Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)

Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)

ABSTRACT
This specification covers the requirements and test methods for the material, dimensions, and workmanship, and the properties of extruded sheet, rod and tubular bar manufactured from Poly(Vinylidene Fluoride) (PVDF). The type of PVDF shape product may be categorized by type, grade and class depending on resin and filler compositions. Each type of shape may be categorized into one of several grades as follows: Grade 1 - unmodified virgin-extruded or compression molded product made using only 100 % virgin PVDF material; Grade 2 - general purpose-extruded or compression molded product made using up to 20 % PVDF regrind developed during internal processing steps may be used; and Grade 3 - recycled-extruded or compression molded product made using up to 100 % recycled PVDF resin. The type, class and grade is further differentiated based on dimensional stability (elevated temperature excursion test), and dimensional requirements. Materials shall be tested and the individual grades shall conform to specified values of the physical properties such as tensile strength, tensile elongation, tensile modulus, dimensional stability, flexural modulus, and Izod impact; and dimensional properties such as diameter tolerance, roundness, camber, thickness tolerance, length camber, and width bow.
SCOPE
1.1 This specification covers the requirements and test methods for the material, dimensions, and workmanship, and the properties of extruded sheet, rod and tubular bar manufactured from PVDF.
1.2 The properties included in this specification are those required for the compositions covered. Requirements necessary to identify particular characteristics important to specialized applications may be described by using the classification system given in Section 4.
1.3 This specification allows for the use of recycled plastics (as defined in Guide D 5033).
1.4 The values stated in English units are to be regarded as the standard in all property and dimensional tables. For reference purposes, SI units are also included in Tables X and S-PVDF only.
1.5 The following precautionary caveat pertains only to the test method portions of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.
Note 1—There is no similar or equivalent ISO standard. ISO 12086-1 and ISO 12086-2 have pertinent information.

General Information

Status
Historical
Publication Date
31-Jan-2009
ICS
83.080.20 - Thermoplastic materials
Technical Committee
D20 - Plastics
Drafting Committee
D20.15 - Thermoplastic Materials
Current Stage
Ref Project

Relations

Replaces
ASTM D6713-01 - Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)
Effective Date
01-Feb-2009
Replaced By
ASTM D6713-14 - Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)
Effective Date
01-May-2014

Buy Standard

ASTM D6713-01(2009) - Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)ASTM D6713-01(2009) - Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)
PreviousNext
Technical specification
ASTM D6713-01(2009) - Standard Specification for Extruded and Compression Molded Shapes Made from Poly(Vinylidene Fluoride) (PVDF)
English language
5 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:D6713 −01(Reapproved 2009)
Standard Specification for
Extruded and Compression Molded Shapes Made from
1
Poly(Vinylidene Fluoride) (PVDF)
This standard is issued under the fixed designation D6713; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope D790 Test Methods for Flexural Properties of Unreinforced
and Reinforced Plastics and Electrical Insulating Materi-
1.1 This specification covers the requirements and test
als
methods for the material, dimensions, and workmanship, and
D883 Terminology Relating to Plastics
the properties of extruded sheet, rod and tubular bar manufac-
D1600 Terminology forAbbreviatedTerms Relating to Plas-
tured from PVDF.
tics
1.2 The properties included in this specification are those
D3222 Specification for Unmodified Poly(Vinylidene Fluo-
required for the compositions covered. Requirements neces-
ride) (PVDF) Molding Extrusion and Coating Materials
sary to identify particular characteristics important to special-
D3892 Practice for Packaging/Packing of Plastics
ized applications may be described by using the classification
D4000 Classification System for Specifying Plastic Materi-
system given in Section 4.
als
D5033 GuideforDevelopmentofASTMStandardsRelating
1.3 This specification allows for the use of recycled plastics
(as defined in Guide D5033). to Recycling and Use of Recycled Plastics (Withdrawn
3
2007)
1.4 The values stated in English units are to be regarded as
4
the standard in all property and dimensional tables. For 2.2 ANSI Standard:
Z1.4-1993 Sampling Procedures and Tables for Inspection
reference purposes, SI units are also included in Tables X and
S-PVDF only. by Attributes
1.5 The following precautionary caveat pertains only to the
3. Terminology
test method portions of this specification. This standard does
not purport to address all of the safety concerns, if any, 3.1 Definitions:
associated with its use. It is the responsibility of the user of this
3.1.1 regrind (plastic), n—a product or scrap such as sprues
standard to establish appropriate safety and health practices
and runners that have been reclaimed by shredding and
and determine the applicability of regulatory requirements
granulating for use in-house. D5033
prior to use.
3.1.2 For definitions of other technical terms pertaining to
NOTE 1—There is no similar or equivalent ISO standard. ISO 12086-1
plastics used in this specification, see Terminology D883 or
and ISO 12086-2 have pertinent information.
Guide D5033.
3.2 Definitions of Terms Specific to This Standard:
2. Referenced Documents
3.2.1 recycled-plastic shape, n—a product made from up to
2
2.1 ASTM Standards:
100 % post-consumer material.
D256 Test Methods for Determining the Izod Pendulum
3.2.2 rod, n—an extruded solid cylindrical shape with a
Impact Resistance of Plastics
1
minimum diameter of ⁄16 in.
D638 Test Method for Tensile Properties of Plastics
3.2.3 sheet, n—flat stock greater than and including 0.010
in. thickness.
1
This specification is under the jurisdiction of ASTM Committee D20 on
3.2.4 tubular bar, n—extruded annular shapes with mini-
Plastics and is the direct responsibility of Subcommittee D20.15 on Thermoplastic
1 1
mum inside diameter of ⁄16 in., and a minimum wall of ⁄4 in.
Materials.
Current edition approved Feb. 1, 2009. Published March 2009. Originally
approved in 2001. Last previous edition approved in 2001 as D6713 - 01. DOI:
10.1520/D6713-01R09.
2 3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or The last approved version of this historical standard is referenced on
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM www.astm.org.
4
Standards volume information, refer to the standard’s Document Summary page on Available fromAmerican National Standards Institute (ANSI), 25 W. 43rd St.,
the ASTM website. 4th Floor, New York, NY 10036, http://www.ansi.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D6713−01 (2009)
3.2.5 unmodified virgin plastic shape, n—a product pro- system uses predefined cells to refer to specific aspects of this
duced from virgin plastic, as furnished by a manufacturer, with specification as illustrated below:
no additives or processing aids.
4.5.1 Examples:
4.5.1.1 Example 1—Product made from unfilled virgin
4. Classification and Material PVDF:
CELL CALLOUT: S-PVDF0111
4.1 Product shape and size as defined in the applicable
purchase order.
where:
S-PVDF01 = product made from PVDF in accordance with
4.2 Thisspecificatio
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM D1238-23a(Test Method)
Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer

SIGNIFICANCE AND USE
5.1 This test method is particularly useful for quality control tests on thermoplastics.  
5.2 The data produced by this test method serves to indicate the uniformity of the flow rate of the polymer as made by an individual process. It is not to be used as an indication of uniformity of other properties without valid correlation with data from other tests.  
5.3 The flow rate obtained with the extrusion plastometer is not a fundamental polymer property. It is an empirically defined parameter critically influenced by the physical properties and molecular structure of the polymer and the conditions of measurement. The rheological characteristics of polymer melts depend on a number of variables. It is possible that the values of these variables occurring in this test will differ substantially from those in large-scale processes, which would result in data that does not correlate directly with processing behavior.  
5.4 Measure the flow rate of a material using any of the conditions listed for the material in X4.1. For many materials, there are specifications that require the use of this test method, but with some procedural modifications that take precedence when adhering to the specification. Therefore, it is advisable to refer to that material specification before using this test method. Table 1 in Classification D4000 lists the ASTM materials standards that currently exist. An alternative test method for poly (vinyl chloride) (PVC) compounds is found in Test Method D3364.  
5.5 Additional characterization of a material can be obtained if more than one condition is used. In the case that two or more conditions are employed, a Flow Rate Ratio (FRR) is obtained by dividing the flow rate at one condition by the flow rate at another condition. Procedure D provides one method to measure more than one condition in a single charge.  
5.6 Frequently, variations in test technique, apparatus geometry, or test conditions, which defy all but the most careful scrutiny, exist...
SCOPE
1.1 This test method covers the determination of the rate of extrusion of molten thermoplastic resins using an extrusion plastometer.  
1.2 The values stated in SI units are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This standard and ISO 1133 address the same subject matter, but differ in technical content.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    19 pages
    English language
    sale 15% off
  • Standard
    19 pages
    English language
    sale 15% off
ASTM
ASTM D6040-18(2023)(Guide)
Standard Guide to Standard Test Methods for Unsintered Polytetrafluoroethylene (PTFE) Extruded Film or Tape

ABSTRACT
This guide identifies the standard test methods to use in evaluating unsintered extruded films or tapes manufactured from polytetrafluoroethylene (PTFE). The test methods covered here shall be capable of investigating the following material properties: width; thickness; tensile properties (tensile strength and elongation); specificat gravity (relative density); residual extrusion aids or other volatile components; dielectric constant; volume resistivity; dielectric breakdown voltage; and unit weight.
SCOPE
1.1 This guide identifies test methods to use in evaluating unsintered extruded films or tapes manufactured from polytetrafluoroethylene.  
1.2 The values stated in SI units as detailed in IEEE/ASTM SI 10, are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This test method is equivalent to ISO 12086-2:2006 in the measurement of tensile properties, specific gravity, and dielectric constant. These are in ISO 12086-2:2006, sections 8.2.2, 10.6 and 8.1.1. It is not equivalent to ISO 12086-2:2006 in any other measurement or section..  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    3 pages
    English language
    sale 15% off
ASTM
ASTM D2561-17(2023)(Test Method)
Standard Test Method for Environmental Stress-Crack Resistance of Blow-Molded Polyethylene Containers

SIGNIFICANCE AND USE
5.1 When properly used, these procedures serve to isolate such factors as material, blow-molding conditions, post-treatment, and so forth, on the stress-crack resistance of the container.  
5.2 Environmental stress cracking of blow-molded containers is governed by many factors. Since variance of any of these factors can change the environmental stress-crack resistance of the container, the test results are representative only of a given test performed under defined conditions in the laboratory. The reproducibility of results between laboratories on containers made on more than one machine from more than one mold has not been established.  
5.3 Results can be used for estimating the shelf life of blow-molded containers in terms of their resistance to environmental stress cracking provided this is done against a rigorous background of practical field experience and reproducible test data.
SCOPE
1.1 Under certain conditions of stress, and in the presence of environments such as soaps, wetting agents, oils, or detergents, blow-molded polyethylene containers exhibit mechanical failure by cracking at stresses appreciably below those that would cause cracking in the absence of these environments.  
1.2 This test method measures the environmental stress crack resistance of blow-molded containers, which is the summation of the influence of container design, resin, blow-molding conditions, post treatment, or other factors that can affect this property. Three procedures are provided as follows:  
1.2.1 Procedure A, Stress-Crack Resistance of Containers to Potential Stress-cracking Liquids—This procedure is particularly useful for determining the effect of container design on stress-crack resistance or the stress-crack resistance of a proposed container that contains a liquid product.  
1.2.2 Procedure B, Stress-Crack Resistance of a Specific Container to Polyoxyethylated Nonylphenol (CAS 68412-54-4), a Stress-Cracking Agent—The conditions of test described in this procedure are designed for testing containers made from Class 3 polyethylene Specification D4976. Therefore, this procedure is recommended for containers made from Class 3 polyethylene only. This procedure is particularly useful for determining the effect of resin on the stress-crack resistance of the container.  
1.2.3 Procedure C, Controlled Elevated Pressure Stress-Crack Resistance of a Specific Container to Polyoxyethylated Nonylphenol (CAS 68412-54-4), a Stress-Cracking Agent—The internal pressure is controlled at a constant elevated level.
Note 1: There are environmental concerns regarding the disposal of Polyoxyethylated Nonylphenol (Nonylphenoxy poly(ethyleneoxy) ethanol (CAS 68412-54-4), for example, Igepal CO-630). Users are advised to consult their supplier or local environmental office and follow the guidelines provided for the proper disposal of this chemical.  
1.3 These procedures are not designed to test the propensity for environmental stress cracking in the neck of containers, such as when the neck is subjected to a controlled strain by inserting a plug.  
1.4 The values stated in SI units are to be regarded as standard.  
Note 2: There is no known ISO equivalent to this standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Section 8 and Note 1.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    6 pages
    English language
    sale 15% off
ASTM
ASTM D8501-23a(Specification)
Standard Classification System for and Basis for Specification for Unfilled Poly(Ether Ketone Ketone) (PEKK) Materials for Molding, Extrusion, Composites, Powder Coating and Additive Manufacturing

SCOPE
1.1 This specification covers poly(ether ketone ketone) materials, commonly referred to as PEKK, which are suitable for molding, extrusion, composites, powder coating and additive manufacturing. Only materials in this Class 6-8 are covered by this specification. This classification system provides requirements for the use of regrind or reprocessed materials.  
1.2 This specification covers thermoplastic resin materials supplied in pellet as well as powder form.  
1.3 This specification applies only to PEKK copolymers, without any additional fillers or inorganic additives, alloys, or treatments for modification of attributes.  
1.4 This classification system and subsequent line callout (specification) are intended to provide means of calling out poly(ether ketone ketone) materials used in the fabrication of end items or parts.  
1.5 Poly(ether ketone ketone) (PEKK) is a member of the poly (aryl ether ketone) or PAEK polymer family. PEKK has a broad range of repeat unit combinations of Isophthaloyl and Terephthaloyl repeat units. This standard classifies the polymer options.  
1.6 The values stated in SI units, as detailed in IEEE/ASTM S-10, are to be regarded as the standard. The values given in parentheses are for information only.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: There is no known ISO equivalent to this standard.
Note 2: PEKK is a thermoplastic polymer. Testing conditions can affect the technical results. Specimens prepared by techniques different than prescribed in this specification can have properties that vary from the values specified.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    7 pages
    English language
    sale 15% off
  • Technical specification
    7 pages
    English language
    sale 15% off
ASTM
ASTM D4440-23(Test Method)
Standard Test Method for Plastics: Dynamic Mechanical Properties Melt Rheology

SIGNIFICANCE AND USE
5.1 This test method provides a simple means of characterizing the important rheological properties and viscosity of thermoplastic polymers using very small amounts of material (approximately 25 to 50 mm in diameter by 1 to 3 mm in thickness ... approximately 3 to 5 g). Data are generally used for quality control, research and development, and establishment of optimum processing conditions.  
5.2 Dynamic mechanical testing provides a sensitive method for determining molten polymer properties by measuring the elastic and loss moduli as a function of frequency, strain, temperature, or time. Plots of viscosity, storage, and loss moduli, and tan delta as a function of the aforementioned process parameters provide graphical representation indicative of molecular weight, molecular weight distribution, effects of chain branching, and melt-processability for specified conditions.  
5.2.1 Observed data are specific to experimental conditions. Reporting in full (as described in this test method) the conditions under which the data was obtained is essential to assist users with interpreting the data an reconciling apparent or perceived discrepancies.  
5.3 Values obtained in this test method can be used to assess the following:  
5.3.1 Complex viscosity of the polymer melt as a function of dynamic oscillation,  
5.3.2 Processing viscosity, minimum as well as changes in viscosity as a function of experimental parameters,  
5.3.3 Effects of processing treatment,  
5.3.4 Relative polymer behavioral properties, including viscosity and damping, and  
5.3.5 Effects of formulation additives that might affect processability or performance.  
5.4 Before proceeding with this test method, refer to the specification for the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or combination thereof, covered in the relevant ASTM materials specification shall take precedence over those mentioned in the test method. If there are no r...
SCOPE
1.1 This test method outlines the use of dynamic mechanical instrumentation in determining and reporting the rheological properties of thermoplastic resins and other types of molten polymers. The method is useful for determining the complex viscosity and other significant viscoelastic characteristics of such materials as a function of frequency, strain amplitude, temperature, and time. It is known that fillers and other additives influence rheological properties.  
1.2 It incorporates a laboratory test method for determining the relevant rheological properties of a polymer melt subjected to various oscillatory deformations on an instrument of the type commonly referred to as a mechanical or dynamic spectrometer.  
1.3 This test method is intended to provide a means of determining the rheological properties of molten polymers, such as thermoplastics and thermoplastic elastomers over a range of temperatures by nonresonant, forced-vibration techniques. Plots of modulus, viscosity, and tan delta as a function of dynamic oscillation (frequency), strain amplitude, temperature, and time are indicative of the viscoelastic properties of a molten polymer.  
1.4 This test method is valid for a wide range of frequencies, typically from 0.01 Hz to 100 Hz.  
1.5 This test method is intended for homogenous and heterogeneous molten polymeric systems and composite formulations containing chemical additives, including fillers, reinforcements, stabilizers, plasticizers, flame retardants, impact modifiers, processing aids, and other important chemical additives often incorporated into a polymeric system for specific functional properties, and which could affect the processability and functional performance. These polymeric material systems have molten viscosities typically less than 106 Pa·s (107 poise).  
1.6 Test data obtained by this test method are relevant and appropriate for use in engineering design.  
1.7 The values stated in ...

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D6835-23(Classification)
Standard Classification System for Thermoplastic Elastomer-Ether-Ester Molding and Extrusion Materials (TEEE)

SCOPE
1.1 This classification system covers segmented block copolyether-ester elastomers suitable for molding and extrusion.  
1.2 This classification system allows for the use of segmented block copolyether-ester elastomers that are recycled provided that the requirements as stated in this classification system are met. The proportions of recycled material used, as well as the nature and amount of any contaminant, however, cannot be covered practically in this specification.  
1.3 The properties included in this classification system are those required to identify the compositions covered. It is possible that there are other requirements necessary to identify particular characteristics important to specialized applications. One way of specifying them is by using the suffixes as given in Section 5.  
1.4 This classification system and subsequent line callout (specification) are intended to provide a means of calling out plastic materials used in the fabrication of end items or parts. It is not intended for the selection of materials. Material selection is best made by those having expertise in the plastic field after careful consideration of the design and the performance required of the part, the environment to which it will be exposed, the fabrication process to be employed, the costs involved, and the inherent properties of the material other than those covered by this classification system.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.6 The following precautionary caveat pertains only to the test methods portion, Section 11, of this classification system. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This standard, ISO 20029-1, and ISO 20029-2 address the same subject matter, but differ in technical content.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D2463-23(Test Method)
Standard Test Method for Drop Impact Resistance of Blow-Molded Thermoplastic Containers

SIGNIFICANCE AND USE
5.1 These procedures provide a means to assess the drop impact resistance of the group or lot of blown containers from which the test specimens were selected.  
5.2 It is acceptable to use these procedures for routine inspection purposes.  
5.3 These procedures will evaluate the combined effect of construction, materials, and processing conditions on the impact resistance of the blown containers.  
5.4 Before proceeding with this test method, reference the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or combination thereof, covered in the materials specification shall take precedence over those mentioned in this test method. If there are no material specifications, then the default conditions apply.
SCOPE
1.1 This test method provides a means to assess the drop impact resistance of water-filled, blow-molded thermoplastic containers, which is a summation of the effects of material, manufacturing conditions, container design, and perhaps other factors.  
1.2 Two procedures are provided as follows:  
1.2.1 Procedure A, Static Drop Height Method—This procedure is particularly useful for quality control since it is quick.  
1.2.2 Procedure B, Bruceton Staircase Method—This procedure is used to determine the mean failure height and the standard deviation of the distribution.  
1.3 The values stated in SI units are to be regarded as standard. The inch-pound units given in parentheses are for information only.  
Note 1: There is no known ISO equivalent to this standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM D3030-23(Test Method)
Standard Test Method for Volatile Matter (Including Water) of Vinyl Chloride Resins

SIGNIFICANCE AND USE
5.1 The quantity of volatile components in a vinyl chloride resin can be established by this test method. This test method does not identify the components.
SCOPE
1.1 This test method covers the quantitative determination of the volatile matter (including water) present in vinyl chloride resins.  
1.2 The values stated in SI units are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: This test method is identical ISO 1269.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D3275-18(2023)(Classification)
Standard Classification System for E-CTFE-Fluoroplastic Molding, Extrusion, and Coating Materials

ABSTRACT
This classification system covers melt processible molding, extrusion, and coating materials of ethylene-chlorotrifluoroethylene (E-CTFE) fluoroplastics. The resin is a copolymer of ethylene and chlorotrifluoroethylene. The classification of ECTFE materials into groups in accordance with their physical appearance, and further into classes based on melt flow rate, is provided. The test specimens shall be subjected to tests to determine their melt flow rate, melting endotherm peak, specific gravity, tensile property, dielectric constant and dissipation factor, and oxygen index.
SCOPE
1.1 This classification system covers melt processible molding, extrusion, and coating materials of ethylene-chlorotrifluoroethylene (E-CTFE) fluoroplastics. The resin is a copolymer of ethylene and chlorotrifluoroethylene containing approximately 80 weight % of chlorotrifluoroethylene.  
1.2 The values stated in SI units, as detailed in IEEE/ASTM SI-10, are to be regarded as standard.  
1.3 The following precautionary statement pertains only to the test methods portion, Section 11 of this classification system. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Although this classification system and ISO 20568-1 and ISO 20568-2 differ in approach or detail, data obtained using either are technically equivalent.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    4 pages
    English language
    sale 15% off
ASTM
ASTM D4878-23(Test Method)
Standard Test Methods for Polyurethane Raw Materials: Determination of Viscosity of Polyols

SIGNIFICANCE AND USE
4.1 These test methods are suitable for research or as quality control or specification tests.  
4.2 Viscosity measures the resistance of a fluid to uniformly continuous flow without turbulence or other forces.
SCOPE
1.1 These test methods (A and B) determine the viscosity of polyols in the range from 10 to 100 000 mPa·s(cP) at 25°C. Test Method A is a rotational procedure for determining dynamic viscosity. Test Method B is a general procedure for kinematic viscosity of transparent polyols. (See Note 1.)  
1.2 The values stated in SI units are to be regarded as the standard. Other equivalent units are provided because of current common usage.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: Test Method A is equivalent to ISO 3219. Test Method B is equivalent to ISO 3104.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off