ASTM B536-07(2013)

Standard Specification for Nickel-Iron-Chromium-Silicon Alloys (UNS N08330 and N08332) Plate, Sheet, and Strip

ABSTRACT
This specification covers nickel-iron-chromium-silicon alloys (UNS N08330 and N08332) plate, sheet, and strip intended for heat resisting applications and general corrosive service. The alloy UNS N08830 and UNS N08332 shall be annealed at a certain temperature. The material shall conform to the chemical composition requirements prescribed by the reference material. The tensile properties of the material at room temperature shall conform to the reference material. The annealed alloy UNS N08332 shall conform to an average grain size, there are no grain size requirements for UNS N08330.
SCOPE
1.1 This specification covers nickel-iron-chromium silicon alloys (UNS N08330 and UNS N08332)* plate, sheet, and strip intended for heat resisting applications and general corrosive service.  
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 31-Jan-2013
• ICS: 77.150.40 - Nickel and chromium products
• Technical Committee: B02 - Nonferrous Metals and Alloys
• Drafting Committee: B02.07 - Refined Nickel and Cobalt and Their Alloys

Relations

• Replaces: ASTM B536-07 - Standard Specification for Nickel-Iron-Chromium-Silicon Alloys (UNS N08330 and N08332) Plate, Sheet, and Strip
• Effective Date: 01-Feb-2013
• Replaced By: ASTM B536-19 - Standard Specification for Nickel-Iron-Chromium-Silicon Alloys Plate, Sheet, and Strip
• Effective Date: 01-Apr-2019
• Referred By: ASTM B511/B511M-21 - Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Bars and Shapes
• Effective Date: 01-Feb-2013
• Referred By: ASTM B474/B474M-19 - Standard Specification for Electric Fusion Welded Nickel and Nickel Alloy Pipe
• Effective Date: 01-Feb-2013
• Referred By: ASTM B710-20ae1 - Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Welded Pipe
• Effective Date: 01-Feb-2013
• Referred By: ASTM B366/B366M-23 - Standard Specification for Factory-Made Wrought Nickel and Nickel Alloy Fittings
• Effective Date: 01-Feb-2013
• Referred By: ASTM B906-22 - Standard Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and Strip
• Effective Date: 01-Feb-2013
• Referred By: ASTM B546-19 - Standard Specification for Electric Fusion-Welded Ni-Cr-Co-Mo Alloy, Ni-Fe-Cr-Si Alloy, Ni-Cr-Fe-Al Alloy, Ni-Cr-Fe Alloy, and Ni-Cr-Fe-Si Alloy Pipe
• Effective Date: 01-Feb-2013
• Referred By: ASTM B739-03(2023) - Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Welded Tube
• Effective Date: 01-Feb-2013

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:B536 −07 (Reapproved 2013)
Standard Specification for
Nickel-Iron-Chromium-Silicon Alloys (UNS N08330 and
N08332) Plate, Sheet, and Strip
This standard is issued under the fixed designation B536; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope* 3. Terminology
1.1 This specification covers nickel-iron-chromium silicon 3.1 Terms shall be defined in accordance with Terminology
alloys(UNSN08330andUNSN08332)*plate,sheet,andstrip B899.
intended for heat resisting applications and general corrosive
service. 4. General Requirements
1.2 The values stated in inch-pound units are to be regarded
4.1 Material furnished under this specification shall con-
as standard. The values given in parentheses are mathematical form to the requirements of Specification B906 unless other-
conversions to SI units that are provided for information only
wise provided herein. In the case of conflict, the requirements
and are not considered standard. of this specification shall take precedence.
1.3 This standard does not purport to address all of the
5. Material and Manufacture
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to become familiar
5.1 Annealing Temperature—Alloy UNS N08330 shall be
with all hazards including those identified in the appropriate
annealed at 1900°F (1040°C) minimum. Alloy UNS N08332
Material Safety Data Sheet (MSDS) for this product/material
shall be annealed at 2100°F (1150°C) minimum.
as provided by the manufacturer, to establish appropriate
safety and health practices, and determine the applicability of
6. Chemical Composition
regulatory limitations prior to use.
6.1 The material shall conform to the requirements as to
chemical composition specified in Table 1.
2. Referenced Documents
2.1 ASTM Standards:
7. Mechanical and Other Properties
B899 Terminology Relating to Non-ferrous Metals and Al-
7.1 The tensile properties of the material at room tempera-
loys
ture shall conform to those shown in Table 2.
B906 Specification for General Requirements for Flat-
Rolled Nickel and Nickel Alloys Plate, Sheet, and Strip
7.2 Grain Size—Annealed alloy UNS N08332 shall con-
form to an average grain size ofASTM No. 5 or coarser. There
are no grain size requirements for UNS N08330.
This specification is under the jurisdiction of ASTM Committee B02 on
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee
B02.07 on Refined Nickel and Cobalt and Their Alloys.
8. Permissible Variations in Dimensions and Weight
Current edition approved Feb. 1, 2013. Published February 2013. Originally
approved in 1970. Last previous edition approved in 2007 as B536 – 07. DOI:
8.1 The tolerances and permissible variations provided in
10.1520/B0536-07R13.
Annex A1, Permissible Variations in Dimensions, Etc.–Inch-
* New designation established in accordance withASTM E527 and SAE J1086,
Pound (SI) Units, of Specification B906 shall apply.
Practice for Numbering Metals and Alloys (UNS).
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
9. Keywords
Standards volume information, refer to the standard’s Document Summary page on
the ASTM website. 9.1 N08330; N08332; plate; sheet; strip
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
B536−07 (2013)
TABLE 1 Chemical Requirements
Composition
Element
Limits, %
A
C .
Mn 2.00 max
P 0.03 max
S 0.03 max
Si 0.75–1.50
Cr 17.0–20.0
Ni 34.0–37.0
Cu 1.00 max
Pb 0.005 max
Sn 0.025 max
B
Fe remainder
A
Alloy UNS N08330: 0.08 max
Alloy UNS N08332: 0.05–0.10
B
Element shall be determined arithmetically by difference.
TABLE 2 Mechanical Properties
Elongation
Tensile Strength, Yield Strength, 0.2 % in 2 in. or 50
A
Alloy Condition Hardness
min, psi (MPa) offset, min, psi (MPa) mm, or 4D,
min, %
UNS N08330 annealed 70 000 (483) 30 000 (207) 30 70 to 90 HRB
UNS N08332 annealed 67 000 (462) 27 000 (186) 30 65 to 88 HRB
A
Hardness values are informative only and not to be constructed as the basis for acceptance.
APPENDIX
(Nonmandatory Information)
X1. FINISHES
polished rolls. This is a general purpose cold-rolled finish. It is commonly
X1.1 Scope—This appendix lists the finishes in which plate,
used for all but exceptionally difficult deep drawing application. This
sheet, and strip are normally supplied. These are subject to
finish is more readily polished than No. 1 or No. 2D finish.
change and the manufacturer should be consulted for the latest
Bright-Annealed Finish—A bright cold-rolled highly reflective finish
information available.
retained by final annealing in a controlled atmosphere furnace. The
purpose of the atmosphere is to prevent scaling or oxidatio
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: B536 − 07 B536 − 07 (Reapproved 2013)
Standard Specification for
Nickel-Iron-Chromium-Silicon Alloys (UNS N08330 and
N08332) Plate, Sheet, and Strip
This standard is issued under the fixed designation B536; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope*
1.1 This specification covers nickel-iron-chromium silicon alloys (UNS N08330 and UNS N08332)* plate, sheet, and strip
intended for heat resisting applications and general corrosive service.
1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information
only.mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data
Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and
determine the applicability of regulatory limitations prior to use.
2. Referenced Documents
2.1 ASTM Standards:
B899 Terminology Relating to Non-ferrous Metals and Alloys
B906 Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and Strip
3. Terminology
3.1 Terms shall be defined in accordance with Terminology B899.
4. General Requirements
4.1 Material furnished under this specification shall conform to the requirements of Specification B906 unless otherwise
provided herein. In the case of conflict, the requirements of this specification shall take precedence.
5. Material and Manufacture
5.1 Annealing Temperature—Alloy UNS N08330 shall be annealed at 1900°F (1040°C) minimum. Alloy UNS N08332 shall be
annealed at 2100°F (1150°C) minimum.
6. Chemical Composition
6.1 The material shall conform to the requirements as to chemical composition specified in Table 1.
7. Mechanical and Other Properties
7.1 The tensile properties of the material at room temperature shall conform to those shown in Table 2.
7.2 Grain Size—Annealed alloy UNS N08332 shall conform to an average grain size of ASTM No. 5 or coarser. There are no
grain size requirements for UNS N08330.
This specification is under the jurisdiction of ASTM Committee B02 on Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee B02.07 on Refined
Nickel and Cobalt and Their Alloys.
Current edition approved May 1, 2007Feb. 1, 2013. Published June 2007February 2013. Originally approved in 1970. Last previous edition approved in 20022007 as
B536 – 02.B536 – 07. DOI: 10.1520/B0536-07.10.1520/B0536-07R13.
* New designation established in accordance with ASTM E527 and SAE J1086, Practice for Numbering Metals and Alloys (UNS).
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
B536 − 07 (2013)
TABLE 1 Chemical Requirements
Composition
Element
Limits, %
A
C .
Mn 2.00 max
P 0.03 max
S 0.03 max
Si 0.75–1.50
Cr 17.0–20.0
Ni 34.0–37.0
Cu 1.00 max
Pb 0.005 max
Sn 0.025 max
B
Fe remainder
A
Alloy UNS N08330: 0.08 max
Alloy UNS N08332: 0.05–0.10
B
Element shall be determined arithmetically by difference.
TABLE 2 Mechanical Properties
Elongation
Tensile Strength, Yield Strength, 0.2 % in 2 in. or 50
A
Alloy Condition Hardness
min, psi (MPa) offset, min, psi (MPa) mm, or 4D,
min, %
UNS N08330 annealed 70 000 (483) 30 000 (207) 30 70 to 90 HRB
UNS N08332 annealed 67 000 (462) 27 000 (186) 30 65 to 88 HRB
A
Hardness values are informative only and not to be constructed as the basis for acceptance.
8. Permissible Variations in Dimensions and Weight
8.1 The tolerances and permissible variations provided in Annex A1, Permissible Variations in Dimensions, Etc.–Inch-Pound
(SI) Units, of Specification B906 shall apply.
9. Keywords
9.1 N08330; N08332; plate; sheet; strip
APPENDIX
(Nonmandatory Information)
X1. FINISHES
X1.1 Scope—This appendix lists the finishes in which plate, sheet, and strip are normally supplied. These are subject to change
and the manufacturer should be consulted for the latest information available.
X1.2 Sheet—The various types of finish procurable on sheet products are:
X1.2.1 No. 1 Finish—Hot-rolled, annealed, and descaled.
X1.2.2 No. 2D Finish—Dull, cold-rolled finish.
X1.2.3 No. 2B Finish—Bright, cold-rolled finish.
X1.2.3.1 Bright-
...