ISO 2106:2011
(Main)Anodizing of aluminium and its alloys — Determination of mass per unit area (surface density) of anodic oxidation coatings — Gravimetric method
Anodizing of aluminium and its alloys — Determination of mass per unit area (surface density) of anodic oxidation coatings — Gravimetric method
ISO 2106:2011 specifies a gravimetric method for determining the mass per unit area (surface density) of anodic oxidation coatings on aluminium and its alloys. The method is applicable to all oxidation coatings formed by anodizing aluminium and its alloys, either cast or wrought, and is suitable for most aluminium alloys, except those in which the copper content is greater than 6 %.
Anodisation de l'aluminium et de ses alliages — Détermination de la masse par unité de surface (masse surfacique) des couches anodiques — Méthode gravimétrique
L'ISO 2106:2011 spécifie une méthode gravimétrique de détermination de la masse par unité de surface (masse surfacique) des couches anodiques sur l'aluminium et ses alliages. Cette méthode est applicable à toutes les couches d'oxyde obtenues par anodisation sur l'aluminium et ses alliages, aussi bien sur pièces moulées que sur produits corroyés, et elle est valable pour la plupart des alliages d'aluminium, à l'exception de ceux dont la teneur en cuivre est supérieure à 6 %.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 2106
Third edition
2011-03-01
Anodizing of aluminium and its alloys —
Determination of mass per unit area
(surface density) of anodic oxidation
coatings — Gravimetric method
Anodisation de l'aluminium et de ses alliages — Détermination de la
masse par unité de surface (masse surfacique) des couches
anodiques — Méthode gravimétrique
Reference number
ISO 2106:2011(E)
©
ISO 2011
---------------------- Page: 1 ----------------------
ISO 2106:2011(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.
COPYRIGHT PROTECTED DOCUMENT
© ISO 2011
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2011 – All rights reserved
---------------------- Page: 2 ----------------------
ISO 2106:2011(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 2106 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee
SC 2, Organic and anodic oxidation coatings on aluminium.
This third edition cancels and replaces the second edition (ISO 2106:1982), which has been technically
revised. It also incorporates the Amendment ISO 2106:1982/Amd.1:1983.
© ISO 2011 – All rights reserved iii
---------------------- Page: 3 ----------------------
INTERNATIONAL STANDARD ISO 2106:2011(E)
Anodizing of aluminium and its alloys — Determination of mass
per unit area (surface density) of anodic oxidation coatings —
Gravimetric method
1 Scope
This International Standard specifies a gravimetric method for determining the mass per unit area (surface
density) of anodic oxidation coatings on aluminium and its alloys.
The method is applicable to all oxidation coatings formed by anodizing aluminium and its alloys, either cast or
wrought, and is suitable for most aluminium alloys, except those in which the copper content is greater than
6 %.
NOTE 1 A high content of copper in the alloy can lead to increased dissolution of the basis aluminium.
NOTE 2 If the thickness is known with sufficient precision (for example, using the method specified in ISO 2128),
determination of the mass per unit area (surface density) of the coatings will enable its apparent density to be calculated.
Conversely, if the conditions of application of the coating and its density are known, the determination of its mass per unit
area (surface density) can permit calculation of the average mass and an approximate evaluation of the thickness (see the
Note in Clause 6).
2 Principle
The anodic oxidation coating on a weighed test piece of known surface area is dissolved without significantly
attacking the basis metal, using a mixture of phosphoric acid and chromium(VI) of specified concentration.
After dissolution of the coating, the test piece is reweighed, and the loss in mass is calculated. The mass loss
is related to the unit area covered by the coating, and is expressed in milligrams of coating per square
decimetre of surface.
NOTE This is a destructive test .
...
NORME ISO
INTERNATIONALE 2106
Troisième édition
2011-03-01
Anodisation de l'aluminium et de ses
alliages — Détermination de la masse par
unité de surface (masse surfacique) des
couches anodiques — Méthode
gravimétrique
Anodizing of aluminium and its alloys — Determination of mass per unit
area (surface density) of anodic oxidation coatings — Gravimetric
method
Numéro de référence
ISO 2106:2011(F)
©
ISO 2011
---------------------- Page: 1 ----------------------
ISO 2106:2011(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2011
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2011 – Tous droits réservés
---------------------- Page: 2 ----------------------
ISO 2106:2011(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 2106 a été élaborée par le comité technique ISO/TC 79, Métaux légers et leurs alliages, sous-comité
SC 2, Couches organiques et couches d'oxydation anodique sur l'aluminium.
Cette troisième édition annule et remplace la deuxième édition (ISO 2106:1982), qui a fait l'objet d'une
révision technique. Elle incorpore également l'Amendement ISO 2106:1982/Amd.1:1983.
© ISO 2011 – Tous droits réservés iii
---------------------- Page: 3 ----------------------
NORME INTERNATIONALE ISO 2106:2011(F)
Anodisation de l'aluminium et de ses alliages — Détermination
de la masse par unité de surface (masse surfacique) des
couches anodiques — Méthode gravimétrique
1 Domaine d'application
La présente Norme internationale spécifie une méthode gravimétrique de détermination de la masse par unité
de surface (masse surfacique) des couches anodiques sur l'aluminium et ses alliages.
Cette méthode est applicable à toutes les couches d'oxyde obtenues par anodisation sur l'aluminium et ses
alliages, aussi bien sur pièces moulées que sur produits corroyés, et elle est valable pour la plupart des
alliages d'aluminium, à l'exception de ceux dont la teneur en cuivre est supérieure à 6 %.
NOTE 1 Une forte teneur en cuivre dans l'alliage peut conduire à une forte dissolution de l'aluminium de base.
NOTE 2 Si l'épaisseur est connue avec une précision suffisante (par exemple au moyen de la méthode spécifiée dans
l'ISO 2128), la détermination de la masse par unité de surface (masse surfacique) des couches permettra de calculer sa
masse volumique apparente. Inversement, si les conditions d'application de la couche et sa masse volumique sont
connues, la détermination de la masse par unité de surface (masse surfacique) peut permettre le calcul de la masse
moyenne et une estimation approximative de l'épaisseur (voir la Note de l'Article 6).
2 Principe
La couche anodique sur une éprouvette pesée, de surface connue, est dissoute, sans attaque significative du
métal de base, au moyen d'un mélange d'acide phosphorique et de chrome hexavalent de concentration
spécifiée.
Après dissolution de la couche, l'éprouvette est à nouveau pesée et la perte de masse est calculée. La perte
de masse est rapportée à l'unité de surface couverte par la couche, et elle est
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.