ISO 898-5:1980

Mechanical properties of fasteners — Part 5: Set screws and similar threaded fasteners not under tensile stresses

Propriétés mécaniques des éléments de fixation — Partie 5: Vis sans tête et éléments de fixation filetés similaires non soumis à des contraintes de traction

Mehanske lastnosti veznih elementov - 5. del: Navojni zatiči in podobni deli z navoji

General Information

• Status: Withdrawn
• Publication Date: 30-Jun-1980
• Withdrawal Date: 30-Jun-1980
• ICS: 21.060.10 - Bolts, screws, studs
• Technical Committee: ISO/TC 2 - Fasteners
• Drafting Committee: ISO/TC 2 - Fasteners
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 23-Jul-1998
• Ref Project: SIST ISO 898-5:1996 - Mechanical properties of fasteners -- Part 5: Set screws and similar threaded fasteners not under tensile stresses

Relations

• Revised: ISO 898-5:1998 - Mechanical properties of fasteners made of carbon steel and alloy steel — Part 5: Set screws and similar threaded fasteners not under tensile stresses
• Effective Date: 15-Apr-2008
• Revised: SIST ISO 898-5:2000 - Mechanical properties of fasteners made of carbon steel and alloy steel -- Part 5: Set screws and similar threaded fasteners not under tensile stresses
• Effective Date: 12-May-2008

Standards Content (Sample)

International Standard @ 89815
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONOMEXYHAPOJlHAR OPTAHH3AUHR no CTAHAAPTH3AUHH.ORGANlSATlON INTERNATIONALE DE hORMALISATION
Mechanical properties of fasteners -
'-
Part 5 : Set screws and similar threaded fasteners not
under tensile stresses
Propriétés mécaniques des éléments de fixation - Partie 5 : Vis sans tête et éléments de fixation filetés similaires non soumis a
des contraintes de traction
First edition - 1980-07-15
1 Lu UDC 621.882.219.4
Ref. No. IS0 898/5-1980 (E)
Descriptors : fasteners, screws, set screws, designation, materials specifications, chemical composition, mechanical properties, mechanical
' -
a
tests, hardness tests, decarburisation, torque.
8
Price based on 6 pages

---------------------- Page: 1 ----------------------
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
righ? to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with EO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 û98/5 was developed by Technical Committee ISO/TC 2,
Fasteners, and was circulated to the member bodies in April 1979.
It has been approved by the member bodies of the following countries :
Australia Germany, F. R. Poland
Austria Hungary Romania
South Africa, Rep. of
Belgium India
Bulgaria Ireland Spain
Canada Italy Sweden
Switzerland
Chile Japan
Czechoslovakia Korea, Rep. of United Kingdom
Denmark Netherlands USA
Finland New Zealand USSR
France Norway Yugoslavia
No member body expressed disapproval of the document.
0 International Organization for Standardization, 1980 O
Printed in Switzerland

---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD IS0 898/5-1980 (E)
Mechanical properties of fasteners -
Part 5 : Set screws and similar threaded fasteners not
under tensile stresses
1
Scope and field of application ISOIR 80, Rockwell hardness test IB and C scales) for steel.
This International Standard specifies the mechanical properties ISOIR 81, Vickers hardness test for steel.
of set screws and similar fasteners not under tensile stresses in
the range from 1,6 up to and including 39 mm thread diameter IS0 615711, Surface discontinuities on bolts, screws and
which are made of carbon steel or alloy steel. studs’).
It does not apply to screws requiring special properties such as
-
specified tensile stresses (see IS0 89811 1;
3 Designation system
- weldability;
The property classes are designated by the symbols shown in
\-
table 1.
-
corrosion resistance (see IS0 3506);
The numerical part of the symbol represents 1/10 of the
-
ability to withstand temperatures above + 300 OC or
minimum Vickers hardness.
below - 50 OC.
The letter H in the symbol refers to hardness.
NOTE - Screws made from free-cutting steel should not be used
above + 250 OC.
2 References
Property class 14H 22H 33H 45H
ISOIR 79, Brinell hardness test for steel.
1) At present at the stage of draft.
1

---------------------- Page: 3 ----------------------
IS0 898/5-1980 (E)
4 Raw materials 5 Mechanical properties
Set screws shall be made of steel conforming to the re-
When tested by the methods specified in clause 6, the set
quirements specified in table 2. screws shall have, at ambient temperature, the mechanical pro-
perties specified in table 3.
For property class 45H, other materials may be used provided
that the torque test requirements in 6.4 are met.
Table 2 - Steel specifications
Chemical composition, %
Property class Material Heat treatment C P S
rnax. min. rnax. max.
Carbon steell)2) - 0.50 - 0,11 0,15
22H Carbon steel3) Quenched and tempered 0,50 - 0,05
33H Carbon steel3) Quenched and tempered 0.50 - 0.05
Quenched and temDered 0.50 0.19 0.05 0.05
45H Allov ~tee13)~)
1) Free-cutting steel may be used, with lead content 0,35 % rnax., phosphorus content 0,11 % rnax. and sulphur content 0.34 % rnax.
2) Case hardening is allowed in the case of square-head set screws.
Steel with lead content 0,35 % max. may be used.
3)
4) Shall contain one or more of alloying elements chromium, nickel, molybdenum, vanadium or boron.
Table 3 - Mechanical properties
Property class*
Mechanical properties
14H I 22H I 33H I 45H
min. I 140 I 220 I 330 1 450
Vickers hardness HV
min.
133 209 314 428
Brinell hardness HB, F = 30 02
max. I 276 285 418 532
- -
min. 75 95
- - -
max. 105
I
Rockwell hardness
-
min. - 33 45
-
30 44 53
max. I
-
Torque strength -
- I see table 5
Minimum height of non-decarburized thread zone, E
**
Maximum depth of complete decarburization, G mm - 0,015 0,015
Surface-hardness HV 0.3 max. - 320 450 580
Classes 14H, 22H and 33H are not for hexagon socket set screws.
**
No complete decarburization permitted in property class 45H.
2

---------------------- Page: 4 ----------------------
IS0 898/5-1980 (E)
6.2.1 Definitions
6 Test methods for determination of
mechanical properties
base metal hardness : The hardness closest to the surface
(when traversing from core to outside diameter) just before an
6.1 Hardness tests
increase or decrease occurs denoting carburization or decarbu-
rization.
Hardness tests shall be conducted as near as practicable to the
centre position of the point ends of the screw. If the maximum
decarburization : Generally, the loss of carbon at the surface
hardness is exceeded, a retest shall be conducted on a cross-
section 0,5 mm back from the point end. In case of doubt, the of commercial ferrous materials (steels).
Vickers hardness test is decisive for acceptance.
partial decar
...

SLOVENSKI STANDARD
SIST ISO 898-5:1996
01-april-1996
0HKDQVNHODVWQRVWLYH]QLKHOHPHQWRYGHO1DYRMQL]DWLþLLQSRGREQLGHOL]
QDYRML
Mechanical properties of fasteners -- Part 5: Set screws and similar threaded fasteners
not under tensile stresses
Propriétés mécaniques des éléments de fixation -- Partie 5: Vis sans tête et éléments de
fixation filetés similaires non soumis à des contraintes de traction
Ta slovenski standard je istoveten z: ISO 898-5:1980
ICS:
21.060.10 Sorniki, vijaki, stebelni vijaki Bolts, screws, studs
SIST ISO 898-5:1996 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST ISO 898-5:1996

---------------------- Page: 2 ----------------------

SIST ISO 898-5:1996
International Standard @ 89815
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONOMEXYHAPOJlHAR OPTAHH3AUHR no CTAHAAPTH3AUHH.ORGANlSATlON INTERNATIONALE DE hORMALISATION
Mechanical properties of fasteners -
'-
Part 5 : Set screws and similar threaded fasteners not
under tensile stresses
Propriétés mécaniques des éléments de fixation - Partie 5 : Vis sans tête et éléments de fixation filetés similaires non soumis a
des contraintes de traction
First edition - 1980-07-15
1 Lu UDC 621.882.219.4
Ref. No. IS0 898/5-1980 (E)
Descriptors : fasteners, screws, set screws, designation, materials specifications, chemical composition, mechanical properties, mechanical
' -
a
tests, hardness tests, decarburisation, torque.
8
Price based on 6 pages

---------------------- Page: 3 ----------------------

SIST ISO 898-5:1996
Foreword
IS0 (the International Organization for Standardization) is a worldwide federation of
national standards institutes (IS0 member bodies). The work of developing Inter-
national Standards is carried out through IS0 technical committees. Every member
body interested in a subject for which a technical committee has been set up has the
righ? to be represented on that committee. International organizations, governmental
and non-governmental, in liaison with EO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the IS0 Council.
International Standard IS0 û98/5 was developed by Technical Committee ISO/TC 2,
Fasteners, and was circulated to the member bodies in April 1979.
It has been approved by the member bodies of the following countries :
Australia Germany, F. R. Poland
Austria Hungary Romania
South Africa, Rep. of
Belgium India
Bulgaria Ireland Spain
Canada Italy Sweden
Switzerland
Chile Japan
Czechoslovakia Korea, Rep. of United Kingdom
Denmark Netherlands USA
Finland New Zealand USSR
France Norway Yugoslavia
No member body expressed disapproval of the document.
0 International Organization for Standardization, 1980 O
Printed in Switzerland

---------------------- Page: 4 ----------------------

SIST ISO 898-5:1996
INTERNATIONAL STANDARD IS0 898/5-1980 (E)
Mechanical properties of fasteners -
Part 5 : Set screws and similar threaded fasteners not
under tensile stresses
1
Scope and field of application ISOIR 80, Rockwell hardness test IB and C scales) for steel.
This International Standard specifies the mechanical properties ISOIR 81, Vickers hardness test for steel.
of set screws and similar fasteners not under tensile stresses in
the range from 1,6 up to and including 39 mm thread diameter IS0 615711, Surface discontinuities on bolts, screws and
which are made of carbon steel or alloy steel. studs’).
It does not apply to screws requiring special properties such as
-
specified tensile stresses (see IS0 89811 1;
3 Designation system
- weldability;
The property classes are designated by the symbols shown in
\-
table 1.
-
corrosion resistance (see IS0 3506);
The numerical part of the symbol represents 1/10 of the
-
ability to withstand temperatures above + 300 OC or
minimum Vickers hardness.
below - 50 OC.
The letter H in the symbol refers to hardness.
NOTE - Screws made from free-cutting steel should not be used
above + 250 OC.
2 References
Property class 14H 22H 33H 45H
ISOIR 79, Brinell hardness test for steel.
1) At present at the stage of draft.
1

---------------------- Page: 5 ----------------------

SIST ISO 898-5:1996
IS0 898/5-1980 (E)
4 Raw materials 5 Mechanical properties
Set screws shall be made of steel conforming to the re-
When tested by the methods specified in clause 6, the set
quirements specified in table 2. screws shall have, at ambient temperature, the mechanical pro-
perties specified in table 3.
For property class 45H, other materials may be used provided
that the torque test requirements in 6.4 are met.
Table 2 - Steel specifications
Chemical composition, %
Property class Material Heat treatment C P S
rnax. min. rnax. max.
Carbon steell)2) - 0.50 - 0,11 0,15
22H Carbon steel3) Quenched and tempered 0,50 - 0,05
33H Carbon steel3) Quenched and tempered 0.50 - 0.05
Quenched and temDered 0.50 0.19 0.05 0.05
45H Allov ~tee13)~)
1) Free-cutting steel may be used, with lead content 0,35 % rnax., phosphorus content 0,11 % rnax. and sulphur content 0.34 % rnax.
2) Case hardening is allowed in the case of square-head set screws.
Steel with lead content 0,35 % max. may be used.
3)
4) Shall contain one or more of alloying elements chromium, nickel, molybdenum, vanadium or boron.
Table 3 - Mechanical properties
Property class*
Mechanical properties
14H I 22H I 33H I 45H
min. I 140 I 220 I 330 1 450
Vickers hardness HV
min.
133 209 314 428
Brinell hardness HB, F = 30 02
max. I 276 285 418 532
- -
min. 75 95
- - -
max. 105
I
Rockwell hardness
-
min. - 33 45
-
30 44 53
max. I
-
Torque strength -
- I see table 5
Minimum height of non-decarburized thread zone, E
**
Maximum depth of complete decarburization, G mm - 0,015 0,015
Surface-hardness HV 0.3 max. - 320 450 580
Classes 14H, 22H and 33H are not for hexagon socket set screws.
**
No complete decarburization permitted in property class 45H.
2

---------------------- Page: 6 ----------------------

SIST ISO 898-5:1996
IS0 898/5-1980 (E)
6.2.1 Definitions
6 Test methods for determination of
mechanical properties
base metal hardness : The hardness closest to the surface
(when traversing from core to outside diameter) just before an
6.1 Hardness tests
increase or decrease occurs denoting carburization or decarbu-
rization.
Ha
...

n
Norme internationale 89815
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION*MEWlYHAPOflHAR OPrAHHBAUHR no CTAHAALAPTH3AUHH.OAGANlSATlON INTERNATIONALE DE NORMALISATION
Propriétés mécaniques des éléments de fixation -
.-
Partie 5 : Vis sans tête et éléments de fixation filetés
similaires non soumis à des contraintes de traction
Mechanical properties of fasteners - Part 5 : Set screws and similar threaded fasteners not under tensile stresses
Première édition - 1980-07-15
g CDU 621.882.219.4 Réf. no : IS0 89W5-1980 (FI
Descripteurs : élément de fixation, vis, vis sans tête, désignation, spécification de matière, composition chimique, propriété mécanique, essai
mécanique, essai de dureté, décarbonisation, couple de torsion.
ii
Prix basé sur 6 pages
s

---------------------- Page: 1 ----------------------
Avant-propos
L'ISO (Organisation internationale de normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (comités membres de I'ISO). L'élaboration
des Normes internationales est confiée aux comités techniques de I'ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
I'ISO, participent également aux travaux.
mentales, en liaison avec
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I'ISO.
La Norme internationale IS0 W/5 a été élaborée par le comité technique ISO/TC 2,
Eiéments de fixation, et a été soumise aux comités membres en avril 1979.
Les comités membres des pays suivants l'ont approuvée :
Pays-Bas
Afrique du Sud, Rép. d' Espagne
Allemagne, R. F. Finlande Pologne
Australie France Roumanie
Autriche Hongrie Royaume-Uni
Belgique Inde Suède
Suisse
Bulgarie Irlande
Canada Italie Tchécoslovaquie
Chili Japon URSS
Norvège USA
Corée, Rép. de
Danemark Nouvelle-Zélande Yougoslavie
Aucun comité membre ne l'a désapprouvée.
0 Organisation internationale de normalisation, 1980 O
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORM E I NTE R NAT1 O NALE IS0 898/519ûû (FI
Propriétés mécaniques des éléments de fixation -
Partie 5 : Vis sans tête et éléments de fixation filetés
similaires non soumis à des contraintes de traction
1 Objet et domaine d'application ISOIR 80, Essai de dureté Rockwell (échelles B et Ci pour
l'acier.
La présente Norme internationale spécifie les propriétés méca-
niques des vis sans tête et éléments de fixation filetés similaires, ISOIR 81, Essai de dureté Vickers pour l'acier.
non soumis à des contraintes de traction dans la gamme des
diamètres de filetages compris entre 1,6 et 39 mm, en acier au IS0 615711, Défauts affectant la surface des boulons, vis et
goujons. 1 1
carbone ou en acier allié.
Elle ne s'applique pas aux vis à propriétés spéciales telles que :
-
contraintes de traction spécifiées (voir IS0 89811 1;
3 Désignation
- aptitude au soudage;
Les classes de qualité sont désignées par les symboles du
tableau 1.
-
résistance à la corrosion (voir IS0 3%);
Le symbole numérique représente le 1110e de la dureté Vickers
- résistance aux températures supérieures à + 300 OC
minimale.
ou inférieures à - 50 OC.
La lettre H représente la dureté.
NOTE - Les vis en acier de décolletage ne doivent pas être utilisées
au-delà de + 250 OC.
Tableau 1 - Désignations des classes de qualité basées
sur la dureté Vickers
2 Références
I Classe de qualité I 14H I î2H I 33H 1 45H I
Dureté Vickers, HV min I 140 I 220 I 330 I 450 I
ISOIR 79, Essai de dureté Brinell pour l'acier.
Actuellement au stade de projet.
1)
1

---------------------- Page: 3 ----------------------
IS0 898/5-1980 (FI
4 Matières 5 Caractéristiques mécaniques
Les vis soumises aux méthodes d'essai spécifiées au chapitre 6
Les vis sans tête doivent être fabriquées en acier, conformé-
du tableau 2. doivent avoir, à la température ambiante, les caractéristiques
ment aux spécifications
mécaniques spécifiées dans le tableau 3.
D'autres aciers sont admissibles pour la classe 45H, à condition
qu'ils satisfassent aux exigences de l'essai de couple spécifié en
6.4.
Tableau 2 - Spécifications pour l'acier
Composition Composition chimique, chimique, % %
Classe Classe de de qualité qualité Acier Acier Traitement Traitement C C P P S S
rnax. rnax. rnin. rnin. rnax. rnax. rnax. rnax.
14H Acier au carbonel)2) - 03 - 0,11 0,15
I 14H I Acier au carbone1)2) 1 - I 0,50 I - I 0,11 I 0,15
22H 22H Acier Acier au au carbone3) carbone3) Trempé Trempé et et revenu revenu 09 09 ~ ~ 0.05 0.05 0,05 0,05
33H 33H Acier Acier au au carbone31 carbone31 Trempé Trempé et et revenu revenu 09 09 ~ ~ 0.05 0.05 0.05 0.05
45H 45H Acier Acier allié314) allié314)
Trempé Trempé et et revenu revenu 0,50 0,50 0,19 0,19 0.05 0.05 0.05 0.05
Acier de décolletage admis avec Pb rnax. = 0,35 %; P rnax. = 0.11 %; S rnax. = 0,34 %
1)
2) Cémentation admise dans le cas des vis à entraînement par carré.
3) Un acier avec Pb max. = 0,35 % peut être utilisé.
Doit contenir un ou plusieurs éléments d'alliage, tels que : chrome, nickel, molybdène, vanadium ou bore.
41
Tableau 3 - Caractéristiques mécaniques
Classe de qualité*
Caractéristiques mécaniques
I 14H I 22H I 33H 1 45H
min. 140 220 330 450
Dureté Vickers HV
max. 290 300 440 560
min. I 133 I 209 I 314 I 428
Dureté Brinell HB, F = 30 02
max. I 276 I 285 I 418 I 532
- -
min. 75 95
HRB
- - -
max. 105
Dureté Rockwell
-
- 33 45
min.
HRC
max. - 30 44 53
Résistance à la torsion I- I - I - I voir tableau 5
1 2 3
-
Hauteur minimale de la zone filetée non décarburée, E
-H 21 3Hi $4
xx
Profondeur maximale de décarburation complète, G mm - 0,015 0,015
Dureté suDerficielle. HV 0.3 max.
- 320 450 580
*
Classes de qualité 14H, î2H et 33H, à l'exception des vis sans tête à six-pans creux.
**
Pas de décarburation complète autorisée pour la classe de qualité 45H.
2

---------------------- Page: 4 ----------------------
IS0 898/5-1980 (F)
6 Méthodes d'essai pour la détermination 6.2.1 Définitions
des caractéristiques mécaniques
dureté du métal de base : Dureté mesurée au plus près de la
surface de l'élément (à partir du cœur jusqu'au diamètre exté-
6.1 Essais de dureté
rieur), à la limite où débute l'augmentation de la teneur en car-
bone ou la décarburation.
Les essais de dureté doivent être effectués aussi près que possi-
ble du centre de l'extrémité de la vis. Si la dureté maximale
décarburation : En général, manque de carbone à la surface
autorisée est dépassée, un nouvel essai doit être effectué sur
de matériaux ferreux (aciers).
une section droite à une distance de l'extrémité égale à 0,5 mm.
En cas de doute, l'essai de dureté Vickers est décisif pour
décarburation partielle : Décarburation correspondant à une
l'acceptation.
perte de carbone suffisante pour provoquer une légère décolo-
r
...