SIST ISO 898-5:2000

Mechanical properties of fasteners made of carbon steel and alloy steel -- Part 5: Set screws and similar threaded fasteners not under tensile stresses

Caractéristiques mécaniques des éléments de fixation en acier au carbone et en acier allié -- Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à des contraintes de traction

Mehanske lastnosti veznih elementov - 5. del: Navojni zatiči in podobni deli z navoji, vzdolžno neobremenjeni

General Information

• Status: Withdrawn
• Publication Date: 31-Dec-1999
• Withdrawal Date: 30-Jun-2002
• ICS: 21.060.10 - Bolts, screws, studs
• Technical Committee: ISEL - Mechanical elements
• Current Stage: 9900 - Withdrawal (Adopted Project)
• Start Date: 01-Jul-2002
• Due Date: 01-Jul-2002
• Completion Date: 01-Jul-2002
• Ref Project: ISO 898-5:1998 - Mechanical properties of fasteners made of carbon steel and alloy steel — Part 5: Set screws and similar threaded fasteners not under tensile stresses

Relations

• Revised: SIST ISO 898-5:1996 - Mechanical properties of fasteners -- Part 5: Set screws and similar threaded fasteners not under tensile stresses
• Effective Date: 12-May-2008
• Revised: ISO 898-5:1980 - Mechanical properties of fasteners — Part 5: Set screws and similar threaded fasteners not under tensile stresses
• Effective Date: 12-May-2008

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 898-5
Second edition
1998-08-01
Mechanical properties of fasteners made
of carbon steel and alloy steel —
Part 5:
Set screws and similar threaded fasteners not
under tensile stresses
Caractéristiques mécaniques des éléments de fixation en acier au carbone
et en acier allié —
Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à
des contraintes de traction
A
Reference number
ISO 898-5:1998(E)

---------------------- Page: 1 ----------------------
ISO 898-5:1998(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has the
right to be represented on that committee. International organizations, governmental and non-governmental, in liaison
with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on
all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
International Standard ISO 898-5 was prepared by Technical Committee ISO/TC 2, Fasteners, Subcommittee SC 1,
Mechanical properties of fasteners.
This second edition cancels and replaces the first edition (ISO 898-5:1980), which has been technically revised.
ISO 898 consists of the following parts, under the general title Mechanical properties of fasteners made of carbon steel
and alloy steel:
— Part 1: Bolts screws and studs
— Part 2: Nuts with specified proof load values — Coarse thread
— Part 5: Set screws and similar threaded fasteners not under tensile stresses
— Part 6: Nuts with specified proof load values — Fine pitch thread
— Part 7: Torsional test and minimum torques for bolts and screws with nominal diameters 1 mm to 10 mm
Annex A of this part of ISO 898 is for information only.
©  ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [e-mail]
Printed in Switzerland
ii

---------------------- Page: 2 ----------------------
©
INTERNATIONAL STANDARD  ISO ISO 898-5:1998(E)
Mechanical properties of fasteners made of carbon steel and alloy
steel —
Part 5:
Set screws and similar threaded fasteners not under tensile stresses
1  Scope
This part of ISO 898 specifies the mechanical properties of set screws and similar threaded fasteners not under tensile
stresses with nominal thread diameters from 1,6 mm up to and including 24 mm, which are made of carbon steel or alloy
steel.
The mechanical and physical properties apply when tested at an ambient temperature of 10 °C to 35 °C and will vary at
higher or lower temperatures.
This part of ISO 898 does not apply to set screws requiring special properties such as
— specified tensile stresses (see ISO 898-1);
— weldability;
— corrosion resistance;
— ability to withstand temperatures above + 300 °C or below – 50 °C.
NOTE —  Set screws made from free-cutting steel should not be used above + 250 °C.
2  Normative references
The following standards contain provisions which, through reference in this text, constitute provisions of this part of ISO 898.
At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements
based on this part of ISO 898 are encouraged to investigate the possibility of applying the most recent editions of the
standards indicated below. Members of IEC and ISO maintain registers of currently valid International Standards.
ISO 965-3:1998, ISO general purpose metric screw threads —Tolerances — Part 3: Deviations for constructional threads.
ISO 4948-1:1982, Steels — Classification — Part 1: Classification of steels into unalloyed and alloy steels based on
chemical composition.
ISO 6506:1981, Metallic materials — Hardness test — Brinell test.
ISO 6507-1:1997, Metallic materials — Vickers hardness test — Part 1: Test method.
ISO 6508:1986, Metallic materials — Hardness test — Rockwell test (scales A - B - C - D - E - F - G - H - K).
1

---------------------- Page: 3 ----------------------
©
ISO
ISO 898-5:1998(E)
3  Designation system
The property classes are designated by the symbols shown in table 1.
The numerical part of the symbol represents 1/10 of the minimum Vickers hardness.
The letter H in the symbol refers to hardness.
Table 1 — Designations of property classes in relation to Vickers hardness
Property class 14H 22H 33H 45H
Vickers hardness, HV min. 140 220 330 450
4  Materials
Set screws shall be made of steel conforming to the requirements specified in table 2.
For property class 45H, other materials may be used provided that the proof torque requirements in 6.3 are met.
Table 2 — Steel specifications
Property class Material Heat treatment Chemical composition
% (m/m)
CP S
max. min. max. max.
1, 2)
Carbon steel — 0,50 — 0,11 0,15
14H
3)
22H Carbon steel Quenched and tempered 0,50 — 0,05 0,05
3)
33H Carbon steel Quenched and tempered 0,50 — 0,05 0,05
3, 4)
45H Alloy steel Quenched and tempered 0,50 0,19 0,05 0,05
1)  Free-cutting steel may be used, with lead content 0,35 % maximum, phosphorus content 0,11 % maximum and sulphur content
0,34 % maximum.
2)  Case hardening is allowed in the case of square-head set screws.
3)  Steel with lead content 0,35 % maximum may be used.
4)  Shall contain one or more of alloying elements chromium, nickel, molybdenum, vanadium or boron, see ISO 4948-1.
2

---------------------- Page: 4 ----------------------
©
ISO
ISO 898-5:1998(E)
5  Mechanical properties
When tested by the methods specified in clause 6, the set screws shall have, at ambient temperature, the mechanical
properties specified in table 3.
Table 3 — Mechanical properties
1)
Mechanical properties Property class
14H 22H 33H 45H
Vickers hardness HV 10 min. 140 220 330 450
max. 290 300 440 560
2
Brinell hardness HB, F = 30 D min. 133 209 314 428
max. 276 285 418 532
HRB min. 75 95 — —
2)
Rockwell hardness max. 105 ——
2)
HRC min. — 33 45
max. — 30 44 53
Torque strength — — — see table 5
1 2 3
H H H
Minimum height of non-decarburized thread zone, E —

1 1 1
2 3 4
3)
Maximum depth of complete decarburization, G mm — 0,015 0,015
Surface hardness HV 0,3 max. — 320 450 580
1)  Property classes 14H, 22H and 33H are not for hexagon socket set screws.
2)  For property class 22H, it is necessary to test the minimum value in HRB and the maximum value in HRC, if Rockwell hardness
is tested.
3)  No complete decarburization permitted in property class 45H.
6  Test methods for determination of mechanical properties
6.1  Hardness tests
Hardness tests shall be conducted as near as practicable to the centre position of the point end of the screw. If the maximum
hardness as given in table 3 is exceeded, a retest shall be conducted on a cross-section 0,5 d back from the point end where
d is the nominal thread diameter. In case of doubt, the Vickers hardness test is decisive for acceptance.
Hardness readings for the surface hardness shall be taken on the end of the screw, which will be prepared by slightly
grinding or polishing to ensure reproducible readings.
6.1.1  Vickers hardness test
T
...

SLOVENSKI STANDARD
SIST ISO 898-5:2000
01-januar-2000
0HKDQVNHODVWQRVWLYH]QLKHOHPHQWRYGHO1DYRMQL]DWLþLLQSRGREQLGHOL]
QDYRMLY]GROåQRQHREUHPHQMHQL
Mechanical properties of fasteners made of carbon steel and alloy steel -- Part 5: Set
screws and similar threaded fasteners not under tensile stresses
Caractéristiques mécaniques des éléments de fixation en acier au carbone et en acier
allié -- Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à des
contraintes de traction
Ta slovenski standard je istoveten z: ISO 898-5:1998
ICS:
21.060.10 Sorniki, vijaki, stebelni vijaki Bolts, screws, studs
SIST ISO 898-5:2000 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST ISO 898-5:2000

---------------------- Page: 2 ----------------------

SIST ISO 898-5:2000
INTERNATIONAL ISO
STANDARD 898-5
Second edition
1998-08-01
Mechanical properties of fasteners made
of carbon steel and alloy steel —
Part 5:
Set screws and similar threaded fasteners not
under tensile stresses
Caractéristiques mécaniques des éléments de fixation en acier au carbone
et en acier allié —
Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à
des contraintes de traction
A
Reference number
ISO 898-5:1998(E)

---------------------- Page: 3 ----------------------

SIST ISO 898-5:2000
ISO 898-5:1998(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has the
right to be represented on that committee. International organizations, governmental and non-governmental, in liaison
with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on
all matters of electrotechnical standardization.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
International Standard ISO 898-5 was prepared by Technical Committee ISO/TC 2, Fasteners, Subcommittee SC 1,
Mechanical properties of fasteners.
This second edition cancels and replaces the first edition (ISO 898-5:1980), which has been technically revised.
ISO 898 consists of the following parts, under the general title Mechanical properties of fasteners made of carbon steel
and alloy steel:
— Part 1: Bolts screws and studs
— Part 2: Nuts with specified proof load values — Coarse thread
— Part 5: Set screws and similar threaded fasteners not under tensile stresses
— Part 6: Nuts with specified proof load values — Fine pitch thread
— Part 7: Torsional test and minimum torques for bolts and screws with nominal diameters 1 mm to 10 mm
Annex A of this part of ISO 898 is for information only.
©  ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [e-mail]
Printed in Switzerland
ii

---------------------- Page: 4 ----------------------

SIST ISO 898-5:2000
©
INTERNATIONAL STANDARD  ISO ISO 898-5:1998(E)
Mechanical properties of fasteners made of carbon steel and alloy
steel —
Part 5:
Set screws and similar threaded fasteners not under tensile stresses
1  Scope
This part of ISO 898 specifies the mechanical properties of set screws and similar threaded fasteners not under tensile
stresses with nominal thread diameters from 1,6 mm up to and including 24 mm, which are made of carbon steel or alloy
steel.
The mechanical and physical properties apply when tested at an ambient temperature of 10 °C to 35 °C and will vary at
higher or lower temperatures.
This part of ISO 898 does not apply to set screws requiring special properties such as
— specified tensile stresses (see ISO 898-1);
— weldability;
— corrosion resistance;
— ability to withstand temperatures above + 300 °C or below – 50 °C.
NOTE —  Set screws made from free-cutting steel should not be used above + 250 °C.
2  Normative references
The following standards contain provisions which, through reference in this text, constitute provisions of this part of ISO 898.
At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements
based on this part of ISO 898 are encouraged to investigate the possibility of applying the most recent editions of the
standards indicated below. Members of IEC and ISO maintain registers of currently valid International Standards.
ISO 965-3:1998, ISO general purpose metric screw threads —Tolerances — Part 3: Deviations for constructional threads.
ISO 4948-1:1982, Steels — Classification — Part 1: Classification of steels into unalloyed and alloy steels based on
chemical composition.
ISO 6506:1981, Metallic materials — Hardness test — Brinell test.
ISO 6507-1:1997, Metallic materials — Vickers hardness test — Part 1: Test method.
ISO 6508:1986, Metallic materials — Hardness test — Rockwell test (scales A - B - C - D - E - F - G - H - K).
1

---------------------- Page: 5 ----------------------

SIST ISO 898-5:2000
©
ISO
ISO 898-5:1998(E)
3  Designation system
The property classes are designated by the symbols shown in table 1.
The numerical part of the symbol represents 1/10 of the minimum Vickers hardness.
The letter H in the symbol refers to hardness.
Table 1 — Designations of property classes in relation to Vickers hardness
Property class 14H 22H 33H 45H
Vickers hardness, HV min. 140 220 330 450
4  Materials
Set screws shall be made of steel conforming to the requirements specified in table 2.
For property class 45H, other materials may be used provided that the proof torque requirements in 6.3 are met.
Table 2 — Steel specifications
Property class Material Heat treatment Chemical composition
% (m/m)
CP S
max. min. max. max.
1, 2)
Carbon steel — 0,50 — 0,11 0,15
14H
3)
22H Carbon steel Quenched and tempered 0,50 — 0,05 0,05
3)
33H Carbon steel Quenched and tempered 0,50 — 0,05 0,05
3, 4)
45H Alloy steel Quenched and tempered 0,50 0,19 0,05 0,05
1)  Free-cutting steel may be used, with lead content 0,35 % maximum, phosphorus content 0,11 % maximum and sulphur content
0,34 % maximum.
2)  Case hardening is allowed in the case of square-head set screws.
3)  Steel with lead content 0,35 % maximum may be used.
4)  Shall contain one or more of alloying elements chromium, nickel, molybdenum, vanadium or boron, see ISO 4948-1.
2

---------------------- Page: 6 ----------------------

SIST ISO 898-5:2000
©
ISO
ISO 898-5:1998(E)
5  Mechanical properties
When tested by the methods specified in clause 6, the set screws shall have, at ambient temperature, the mechanical
properties specified in table 3.
Table 3 — Mechanical properties
1)
Mechanical properties Property class
14H 22H 33H 45H
Vickers hardness HV 10 min. 140 220 330 450
max. 290 300 440 560
2
Brinell hardness HB, F = 30 D min. 133 209 314 428
max. 276 285 418 532
HRB min. 75 95 — —
2)
Rockwell hardness max. 105 ——
2)
HRC min. — 33 45
max. — 30 44 53
Torque strength — — — see table 5
1 2 3
H H H
Minimum height of non-decarburized thread zone, E —

1 1 1
2 3 4
3)
Maximum depth of complete decarburization, G mm — 0,015 0,015
Surface hardness HV 0,3 max. — 320 450 580
1)  Property classes 14H, 22H and 33H are not for hexagon socket set screws.
2)  For property class 22H, it is necessary to test the minimum value in HRB and the maximum value in HRC, if Rockwell hardness
is tested.
3)  No complete decarburization permitted in property class 45H.
6  Test methods for determination
...

NORME ISO
INTERNATIONALE 898-5
Deuxième édition
1998-08-01
Caractéristiques mécaniques des éléments
de fixation en acier au carbone et en acier
allié —
Partie 5:
Vis sans tête et éléments de fixation filetés
similaires non soumis à des contraintes de
traction
Mechanical properties of fasteners made of carbon steel and alloy steel —
Part 5: Set screws and similar threaded fasteners not under tensile stresses
A
Numéro de référence
ISO 898-5:1998(F)

---------------------- Page: 1 ----------------------
ISO 898-5:1998(F)
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale d'organismes nationaux de
normalisation (comités membres de l'ISO). L'élaboration des Normes internationales est en général confiée aux
comités techniques de l'ISO. Chaque comité membre intéressé par une étude a le droit de faire partie du comité
technique créé à cet effet. Les organisations internationales, gouvernementales et non gouvernementales, en
liaison avec l'ISO, participent également aux travaux. L'ISO collabore étroitement avec la Commission
électrotechnique internationale (CEI) en ce qui concerne la normalisation électrotechnique.
Les projets de Normes internationales adoptés par les comités techniques sont soumis aux comités membres pour
vote. Leur publication comme Normes internationales requiert l'approbation de 75 % au moins des comités
membres votants.
La Norme internationale ISO 898-5 a été élaborée par le comité technique ISO/TC 2, Éléments de fixation, sous-
comité SC 1, Propriétés mécaniques des éléments de fixation.
Cette deuxième édition annule et remplace la première édition (ISO 898-5:1980), dont elle constitue une révision
technique.
L’ISO 898 comprend les parties suivantes, présentées sous le titre général Caractéristiques mécaniques des
éléments de fixation en acier au carbone et en acier allié:
— Partie 1: Vis et goujons
— Partie 2: Écrous avec charges d’épreuve spécifiées — Filetages à pas gros
— Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à des contraintes de traction
— Partie 6: Écrous avec charges d’épreuve spécifiées — Filetages à pas fin
— Partie 7: Essai de torsion et couples minimaux de rupture des vis de diamètre nominal de filetage de 1 mm
à 10 mm
L’annexe A de la présente partie de l’ISO 898 est donnée uniquement à titre d’information.
©  ISO 1998
Droits de reproduction réservés. Sauf prescription différente, aucune partie de cette publi-
cation ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun pro-
cédé, électronique ou mécanique, y compris la photocopie et les microfilms, sans l'accord
écrit de l'éditeur.
Organisation internationale de normalisation
Case postale 56 • CH-1211 Genève 20 • Suisse
Internet [e-mail]
Imprimé en Suisse
ii

---------------------- Page: 2 ----------------------
©
NORME INTERNATIONALE  ISO ISO 898-5:1998(F)
Caractéristiques mécaniques des éléments de fixation en acier
au carbone et en acier allié —
Partie 5:
Vis sans tête et éléments de fixation filetés similaires non soumis à
des contraintes de traction
1 Domaine d’application
La présente partie de l'ISO 898 prescrit les caractéristiques mécaniques des vis sans tête et éléments de fixation
filetés similaires, non soumis à des contraintes de traction, dans la gamme des diamètres nominaux de filetage
compris entre 1,6 mm et 24 mm, en acier au carbone ou en acier allié.
Les caractéristiques mécaniques et physiques s'appliquent lors d'essais à température ambiante comprise entre
10 °C et 35 °C et varient en fonction des hautes et basses températures.
La présente partie de l'ISO 898 ne s'applique pas aux vis pour lesquelles on exige des caractéristiques spéciales
telles que:
— contraintes de traction prescrites (voir ISO 898-1);
— aptitude au soudage;
— résistance à la corrosion;
— résistance aux températures supérieures à + 300 °C ou inférieures à − 50 °C.
NOTE —  Il convient de ne pas utiliser les vis en acier de décolletage à des températures supérieures à + 250 °C.
2 Références normatives
Les normes suivantes contiennent des dispositions qui, par suite de la référence qui en est faite, constituent des
dispositions valables pour la présente partie de l’ISO 898. Au moment de la publication, les éditions indiquées
étaient en vigueur. Toute norme est sujette à révision et les parties prenantes des accords fondés sur la présente
partie de l’ISO 898 sont invitées à rechercher la possibilité d'appliquer les éditions les plus récentes des normes
indiquées ci-après. Les membres de la CEI et de l'ISO possèdent le registre des Normes internationales en vigueur
à un moment donné.
ISO 965-3:1998, Filetages métriques ISO pour usages généraux — Tolérances — Écarts pour filetages de
construction.
ISO 4948-1:1982, Aciers — Classification — Partie 1: Classification en aciers alliés et en acier non alliés basée sur
la composition chimique.
1

---------------------- Page: 3 ----------------------
©
ISO
ISO 898-5:1998(F)
ISO 6506:1981, Matériaux métalliques — Essai de dureté — Essai Brinell.
ISO 6507-1:1997, Matériaux métalliques — Essai de dureté Vickers — Méthode d’essai.
ISO 6508:1986, Matériaux métalliques — Essai de dureté — Essai Rockwell (échelles A - B - C - D - E - F - G - H - K).
3 Système de désignation
Les classes de qualité sont désignées par les symboles du tableau 1.
e
Le symbole numérique représente le 1/10 de la dureté Vickers minimale.
La lettre H représente la dureté.
Tableau 1 — Désignations des classes de qualité
basées sur la dureté Vickers
Classe de qualité 14H 22H 33H 45H
Dureté Vickers, HV min. 140 220 330 450
4 Matières
Les vis sans tête doivent être fabriquées en acier, conformément aux spécifications du tableau 2.
D'autres aciers sont admissibles pour la classe 45H, à condition qu'ils satisfassent aux exigences de l'essai de
couple prescrit en 6.3.
Tableau 2 — Spécifications de l'acier
Composition chimique
% (m /m)
Classe de qualité Matière Traitement C P S
max. min. max. max.
1) 2)
14H Acier au carbone — 0,50 — 0,11 0,15
3)
22H Acier au carbone Trempé et revenu 0,50 — 0,05 0,05
3)
33H Acier au carbone Trempé et revenu 0,50 — 0,05 0,05
3) 4)
45H Acier allié Trempé et revenu 0,50 0,19 0,05 0,05
1)  Acier de décolletage admis avec Pb max. = 0,35 %; P max. = 0,11 %; S max. = 0,34 %.
2)  Cémentation admise dans le cas des vis à entraînement par carré.
3)  Un acier avec Pb max. = 0,35 % peut être utilisé.
4)  Doit contenir un ou plusieurs éléments d'alliage, tels que: chrome, nickel, molybdène, vanadium ou bore, voir ISO 4948-1.
2

---------------------- Page: 4 ----------------------
©
ISO
ISO 898-5:1998(F)
5 Caractéristiques mécaniques
Les vis soumises aux méthodes d'essai décrites dans l'article 6 doivent avoir, à température ambiante, les
caractéristiques mécaniques prescrites dans le tableau 3.
Tableau 3 — Caractéristiques mécaniques
1)
Caractéristiques mécaniques Classe de qualité
14H 22H 33H 45H
Dureté Vickers HV 10 min. 140 220 330 450
max. 290 300 440 560
2
Dureté Brinell HB, F = 30 D min. 133 209 314 428
max. 276 285 418 532
min. 75 95 — —
HRB
2)
Dureté Rockwell max. 105 ——
2)
min. — 33 45
HRC
max. — 30 44 53
Résistance à la torsion — — — voir tableau 5
2
1 3
Hauteur minimale de la zone filetée non —
H
H H
1
1 1
décarburée, E 3
2 4
3)
Profondeur maximale de décarburation mm — 0,015 0,015
complète,
G
Dureté superficielle, HV 0,3 max. — 320 450 580
1)  Classes de qualité 14H, 22H et 33H, à l'exception des vis sans tête à six pans creux.
2)  Pour la classe de qualité 22H, si la dureté Rockwell est utilisée, il est nécessaire d'effectuer l'essai à la valeur minimale en HRB et à la
valeur maximale en HRC.
3)  Pas de décarburation complète autorisée pour la classe de qualité 45H.
6 Méthode d'essai pour la détermination des caractéristiques mécaniques
6.1 Essais de dureté
Les essais de dureté doivent être effectués aussi près que possible du centre de l'extrémité de la vis. Si la dureté
maximale autorisée est dépassée, un nouvel essai doit être effectué sur une section droite à une distance de
l'extrémité égale à 0,5 d, où d est le diamètre nominal de filetage. En cas de doute, l'essai de dureté Vickers est
décisif pour l'acceptation.
Les mesurages de dureté de surface doivent être effectués sur l'extrémité de la vis préparée par un léger meulage
ou polissage pour assurer la reprod
...