ISO 176:2005

Plastics — Determination of loss of plasticizers — Activated carbon method

ISO 176:2005 specifies two empirical methods for the quantitative determination of the loss of mass from a plastic material under defined conditions of rime and temperature, in the presence of activated carbon. Method A -- The test specimens are in direct contact with the carbon; this method is particularly useful for materials that have to be tested at relatively low temperatures because they flow at higher temperatures. Method B -- The test specimens are placed in wire cages that prevent direct contact between the test specimens and the carbon. These methods apply, in particular, to the quantitative determination of the loss on heating of plasticizers from plasticized plastic materials, in which case it is generally assumed that no significant amounts of other volatile materials are present. They are empirical test methods, suitable only for a rather rapid comparison of the losses of plasticizers or, in general, of volatile compounds, from different plastics. ISO 176:2005 also applies to the comparison of different types of plasticizers; in this case standard compounds should be prepared, on the basis of a well characterized resin, with known ratios of resin to plasticizer.

Matières plastiques — Détermination des pertes en plastifiants — Méthode au charbon actif

L'ISO 176:2005 spécifie deux méthodes empiriques de détermination quantitative de la perte de masse affectant une matière plastique, dans des conditions données de température et de temps, en présence de charbon actif. Deux méthodes sont spécifiées: Méthode A - Les éprouvettes sont en contact direct avec le charbon actif; cette méthode est particulièrement utile dans le cas où les matières plastiques doivent être soumises à essai à des températures relativement basses du fait qu'elles se ramollissent à des températures plus élevées. Méthode B - Les éprouvettes sont placées dans des cages métalliques pour éviter qu'elles ne soient en contact direct avec le charbon actif. Ces méthodes sont employées, en particulier, pour déterminer quantitativement la perte en plastifiants de matières plastiques plastifiées, soumises à l'action de la chaleur. On admet, en général, que dans ce cas, il n'existe pas d'autres composés volatils, en quantité notable. Ces méthodes sont empiriques et ne conviennent que pour comparer, d'une manière rapide, les pertes en plastifiants ou, d'une façon plus générale, en composés volatils, de différentes matières plastiques. L'ISO 176:2005 s'applique aussi à la comparaison de différents types de plastifiants; il convient alors de préparer des mélanges types, à base de résine bien déterminée et dans des proportions bien définies de plastifiant par rapport à la résine.

General Information

• Status: Published
• Publication Date: 03-Jan-2005
• ICS: 83.080.01 - Plastics in general
• Technical Committee: ISO/TC 61/SC 6 - Ageing, chemical and environmental resistance
• Drafting Committee: ISO/TC 61/SC 6/WG 7 - Basic standards
• Current Stage: 9093 - International Standard confirmed
• Completion Date: 06-Jun-2023

Relations

• Consolidates: ISO 6115:1981 - Shipbuilding — Trawl winches
• Effective Date: 06-Jun-2022
• Revises: ISO 176:1976 - Plastics — Determination of loss of plasticizers — Activated carbon method
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 176
Second edition
2005-02-01


Plastics — Determination of loss of
plasticizers — Activated carbon method
Matières plastiques — Détermination des pertes en plastifiants —
Méthode au charbon actif




Reference number
ISO 176:2005(E)
©
ISO 2005

---------------------- Page: 1 ----------------------
ISO 176:2005(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but
shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In
downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat
accepts no liability in this area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation
parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In
the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below.


©  ISO 2005
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means,
electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or
ISO's member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland

ii © ISO 2005 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 176:2005(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 176 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 6, Ageing, chemical
and environmental resistance.
This second edition cancels and replaces the first edition (ISO 176:1976), Clause 8 of which is now Clause 9
and a new Clause 8 has been added.

© ISO 2005 – All rights reserved iii

---------------------- Page: 3 ----------------------
INTERNATIONAL STANDARD ISO 176:2005(E)

Plastics — Determination of loss of plasticizers — Activated
carbon method
1 Scope
This International Standard specifies two empirical methods for the quantitative determination of the loss of
mass from a plastic material under defined conditions of time and temperature, in the presence of activated
carbon.
These methods are used, in particular, for the quantitative determination of the loss on heating of plasticizers
from plasticized plastic materials, in which case it is generally assumed that no significant amounts of other
volatile materials are present.
These are empirical test methods, suitable only for a rather rapid comparison of the losses of plasticizers or, in
general, of volatile compounds, from different plastics.
They may also be employed for the comparison of different types of plasticizers; in this case, standard
compounds should be prepared, on the basis of a well characterized resin, with known ratios of resin to
plasticizer.
NOTE These comparisons are possible only if the test specimens are of the same thickness. If it can be assumed
that, after reconditioning, the moisture content of the exposed specimens is equal to that obtaining after the original
conditioning, the effect of moisture may be ignored.
Two methods are specified:
 Method A: The test specimens are in direct contact with the carbon; this method is particularly useful
for materials that have to be tested at relatively low temperatures because they flow at
higher temperatures.
 Method B: The test specimens are placed in wire cages that prevent direct contact between the test
specimens and the carbon.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 291, Plastics — Standard atmospheres for conditioning and testing
ISO 293, Plastics — Compression moulding of test specimens of thermoplastic materials
3 Apparatus and materials
3.1 Analytical balance, accurate to 0,000 1 g.
3.2 Micrometer, accurate to 0,01 mm.
© ISO 2005 – All rights reserved 1

---------------------- Page: 4 ----------------------
ISO 176:2005(E)
3.3 Thermostatic bath or oven, capable of maintaining the temperature to within ± 1 °C of the test
temperature, in the range of 50 °C to 150 °C.
3.4 Containers, metal cans, of cylindrical form, about 100 mm in diameter and 120 mm in height, provided
with a non-air-tight cover; a lid with a small vent hole of 3 mm diameter may be suitable.
3.5 Wire cages, constructed from bronze gauze having apertures of approximately 500 µm with a diameter
of 60 mm and a height of 6 mm, formed by soldering a strip of the gauze a right angles to the periphery of
...

NORME ISO
INTERNATIONALE 176
Deuxième édition
2005-02-01



Matières plastiques — Détermination des
pertes en plastifiants — Méthode au
charbon actif
Plastics — Determination of loss of plasticizers — Activated carbon
method




Numéro de référence
ISO 176:2005(F)
©
ISO 2005

---------------------- Page: 1 ----------------------
ISO 176:2005(F)
PDF – Exonération de responsabilité
Le présent fichier PDF peut contenir des polices de caractères intégrées. Conformément aux conditions de licence d'Adobe, ce fichier
peut être imprimé ou visualisé, mais ne doit pas être modifié à moins que l'ordinateur employé à cet effet ne bénéficie d'une licence
autorisant l'utilisation de ces polices et que celles-ci y soient installées. Lors du téléchargement de ce fichier, les parties concernées
acceptent de fait la responsabilité de ne pas enfreindre les conditions de licence d'Adobe. Le Secrétariat central de l'ISO décline toute
responsabilité en la matière.
Adobe est une marque déposée d'Adobe Systems Incorporated.
Les détails relatifs aux produits logiciels utilisés pour la création du présent fichier PDF sont disponibles dans la rubrique General Info
du fichier; les paramètres de création PDF ont été optimisés pour l'impression. Toutes les mesures ont été prises pour garantir
l'exploitation de ce fichier par les comités membres de l'ISO. Dans le cas peu probable où surviendrait un problème d'utilisation,
veuillez en informer le Secrétariat central à l'adresse donnée ci-dessous.


©  ISO 2005
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publication ne peut être reproduite ni utilisée sous
quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord écrit
de l'ISO à l'adresse ci-après ou du comité membre de l'ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax. + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Publié en Suisse

ii © ISO 2005 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 176:2005(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée
aux comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du
comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l'ISO participent également aux travaux. L'ISO collabore étroitement avec
la Commission électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les Normes internationales sont rédigées conformément aux règles données dans les Directives ISO/CEI,
Partie 2.
La tâche principale des comités techniques est d'élaborer les Normes internationales. Les projets de Normes
internationales adoptés par les comités techniques sont soumis aux comités membres pour vote. Leur
publication comme Normes internationales requiert l'approbation de 75 % au moins des comités membres
votants.
L'attention est appelée sur le fait que certains des éléments du présent document peuvent faire l'objet de
droits de propriété intellectuelle ou de droits analogues. L'ISO ne saurait être tenue pour responsable de ne
pas avoir identifié de tels droits de propriété et averti de leur existence.
L'ISO 176 a été élaborée par le comité technique ISO/TC 61, Plastiques, sous-comité SC 6, Vieillissement et
résistance aux agents chimiques et environnants.
Cette deuxième édition annule et remplace la première édition (ISO 176:1976), dont l'Article 8 est devenu
maintenant l'Article 9 et un nouvel Article 8 a été ajouté.

© ISO 2005 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
NORME INTERNATIONALE ISO 176:2005(F)

Matières plastiques — Détermination des pertes en
plastifiants — Méthode au charbon actif
1 Domaine d'application
La présente Norme internationale spécifie deux méthodes empiriques de détermination quantitative de la
perte de masse affectant une matière plastique, dans des conditions données de température et de temps, en
présence de charbon actif.
Ces méthodes sont employées, en particulier, pour déterminer quantitativement la perte en plastifiants de
matières plastiques plastifiées, soumises à l'action de la chaleur. On admet, en général, que dans ce cas, il
n'existe pas d'autres composés volatils, en quantité notable.
Ces méthodes sont empiriques et ne conviennent que pour comparer, d'une manière rapide, les pertes en
plastifiants ou, d'une façon plus générale, en composés volatils, de différentes matières plastiques.
Ces méthodes peuvent également être employées pour comparer différents types de plastifiants; il convient
alors de préparer des mélanges types, à base de résine bien déterminée et dans des proportions bien
définies de plastifiant par rapport à la résine.
NOTE Ces comparaisons ne sont possibles que si les éprouvettes ont la même épaisseur. Si l'on peut admettre
qu'après reconditionnement le taux d'humidité des éprouvettes exposées est égal au taux obtenu à l'issue du
conditionnement initial, l'effet de l'humidité peut être considéré comme négligeable.
Deux méthodes sont spécifiées:
 Méthode A: Les éprouvettes sont en contact direct avec le charbon actif; cette méthode est
particulièrement utile dans le cas où les matières plastiques doivent être soumises à essai
à des températures relativement basses du fait qu'elles se ramollissent à des
températures plus élevées.
 Méthode B: Les éprouvettes sont placées dans des cages métalliques pour éviter qu'elles ne soient en
contact direct avec le charbon actif.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent document. Pour les
références datées, seule l'édition citée s'applique. Pour les références non datées, la dernière édition du
document de référence s'applique (y compris les éventuels amendements).
ISO 291, Plastiques — Atmosphères normales de conditionnement et d'essai
ISO 293, Plastiques — Moulage par compression des éprouvettes en matières thermoplastiques
3 Appareillage et produits
3.1 Balance analytique, précise à 0,000 1 g.
3.2 Micromètre, précis à 0,01 mm.
© ISO 2005 – Tous droits réservés 1

---------------------- Page: 4 ----------------------
ISO 176:2005(F)
3.3 Bain thermostatique ou étuve, permettant de maintenir la température à ± 1 °C de la température
d'essai, comprise entre 50 °C et 150 °C.
3.4 Récipients, métalliques, de forme cylindrique, d'environ 100 mm de diamètre et de 120 mm de hauteur,
recouverts de façon non hermétique; un couvercle percé d'un petit trou de 3 mm de diamètre peut convenir.
3.5 Cages métalliques, en toile à tamis en bronze, ayant des ouvertures d'environ 500 µm, de 60 mm de
diamètre et de 6 mm de hauteur, fabriquées par soudage à angle droit d'une bande de toile métallique sur le
...