ISO 17228:2015
(Main)Leather — Tests for colour fastness — Change in colour with accelerated ageing
Leather — Tests for colour fastness — Change in colour with accelerated ageing
ISO 17228:2015 specifies various ageing procedures to obtain an indication of the changes that could occur when leather is exposed to a certain environment for a prolonged time. Over time, the surface colour of leather and the leather itself change due to ageing and to the action of the surroundings on the leather. The test conditions to be used depend on the type of leather and its intended use. This procedure can also be used to age specimens for the test of dimensional change according to ISO 17130.
Cuir — Essais de solidité des coloris — Changement de couleur avec vieillissement accéléré
L'ISO 17228:2015 spécifie des méthodes d'essai de vieillissement ayant pour but de décrire les dégradations susceptibles de se produire lorsque le cuir est longtemps exposé à un certain milieu. Au fil du temps, la couleur de surface du cuir et le cuir lui-même s'altèrent en raison de leur vieillissement et de l'influence du milieu environnant sur le cuir. Les conditions d'essai préconisées dépendent du type de cuir et de l'usage auquel il est destiné. Ce mode opératoire peut également être utilisé pour le vieillissement d'échantillons dans le cadre de l'essai de variations dimensionnelles selon l'ISO 17130.
General Information
Relations
Buy Standard
Standards Content (Sample)
INTERNATIONAL ISO
STANDARD 17228
IULTCS/IUF 412
Second edition
2015-03-01
Leather — Tests for colour fastness
— Change in colour with accelerated
ageing
Cuir — Essais de solidité des coloris — Changement de couleur avec
vieillissement accéléré
Reference numbers
IULTCS/IUF 412:2015(E)
©
ISO 2015
IULTCS/IUF 412:2015(E)
© ISO 2015
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2015 – All rights reserved
IULTCS/IUF 412:2015(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Principle . 1
4 Apparatus . 2
5 Test specimens. 2
6 Ageing by heat alone . 2
6.1 Principle . 2
6.2 Procedure . 3
7 Ageing by heat and elevated humidity . 4
7.1 Principle . 4
7.2 Procedure . 4
8 Cyclic variation in heat and elevated humidity . 5
8.1 Principle . 5
8.2 Procedure . 5
9 Test report . 7
Annex A (informative) Comments on specific aspects of the colour-measurement procedure .8
Bibliography . 9
IULTCS/IUF 412:2015(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
ISO 17228 was prepared by the Fastness Tests Commission of the International Union of Leather
Technologists and Chemists Societies (IUF Commission, IULTCS) in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 289, Leather, the secretariat of
which is held by UNI, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
It is based on IUF 412 published in J. Soc. Leather Tech. Chem., 86 pp. 325-331, 2002, and declared an
official method of the IULTCS in May 2003.
IULTCS, originally formed in 1897, is a world-wide organization of professional leather societies to
further the advancement of leather science and technology. IULTCS has three Commissions, which are
responsible for establishing international methods for the sampling and testing of leather. ISO recognizes
IULTCS as an international standardizing body for the preparation of test methods for leather.
This second edition cancels and replaces the first edition (ISO 17228:2005), which has been technically
revised. This new version is a general update of the procedures and in Tables 1, 2, and 3 includes
additional ageing options.
Annex A is informative.
iv © ISO 2015 – All rights reserved
INTERNATIONAL STANDARD ISO 17228:2015(E)
Leather — Tests for colour fastness — Change in colour
with accelerated ageing
1 Scope
This International Standard specifies various ageing procedures to obtain an indication of the changes
that could occur when leather is exposed to a certain environment for a prolonged time. Over time, the
surface colour of leather and the leather itself change due to ageing and to the action of the surroundings
on the leather. The test conditions to be used depend on the type of leather and its intended use.
This procedure can also be used to age specimens for the test of dimensional change according to
ISO 17130.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 105-A01, Textiles — Tests for colour fastness — Part A01: General principles of testing
ISO 105-A02, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour
ISO 105-A03, Textiles — Tests for colour fastness — Part A03: Grey scale for assessing staining
ISO 105-A04, Textiles — Tests for colour fastness — Part A04: Method for the instrumental assessment of
the degree of staining of adjacent fabrics
ISO 105-A05, Textiles — Tests for colour fastness — Part A05: Instrumental assessment of change in colour
for determination of grey scale rating
ISO 2418, Leather — Chemical, physical and mechanical and fastness tests — Sampling location
ISO 2419, Leather — Physical and mechanical tests — Sample preparation and conditioning
ISO 17130, Leather — Physical and mechanical tests — Determination of dimensional change
3 Principle
A test specimen of leather is exposed to at least one of the three following conditions:
— heat (see Clause 6);
— heat and humidity (see Clause 7);
— cycles of different temperature and humidity (see Clause 8).
One or more of these procedures may take place simultaneously. The change in colour of the specimen
is assessed with the standard grey scale and, if applicable, any changes in the finish or appearance are
noted.
These procedures can also be used to prepare the leather specimen for other physical or fastness tests
after accelerated ageing. The assessment of dimension change is described in ISO 17130.
NOTE Accelerated ageing tests are for guidance only and they are not necessarily representative of long term
use at ambient temperatures.
IULTCS/IUF 412:2015(E)
The general colour fastness testing principles shall be in accordance with those described in ISO 105-
A01, taking into account that the substrate is leather.
4 Apparatus
Use normal laboratory apparatus and the following:
4.1 Oven, fitted with a central rack, capable of maintaining a temperature within ±2 °C of the defined
temperature. The oven should have a vent, preferably with a circulating fan, and an inside made of inert
materials.
4.2 Climate chamber, fitted with a central rack, capable of maintaining a temperature within ±2 °C of
the defined temperature and a relative humidity within ±5 % of the defined relative humidity.
4.3 Suitable system for holding the specimen and preventing contact with the oven or climate
chamber sides.
4.4 Grey scale for assessing change in colour, complying with ISO 105-A02, or an instrumental
system for assessing change in colour, complying with ISO 105-A05.
4.5 Grey scale for assessing staining, complying with ISO 105-A03, or an instrumental system for
assessing staining, complying with ISO 105-A04.
4.6 Stop clock, readable to 1 s.
5 Test specimens
5.1 Prior to cutting out specimens, condition the piece of leather in accordance with ISO 2419.
5.2 Cut out two representative test specimens measuring not less than 100 mm × 100 mm.
If the piece of leather available for testing is a whole hide or skin, then the specimens shall be taken in
accordance with standard procedures given in ISO 2418.
NOTE If other properties, such as dimensional change, are to be measured, then additional test specimens
are used due to different kind of storage during the ageing step.
6 Ageing by heat alone
6.1 Principle
The purpose of this procedure is to simulate ageing by the application of heat. Two different types of
change can be involved:
a) the change in colour of the substances in the leather;
b) the evaporation of volatile substances or the migration of substances, leading to a change in the
colour and/or other properties of the leather or finish.
As both the exposure time and the temperature can be varied, this procedure can be used for a variety
of purposes, including preparing specimens for other tests.
2 © ISO 2015 – All rights reserved
IULTCS/IUF 412:2015(E)
6.2 Procedure
6.2.1 Pre-heat the oven (4.1) to the desired temperature (see 6.2.3).
6.2.2 Place one test specimen (the reference specimen) in a place where it is protected from light and
kept under standard conditions, according to ISO 2419.
6.2.3 Hang the other test specimen with a clip from, or place it on, the holder (4.3) in the middle of the
oven such that the air has free access to both sides.
Unless specified otherwise, age the specimen under one of the sets of conditions indicated in Table 1.
Table 1 — Ageing by heat
Method Conditions for ageing by heat Recommended use
6A 24 h ± 1 h at 60 °C ± 2 °C General-purpose ageing conditions
Specifically for yellowing of individual products in
6B 24 h ± 1 h at 100 °C ± 2 °C
undyed leather
6C 72 h ± 2 h at 60 °C ± 2 °C Extended general-purpose ageing
6D 72 h ± 2 h at 100 °C ± 2 °C Ageing of automotive leather
6E 168 h ± 2 h at 90 °C ± 2 °C Extended ageing of automotive leather
6F 168 h ± 2 h at 60 °C ± 2 °C Extended ageing at moderate temperature
6G 168 h ± 2 h at 100 °C ± 2 °C Extended ageing at elevated temperature
6H 4 h ± 0,2 h at 100 °C ± 2 °C Short ageing of automotive leather
6J 144 h ± 2 h at 100 °C ± 2 °C Ageing of automotive leather
Extended ageing of automotive leather at
6K 168 h ± 2 h at 120 °C ± 2 °C
high temperature
The sets of conditions given in Table 1 have been selected to provide a range of conditions for different
applications. If other conditions are used, then they shall be clearly noted in the test report.
6.2.4 After the period of time has elapsed, remove the test specimen from the oven. Allow the specimen
to cool. Then, recondition both the test and the reference specimen under standard conditions according
to ISO 2419 f
...
INTERNATIONAL ISO
STANDARD 17228
IULTCS/IUF 412
Second edition
2015-03-01
Leather — Tests for colour fastness
— Change in colour with accelerated
ageing
Cuir — Essais de solidité des coloris — Changement de couleur avec
vieillissement accéléré
Reference numbers
IULTCS/IUF 412:2015(E)
©
ISO 2015
IULTCS/IUF 412:2015(E)
© ISO 2015
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Published in Switzerland
ii © ISO 2015 – All rights reserved
IULTCS/IUF 412:2015(E)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Principle . 1
4 Apparatus . 2
5 Test specimens. 2
6 Ageing by heat alone . 2
6.1 Principle . 2
6.2 Procedure . 3
7 Ageing by heat and elevated humidity . 4
7.1 Principle . 4
7.2 Procedure . 4
8 Cyclic variation in heat and elevated humidity . 5
8.1 Principle . 5
8.2 Procedure . 5
9 Test report . 7
Annex A (informative) Comments on specific aspects of the colour-measurement procedure .8
Bibliography . 9
IULTCS/IUF 412:2015(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
ISO 17228 was prepared by the Fastness Tests Commission of the International Union of Leather
Technologists and Chemists Societies (IUF Commission, IULTCS) in collaboration with the European
Committee for Standardization (CEN) Technical Committee CEN/TC 289, Leather, the secretariat of
which is held by UNI, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
It is based on IUF 412 published in J. Soc. Leather Tech. Chem., 86 pp. 325-331, 2002, and declared an
official method of the IULTCS in May 2003.
IULTCS, originally formed in 1897, is a world-wide organization of professional leather societies to
further the advancement of leather science and technology. IULTCS has three Commissions, which are
responsible for establishing international methods for the sampling and testing of leather. ISO recognizes
IULTCS as an international standardizing body for the preparation of test methods for leather.
This second edition cancels and replaces the first edition (ISO 17228:2005), which has been technically
revised. This new version is a general update of the procedures and in Tables 1, 2, and 3 includes
additional ageing options.
Annex A is informative.
iv © ISO 2015 – All rights reserved
INTERNATIONAL STANDARD ISO 17228:2015(E)
Leather — Tests for colour fastness — Change in colour
with accelerated ageing
1 Scope
This International Standard specifies various ageing procedures to obtain an indication of the changes
that could occur when leather is exposed to a certain environment for a prolonged time. Over time, the
surface colour of leather and the leather itself change due to ageing and to the action of the surroundings
on the leather. The test conditions to be used depend on the type of leather and its intended use.
This procedure can also be used to age specimens for the test of dimensional change according to
ISO 17130.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 105-A01, Textiles — Tests for colour fastness — Part A01: General principles of testing
ISO 105-A02, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour
ISO 105-A03, Textiles — Tests for colour fastness — Part A03: Grey scale for assessing staining
ISO 105-A04, Textiles — Tests for colour fastness — Part A04: Method for the instrumental assessment of
the degree of staining of adjacent fabrics
ISO 105-A05, Textiles — Tests for colour fastness — Part A05: Instrumental assessment of change in colour
for determination of grey scale rating
ISO 2418, Leather — Chemical, physical and mechanical and fastness tests — Sampling location
ISO 2419, Leather — Physical and mechanical tests — Sample preparation and conditioning
ISO 17130, Leather — Physical and mechanical tests — Determination of dimensional change
3 Principle
A test specimen of leather is exposed to at least one of the three following conditions:
— heat (see Clause 6);
— heat and humidity (see Clause 7);
— cycles of different temperature and humidity (see Clause 8).
One or more of these procedures may take place simultaneously. The change in colour of the specimen
is assessed with the standard grey scale and, if applicable, any changes in the finish or appearance are
noted.
These procedures can also be used to prepare the leather specimen for other physical or fastness tests
after accelerated ageing. The assessment of dimension change is described in ISO 17130.
NOTE Accelerated ageing tests are for guidance only and they are not necessarily representative of long term
use at ambient temperatures.
IULTCS/IUF 412:2015(E)
The general colour fastness testing principles shall be in accordance with those described in ISO 105-
A01, taking into account that the substrate is leather.
4 Apparatus
Use normal laboratory apparatus and the following:
4.1 Oven, fitted with a central rack, capable of maintaining a temperature within ±2 °C of the defined
temperature. The oven should have a vent, preferably with a circulating fan, and an inside made of inert
materials.
4.2 Climate chamber, fitted with a central rack, capable of maintaining a temperature within ±2 °C of
the defined temperature and a relative humidity within ±5 % of the defined relative humidity.
4.3 Suitable system for holding the specimen and preventing contact with the oven or climate
chamber sides.
4.4 Grey scale for assessing change in colour, complying with ISO 105-A02, or an instrumental
system for assessing change in colour, complying with ISO 105-A05.
4.5 Grey scale for assessing staining, complying with ISO 105-A03, or an instrumental system for
assessing staining, complying with ISO 105-A04.
4.6 Stop clock, readable to 1 s.
5 Test specimens
5.1 Prior to cutting out specimens, condition the piece of leather in accordance with ISO 2419.
5.2 Cut out two representative test specimens measuring not less than 100 mm × 100 mm.
If the piece of leather available for testing is a whole hide or skin, then the specimens shall be taken in
accordance with standard procedures given in ISO 2418.
NOTE If other properties, such as dimensional change, are to be measured, then additional test specimens
are used due to different kind of storage during the ageing step.
6 Ageing by heat alone
6.1 Principle
The purpose of this procedure is to simulate ageing by the application of heat. Two different types of
change can be involved:
a) the change in colour of the substances in the leather;
b) the evaporation of volatile substances or the migration of substances, leading to a change in the
colour and/or other properties of the leather or finish.
As both the exposure time and the temperature can be varied, this procedure can be used for a variety
of purposes, including preparing specimens for other tests.
2 © ISO 2015 – All rights reserved
IULTCS/IUF 412:2015(E)
6.2 Procedure
6.2.1 Pre-heat the oven (4.1) to the desired temperature (see 6.2.3).
6.2.2 Place one test specimen (the reference specimen) in a place where it is protected from light and
kept under standard conditions, according to ISO 2419.
6.2.3 Hang the other test specimen with a clip from, or place it on, the holder (4.3) in the middle of the
oven such that the air has free access to both sides.
Unless specified otherwise, age the specimen under one of the sets of conditions indicated in Table 1.
Table 1 — Ageing by heat
Method Conditions for ageing by heat Recommended use
6A 24 h ± 1 h at 60 °C ± 2 °C General-purpose ageing conditions
Specifically for yellowing of individual products in
6B 24 h ± 1 h at 100 °C ± 2 °C
undyed leather
6C 72 h ± 2 h at 60 °C ± 2 °C Extended general-purpose ageing
6D 72 h ± 2 h at 100 °C ± 2 °C Ageing of automotive leather
6E 168 h ± 2 h at 90 °C ± 2 °C Extended ageing of automotive leather
6F 168 h ± 2 h at 60 °C ± 2 °C Extended ageing at moderate temperature
6G 168 h ± 2 h at 100 °C ± 2 °C Extended ageing at elevated temperature
6H 4 h ± 0,2 h at 100 °C ± 2 °C Short ageing of automotive leather
6J 144 h ± 2 h at 100 °C ± 2 °C Ageing of automotive leather
Extended ageing of automotive leather at
6K 168 h ± 2 h at 120 °C ± 2 °C
high temperature
The sets of conditions given in Table 1 have been selected to provide a range of conditions for different
applications. If other conditions are used, then they shall be clearly noted in the test report.
6.2.4 After the period of time has elapsed, remove the test specimen from the oven. Allow the specimen
to cool. Then, recondition both the test and the reference specimen under standard conditions according
to ISO 2419 f
...
NORME ISO
INTERNATIONALE 17228
IULTCS/IUF 412
Deuxième édition
2015-03-01
Cuir — Essais de solidité des coloris
— Changement de couleur avec
vieillissement accéléré
Leather — Tests for colour fastness — Change in colour with
accelerated ageing
Numéros de référence
IULTCS/IUF 412:2015(F)
©
ISO 2015
IULTCS/IUF 412:2015(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2015
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2015 – Tous droits réservés
IULTCS/IUF 412:2015(F)
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Principe . 1
4 Appareillage . 2
5 Éprouvettes . 2
6 Vieillissement thermique . 2
6.1 Principe . 2
6.2 Mode opératoire . 3
7 Vieillissement thermique avec forte teneur en humidité . 4
7.1 Principe . 4
7.2 Mode opératoire . 4
8 Essais cycliques de variation de la température et de l’humidité . 5
8.1 Principe . 5
8.2 Mode opératoire . 5
9 Rapport d’essai . 7
Annexe A (informative) Commentaires sur les spécificités de la méthode de mesurage de
la couleur . 8
Bibliographie . 9
IULTCS/IUF 412:2015(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne
la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant les
références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de l’élaboration
du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation de
la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’OMC concernant
les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos — Informations
supplémentaires.
L’ISO 17228 a été élaborée par la Commission des essais de solidité de l’Union internationale des sociétés
de techniciens et chimistes du cuir (commission IUF, IULTCS), en collaboration avec le comité technique
du Comité européen de normalisation (CEN) CEN/TC 289, Cuir, dont le secrétariat est tenu par l’UNI,
conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Elle est fondée sur l’IUF 412 publié dans le J. Soc. Leather Tech. Chem., 86, pp. 325-331, 2002, et déclarée
méthode officielle de l’IULTCS en mai 2003.
L’IULTCS est une organisation mondiale de sociétés professionnelles des industries du cuir fondée en
1897 ayant pour mission de favoriser l’avancement des sciences et technologies du cuir. L’IULTCS a trois
commissions, qui sont responsables de l’établissement des méthodes internationales d’échantillonnage
et d’essai des cuirs. L’ISO reconnaît l’IULTCS en tant qu’organisme international à activités normatives
pour l’élaboration de méthodes d’essai relatives au cuir.
Cette deuxième édition annule et remplace la première édition (ISO 17228:2005) qui a fait l’objet d’une
révision technique. Cette nouvelle version est une mise à jour générale des modes opératoires et inclut
des options de vieillissement supplémentaires dans les Tableaux 1, 2 et 3.
L’Annexe A est informative.
iv © ISO 2015 – Tous droits réservés
NORME INTERNATIONALE ISO 17228:2015(F)
Cuir — Essais de solidité des coloris — Changement de
couleur avec vieillissement accéléré
1 Domaine d’application
La présente Norme internationale spécifie des méthodes d’essai de vieillissement ayant pour but de
décrire les dégradations susceptibles de se produire lorsque le cuir est longtemps exposé à un certain
milieu. Au fil du temps, la couleur de surface du cuir et le cuir lui-même s’altèrent en raison de leur
vieillissement et de l’influence du milieu environnant sur le cuir. Les conditions d’essai préconisées
dépendent du type de cuir et de l’usage auquel il est destiné.
Ce mode opératoire peut également être utilisé pour le vieillissement d’échantillons dans le cadre de
l’essai de variations dimensionnelles selon l’ISO 17130.
2 Références normatives
Les documents ci-après, dans leur intégralité ou non, sont des références normatives indispensables
à l’application du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence (y compris les éventuels
amendements) s’applique.
ISO 105-A01, Textiles — Essais de solidité des coloris — Partie A01: Principes généraux pour effectuer les
essais
ISO 105-A02, Textiles — Essais de solidité des teintures — Partie A02: Échelle de gris pour l’évaluation des
dégradations
ISO 105-A03, Textiles — Essais de solidité des teintures — Partie A03: Échelle de gris pour l’évaluation des
dégorgements
ISO 105-A04, Textiles — Essais de solidité des teintures — Partie A04: Méthode instrumentale pour
l’évaluation du degré de dégorgement des tissus témoins
ISO 105-A05, Textiles — Essais de solidité des teintures — Partie A05: Évaluation instrumentale du
changement de couleur pour conversion en degrés de l’échelle de gris
ISO 2418, Cuir — Essais chimiques, physiques, mécaniques et de solidité — Emplacement de l’échantillonnage
ISO 2419, Cuir — Essais physiques et mécaniques — Préparation et conditionnement des échantillons
ISO 17130, Cuir — Essais physiques et mécaniques — Détermination des variations dimensionnelles
3 Principe
Une éprouvette de cuir est exposée à au moins une des trois conditions suivantes:
— chaleur (voir Article 6);
— chaleur et humidité (voir Article 7);
— variations cycliques de la température et de l’humidité (voir Article 8).
Ces essais peuvent être réalisés individuellement ou simultanément. La détérioration de la coloration de
l’éprouvette est évaluée au moyen d’une échelle de gris standard et, le cas échéant, toute altération du
fini ou de l’aspect est consignée.
IULTCS/IUF 412:2015(F)
Ces modes opératoires peuvent également être utilisés afin de préparer l’éprouvette de cuir pour
d’autres essais physiques ou de solidité postérieurs à l’essai de vieillissement accéléré. L’évaluation des
variations dimensionnelles fait l’objet de l’ISO 17130.
NOTE Les essais de vieillissement accéléré sont à usage exclusivement indicatif et ne sont pas nécessairement
représentatifs d’une utilisation sur le long terme, à température ambiante.
Les principes généraux pour les essais de solidité des coloris doivent être conformes à ceux décrits dans
l’ISO 105-A01, en tenant compte du fait que le substrat est du cuir.
4 Appareillage
Utiliser un appareillage courant de laboratoire et:
4.1 Étuve, équipée d’un support central, permettant de maintenir la température définie, à ± 2 °C près.
Il convient d’équiper l’étuve d’un évent, de préférence avec un ventilateur brasseur d’air, et de choisir
comme matériaux de revêtement intérieur de l’étuve des matériaux inertes.
4.2 Enceinte climatique, équipée d’un support central, permettant de maintenir la température
définie, à ± 2 °C près et l’humidité relative définie, à ± 5 % près.
4.3 Dispositif conçu pour supporter les éprouvettes tout en garantissant l’absence de contacts de
celles-ci avec les parois de l’étuve ou de l’enceinte climatique.
4.4 Échelle de gris pour évaluer les changements de couleur, conformément à l’ISO 105-A02, ou
système instrumental pour évaluer les changements de couleur, conformément à l’ISO 105-A05.
4.5 Échelle de gris pour évaluer les dégorgements, conformément à l’ISO 105-A03, ou système
instrumental pour évaluer les dégorgements, conformément à l’ISO 105-A04.
4.6 Chronomètre, précis à 1 s.
5 Éprouvettes
5.1 Avant le découpage des éprouvettes, conditionner la pièce de cuir conformément à l’ISO 2419.
5.2 Découper deux éprouvettes représentatives, mesurant au minimum 100 mm × 100 mm.
Si la pièce de cuir servant à l’essai est une peau entière, les éprouvettes doivent en être prélevées
conformément aux modes opératoires normalisés décrits dans l’ISO 2418.
NOTE Si d’autres propriétés, comme les variations dimensionnelles, sont à mesurer, utiliser des éprouvettes
supplémentaires car les conditions de stockage pendant l’étape de vieillissement sont différentes.
6 Vieillissement thermique
6.1 Principe
Ce mode opératoire a pour but de simuler un vieillissement du cuir en l’exposant à la chaleur. Deux types
d’altération sont susceptibles de se produire:
a) un changement de couleur des composants du cuir;
b) l’évaporation de composants volatils ou la migration de composants, entraînant une altération de la
couleur et/ou d’autres propriétés du cuir ou du fini de surface.
2 © ISO 2015 – Tous droits réservés
IULTCS/IUF 412:2015(F)
La durée d’exposition et la température pouvant varier, ce mode opératoire peut servir à des fins
multiples, par exemple pour la préparation des éprouvettes destinées à d’autres essais.
6.2 Mode opératoire
6.2.1 Préchauffer l’étuve (4.1) jusqu’à atteindre la température souhaitée (voir 6.2.3).
6.2.2 Conserver une éprouvette d’essai (l’éprouvette de référence) à l’abri de la lumière et dans des
conditions normalisées selon l’ISO 2419.
6.2.3 Accrocher l’autre éprouvette à une attache du dispositif porte-éprouvette (4.3), ou la poser sur ce
dernier, au m
...
NORME ISO
INTERNATIONALE 17228
IULTCS/IUF 412
Deuxième édition
2015-03-01
Cuir — Essais de solidité des coloris
— Changement de couleur avec
vieillissement accéléré
Leather — Tests for colour fastness — Change in colour with
accelerated ageing
Numéros de référence
IULTCS/IUF 412:2015(F)
©
ISO 2015
IULTCS/IUF 412:2015(F)
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2015
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.org
Web www.iso.org
Publié en Suisse
ii © ISO 2015 – Tous droits réservés
IULTCS/IUF 412:2015(F)
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Principe . 1
4 Appareillage . 2
5 Éprouvettes . 2
6 Vieillissement thermique . 2
6.1 Principe . 2
6.2 Mode opératoire . 3
7 Vieillissement thermique avec forte teneur en humidité . 4
7.1 Principe . 4
7.2 Mode opératoire . 4
8 Essais cycliques de variation de la température et de l’humidité . 5
8.1 Principe . 5
8.2 Mode opératoire . 5
9 Rapport d’essai . 7
Annexe A (informative) Commentaires sur les spécificités de la méthode de mesurage de
la couleur . 8
Bibliographie . 9
IULTCS/IUF 412:2015(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui concerne
la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www.
iso.org/directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant les
références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de l’élaboration
du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par
l’ISO (voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la signification des termes et expressions spécifiques de l’ISO liés à l’évaluation de
la conformité, ou pour toute information au sujet de l’adhésion de l’ISO aux principes de l’OMC concernant
les obstacles techniques au commerce (OTC), voir le lien suivant: Avant-propos — Informations
supplémentaires.
L’ISO 17228 a été élaborée par la Commission des essais de solidité de l’Union internationale des sociétés
de techniciens et chimistes du cuir (commission IUF, IULTCS), en collaboration avec le comité technique
du Comité européen de normalisation (CEN) CEN/TC 289, Cuir, dont le secrétariat est tenu par l’UNI,
conformément à l’Accord de coopération technique entre l’ISO et le CEN (Accord de Vienne).
Elle est fondée sur l’IUF 412 publié dans le J. Soc. Leather Tech. Chem., 86, pp. 325-331, 2002, et déclarée
méthode officielle de l’IULTCS en mai 2003.
L’IULTCS est une organisation mondiale de sociétés professionnelles des industries du cuir fondée en
1897 ayant pour mission de favoriser l’avancement des sciences et technologies du cuir. L’IULTCS a trois
commissions, qui sont responsables de l’établissement des méthodes internationales d’échantillonnage
et d’essai des cuirs. L’ISO reconnaît l’IULTCS en tant qu’organisme international à activités normatives
pour l’élaboration de méthodes d’essai relatives au cuir.
Cette deuxième édition annule et remplace la première édition (ISO 17228:2005) qui a fait l’objet d’une
révision technique. Cette nouvelle version est une mise à jour générale des modes opératoires et inclut
des options de vieillissement supplémentaires dans les Tableaux 1, 2 et 3.
L’Annexe A est informative.
iv © ISO 2015 – Tous droits réservés
NORME INTERNATIONALE ISO 17228:2015(F)
Cuir — Essais de solidité des coloris — Changement de
couleur avec vieillissement accéléré
1 Domaine d’application
La présente Norme internationale spécifie des méthodes d’essai de vieillissement ayant pour but de
décrire les dégradations susceptibles de se produire lorsque le cuir est longtemps exposé à un certain
milieu. Au fil du temps, la couleur de surface du cuir et le cuir lui-même s’altèrent en raison de leur
vieillissement et de l’influence du milieu environnant sur le cuir. Les conditions d’essai préconisées
dépendent du type de cuir et de l’usage auquel il est destiné.
Ce mode opératoire peut également être utilisé pour le vieillissement d’échantillons dans le cadre de
l’essai de variations dimensionnelles selon l’ISO 17130.
2 Références normatives
Les documents ci-après, dans leur intégralité ou non, sont des références normatives indispensables
à l’application du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence (y compris les éventuels
amendements) s’applique.
ISO 105-A01, Textiles — Essais de solidité des coloris — Partie A01: Principes généraux pour effectuer les
essais
ISO 105-A02, Textiles — Essais de solidité des teintures — Partie A02: Échelle de gris pour l’évaluation des
dégradations
ISO 105-A03, Textiles — Essais de solidité des teintures — Partie A03: Échelle de gris pour l’évaluation des
dégorgements
ISO 105-A04, Textiles — Essais de solidité des teintures — Partie A04: Méthode instrumentale pour
l’évaluation du degré de dégorgement des tissus témoins
ISO 105-A05, Textiles — Essais de solidité des teintures — Partie A05: Évaluation instrumentale du
changement de couleur pour conversion en degrés de l’échelle de gris
ISO 2418, Cuir — Essais chimiques, physiques, mécaniques et de solidité — Emplacement de l’échantillonnage
ISO 2419, Cuir — Essais physiques et mécaniques — Préparation et conditionnement des échantillons
ISO 17130, Cuir — Essais physiques et mécaniques — Détermination des variations dimensionnelles
3 Principe
Une éprouvette de cuir est exposée à au moins une des trois conditions suivantes:
— chaleur (voir Article 6);
— chaleur et humidité (voir Article 7);
— variations cycliques de la température et de l’humidité (voir Article 8).
Ces essais peuvent être réalisés individuellement ou simultanément. La détérioration de la coloration de
l’éprouvette est évaluée au moyen d’une échelle de gris standard et, le cas échéant, toute altération du
fini ou de l’aspect est consignée.
IULTCS/IUF 412:2015(F)
Ces modes opératoires peuvent également être utilisés afin de préparer l’éprouvette de cuir pour
d’autres essais physiques ou de solidité postérieurs à l’essai de vieillissement accéléré. L’évaluation des
variations dimensionnelles fait l’objet de l’ISO 17130.
NOTE Les essais de vieillissement accéléré sont à usage exclusivement indicatif et ne sont pas nécessairement
représentatifs d’une utilisation sur le long terme, à température ambiante.
Les principes généraux pour les essais de solidité des coloris doivent être conformes à ceux décrits dans
l’ISO 105-A01, en tenant compte du fait que le substrat est du cuir.
4 Appareillage
Utiliser un appareillage courant de laboratoire et:
4.1 Étuve, équipée d’un support central, permettant de maintenir la température définie, à ± 2 °C près.
Il convient d’équiper l’étuve d’un évent, de préférence avec un ventilateur brasseur d’air, et de choisir
comme matériaux de revêtement intérieur de l’étuve des matériaux inertes.
4.2 Enceinte climatique, équipée d’un support central, permettant de maintenir la température
définie, à ± 2 °C près et l’humidité relative définie, à ± 5 % près.
4.3 Dispositif conçu pour supporter les éprouvettes tout en garantissant l’absence de contacts de
celles-ci avec les parois de l’étuve ou de l’enceinte climatique.
4.4 Échelle de gris pour évaluer les changements de couleur, conformément à l’ISO 105-A02, ou
système instrumental pour évaluer les changements de couleur, conformément à l’ISO 105-A05.
4.5 Échelle de gris pour évaluer les dégorgements, conformément à l’ISO 105-A03, ou système
instrumental pour évaluer les dégorgements, conformément à l’ISO 105-A04.
4.6 Chronomètre, précis à 1 s.
5 Éprouvettes
5.1 Avant le découpage des éprouvettes, conditionner la pièce de cuir conformément à l’ISO 2419.
5.2 Découper deux éprouvettes représentatives, mesurant au minimum 100 mm × 100 mm.
Si la pièce de cuir servant à l’essai est une peau entière, les éprouvettes doivent en être prélevées
conformément aux modes opératoires normalisés décrits dans l’ISO 2418.
NOTE Si d’autres propriétés, comme les variations dimensionnelles, sont à mesurer, utiliser des éprouvettes
supplémentaires car les conditions de stockage pendant l’étape de vieillissement sont différentes.
6 Vieillissement thermique
6.1 Principe
Ce mode opératoire a pour but de simuler un vieillissement du cuir en l’exposant à la chaleur. Deux types
d’altération sont susceptibles de se produire:
a) un changement de couleur des composants du cuir;
b) l’évaporation de composants volatils ou la migration de composants, entraînant une altération de la
couleur et/ou d’autres propriétés du cuir ou du fini de surface.
2 © ISO 2015 – Tous droits réservés
IULTCS/IUF 412:2015(F)
La durée d’exposition et la température pouvant varier, ce mode opératoire peut servir à des fins
multiples, par exemple pour la préparation des éprouvettes destinées à d’autres essais.
6.2 Mode opératoire
6.2.1 Préchauffer l’étuve (4.1) jusqu’à atteindre la température souhaitée (voir 6.2.3).
6.2.2 Conserver une éprouvette d’essai (l’éprouvette de référence) à l’abri de la lumière et dans des
conditions normalisées selon l’ISO 2419.
6.2.3 Accrocher l’autre éprouvette à une attache du dispositif porte-éprouvette (4.3), ou la poser sur ce
dernier, au m
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.