ISO 11431:2025
(Main)Building and civil engineering sealants — Determination of adhesion and cohesion properties of sealants after exposure to heat, water and artificial light through glass
Building and civil engineering sealants — Determination of adhesion and cohesion properties of sealants after exposure to heat, water and artificial light through glass
This document specifies a method for the determination of the adhesion and cohesion properties of sealants after cyclic exposure to heat and artificial light followed by a period of exposure to water at a defined temperature.
Mastics pour le bâtiment et le génie civil — Détermination des propriétés d'adhésivité et de cohésion des mastics après exposition à la chaleur, à l'eau et à la lumière artificielle à travers le verre
Le présent document prescrit une méthode de détermination des propriétés d’adhésivité et de cohésion des mastics soumis à un certain nombre de cycles d’exposition à la chaleur et à la lumière artificielle, suivis d’une exposition à l’eau à une température élevée.
General Information
Relations
Buy Standard
Standards Content (Sample)
International
Standard
ISO 11431
Third edition
Building and civil engineering
2025-08
sealants — Determination of
adhesion and cohesion properties of
sealants after exposure to heat, water
and artificial light through glass
Mastics pour le bâtiment et le génie civil — Détermination
des propriétés d'adhésivité et de cohésion des mastics après
exposition à la chaleur, à l'eau et à la lumière artificielle à travers
le verre
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 Glass supports .2
5.2 Spacers .2
5.3 Anti-adherent substrate .3
5.4 Ventilated convection-type oven .3
5.5 Container .3
5.6 Test chamber with an artificial light source .3
5.7 Artificial light source with suitable filters .3
5.8 Black standard thermometer .3
5.9 Extension machine .4
5.10 Separators . .4
5.11 Measuring device .4
6 Preparation of specimens . 4
7 Conditioning . 4
7.1 General .4
7.2 Method A .4
7.3 Method B .4
8 Test procedures . 5
8.1 General .5
8.2 Exposure conditions .5
8.2.1 General .5
8.2.2 Automatic cycling .5
8.2.3 Manual cycling .5
8.3 Elongation of the specimens.5
9 Test report . 6
iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 59, Buildings and civil engineering works,
Subcommittee SC 8, Sealants,in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/BT Technical Board, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 11431:2002), which has been technically
revised.
The main changes are as follows:
— the title has been revised from Building construction — Jointing products — Determination of adhesion/
cohesion properties of sealants after exposure to heat, water and artificial light through glass;
— normative references have been updated;
— a normative reference to ISO 4892-2 has been added in 5.6;
— 5.7 has been revised;
— in 5.8, the subclause of referenced document has been revised and the preferred device for measuring
the maximum surface temperature has been added;
— the tolerance for relative humidity has been revised in 7.2 and 8.3.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
International Standard ISO 11431:2025(en)
Building and civil engineering sealants — Determination of
adhesion and cohesion properties of sealants after exposure
to heat, water and artificial light through glass
1 Scope
This document specifies a method for the determination of the adhesion and cohesion properties of sealants
after cyclic exposure to heat and artificial light followed by a period of exposure to water at a defined
temperature.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 4892-1, Plastics — Methods of exposure to laboratory light sources — Part 1: General guidance and
requirements
ISO 4892-2:2013, Plastics — Methods of exposure to laboratory light sources — Part 2: Xenon-arc lamps
ISO 6927, Building and civil engineering sealants — Vocabulary
ISO 13640, Building and civil engineering sealants — Specifications for test substrates
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6927 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Principle
Specimens are prepared in which the sealant to be tested adheres to two parallel glass surfaces. After
submitting the specimens to a cyclic exposure to artificial light at elevated temperature and to water, the
specimens are extended to a defined width. After maintenance of the extension for a defined time, the
specimens are examined for evidence of loss of adhesion or cohesion.
NOTE The cyclic exposure of the test specimens to water and to radiation and heat is meant to simulate the
exposure of sealants in service to natural weather conditions. The acceleration factor in comparison with the real
situation is unknown. The intention is not to receive durability data for the sealants under evaluation but to ensure a
minimum performance in glazing applications.
5 Apparatus
5.1 Glass supports
Glass supports shall be used for the preparation of the specimens.
The glass supports shall be as defined in ISO 13640. For each test specimen, two glass supports shall be used
with a cross-section of dimensions as shown in Figure 1. Test substrates of other dimensions may be used,
but the dimensions of the sealant bead, the thickness of the glass and the area of adhesion shall be the same
as those shown in Figure 1.
5.2 Spacers
Spacers of cross-section with anti-adherent surface, e.g. by a thin wax coating or a polyethylene film shall be
used for the preparation of the specimens. The dimensions of spacers are 12 mm ⨯ 12 mm ⨯ 12,5 mm (see
Figure 1).
Dimensions in millimetres
Key
1 light
2 glass supports
3 spacers
4 sealant
Figure 1 — Assembly and dimensions of a specimen and direction of light exposure
5.3 Anti-adherent substrate
An anti-adherent substrate, such as a polyethylene (PE) film, shall be used for preparation of the test
specimens and should be according to the advice of the sealant manufacturer.
5.
...
Norme
internationale
ISO 11431
Troisième édition
Mastics pour le bâtiment et le
2025-08
génie civil — Détermination
des propriétés d'adhésivité et
de cohésion des mastics après
exposition à la chaleur, à l'eau et à la
lumière artificielle à travers le verre
Building and civil engineering sealants — Determination of
adhesion and cohesion properties of sealants after exposure to
heat, water and artificial light through glass
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 1
5 Appareillage . 2
5.1 Supports en verre .2
5.2 Espaceurs .2
5.3 Support anti-adhérent .3
5.4 Étuve ventilée à convection .3
5.5 Récipient . .3
5.6 Enceinte d'essai avec une source de lumière artificielle .3
5.7 Source de lumière artificielle avec filtres appropriés .3
5.8 Capteur de température noir .3
5.9 Appareil d’extension .4
5.10 Écarteurs .4
5.11 Dispositif de mesure .4
6 Préparation des éprouvettes . 4
7 Conditionnement . 4
7.1 Généralités .4
7.2 Méthode A .4
7.3 Méthode B .4
8 Mode opératoire . 5
8.1 Généralités .5
8.2 Conditions d'exposition .5
8.2.1 Généralités .5
8.2.2 Cycle automatique .5
8.2.3 Cycle manuel .5
8.3 Allongement des éprouvettes .5
9 Rapport d'essai . 6
iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/patents. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/iso/foreword.html.
Le présent document a été élaboré par le comité technique ISO/TC 59, Bâtiments et ouvrages de génie civil,
sous-comité SC 8, Mastics, en collaboration avec le Comité Technique et le Bureau Technique CEN/BT du
Comité Européen de Normalisation (CEN), conformément à l’Accord de coopération technique entre l’ISO et
le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 11431:2002) qui a fait l'objet d'une
révision technique.
Les principales modifications sont les suivantes:
— le titre a été modifié: Construction immobilière - Produits pour joints - Détermination des propriétés d'adhésion/
cohésion des mastics après exposition à la chaleur, à l'eau et à la lumière artificielle à travers le verre;
— mise à jour des références normatives;
— ajout d'une référence normative ISO 4892-2 au 5.6;
— révision du 5.7;
— révision d’un paragraphe du document de référence et ajout du dispositif préféré pour mesure la
température maximale de surface au 5.8;
— révision de la tolérance pour l'humidité relative au 7.2 et 8.3.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html
iv
Norme internationale ISO 11431:2025(fr)
Mastics pour le bâtiment et le génie civil — Détermination
des propriétés d'adhésivité et de cohésion des mastics après
exposition à la chaleur, à l'eau et à la lumière artificielle à
travers le verre
1 Domaine d’application
Le présent document prescrit une méthode de détermination des propriétés d’adhésivité et de cohésion des
mastics soumis à un certain nombre de cycles d’exposition à la chaleur et à la lumière artificielle, suivis
d’une exposition à l’eau à une température élevée.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 4892-1, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 1: Lignes
directrices générales et exigences
ISO 4892-2:2013, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 2:
Lampes à arc au xénon
ISO 6927, Mastics pour le bâtiment et le génie civil — Vocabulaire
ISO 13640, Mastics pour le bâtiment et le génie civil — Prescriptions relatives aux supports d’essais
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions donnés dans l'ISO 6927 s'appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en normalisation,
consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
4 Principe
Des éprouvettes sont préparées dans lesquelles le mastic à examiner adhère à deux surfaces de contact
parallèles. Après avoir soumis les éprouvettes à un cycle d'exposition à la lumière artificielle, à température
élevée et à l'eau, les éprouvettes sont mises en extension à une largeur définie. Après les avoir maintenues
sous traction pendant un temps donné, les éprouvettes sont examinées afin de détecter toute perte
d'adhérence ou de cohésion.
NOTE L’exposition cyclique à l’eau, au rayonnement lumineux et à la chaleur des éprouvettes a pour objet de
simuler l’exposition à des conditions climatiques naturelles des mastics utilisés dans la construction immobilière. Le
facteur d’accélération comparé à la situation réelle est inconnu. Cet essai a pour objectif de garantir les performances
minimales du mastic dans les applications de pose de vitres, et non de recueillir des données relatives à sa durabilité.
5 Appareillage
5.1 Supports en verre
Les supports en verre doivent être utilisés pour la préparation des éprouvettes.
Les supports en verre doivent être tels que définis selon l’ISO 13640. Pour chaque éprouvette, deux supports
en verre doivent être utilisés avec les dimensions indiquées selon la Figure 1. Des supports d'essais d'autres
dimensions peuvent être
...
FINAL DRAFT
International
Standard
ISO/FDIS 11431
ISO/TC 59/SC 8
Building and civil engineering
Secretariat: SAC
sealants — Determination of
Voting begins on:
adhesion and cohesion properties
2025-06-09
of sealants after exposure to heat,
Voting terminates on:
water and artificial light through
2025-08-04
glass
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/FDIS 11431:2025(en) © ISO 2025
FINAL DRAFT
ISO/FDIS 11431:2025(en)
International
Standard
ISO/FDIS 11431
ISO/TC 59/SC 8
Building and civil engineering
Secretariat: SAC
sealants — Determination of
Voting begins on:
adhesion and cohesion properties of
sealants after exposure to heat, water
Voting terminates on:
and artificial light through glass
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: +41 22 749 01 11
Email: copyright@iso.org
Website: www.iso.org
Published in Switzerland Reference number
ISO/FDIS 11431:2025(en) © ISO 2025
ii
ISO/FDIS 11431:2025(en)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 Glass supports .2
5.2 Spacers .2
5.3 Anti-adherent substrate .3
5.4 Ventilated convection-type oven .3
5.5 Container .3
5.6 Test chamber with an artificial light source .3
5.7 Artificial light source with suitable filters .3
5.8 Black standard thermometer .3
5.9 Extension machine .4
5.10 Separators . .4
5.11 Measuring device .4
6 Preparation of specimens . 4
7 Conditioning . 4
7.1 General .4
7.2 Method A .4
7.3 Method B .4
8 Test procedures . 5
8.1 General .5
8.2 Exposure conditions .5
8.2.1 General .5
8.2.2 Automatic cycling .5
8.2.3 Manual cycling .5
8.3 Elongation of the specimens.5
9 Test report . 6
iii
ISO/FDIS 11431:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 59, Buildings and civil engineering works,
Subcommittee SC 8, Sealants,in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/BT Technical Board, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 11431:2002), which has been technically
revised.
The main changes are as follows:
— the title has been revised from Building construction — Jointing products — Determination of adhesion/
cohesion properties of sealants after exposure to heat, water and artificial light through glass;
— normative references have been updated;
— a normative reference to ISO 4892-2 has been added in 5.6;
— 5.7 has been revised;
— in 5.8, the subclause of referenced document has been revised and the preferred device for measuring
the maximum surface temperature has been added;
— the tolerance for relative humidity has been revised in 7.2 and 8.3.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
FINAL DRAFT International Standard ISO/FDIS 11431:2025(en)
Building and civil engineering sealants — Determination of
adhesion and cohesion properties of sealants after exposure
to heat, water and artificial light through glass
1 Scope
This document specifies a method for the determination of the adhesion and cohesion properties of sealants
after cyclic exposure to heat and artificial light followed by a period of exposure to water at a defined
temperature.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 4892-1, Plastics — Methods of exposure to laboratory light sources — Part 1: General guidance and
requirements
ISO 4892-2:2013, Plastics — Methods of exposure to laboratory light sources — Part 2: Xenon-arc lamps
ISO 6927, Building and civil engineering sealants — Vocabulary
ISO 13640, Building and civil engineering sealants — Specifications for test substrates
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6927 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
4 Principle
Specimens are prepared in which the sealant to be tested adheres to two parallel glass surfaces. After
submitting the specimens to a cyclic exposure to artificial light at elevated temperature and to water, the
specimens are extended to a defined width. After maintenance of the extension for a defined time, the
specimens are examined for evidence of loss of adhesion or cohesion.
NOTE The cyclic exposure of the test specimens to water and to radiation and heat is meant to simulate the
exposure of sealants in service to natural weather conditions. The acceleration factor in comparison with the real
situation is unknown. The intention is not to receive durability data for the sealants under evaluation but to ensure a
minimum performance in glazing application
...
2025-4-3
ISO/FDIS 11431:2024(en)
ISO/TC 59/SC 8/WG 1
Secretariat: SAC
Date: 2025-05-23
Building and civil engineering sealants — Determination of adhesion
and cohesion properties of sealants after exposure to heat, water and
artificial light through glass
FDIS stage
ISO/FDIS 11431:202X(E2025(en)
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication
may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying,
or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO
at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
EmailE-mail: copyright@iso.org
Website: www.iso.org
Published in Switzerland
ii
ISO/FDIS 11431:20242025(en)
Contents
Foreword . iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 1
5.1 Glass supports . 1
5.2 Spacers . 2
5.3 Anti-adherent substrate . 4
5.4 Ventilated convection-type oven . 4
5.5 Container . 4
5.6 Test chamber with an artificial light source . 5
5.7 Artificial light source with suitable filters . 5
5.8 Black standard thermometer . 5
5.9 Extension machine . 5
5.10 Separators . 5
5.11 Measuring device . 5
6 Preparation of specimens . 6
7 Conditioning . 6
7.1 General . 6
7.2 Method A . 6
7.3 Method B . 6
8 Test procedures . 7
8.1 General . 7
8.2 Exposure conditions . 7
8.3 Elongation of the specimens . 7
9 Test report . 8
iii
ISO/FDIS 11431:202X(E2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO documents should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s)
which may be required to implement this document. However, implementers are cautioned that this may not
represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 59, Buildings and civil engineering works,
Subcommittee SC 8, Sealants.,in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/BT Technical Board, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 11431:2002), which has been technically
revised.
The main changes are as follows:
— — the title has been revised from Building construction — Jointing products — Determination of
adhesion/cohesion properties of sealants after exposure to heat, water and artificial light through glass;
— — normative references have been updated;
— — a normative reference to ISO 4892-2 has been added in 5.65.6;;
— 5.7— 5.7 has been revised;
— — in 5.85.8,, the subclause of referenced document has been revised and the preferred device for
measuring the maximum surface temperature has been added;
— — the tolerance for relative humidity has been revised in 7.27.2 and 8.38.3.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
ISO/FDIS 11431:20242025(en)
Building and civil engineering sealants — Determination of adhesion
and cohesion properties of sealants after exposure to heat, water and
artificial light through glass
1 Scope
This document specifies a method for the determination of the adhesion and cohesion properties of sealants
after cyclic exposure to heat and artificial light followed by a period of exposure to water at a defined
temperature.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 4892--1, Plastics — Methods of exposure to laboratory light sources— — Part 1: General guidance and
requirements
ISO 4892--2:2013, Plastics — Methods of exposure to laboratory light sources — Part 2: Xenon-arc lamps
ISO 6927, Building and civil engineering sealants — Vocabulary
ISO 13640, Building and civil engineering sealants — Specifications for test substrates
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 6927 apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— — ISO Online browsing platform: available at https://www.iso.org/obp
— — IEC Electropedia: available at https://www.electropedia.org/
4 Principle
Specimens are prepared in which the sealant to be tested adheres to two parallel glass surfaces. After
submitting the specimens to a cyclic exposure to artificial light at elevated temperature and to water, the
specimens are extended to a defined width. After maintenance of the extension for a defined time, the
specimens are examined for evidence of loss of adhesion or cohesion.
NOTE The cyclic exposure of the test specimens to water and to radiation and heat is meant to simulate the exposure
of sealants in service to natural weather conditions. The acceleration factor in comparison with the real situation is
unknown. The intention is not to receive durability data for the sealants under evaluation but to ensure a minimum
performance in glazing applications.
5 Apparatus
5.1 Glass supports
Glass supports shall be used for the preparation of the specimens.
ISO/FDIS 11431:202X(E2025(en)
The glass supports shall be as defined in ISO 13640. For each test specimen, two glass supports shall be used
with a cross-section of dimensions as shown in Figure 1Figure 1. Test substrates of other dimensions may be
used, but the dimensions of the sealant bead, the thickness of the glass and the area of adhesion shall be the
same as those shown in Figure 1Figure 1.
5.2 Spacers
Spacers of cross-section with anti-adherent surface, e.g. by a thin wax coating or a polyethylene film shall be
used for the preparation of the specimens. The dimensions of spacers are 12 mm ⨯ 12 mm ⨯ 12.,5 mm (see
Figure 1figure 1).).
ISO/FDIS 11431:20242025(en)
Dimensions in millimetres
ISO/FDIS 11431:202X(E2025(en)
Key
1 light
2 glass supports
3 spacers
4 sealant
Figure 1 — Assembly and dimensions of a specimen and direction of light exposure
5.3 Anti-adherent substrate
An anti-adherent substrate, such as a polyethylene (PE) film, shall be used for preparation of the test
specimens and should be according to the advice of the sealant manufacturer.
5.4 Ventilated convection-type oven
The ventilated convection-type oven shall be maintained at (70 ± 2) °C for conditioning according to 7.3in
accordance with 7.3 method B.
5.5 Container
The specimens shall be immersed in a container with demineralized or distilled water, according to 7.3 in
accordance with 7.3 method B.
ISO/FDIS 11431:20242025(en)
5.6 Test chamber with an artificial light source
The test chamber shall be capable of exposure of the test specimens to radiation under dry conditions at a
defined temperature, which is measured on a black standard thermometer. The description of an artificial
light source shall be as defined in 5.75.7.
The test chamber shall be sufficiently ventilated to maintain the test temperature in the dry phase. The
radiation is directed to the surface of one of the glass substrates (see Figure 1Figure 1).).
If fully automated equipment is used, the exposure to water is accomplished in the same test chamber. This
can be done either by immersion or by water spray. Demineralized water shall be used.
The equipment and test procedures for cyclic exposures with intermittent water spray shall be in accordance
with ISO 4892-1 and ISO 4892-2. If exposure to water is done outside the test chamber in a device where the
test specimens are transferred manually, they shall be immersed in demineralized water at a defined
temperature.
Contamination of the water for immersion or spray by-products leached out from the sealants shall be
avoided. Sealants of different chemical type should be tested separately; and fresh water should be used. If the
water must be recycled because of high consumption (e.g. in spraying), a sufficient exchange with clean water
shall be maintained.
5.7 Artificial light source with suitable filters
The spectral range and distribution of the artificial light source shall conform to the
...
PROJET FINAL
Norme
internationale
ISO/FDIS 11431
ISO/TC 59/SC 8
Mastics pour le bâtiment et le
Secrétariat: SAC
génie civil — Détermination
Début de vote:
des propriétés d'adhésivité et
2025-06-09
de cohésion des mastics après
Vote clos le:
exposition à la chaleur, à l'eau et à la
2025-08-04
lumière artificielle à travers le verre
Building and civil engineering sealants — Determination of
adhesion and cohesion properties of sealants after exposure to
heat, water and artificial light through glass
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
ISO/FDIS 11431:2025(fr) © ISO 2025
PROJET FINAL
ISO/FDIS 11431:2025(fr)
Norme
internationale
ISO/FDIS 11431
ISO/TC 59/SC 8
Mastics pour le bâtiment et le
Secrétariat: SAC
génie civil — Détermination
Début de vote:
des propriétés d'adhésivité et
2025-06-09
de cohésion des mastics après
Vote clos le:
exposition à la chaleur, à l'eau et à la
2025-08-04
lumière artificielle à travers le verre
Building and civil engineering sealants — Determination of
adhesion and cohesion properties of sealants after exposure to
heat, water and artificial light through glass
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: +41 22 749 01 11
E-mail: copyright@iso.org
Web: www.iso.org
Publié en Suisse Numéro de référence
ISO/FDIS 11431:2025(fr) © ISO 2025
ii
ISO/FDIS 11431:2025(fr)
Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 1
5 Appareillage . 2
5.1 Supports en verre .2
5.2 Espaceurs .2
5.3 Support anti-adhérent .3
5.4 Étuve ventilée à convection .3
5.5 Récipient . .3
5.6 Enceinte d'essai avec une source de lumière artificielle .3
5.7 Source de lumière artificielle avec filtres appropriés .3
5.8 Capteur de température noir .3
5.9 Appareil d’extension .4
5.10 Écarteurs .4
5.11 Dispositif de mesure .4
6 Préparation des éprouvettes . 4
7 Conditionnement . 4
7.1 Généralités .4
7.2 Méthode A .4
7.3 Méthode B .4
8 Mode opératoire . 5
8.1 Généralités .5
8.2 Conditions d'exposition .5
8.2.1 Généralités .5
8.2.2 Cycle automatique .5
8.2.3 Cycle manuel .5
8.3 Allongement des éprouvettes .5
9 Rapport d'essai . 6
iii
ISO/FDIS 11431:2025(fr)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de propriété revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/patents. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de propriété.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l'ISO liés à l'évaluation de la conformité, ou pour toute information au sujet de l'adhésion de
l'ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/iso/foreword.html.
Le présent document a été élaboré par le comité technique ISO/TC 59, Bâtiments et ouvrages de génie civil,
sous-comité SC 8, Mastics, en collaboration avec le Comité Technique et le Bureau Technique CEN/BT du
Comité Européen de Normalisation (CEN), conformément à l’Accord de coopération technique entre l’ISO et
le CEN (Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 11431:2002) qui a fait l'objet d'une
révision technique.
Les principales modifications sont les suivantes:
— le titre a été modifié: Construction immobilière - Produits pour joints - Détermination des propriétés d'adhésion/
cohésion des mastics après exposition à la chaleur, à l'eau et à la lumière artificielle à travers le verre;
— mise à jour des références normatives;
— ajout d'une référence normative ISO 4892-2 au 5.6;
— révision du 5.7;
— révision d’un paragraphe du document de référence et ajout du dispositif préféré pour mesure la
température maximale de surface au 5.8;
— révision de la tolérance pour l'humidité relative au 7.2 et 8.3.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html
iv
PROJET FINAL Norme internationale ISO/FDIS 11431:2025(fr)
Mastics pour le bâtiment et le génie civil — Détermination
des propriétés d'adhésivité et de cohésion des mastics après
exposition à la chaleur, à l'eau et à la lumière artificielle à
travers le verre
1 Domaine d’application
Le présent document prescrit une méthode de détermination des propriétés d’adhésivité et de cohésion des
mastics soumis à un certain nombre de cycles d’exposition à la chaleur et à la lumière artificielle, suivis
d’une exposition à l’eau à une température élevée.
2 Références normatives
Les documents suivants sont cités dans le texte de sorte qu’ils constituent, pour tout ou partie de leur
contenu, des exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour
les références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 4892-1, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 1: Lignes
directrices générales et exigences
ISO 4892-2:2013, Plastiques — Méthodes d'exposition à des sources lumineuses de laboratoire — Partie 2:
Lampes à arc au xénon
ISO 6927, Mastics pour le bâtiment et le génie civil — Vocabulaire
ISO 13640, Mastics pour le bâ
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.