference number
IS0 1872-2 : 1989 (E)
---------------------- Page: 3 ----------------------
SIST ISO 1872-2:1996
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards bodies (IS0 member bodies). The work of preparing International
Standards is normally carried out through IS0 technical committees. Each member
body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, govern-
mental and non-governmental, in liaison with ISO, also take part in the work. IS0 J
collaborates closely with the International Electrotechnical Commission (IEC) on all
matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council. They are approved in accordance with IS0 procedures requiring at
least 75 % approval by the member bodies voting.
International Standard IS0 1872-2 was prepared by Technical Committee ISO/TC 61,
Plastics.
Together with IS0 1872-1 : 1986, it cancels and replaces International Standard
IS0 1872 :1972.
IS0 1872 consists of the following parts, under the general title Plastics -
Polyethylene (PEI and ethylene copolymer thermoplastics :
- Part I: Designation
-
Part 2: Preparation of test specimens and determination of properties
Annex A of this part of IS0 1872 is for information only.
O IS0 1989
All rights reserved. No part of this publication may be reproduced or utilized in any form or by any
means, electronic or mechanical, including photocopying and microfilm, without permission in
writing from the publisher.
International Organization for Standardization
Case postale 56 0 CH-I21 1 Genève 20 0 Switzerland
Printed in Switzerland
---------------------- Page: 4 ----------------------
SIST ISO 1872-2:1996
IS0 1872-2 : 1989 (E)
INTERNATIONAL STANDARD
Plastics - Polyethylene (PE) and ethylene copolymer
thermoplastics -
Part 2 :
Preparation of test specimens and determination of properties
1 Scope ' were valid. All standards are subject to revision, and parties to
agreements based on this part of IS0 1872 are encouraged to
L This part of 1872 specifies for moulding investigate the possibility of applying the most recent editions
Members Of IEC and ISo
test specimens of polyethylene materials under specified mould- Of the standards indicated below.
maintain registers of currently valid International Standards.
ing conditions and methods for measuring their properties.1)
IS0 62 : 1980, Plastics - Determination of water absorption.
1.2 No figures are quoted for these properties. Those
required for the designation of polyethylene materials for IS0 75 : 1987, Plastics and ebonite - Determination of
moulding and extrusion are given in Is0 1872-1. Other proper-
temperature of deflection under load.
ties are determined by the appropriate methods referred to in
IS0 1872 and values may be obtained from manu-
this part of
IS0 175 : 1981, Plastics - Determination of the effects of
facturers' literature. Values should only be compared if the pro-
liquid chemicals, including water.
cedures described herein for preparing the test specimens and
for determining the properties are followed.
IS0 178 : 1975, Plastics - Determination of flexuralproperties
of rigid plastics.
1.3 The values determined in accordance with this part of
179 : 1982, plastics - Determination of Charpy impact
IS0 1872 will not necessarily be identical to those obtained
strength of rigid materials.
using specimens of different dimensions andior prepared by
different procedures. They may also be influenced by colorants
IS0 180 : 1982, Plastics - Determination of lzod impact
and other additives. The values obtained for the properties of a
strength of rigid materials.
moulding depend on the moulding compound, the shape, the
test method and the state of anisotropy. The last-mentioned
291 : 19n, plastics -
atmospheres for con-
\/
depends on the gating and the moulding conditions, for exam-
ditioning and testing.
ple temperature, pressure and injection rate. Any subsequent
treatment must also be considered, for example conditioning or
IS0 293 : 1986, Plastics - Compression moulding test
annealing.
Specimens of thermoplastic materials.
IS0 294 : 1975, Plastics - Injection moulding test specimens
1.4 The thermal history and the internal stresses of the speci-
mens may strongly influence the thermal and mechanical pro- of thermoplastic materials.
perties and the resistance to environmental stress cracking, but
exert less effect on the electrical properties, which depend
IS0 306 : 1987, Plastics - Thermoplastic materials - Deter-
mainly on the chemical composition of the moulding com-
mination of Vicat softening temperature.
pound.
ISOiR 527 : 1966, Plastics - Determination of tensile proper-
ties.
2 Normative references
IS0 537 : 1980, Plastics - Testing with the torsion pendulum.
The following standards contain provisions which, through
reference in this text, constitute provisions of this part of IS0 868 : 1985, Plastics and ebonite - Detemination of in-
IS0 1872. At the time of publication, the editions indicated dentation hardness by means of a durometer (Shore hardness).
1 i Preferred methods and temperatures in this part of IS0 1872 will become mandatory at the next five-year revision.
1
---------------------- Page: 5 ----------------------
SIST ISO 1872-2:1996
IS0 1872-2 : 1989 (E)
IS0 899 : 1981, Plastics - Determination of tensile creep. IEC Publication 243 : 1967, Recommended methods of test for
electric strength of solid insulating materials at power frequen-
cies.
IS0 974 : 1980, Plastics - Determination of the brittleness
temperature by impact.
IEC Publication 250 : 1969, Recommended methods for the
determination of the permittivity and dielectric dissipation fac-
IS0 1133 : 1981, Plastics - Determination of the melt flow
tor of electrical insulating materials at power, audio and radio
rate of thermoplastics.
frequencies including metre wavelengths.
IS0 1183 : 1987, Plastics - Methods for determining the den-
sity and relative density of non-cellular plastics.
3 Preparation of test specimens
IS0 1628-3 : - 11, Plastics - Determination of viscosity num-
Two methods of preparation of test specimens are described :
ber and limiting viscosity number - Part 3: Polyethylenes and
compression moulding and injection moulding.
polypropylenes .
3.1 Compression moulding
IS0
...
NORME
IS0
INTERNATIONALE
1872-2
Première édition
1989-11-01
Plastiques - Thermoplastiques à base de
polyéthylène (PE) et de copolymères
d'éthylène -
Partie 2 :
Préparation des éprouvettes et détermination des
caractéristiques
Plastics - Polyethylene (PE) and ethylene copolymer thermoplastics -
Part 2 : Preparation of test specimens and determination of properties
Numéro de référence
IS0 1872-2 : 1989 (FI
---------------------- Page: 1 ----------------------
IS0 1872-2 1 1989 (FI
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est en général confiée aux comités techniques de I'ISO.
Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouverhementales et non
gouvernementales, en liaison avec 1'1S0 participent également aux travaux. L'ISO col-
labore étroitement avec la Commission électrotechnique internationale (CEI) en ce qui
concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO. Les Normes internationales sont approuvées confor-
mément aux procédures de I'ISO qui requièrent l'approbation de 75 YO au moins des
comités membres votants.
La Norme internationale IS0 1872-2 a été élaborée par le comité technique ISO/TC 61,
Plastiques.
Conjointement avec la Norme internationale IS0 1872-1 : 1986, elle annule et
remplace la Norme internationale IS0 1872 : 1972.
L'ISO 1872 comprend les parties suivantes, présentées sous le titre général
Plastiques - Thermoplastiques à base de polyéthylène (PEI et de copolymères d'éthy-
lène :
- Partie 1: Désignation
-
Partie 2: Préparation des éprouvettes et détermination des caractéristiques
L'annexe A de la présente partie de 1'1SO1872 est donnée uniquement à titre
d'information.
O IS0 1989
Droits de reproduction réservés. Aucune partie de cette publication ne peut être reproduite ni
utilisée SOUS quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie et les microfilms, sans l'accord écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 O CH-I211 Genève 20 O Suisse
Imorimé en Suisse
---------------------- Page: 2 ----------------------
IS0 1872-2 : 1989 (FI
NORME INTERNATIONALE
Plastiques - Thermoplastiques à base de polyéthylène
(PE) et de copolymères d’éthylène -
Partie 2 :
Préparation des éprouvettes et détermination des
ca ract é rist iq u es
2 Références normatives
L 1 Domaine d’application
Les normes suivantes contiennent des dispositions qui, par
1.1 La présente partie de I‘ISO 1872 prescrit les conditions de
suite de la référence qui en est faite, constituent des disposi-
moulage d’éprouvettes de matériaux polyéthylène dans un état
tions valables pour la présente partie de 1’1S0 1872. Au moment
défini, ainsi que les méthodes pour le mesurage de leurs
de la publication, les éditions indiquées étaient en vigueur.
caractéristiques’).
Toute norme est sujette à révision et les parties prenantes des
accords fondés sur la présente partie de I’ISO 1872 sont invi-
tées à rechercher la possibilité d’appliquer les éditions les plus
1.2 Elle n’indique pas de valeurs pour ces caractéristiques.
récentes des normes indiquées ci-après. Les membres de la CE1
Celles qui sont retenues pour la désignation des polyéthylènes
et de 1‘1S0 possèdent le registre des Normes internationales en
pour moulage et extrusion sont indiquées dans 1’1S0 1872-1.
vigueur à un moment donné.
Les autres caractéristiques appropriées indiquées dans la pré-
sente partie de 1’1S0 1872, et leurs valeurs peuvent être obte-
IS0 62 : 1980, Plastiques - Détermination de l’absorption
nues en se reportant aux notices des fabricants. Les valeurs
d‘eau.
sont comparables les unes aux autres lorsque les éprouvettes
sont moulées et les caractéristiques déterminées suivant les
IS0 75 : 1987, Plastiques et ébonite - Détermination de la
règles décrites ci-après.
température de fléchissement sous charge.
IS0 175 : 1981, Plastiques - Détermination de l’action des
1.3 Les valeurs déterminées conformément à la présente par-
agents chimiques liquides, y compris l’eau.
tie de I‘ISO 1872 ne seront pas nécessairement identiques à cel-
L les qui sont obtenues en utilisant des éprouvettes de dimen-
IS0 178 : 1975, Matièresplastiques - Détermination des cara-
sions différentes et/ou préparées selon des modes opératoires
téristiques de flexion des matières plastiques rigides.
différents. Elles peuvent également être influencées par les
colorants et d’autres additifs. Les valeurs obtenues pour les IS0 179 : 1982, Plastiques - Détermination de la résistance au
caractéristiques d’un objet moulé dépendent, entre autres, de choc Charpy des matières rigides.
la matière à mouler, de la forme de l’objet, de la méthode
IS0 180 : 1982, Plastiques - Détermination de la résistance au
d‘essai et de l’état d’anisotropie. Ce dernier est fonction du
choc lzod des matières rigides.
canal d’alimentation et des conditions de moulage, par exemple
de la température, de la pression ou de la vitesse d‘injection. On
IS0 291 1977, Plastiques - Atmosphères normales de condi-
doit également tenir compte de tout traitement, par exemple du
tionnement et d‘essai.
conditionnement ou du recuit.
IS0 293 : 1986, Plastiques - Moulage par compression des
éprouvettes en matières thermoplastiques.
1.4 L‘histoire thermique et les tensions internes de I‘éprou-
vette peuvent influencer fortement ses propriétés thermoméca-
IS0 294 : 1975, Matières plastiques - Moulage par injection
niques et sa résistance à la fissuration sous contrainte dans un
des éprouvettes en matières thermoplastiques.
environnement donné. Les propriétés électriques sont moins
fortement influencées; elles dépendent surtout de la composi- IS0 306 : 1987, Plastiques - Matières thermoplastiques -
tion chimique de la matière à mouler. Détermination de la température de ramollissement Vicat.
1) Les méthodes et températures recommandées seront obligatoires après la prochaine révision de cinq ans.
1
---------------------- Page: 3 ----------------------
IS0 1872-2 : 1989 (FI
IS0 6252 : 1981, Plastiques - Détemination de la fissuration
ISOIR 527 : 1966, Matières plastiques - Détermination des
sous contrainte dans un environnernent donné (ESCI -
caractéristiques en traction. .
Méthode sous contrainte de traction constante.
IS0 537 : 1980, Plastiques - Essai au pendule de torsion.
IS0 6602 : 1985, Plastiques - Détermination du fluage en
flexion par sollicitation en trois points.
IS0 868 : 1985, Plastiques et ébonite - Détermination de la
dureté par pénétration au moyen d'un duromètre (dureté
CE1 93 : 1980, Méthodes recommandées pour la mesure des
Shore).
résistivités transversales et superficielles d'un matériau isolant
électrisue.
IS0 899 : 1981, Plastiques - Détermination du fluage en trac-
tion.
CE1 112 : 1979, Méthode recommandée pour déterminer
l'indice de résistance au Cheminement des matériaux isolants
IS0 974 : 1980, Plastiques - Détermination de la température
solides dans des conditions humides.
de fragilité au choc.
CE1 243 : 1967, Méthodes d'essai recommandées pour la déter-
IS0 1133 : 1981, Plastiques - Détermination de l'indice de
mination de la rigidité diélectrique des matériaux isolants soli-
fluidité à chaud des thermoplastiques.
des aux fréquences industrielles.
CE1 250 : 1969, Méthodes recommandées pour la détermina-
IS0 1183 : 1987, Plastiques - Méthodes pour déterminer la
..
tion de la permittivité et du facteur de dissipation des isolants
masse volumique et la densité relative des plastiques non alvéo-
électriques aux fréquences industrielles, audibles et radioélec-
laires.
triques (ondes métriques comprises). 1
IS0 1628-3 : - I), Plastiques - Détermination de l'indice de
viscosité et de I'indice limite de viscosité - Partie 3: Polyéthy-
lènes et polypropylènes.
3 Préparation des éprouvettes
IS0 1872-1 : 1986, Plastiques - Thermoplastiques à base de Deux méthodes de préparation des éprouvettes sont décrites :
le moulage par compression et le moulage par injection.
polyéthylène (PEI et de copolymères d'éthylène - Partie 1:
Désignation.
3.1 Moulage par compression
IS0 2039-1 : 1987, Plastiques -
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.