SIST ISO 1110:1996

Plastics -- Polyamides -- Accelerated conditioning of test specimens

The method described is based on storing the test specimens in an atmosphere of (70 ± 1) °C and (62 ± 1) % relative humidity (psychrometric temperature difference of (10 ± 0,3) °C), until moisture absorption by the specimen has reached at least 95 % of its equilibrium level. It is applicable to polyamides and copolyamides in grades containing fillers and other additives, but not to grades containing more than 2 % (m/m) extractables. The equilibrium moisture content attained is close to the equilibrium moisture content obtained in standard atmosphere 23/50.

Plastiques -- Polyamides -- Conditionnement accéléré d'éprouvettes

La présente Norme internationale prescrit une méthode pour le conditionnement accéléré d'éprouvettes des polyamides et copolyamides. La méthode peut aussi être appliquée aux qualités contenant des charges et autres additifs, mais pas aux qualités contenant plus de 2 % (m/m) de matières extractibles. Le taux d'humidité d'équilibre atteint par cette méthode correspond à peu près au taux d'humidité d'équilibre obtenu dans l'atmosphère normale 23/50. Les valeurs de propriétés mécaniques obtenues après conditionnement accéléré selon cette méthode peuvent différer légèrement de celles obtenues après conditionnement dans l'atmosphère normale 23/50.

Polimerni materiali - Poliamidi - Pospešeno kondicioniranje preskušancev

General Information

• Status: Withdrawn
• Publication Date: 31-May-1996
• Withdrawal Date: 06-Mar-2023
• ICS: 83.080.20 - Thermoplastic materials
• Technical Committee: IPMA - Polimer materials and products
• Current Stage: 9900 - Withdrawal (Adopted Project)
• Start Date: 07-Mar-2023
• Due Date: 30-Mar-2023
• Completion Date: 07-Mar-2023
• Ref Project: ISO 1110:1995 - Plastics — Polyamides — Accelerated conditioning of test specimens

Relations

• Revised: ISO 1110:1987 - Plastics — Polyamides — Accelerated conditioning of test specimens
• Effective Date: 12-May-2008
• Revised: SIST ISO 1110:2023 - Plastics - Polyamides - Accelerated conditioning of test specimens
• Effective Date: 07-Jul-2018

Standards Content (Sample)

SLOVENSKI STANDARD
SIST ISO 1110:1996
01-junij-1996
Polimerni materiali - Poliamidi - Pospešeno kondicioniranje preskušancev
Plastics -- Polyamides -- Accelerated conditioning of test specimens
Plastiques -- Polyamides -- Conditionnement accéléré d'éprouvettes
Ta slovenski standard je istoveten z: ISO 1110:1995
ICS:
83.080.20 Plastomeri Thermoplastic materials
SIST ISO 1110:1996 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST ISO 1110:1996

---------------------- Page: 2 ----------------------

SIST ISO 1110:1996
INTERNATIONAL ISO
1110
STANDARD
Third edition
1995-02-01
- Polyamides - Accelerated
Plastics
conditioning of test specimens
- Polyamides - Conditionnemen t accMr6 d ‘eprouve ttes
Plas tiques
Reference number
ISO 11 IO:1 995(E)

---------------------- Page: 3 ----------------------

SIST ISO 1110:1996
ISO 1110:1995(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide
federation of national Standards bodies (ISO member bodies). The work
of preparing International Standards is normally carried out through ISO
technical committees. Esch member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(1 EC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard ISO 1110 was prepared by Technical Committee
lSO/lC 61, Plastics, Subcommittee SC 9, Thermoplastic materials.
This third edition cancels and replaces the second edition
(ISO 11 IO:1 987), which has been technically revised.
0 ISO 1995
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronie or mechanical, including photocopying and
microfilm, without Permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-l 211 Geneve 20 l Switzerland
Printed in Switzerland

---------------------- Page: 4 ----------------------

SIST ISO 1110:1996
Q ISO
ISO 1110:1995(E)
Introduction
Various properties of polyamides (PA) depend upon their moisture content.
Reproducible values of these properties tan only be obtained with speci-
mens having a specified moisture content. Such specimens are obtained
by conditioning, i.e. by allowing them to resch equilibrium in an atmos-
phere with a specified temperature and relative humidity.
The rate of moisture absorption and, therefore, the rate of conditioning, is
a function of the temperature. This rate is very low at room temperature.
For example, a 4 mm thick test specimen of PA66 requires more than a
year to attain its equilibrium moisture content in Standard atmosphere
23/50 (see ISO 291). To condition specimens in a relatively short period
of time, higher temperatures are required. Such a method for accelerated
conditioning is presented in this International Standard.
. . .
Ill

---------------------- Page: 5 ----------------------

SIST ISO 1110:1996
This page intentionally left blank

---------------------- Page: 6 ----------------------

SIST ISO 1110:1996
INTERNATIONAL STANDARD 0 ISO ISO 1110:1995(E)
- Polyamides - Accelerated conditioning
Plastics
of test specimens
chrometric temperature differente of 10 “C + 0,3 “C)
1 Scope
until moisture absorption by the specimen has
reached at least 95 % of its equilibrium level.
This International Standard describes a method for the
accelerated conditioning of test specim
...

INTERNATIONAL ISO
1110
STANDARD
Third edition
1995-02-01
- Polyamides - Accelerated
Plastics
conditioning of test specimens
- Polyamides - Conditionnemen t accMr6 d ‘eprouve ttes
Plas tiques
Reference number
ISO 11 IO:1 995(E)

---------------------- Page: 1 ----------------------
ISO 1110:1995(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide
federation of national Standards bodies (ISO member bodies). The work
of preparing International Standards is normally carried out through ISO
technical committees. Esch member body interested in a subject for
which a technical committee has been established has the right to be
represented on that committee. International organizations, governmental
and non-governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(1 EC) on all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are
circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.
International Standard ISO 1110 was prepared by Technical Committee
lSO/lC 61, Plastics, Subcommittee SC 9, Thermoplastic materials.
This third edition cancels and replaces the second edition
(ISO 11 IO:1 987), which has been technically revised.
0 ISO 1995
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronie or mechanical, including photocopying and
microfilm, without Permission in writing from the publisher.
International Organization for Standardization
Case Postale 56 l CH-l 211 Geneve 20 l Switzerland
Printed in Switzerland

---------------------- Page: 2 ----------------------
Q ISO
ISO 1110:1995(E)
Introduction
Various properties of polyamides (PA) depend upon their moisture content.
Reproducible values of these properties tan only be obtained with speci-
mens having a specified moisture content. Such specimens are obtained
by conditioning, i.e. by allowing them to resch equilibrium in an atmos-
phere with a specified temperature and relative humidity.
The rate of moisture absorption and, therefore, the rate of conditioning, is
a function of the temperature. This rate is very low at room temperature.
For example, a 4 mm thick test specimen of PA66 requires more than a
year to attain its equilibrium moisture content in Standard atmosphere
23/50 (see ISO 291). To condition specimens in a relatively short period
of time, higher temperatures are required. Such a method for accelerated
conditioning is presented in this International Standard.
. . .
Ill

---------------------- Page: 3 ----------------------
This page intentionally left blank

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD 0 ISO ISO 1110:1995(E)
- Polyamides - Accelerated conditioning
Plastics
of test specimens
chrometric temperature differente of 10 “C + 0,3 “C)
1 Scope
until moisture absorption by the specimen has
reached at least 95 % of its equilibrium level.
This International Standard describes a method for the
accelerated conditioning of test specimens of
polyamides and copolyamides. lt is applicable to
4 Apparatus
grades containing fillers and other additives, but not
to grades containing more than 2 % (m/m) extract-
4.1 Cabinet, with closed air circulation by a fan,
ables.
capable of maintaining a temperature of 70 “C within
a tolerante of + 1 “C and a psychrometric tempera-
The equilibrium moisture content attained by this
ture differente of 10 “C within a tolerante of
method is close to the equilibrium moisture content
+ 0,3 “
...

NORME
ISO
INTERNATIONALE
1110
Troisième édition
1995-02-01
Plastiques - Polyamides -
Conditionnement accéléré d’éprouvettes
P/as tics - Polyamides - Accelerated conditioning of test specimens
Numéro de référence
ISO II 10:1995(F)

---------------------- Page: 1 ----------------------
ISO 1110:1995(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comité membre intéressé par une
étude a le droit de faire partie du comité technique créé à cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 1110 a été élaborée par le comité technique
ISO/TC 61, Plastiques, sous-comité SC 9, Matériaux thermoplastiques.
Cette troisième édition annule et remplace la deuxième édition
(ISO 1110:1987), dont elle constitue une révision technique.
0 ISO 1995
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l’accord
écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Genève 20 l Suisse
Imprimé en Suisse
ii

---------------------- Page: 2 ----------------------
0 ISO
ISO 1110:1995(F)
Introduction
Les diverses propriétés des polyamides (PA) dépendent de leur taux
d’humidité. Des valeurs reproductibles de ces propriétés peuvent seu-
lement être obtenues avec des éprouvettes ayant un taux prescrit d’hu-
midité. De telles éprouvettes sont obtenues par conditionnement, par
exemple en les équilibrant dans une atmosphère avec une température
et une humidité relative prescrites.
La vitesse d’absorption d’humidité et, en conséquence, la vitesse de
conditionnement sont fonction de la température. Elles sont très lentes à
température ambiante. Par exemple, une éprouvette de 4 mm d’épaisseur
en PA 66 demande plus de 1 an pour atteindre son équilibre en humidité
dans l’atmosphère normale 23/50 (voir ISO 291). Pour conditionner les
éprouvettes dans une période de temps relativement courte, de plus
hautes températures sont requises. Une telle méthode pour le condition-
nement accéléré est exposée dans la présente Norme internationale.
. . .
III

---------------------- Page: 3 ----------------------
Page blanche

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE 0 ISO ISO 1110:1995(F)
Plastiques - Polyamides - Conditionnement
accéléré d’éprouvettes
3 Principe
1 Domaine d’application
Les éprouvettes sont placées dans une atmosphère
La présente Norme internationale prescrit une mé-
à 70 “C + 1 “C et (62 + 1) % d’humidité relative (dif-
thode pour le conditionnement accéléré d’éprouvettes
férence -de température psychrométrique 10 “C
des polyamides et copolyamides. La méthode peut
+ 0,3 “C), jusqu’à ce que l’absorption d’humidité de
aussi être appliquée aux qualités contenant des char- -
l’éprouvette ait atteint au moins 95 % de son niveau
ges et autres additifs, mais pas aux qualités contenant
d’équilibre.
plus de 2 % (m/m) de matières extractibles.
Le taux d’humidité d’équilibre atteint par cette mé-
4 Appareillage
thode correspond à peu près au taux d’humidité
d’équilibre obtenu dans l’atmosphère normale 23/50.
4.1 Enceinte fermée, avec circulation d’air par un
Les valeurs de propriétés mécaniques obtenues après
ventilateur, capable de maintenir la température de
conditionnement accéléré selon cette méthode
...

NORME
ISO
INTERNATIONALE
1110
Troisième édition
1995-02-01
Plastiques - Polyamides -
Conditionnement accéléré d’éprouvettes
P/as tics - Polyamides - Accelerated conditioning of test specimens
Numéro de référence
ISO II 10:1995(F)

---------------------- Page: 1 ----------------------
ISO 1110:1995(F)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération
mondiale d’organismes nationaux de normalisation (comités membres de
I’ISO). L’élaboration des Normes internationales est en général confiée aux
comités techniques de I’ISO. Chaque comité membre intéressé par une
étude a le droit de faire partie du comité technique créé à cet effet. Les
organisations internationales, gouvernementales et non gouvernemen-
tales, en liaison avec I’ISO participent également aux travaux. L’ISO colla-
bore étroitement avec la Commission électrotechnique internationale (CEI)
en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques
sont soumis aux comités membres pour vote. Leur publication comme
Normes internationales requiert l’approbation de 75 % au moins des co-
mités membres votants.
La Norme internationale ISO 1110 a été élaborée par le comité technique
ISO/TC 61, Plastiques, sous-comité SC 9, Matériaux thermoplastiques.
Cette troisième édition annule et remplace la deuxième édition
(ISO 1110:1987), dont elle constitue une révision technique.
0 ISO 1995
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l’accord
écrit de l’éditeur.
Organisation internationale de normalisation
Case Postale 56 l CH-l 211 Genève 20 l Suisse
Imprimé en Suisse
ii

---------------------- Page: 2 ----------------------
0 ISO
ISO 1110:1995(F)
Introduction
Les diverses propriétés des polyamides (PA) dépendent de leur taux
d’humidité. Des valeurs reproductibles de ces propriétés peuvent seu-
lement être obtenues avec des éprouvettes ayant un taux prescrit d’hu-
midité. De telles éprouvettes sont obtenues par conditionnement, par
exemple en les équilibrant dans une atmosphère avec une température
et une humidité relative prescrites.
La vitesse d’absorption d’humidité et, en conséquence, la vitesse de
conditionnement sont fonction de la température. Elles sont très lentes à
température ambiante. Par exemple, une éprouvette de 4 mm d’épaisseur
en PA 66 demande plus de 1 an pour atteindre son équilibre en humidité
dans l’atmosphère normale 23/50 (voir ISO 291). Pour conditionner les
éprouvettes dans une période de temps relativement courte, de plus
hautes températures sont requises. Une telle méthode pour le condition-
nement accéléré est exposée dans la présente Norme internationale.
. . .
III

---------------------- Page: 3 ----------------------
Page blanche

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE 0 ISO ISO 1110:1995(F)
Plastiques - Polyamides - Conditionnement
accéléré d’éprouvettes
3 Principe
1 Domaine d’application
Les éprouvettes sont placées dans une atmosphère
La présente Norme internationale prescrit une mé-
à 70 “C + 1 “C et (62 + 1) % d’humidité relative (dif-
thode pour le conditionnement accéléré d’éprouvettes
férence -de température psychrométrique 10 “C
des polyamides et copolyamides. La méthode peut
+ 0,3 “C), jusqu’à ce que l’absorption d’humidité de
aussi être appliquée aux qualités contenant des char- -
l’éprouvette ait atteint au moins 95 % de son niveau
ges et autres additifs, mais pas aux qualités contenant
d’équilibre.
plus de 2 % (m/m) de matières extractibles.
Le taux d’humidité d’équilibre atteint par cette mé-
4 Appareillage
thode correspond à peu près au taux d’humidité
d’équilibre obtenu dans l’atmosphère normale 23/50.
4.1 Enceinte fermée, avec circulation d’air par un
Les valeurs de propriétés mécaniques obtenues après
ventilateur, capable de maintenir la température de
conditionnement accéléré selon cette méthode
...