ASTM D2941-13

Standard Test Method for Measuring Break Pattern of Leather (Break Scale)

SIGNIFICANCE AND USE
4.1 Break depends on the fiber structure and on the relation between the grain and other strata of the leather. A fine break, or a grain pattern which shows many fine wrinkles when it is bent to form a concave surface, as it is in the vamp of a shoe, reflects favorably upon appearance and serviceability. A coarse break, on the other hand, where a few coarse wrinkles are formed on bending the grain to form a concave surface may indicate that the grain layer is separating from the corium or main stratum as in pipey leather. Shoes made from fine-break leather are more attractive and tend to wear longer than shoes made from coarse-break leather. (See MIL-STD 663 and the ALCA Journal).4
SCOPE
1.1 This test method covers the measurement of the break pattern of shoe upper leather using an arbitrary break scale. This test method does not apply to wet blue.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 30-Apr-2013
• ICS: 59.140.30 - Leather and furs
• Technical Committee: D31 - Leather
• Drafting Committee: D31.03 - Footwear

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D2941 − 13
Standard Test Method for
1
Measuring Break Pattern of Leather (Break Scale)
This standard is issued under the fixed designation D2941; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope 3.2 For definitions of other terms used in this test method,
refer to Terminology D1517.
1.1 This test method covers the measurement of the break
pattern of shoe upper leather using an arbitrary break scale.
4. Significance and Use
This test method does not apply to wet blue.
4.1 Break depends on the fiber structure and on the relation
1.2 The values stated in inch-pound units are to be regarded
between the grain and other strata of the leather. A fine break,
as standard. The values given in parentheses are mathematical
or a grain pattern which shows many fine wrinkles when it is
conversions to SI units that are provided for information only
bent to form a concave surface, as it is in the vamp of a shoe,
and are not considered standard.
reflects favorably upon appearance and serviceability.Acoarse
1.3 This standard does not purport to address all of the
break, on the other hand, where a few coarse wrinkles are
safety concerns, if any, associated with its use. It is the
formed on bending the grain to form a concave surface may
responsibility of the user of this standard to establish appro-
indicate that the grain layer is separating from the corium or
priate safety and health practices and determine the applica-
main stratum as in pipey leather. Shoes made from fine-break
bility of regulatory limitations prior to use.
leather are more attractive and tend to wear longer than shoes
made from coarse-break leather. (See MIL-STD 663 and the
2. Referenced Documents 4
ALCA Journal).
2
2.1 ASTM Standards:
5,6
5. Apparatus
D1517 Terminology Relating to Leather
D1610 Practice for Conditioning Leather and Leather Prod-
5.1 Satra Mandrel, consisting of two windows or hollows.
ucts for Testing
5.2 Satra Visual Break Scale, consisting of eight levels of
3
2.2 MIL Standard:
break ranging from 1, fine, to 8, coarse.
MIL-STD 663 Visual Inspection Guide for Footwear Upper
Leather
6. Test Specimen
6.1 The sample for the test should be taken from an agreed
3. Terminology
area of the hide, and shall be a piece of leather 2 by 4 in. (51
3.1 Definitions:
by 102 mm) with the long dimension perpendicular to the
3.1.1 break (of leather)—the pattern of wrinkles formed on
backbone; or a cut shoe part.
the grain surface of upper leather when it is bent grain in to
6.2 Unless otherwise specified, one specimen shall be tested
form a concave surface. This characteristic is observed in the
from each sample.
vamp of the shoe in walking. For this reason this test method
is primarily intended for evaluation of cut parts.
7. Conditioning
7.1 AllspecimensshallbeconditionedaccordingtoPractice
1
This test method is under the jurisdiction ofASTM Committee D31 on Leather
D1610.
and is the direct responsibility of Subcommittee D31.03 on Footwear. This test
method was developed in cooperation with the American Leather Chemists Assn.
(Standard Method E64 – 1972).
4
Current edition approved May 1, 2013. Published May 2013. Originally Bailey, M., Journal of the American Leather Chemists Association, JALCA,
approved in 1970. Last previous edition approved in 2012 as D2941 – 00(2012). Vol 53, 1958, p. 568.
5
DOI: 10.1520/D2941-13. Landmann, A. W., and Thompson, R. S., Journal of the Society of Leather
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or Trades Chemists, JSLTC, Vol 47, 1963, p. 429.
6
contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM The sole source of supply of the Satra mandrel and visual break scale known
Standards volume information, refer to the standard’s Document Summary page on to the committee at this time is the Shoe and Allied Trades Research Assn.,
the ASTM website. Kettering, England. If you are aware of alternative suppliers, please provide this
3
Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, information to ASTM Headquarters. Your comments will receive careful consider-
1
Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098 ation at a meeting of the responsible technical committee, which you may attend.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D2941 − 13
1
8. Procedure 9.1.2 The rating to the nearest ⁄2-grade.
8.1 With long dimens
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: D2941 − 00 (Reapproved 2012) D2941 − 13
Standard Test Method for
1
Measuring Break Pattern of Leather (Break Scale)
This standard is issued under the fixed designation D2941; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the Department of Defense.
1. Scope
1.1 This test method covers the measurement of the break pattern of shoe upper leather using an arbitrary break scale. This test
method does not apply to wet blue.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical
conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility
of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory
limitations prior to use.
2. Referenced Documents
2
2.1 ASTM Standards:
D1517 Terminology Relating to Leather
D1610 Practice for Conditioning Leather and Leather Products for Testing
3
2.2 MIL Standard:
MIL-STD 663 Visual Inspection Guide for Footwear Upper Leather
3. Terminology
3.1 Definitions:
3.1.1 break (of leather)—the pattern of wrinkles formed on the grain surface of upper leather when it is bent grain in to form
a concave surface. This characteristic is observed in the vamp of the shoe in walking. For this reason this test method is primarily
intended for evaluation of cut parts.
3.2 For definitions of other terms used in this test method, refer to Terminology D1517.
4. Significance and Use
4.1 Break depends on the fiber structure and on the relation between the grain and other strata of the leather. A fine break, or
a grain pattern which shows many fine wrinkles when it is bent to form a concave surface, as it is in the vamp of a shoe, reflects
favorably upon appearance and serviceability. A coarse break, on the other hand, where a few coarse wrinkles are formed on
bending the grain to form a concave surface may indicate that the grain layer is separating from the corium or main stratum as
in pipey leather. Shoes made from fine-break leather are more attractive and tend to wear longer than shoes made from coarse-break
4
leather. (See MIL-STD 663 and the ALCA Journal).
1
This test method is under the jurisdiction of ASTM Committee D31 on Leather and is the direct responsibility of Subcommittee D31.03 on Footwear. This test method
was developed in cooperation with the American Leather Chemists Assn. (Standard Method E64 – 1972).
Current edition approved Sept. 1, 2012May 1, 2013. Published September 2012May 2013. Originally approved in 1970. Last previous edition approved in 20082012 as
D2941 – 00(2008).(2012). DOI: 10.1520/D2941-00R12.10.1520/D2941-13.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
3
Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098
4
Bailey, M., Journal of the American Leather Chemists Association, JALCA, Vol 53, 1958, p. 568.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D2941 − 13
5,6
5. Apparatus
5.1 Satra Mandrel, consisting of two windows or hollows.
5.2 Satra Visual Break Scale, consisting of eight levels of break ranging from 1, fine, to 8, coarse.
6. Test Specimen
6.1 The sample for the test should be taken from an agreed area of the hide, and shall be a piece of leather 2 by 4 in. (51 by
102 mm) with the long dimension perpendicular to the backbone; or a cut shoe part.
6.2 Unless otherwise specified, one specimen shall be tested from each sample.
7. Conditioning
7.1 All specimens shall be conditioned according to Practice D1610.
8. Procedure
8.1 With long dimension of the specimen parallel to the length of the mandrel, bend it with thumb and fingers to bring it into
contact with the outside of the mandrel, and observe the wrinkles through the windows.
...