Plastics -- Polypropylene and propylene-copolymers -- Determination of thermal oxidative stability in air -- Oven method

Specifies a method for the determination of the resistance of moulded test specimens of propylene and propylene-copolymers to acclerated ageing at specified temperatures in the range from 100 to 150oC in a forced draught oven. Rotating specimen holders are recommended.- The time to failure is determined by visual examination and taken as the number of days after which a specimen shows localized crazing, crumbling and/or discoloration. The test may be conducted at several temperatures and the data interpreted by the use of the Arrhenius relation.

Plastiques -- Polypropylène et copolymères de propylène -- Détermination de la stabilité à l'oxydation à chaud dans l'air -- Méthode à l'étuve

La présente Norme internationale spécifie une méthode de détermination de la résistance d'éprouvettes moulées, en polypropylène ou copolymères du propylène, au vieillissement accéléré à la chaleur en présence d'air, dans une étuve à circulation d'air forcé. La méthode représente une tentative d'estimation de la durée de vie en service des pièces en plastiques propyléniques. La stabilité déterminée par la présente méthode n'est pas directement liée à l'aptitude du matériau à une utilisation dans différentes conditions d'environnement.  NOTE - Les niveaux thermiques spécifiés sont considérés comme suffisamment sévères pour entraîner la dégradation, en un temps raisonnable, des types commerciaux de plastique propylénique résistant à la chaleur. Si on le désire, des températures plus basses peuvent être appliquées pour estimer les performances de types de plastique propylénique de stabilité plus faible à la chaleur.

Polimerni materiali - Polipropilen in kopolimeri propilena - Določanje termično-oksidativne stabilnosti na zraku - Metoda s pečjo

General Information

Status
Withdrawn
Publication Date
31-May-1996
Withdrawal Date
30-Apr-2000
Current Stage
9900 - Withdrawal (Adopted Project)
Start Date
01-May-2000
Due Date
01-May-2000
Completion Date
01-May-2000

Buy Standard

Standard
ISO 4577:1983 - Plastics -- Polypropylene and propylene-copolymers -- Determination of thermal oxidative stability in air -- Oven method
English language
4 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 4577:1996
English language
4 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day
Standard
ISO 4577:1983 - Plastiques -- Polypropylene et copolymeres de propylene -- Détermination de la stabilité a l'oxydation a chaud dans l'air -- Méthode a l'étuve
French language
4 pages
sale 15% off
Preview
sale 15% off
Preview
Standard
ISO 4577:1983 - Plastiques -- Polypropylene et copolymeres de propylene -- Détermination de la stabilité a l'oxydation a chaud dans l'air -- Méthode a l'étuve
French language
4 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

International Standard
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWEIK,QYHAPO~HAR OPl-AHM3AUHR fl0 CTAHL1APTH3A~HM@ORGANISATION INTERNATIONALE DE NORMALISATION
Plastics - Polypropylene and propylene-copolymers -
Determination of thermal oxidative stability in air -
Oven method
Plas tiques - Polyprop yltke et copolymkres de prop ylkne - Determination de Ia stabilitb ti l’ox yda tion S chaud dans l’air -
AMhode a IWuve
. .
First edition - 1983-08-15
UDC 678.742.3-13 : 620.19354
Ref. No. ISO 4577-1983 (EI
Descriptors : plastics, polypropylene, stability tests, thermal stability, high temperature tests,
Oxidation tests, ageing tests (materials).
Price based on 4 pages

---------------------- Page: 1 ----------------------
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of
national Standards bodies (ISO member bodies). The work of developing International
Standards is carried out through ISO technical committees. Every member body
interested in a subject for which a technical committee has been authorized has the
right to be represented on that committee. International organizations, governmental
and non-governmentai, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the ISO Council.
International Standard ISO 4577 was developed by Technical Committee ISO/TC 61,
Plastics, and was circulated to the member bodies in May 1982.
lt has been approved by the member bodies of the following countries:
Australia Germany, F. R. Romania
Austria Hungary South Africa, Rep. of
Belgium Iran Spain
B razil Israel Sri Lanka
Canada Italy Sweden
Jamaica
China Switzerland
Czechoslovakia Japan United Kingdom
Egypt, Arab Rep. of Korea, Rep. of USA
Finland Netherlands USSR
France Poland
The member body of the following country expressed disapproval of the document on
technical grounds
India
0 International Organization for Standardization, 1983
Printed in Switzerland

---------------------- Page: 2 ----------------------
ISO 45774983 (E)
INTERNATIONAL STANDARD
Plastics - Polypropylene and propylene-copolymers -
Determination of thermal oxidative stability in air -
Oven method
1 Scope and field of application 3 Principle
This International Standard specifies a method for the deter- Accelerated ageing of test specimens by heat in the presence of
mination of the resistance of moulded test specimens of air using a forced draught oven. Visual examination and deter-
polypropylene and propylene-copolymers to accelerated ageing mination of the time to failure.
by heat in the presence of air using a forced draught oven.
Under the severe conditions of this test, the specimens
undergo degradation at a rate dependent upon the thermal en-
The method represents an attempt to estimate the Service life
durante of the propylene plastic under examination.
of Parts fabricated from propylene plastics.
For the purpose of this International Standard, the time to
The stability determined by this method is not directly related
failure of the material is taken as the number of days after
to the suitability of the material for use when different en-
vvhich the specimen Shows localized crazing, crumbling and/or
vironmental conditions prevail.
discoloration.
If a more reliable estimate of the life-temperature relationship of
NOTE - The specified thermal levels are considered sufficiently severe
to Cause failure of commercial grades of heat-stable propylene plastics propylene plastics is required, the test may be conducted at
within a reasonable period of time. If desired, lower temperatures tan several temperatures and the data interpreted through use of
be applied to estimate the performante of propylene plastics with
the Arrhenius relation, by plotting the logarithms of times to
lower heat stabilities.
failure against the reciprocals of the temperatures in kelvins.
Temperatures in the range from 100 to 150 OC, with intervals of
10 OC, are suggested for this purpose.
2 References
4 Apparatus
Standard atmospheres for conditioning
ISO 291, plastics -
and tes ting.
4.1 Oven, mechanical convection type, capable of controlled
circulation of air, with adjustable air intake and exhaust, equip-
ISO 1133, Plastics - Determination of the melt flow rate of
ped with a specimen holder and a temperature control System
thermoplas tics.
capable of adjustment to meet the following conditions:
a) exhaust rate: at least one oven-chamber volume in 10
ISO 1191, Plastics - Polyeth ylenes and polyprop ylenes in
min ;
dilu te solu tion - Determination of viscosity number and of
limiting viscosity number.
b) air velocity : from 0,75 to 1 m/s at any oven Position oc-
cupied by the test specimens;
ISO 1873, Plastics -
Polyprop ylene and prop ylene-copolymer c) temperature control: range up to 200 OC and with con-
thermoplas tics - trol throughout the working range to the nearest 1 OC. The
temperature control shall include a device to prevent
Part I : Designa tion.
temperature overrides. lt is recommended that a device be
Part 2: Determination o f properties. 1) used for recording the temperature inside the oven.
1) At present at the Stage of draft.
1

---------------------- Page: 3 ----------------------
ISO4577-1983E)
4.2 Thermometers, covering the temperature range up to Illustrations of suitable apparatus for biaxially and uniaxially
200 OC, graduated in 1 OC intervals or better. Esch ther- rotated specimen holders are shown in figures 1 and 2 respec-
mometer shall be tested for bul
...

SLOVENSKI STANDARD
SIST ISO 4577:1996
01-junij-1996
3ROLPHUQLPDWHULDOL3ROLSURSLOHQLQNRSROLPHULSURSLOHQD'RORþDQMHWHUPLþQR
RNVLGDWLYQHVWDELOQRVWLQD]UDNX0HWRGDVSHþMR
Plastics -- Polypropylene and propylene-copolymers -- Determination of thermal
oxidative stability in air -- Oven method
Plastiques -- Polypropylène et copolymères de propylène -- Détermination de la stabilité
à l'oxydation à chaud dans l'air -- Méthode à l'étuve
Ta slovenski standard je istoveten z: ISO 4577:1983
ICS:
83.080.20 Plastomeri Thermoplastic materials
SIST ISO 4577:1996 en
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST ISO 4577:1996

---------------------- Page: 2 ----------------------

SIST ISO 4577:1996
International Standard
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWEIK,QYHAPO~HAR OPl-AHM3AUHR fl0 CTAHL1APTH3A~HM@ORGANISATION INTERNATIONALE DE NORMALISATION
Plastics - Polypropylene and propylene-copolymers -
Determination of thermal oxidative stability in air -
Oven method
Plas tiques - Polyprop yltke et copolymkres de prop ylkne - Determination de Ia stabilitb ti l’ox yda tion S chaud dans l’air -
AMhode a IWuve
. .
First edition - 1983-08-15
UDC 678.742.3-13 : 620.19354
Ref. No. ISO 4577-1983 (EI
Descriptors : plastics, polypropylene, stability tests, thermal stability, high temperature tests,
Oxidation tests, ageing tests (materials).
Price based on 4 pages

---------------------- Page: 3 ----------------------

SIST ISO 4577:1996
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of
national Standards bodies (ISO member bodies). The work of developing International
Standards is carried out through ISO technical committees. Every member body
interested in a subject for which a technical committee has been authorized has the
right to be represented on that committee. International organizations, governmental
and non-governmentai, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the technical committees are circulated to
the member bodies for approval before their acceptance as International Standards by
the ISO Council.
International Standard ISO 4577 was developed by Technical Committee ISO/TC 61,
Plastics, and was circulated to the member bodies in May 1982.
lt has been approved by the member bodies of the following countries:
Australia Germany, F. R. Romania
Austria Hungary South Africa, Rep. of
Belgium Iran Spain
B razil Israel Sri Lanka
Canada Italy Sweden
Jamaica
China Switzerland
Czechoslovakia Japan United Kingdom
Egypt, Arab Rep. of Korea, Rep. of USA
Finland Netherlands USSR
France Poland
The member body of the following country expressed disapproval of the document on
technical grounds
India
0 International Organization for Standardization, 1983
Printed in Switzerland

---------------------- Page: 4 ----------------------

SIST ISO 4577:1996
ISO 45774983 (E)
INTERNATIONAL STANDARD
Plastics - Polypropylene and propylene-copolymers -
Determination of thermal oxidative stability in air -
Oven method
1 Scope and field of application 3 Principle
This International Standard specifies a method for the deter- Accelerated ageing of test specimens by heat in the presence of
mination of the resistance of moulded test specimens of air using a forced draught oven. Visual examination and deter-
polypropylene and propylene-copolymers to accelerated ageing mination of the time to failure.
by heat in the presence of air using a forced draught oven.
Under the severe conditions of this test, the specimens
undergo degradation at a rate dependent upon the thermal en-
The method represents an attempt to estimate the Service life
durante of the propylene plastic under examination.
of Parts fabricated from propylene plastics.
For the purpose of this International Standard, the time to
The stability determined by this method is not directly related
failure of the material is taken as the number of days after
to the suitability of the material for use when different en-
vvhich the specimen Shows localized crazing, crumbling and/or
vironmental conditions prevail.
discoloration.
If a more reliable estimate of the life-temperature relationship of
NOTE - The specified thermal levels are considered sufficiently severe
to Cause failure of commercial grades of heat-stable propylene plastics propylene plastics is required, the test may be conducted at
within a reasonable period of time. If desired, lower temperatures tan several temperatures and the data interpreted through use of
be applied to estimate the performante of propylene plastics with
the Arrhenius relation, by plotting the logarithms of times to
lower heat stabilities.
failure against the reciprocals of the temperatures in kelvins.
Temperatures in the range from 100 to 150 OC, with intervals of
10 OC, are suggested for this purpose.
2 References
4 Apparatus
Standard atmospheres for conditioning
ISO 291, plastics -
and tes ting.
4.1 Oven, mechanical convection type, capable of controlled
circulation of air, with adjustable air intake and exhaust, equip-
ISO 1133, Plastics - Determination of the melt flow rate of
ped with a specimen holder and a temperature control System
thermoplas tics.
capable of adjustment to meet the following conditions:
a) exhaust rate: at least one oven-chamber volume in 10
ISO 1191, Plastics - Polyeth ylenes and polyprop ylenes in
min ;
dilu te solu tion - Determination of viscosity number and of
limiting viscosity number.
b) air velocity : from 0,75 to 1 m/s at any oven Position oc-
cupied by the test specimens;
ISO 1873, Plastics -
Polyprop ylene and prop ylene-copolymer c) temperature control: range up to 200 OC and with con-
thermoplas tics - trol throughout the working range to the nearest 1 OC. The
temperature control shall include a device to prevent
Part I : Designa tion.
temperature overrides. lt is recommended that a device be
Part 2: Determination o f properties. 1) used for recording the temperature inside the oven.
...

Norme internationale
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWE~YHAPOJJHAR OPTAHHSAL&lR fl0 CTAHAAPTM3AWWORGANISAtlON INTERNATIONALE Di NORMALISATION
Polypropylène et copolymères de
Plastiques -
propylène - Détermination de la stabilité à l’oxydation
à chaud dans l’air - Méthode à ,l’étuve
Determination of thermal oxidative stabiiity in air - Oven method
Plastics - Pofyprop ylene and prop ylene-copolymers -
Première édition - 1983-08-15
Réf. no : ISO 4577-1983 (F)
z CDU 678.742.3-13 : 620.19354
Y
Descripteurs : matiére plastique, polypropyléne, essai de stabilité, stabilité thermique, essai à haute température, essai d’oxydation, essai de
vieillissement.
Prix basé sur 4 pages

---------------------- Page: 1 ----------------------
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO.
La Norme internationale ISO 4577 a été élaborée par le comité technique ISO/TC 61,
Plastiques, et a été soumise aux comités membres en mai 1972.
Les comités membres des pays suivants l’ont approuvée:
Afrique du Sud, Rép. d’ Espagne Pologne
Finlande Roumanie
Allemagne, R. F.
Australie France Royaume-Uni
Autriche Hongrie
Sri Lanka
Belgique Iran Suède
Brésil Israël Suisse
Canada Italie Tchécoslovaquie
Chine Jamaïque URSS
Corée, Rép. de Japon USA
Égypte, Rép. arabe d’ Pays- Bas
Le comité membre du pays suivant l’a désapprouvée pour des raisons techniques:
Inde
@ Organisation internationale de normalisation, 1983 l
Imprimé en Suisse

---------------------- Page: 2 ----------------------
ISO 45774983 (F)
NORME INTERNATIONALE
Polypropylène et copolymères de ,
Plastiques -
Détermination de la stabilité à l’oxydation
propylène -
à chaud dans l’air - Méthode à l’étuve
1 Objet et domaine d’application 3 Principe
La présente Norme internationale spécifie une méthode de Vieillissement accéléré des éprouvettes à la chaleur en présence
détermination de la résistance d’éprouvettes moulées, en poly- d’air, dans une étuve à circulation d’air forcé. Examen visuel et
propylène ou copolymères du propylène, au vieillissement détermination du temps de dégradation du matériau.
accéléré à la chaleur en présence d’air, dans une étuve à circu-
lation d’air forcé. Dans les conditions sévères de cet essai, les éprouvettes subis-
sent une dégradation à une vitesse qui dépend de l’endurance
thermique du plastique propylénique essayé.
La méthode représente une tentative d’estimation de la durée
de vie en service des pièces en plastiques propyléniques.
Pour l’application de la présente Norme internationale, le temps
de dégradation du matériau est noté comme étant le temps, en
La stabilité déterminée par la présente méthode n’est pas direc- jours, au bout duquel apparaissent des craquelures localisées,
tement liée à l’aptitude du matériau à une utilisation dans diffé-
une désagrégation et/ou une altération de couleur.
rentes conditions d’environnement.
Si une estimation plus valable de la relation durée de vie-
température des plastiques propyléniques est requise, l’essai
NOTE - Les niveaux thermiques spécifiés sont considérés comme suf-
peut être effectué à plusieurs températures et les résultats inter-
fisamment sévères pour entraîner la dégradation, en un temps raison-
prétés au moyen de la relation d’Arrhenius, en tracant la courbe
nable, des types commerciaux de plastique propylénique résistant à la
chaleur. Si on le désire, des températures plus basses peuvent être
du logarithme des temps de dégradation en’ fonction de
appliquées pour estimer les performances de types de plastique propy-
l’inverse de la température en kelvins. La gamme de températu-
Iénique de stabilité plus faible à la chaleur.
res de 100 à 150 OC, en échelons de 10 OC, est suggérée dans ce
but.
2 Références
4 Appareillage
ISO 291, Plastiques - Atmosphères normales de conditionne-
4.1 Étuve, du type à convection mécanique apte à un recy-
ment et d’essai.
clage controlé de l’air, avec entrée et extraction d’air réglables,
munie d’un porte-éprouvettes et d’un systéme de réglage des
températures, apte aux réglages nécessaires pour répondre aux
Détermination de l’indice de fluidité à
ISO 1133, Plastiques -
conditions suivantes :
chaud.
un volume au moins égal au
a) vitesse d’extraction :
volume intérieur de l’étuve, en 10 min;
ISO 1191, Matières plastiques - Polyéthylènes et pofypropylè-
nes en solution diluée - Dé termina tion de l’indice de viscosité
b) vitesse de l’air: de 0,75 à 1 m/s dans toutes les posi-
et de l’indice limite de viscosite.
tions occupées par les éprouvettes;
c) régulation de la température : dans une gamme de tem-
pératures jusqu’à 200 OC et avec une précision de + 1 OC
ISO 1873, Plastiques - Materiaux thermoplastiques à base de
dans tout l’espace d’essai. La régulation de la température
pofypropylène et de copolymeres de propylène -
doit comporter un dispositif permettant d’éviter les sur-
Partie 7 : Désignation.
chauffes. II est recommandé d’utiliser un dispositif pour
l’enregistrement de la température à l’intérieur de l’étuve.
Partie 2 : Dé termina tion des carat téris tiques. 1)
1) Actuellement au stade de projet.

---------------------- Page: 3 ----------------------
ISO 45774983 (FI
4.2 Thermomètres, couvrant une gamme de températures
Des illustrations d’appareils appropriés montrant respective-
jusqu’à 200 OC et gradués au moins en intervalles de 1 OC. Cha-
ment un dispositif rotatif biaxial et un dispositif monoaxial sont
que thermomètre doit être essayé pour vérifier la stabilité du
données dans les figures 1 et 2.
réservoir et étalonné à 150 OC.
La technique de rotation biaxiale augmente la probabilité pour
que toutes les éprouvettes soient exposées de facon similaire.
NOTE
...

Norme internationale
INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWE~YHAPOJJHAR OPTAHHSAL&lR fl0 CTAHAAPTM3AWWORGANISAtlON INTERNATIONALE Di NORMALISATION
Polypropylène et copolymères de
Plastiques -
propylène - Détermination de la stabilité à l’oxydation
à chaud dans l’air - Méthode à ,l’étuve
Determination of thermal oxidative stabiiity in air - Oven method
Plastics - Pofyprop ylene and prop ylene-copolymers -
Première édition - 1983-08-15
Réf. no : ISO 4577-1983 (F)
z CDU 678.742.3-13 : 620.19354
Y
Descripteurs : matiére plastique, polypropyléne, essai de stabilité, stabilité thermique, essai à haute température, essai d’oxydation, essai de
vieillissement.
Prix basé sur 4 pages

---------------------- Page: 1 ----------------------
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale
d’organismes nationaux de normalisation (comités membres de I’ISO). L’élaboration
des Normes internationales est confiée aux comités techniques de I’ISO. Chaque
comité membre intéressé par une étude a le droit de faire partie du comité technique
correspondant. Les organisations internationales, gouvernementales et non gouverne-
mentales, en liaison avec I’ISO, participent également aux travaux.
Les projets de Normes internationales adoptés par les comités techniques sont soumis
aux comités membres pour approbation, avant leur acceptation comme Normes inter-
nationales par le Conseil de I’ISO.
La Norme internationale ISO 4577 a été élaborée par le comité technique ISO/TC 61,
Plastiques, et a été soumise aux comités membres en mai 1972.
Les comités membres des pays suivants l’ont approuvée:
Afrique du Sud, Rép. d’ Espagne Pologne
Finlande Roumanie
Allemagne, R. F.
Australie France Royaume-Uni
Autriche Hongrie
Sri Lanka
Belgique Iran Suède
Brésil Israël Suisse
Canada Italie Tchécoslovaquie
Chine Jamaïque URSS
Corée, Rép. de Japon USA
Égypte, Rép. arabe d’ Pays- Bas
Le comité membre du pays suivant l’a désapprouvée pour des raisons techniques:
Inde
@ Organisation internationale de normalisation, 1983 l
Imprimé en Suisse

---------------------- Page: 2 ----------------------
ISO 45774983 (F)
NORME INTERNATIONALE
Polypropylène et copolymères de ,
Plastiques -
Détermination de la stabilité à l’oxydation
propylène -
à chaud dans l’air - Méthode à l’étuve
1 Objet et domaine d’application 3 Principe
La présente Norme internationale spécifie une méthode de Vieillissement accéléré des éprouvettes à la chaleur en présence
détermination de la résistance d’éprouvettes moulées, en poly- d’air, dans une étuve à circulation d’air forcé. Examen visuel et
propylène ou copolymères du propylène, au vieillissement détermination du temps de dégradation du matériau.
accéléré à la chaleur en présence d’air, dans une étuve à circu-
lation d’air forcé. Dans les conditions sévères de cet essai, les éprouvettes subis-
sent une dégradation à une vitesse qui dépend de l’endurance
thermique du plastique propylénique essayé.
La méthode représente une tentative d’estimation de la durée
de vie en service des pièces en plastiques propyléniques.
Pour l’application de la présente Norme internationale, le temps
de dégradation du matériau est noté comme étant le temps, en
La stabilité déterminée par la présente méthode n’est pas direc- jours, au bout duquel apparaissent des craquelures localisées,
tement liée à l’aptitude du matériau à une utilisation dans diffé-
une désagrégation et/ou une altération de couleur.
rentes conditions d’environnement.
Si une estimation plus valable de la relation durée de vie-
température des plastiques propyléniques est requise, l’essai
NOTE - Les niveaux thermiques spécifiés sont considérés comme suf-
peut être effectué à plusieurs températures et les résultats inter-
fisamment sévères pour entraîner la dégradation, en un temps raison-
prétés au moyen de la relation d’Arrhenius, en tracant la courbe
nable, des types commerciaux de plastique propylénique résistant à la
chaleur. Si on le désire, des températures plus basses peuvent être
du logarithme des temps de dégradation en’ fonction de
appliquées pour estimer les performances de types de plastique propy-
l’inverse de la température en kelvins. La gamme de températu-
Iénique de stabilité plus faible à la chaleur.
res de 100 à 150 OC, en échelons de 10 OC, est suggérée dans ce
but.
2 Références
4 Appareillage
ISO 291, Plastiques - Atmosphères normales de conditionne-
4.1 Étuve, du type à convection mécanique apte à un recy-
ment et d’essai.
clage controlé de l’air, avec entrée et extraction d’air réglables,
munie d’un porte-éprouvettes et d’un systéme de réglage des
températures, apte aux réglages nécessaires pour répondre aux
Détermination de l’indice de fluidité à
ISO 1133, Plastiques -
conditions suivantes :
chaud.
un volume au moins égal au
a) vitesse d’extraction :
volume intérieur de l’étuve, en 10 min;
ISO 1191, Matières plastiques - Polyéthylènes et pofypropylè-
nes en solution diluée - Dé termina tion de l’indice de viscosité
b) vitesse de l’air: de 0,75 à 1 m/s dans toutes les posi-
et de l’indice limite de viscosite.
tions occupées par les éprouvettes;
c) régulation de la température : dans une gamme de tem-
pératures jusqu’à 200 OC et avec une précision de + 1 OC
ISO 1873, Plastiques - Materiaux thermoplastiques à base de
dans tout l’espace d’essai. La régulation de la température
pofypropylène et de copolymeres de propylène -
doit comporter un dispositif permettant d’éviter les sur-
Partie 7 : Désignation.
chauffes. II est recommandé d’utiliser un dispositif pour
l’enregistrement de la température à l’intérieur de l’étuve.
Partie 2 : Dé termina tion des carat téris tiques. 1)
1) Actuellement au stade de projet.

---------------------- Page: 3 ----------------------
ISO 45774983 (FI
4.2 Thermomètres, couvrant une gamme de températures
Des illustrations d’appareils appropriés montrant respective-
jusqu’à 200 OC et gradués au moins en intervalles de 1 OC. Cha-
ment un dispositif rotatif biaxial et un dispositif monoaxial sont
que thermomètre doit être essayé pour vérifier la stabilité du
données dans les figures 1 et 2.
réservoir et étalonné à 150 OC.
La technique de rotation biaxiale augmente la probabilité pour
que toutes les éprouvettes soient exposées de facon similaire.
NOTE
...

Questions, Comments and Discussion